CN1970676A - Macromolecule water-proof cloth and producing process thereof - Google Patents
Macromolecule water-proof cloth and producing process thereof Download PDFInfo
- Publication number
- CN1970676A CN1970676A CN 200510032419 CN200510032419A CN1970676A CN 1970676 A CN1970676 A CN 1970676A CN 200510032419 CN200510032419 CN 200510032419 CN 200510032419 A CN200510032419 A CN 200510032419A CN 1970676 A CN1970676 A CN 1970676A
- Authority
- CN
- China
- Prior art keywords
- cloth
- stone
- macromolecule water
- cement modifier
- proof cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a macromolecular jaconet 1, which consists of macromolecular cement modifier 2 and a layer of stone-seed stone 3. the making method comprises the following steps: (1) coating macromolecular cement modifier 2 on the cloth 1; (2) transmitting into drier to bake under 80-120 deg.c; (3) solidifying; (4) covering a layer of stone-seed stone 3; squeezing through heating power. The cloth 1 can be nylon thread cloth. The macromolecular cement modifier 2 is VAE water-proof glue.
Description
Technical field
The present invention relates to a kind of material of construction, the especially a kind of water-proof thermal insulation material macromolecule water-proof cloth of textile fabric making and its making method utilized.
Background technology
At present the used water-proof material of construction market is more asphalt felt paper material or cold water-proof material and hot waterproof roll.Wherein the asphalt felt paper material is made and the construction serious environment pollution, and product is not ageing-resistant, and work-ing life is short; And cold water-proof material and hot waterproof roll, though many advantages are arranged, work-ing life is longer, high-and low-temperature resistance is anti-aging.But its sizing material is inflammable, and storage period is short, and smell stimulates, construction inconvenience, and expense is higher, and needs two kinds of materials are closely bonded on waterproof matrix when using.When basal plane ftractureed, water-proof material ftractureed thereupon.Because material is airtight, be bonded in basal plane after, water evaporates is split its foaming, drum.
Summary of the invention
The technical problem to be solved in the present invention is, the defective at prior art exists provides a kind of not only water-tolerant, good waterproof performance, and good mechanical stability, low-temperature stability might as well the water-proof thermal insulation material macromolecule water-proof cloth.
Technical solution of the present invention is that described macromolecule water-proof cloth as shown in Figure 1, has ply stratum 1, is coated with one deck high-molecular cement modifier 2 on the cloth 1, is coated with one deck stone-seed stone 3 on this layer high-molecular cement modifier 2.
The making method of above-mentioned macromolecule water-proof cloth is following processing step:
(1), use coating machine that high-molecular cement modifier 2 is spread upon on the cloth 1;
(2), the cloth 1 that will be coated with high-molecular cement modifier 2 is sent into baking in the dryer, 80～120 ℃ of storing temperatures;
(3), adopt solidifying agent that the work in-process after drying are cured processing;
(4), on the work in-process after the solidification treatment, cover one deck stone-seed stone 3, use laminator heating power extruding promptly becoming macromolecule water-proof cloth finished product of the present invention.
Above-mentioned cloth 1 generally selects for use POLYAMIDE YARNS to weave cotton cloth.It is the VAE waterproof glue of main constitutive material that high-molecular cement modifier 2 adopts the VAE emulsion.。
The using method of macromolecule water-proof cloth of the present invention is simple, during construction, only needs above-mentioned finished product macromolecule water-proof cloth is bedded in basal plane for example on building roof or other soil layer.On waterproof cloth, lay a bed thickness 3～10mm concrete again, which kind of engineering no matter, only this secondary WATER REPELLENT gets final product.
The invention has the beneficial effects as follows: the main constitutive material VAE of the high-molecular cement modifier of employing emulsion has good water tolerance, and resistance to acids and bases and weathering resistance, tensile strength are 50 times of normal waterproof material.And have premium propertiess such as anti-aging stability and permanent flexibility.Can be widely used in heavy constructions such as water surface room, culvert, dykes and dams.And the price of VAE emulsion is cheap than ACRYLIC EMULSION, has only 1/3rd of developed country's like product present price such as U.S., and is therefore cheap, has vast market prospect.
Description of drawings:
Fig. 1 is the structural representation of an embodiment of macromolecule water-proof cloth of the present invention, is denoted as among the figure:
The 1-cloth,
The 2-high-molecular cement modifier,
The 3-stone-seed stone.
Embodiment:
Embodiment 1, and referring to Fig. 1, the macromolecule water-proof cloth of present embodiment is weaved cotton cloth as the commercially available common POLYAMIDE YARNS of cloth 1 employing of bottom; High-molecular cement modifier 2 adopts the commercially available changde, hunan rising sun to rise the VAE waterproof glue that chemical industry Industrial Co., Ltd. produces.This VAE waterproof glue product is a kind of white emulsion agent that is composited by ethene and vinyl acetate between to for plastic and multiple auxiliary.Can obtain excellent mechanical property and can realize modification thereby act on concrete and sand-cement slurry, make the shock resistance of the thing that is modified, flexural capacity improve 4～6 times.The 3rd layer is the top layer that one deck stone-seed stone 3 constitutes.Use coating machine that above-mentioned VAE waterproof glue is spread upon POLYAMIDE YARNS and weave cotton cloth on the cloth 1, then, the cloth 1 that this layer is coated with the VAE waterproof glue is sent in the dryer and is toasted 100 ℃ of storing temperatures.Work in-process after the oven dry adopt the stone-seed stone polymkeric substance to be cured processing, cover one deck stone-seed stone 3 after the solidification treatment, use at last the extruding of laminator heating power macromolecule water-proof cloth certified products of the present invention.
Embodiment 2, and commercially available industrial regeneration polyamide fibre canvas is a ply stratum 1; Storing temperature transfers to 110 ℃ in the dryer, and all the other are with embodiment 1.
The macromolecule water-proof cloth of the present invention of Gou Chenging is proved to be respond well through manufacturing experimently to try out thus, aspects excellent performances such as water tolerance, water-repellancy, mechanical stability and low-temperature stability, be a kind of antiseep, tension, wear-resisting, waterproof cloth that erosion resistance is extremely strong, work-ing life was above 100 years.Through embankment bank protection, motorway, culvert, airport, divert water from the south to the north project and the checking of multinomial civil building engineering, adhere to specification fully.
Claims (4)
1, a kind of macromolecule water-proof cloth has ply stratum (1), it is characterized in that, is coated with one deck high-molecular cement modifier (2) on the described cloth (1), is coated with one deck stone-seed stone (3) on the high-molecular cement modifier (2).
2, macromolecule water-proof cloth according to claim 1 is characterized in that, described cloth (1) is weaved cotton cloth for POLYAMIDE YARNS.
3, macromolecule water-proof cloth according to claim 1 is characterized in that, described high-molecular cement modifier (2) is the VAE waterproof glue.
4, the making method of the described macromolecule water-proof cloth of a kind of claim 1 is characterized in that, this method is following processing step:
(1), use coating machine that high-molecular cement modifier (2) is spread upon on the cloth (1),
(2), the cloth (1) that will be coated with high-molecular cement modifier (2) sends into baking in the dryer, 80～120 ℃ of storing temperatures,
(3), the work in-process after adopting solidifying agent to oven dry are cured processing,
(4), on the work in-process after the solidification treatment, cover one deck stone-seed stone (3), use laminator heating power extruding promptly becoming macromolecule water-proof cloth finished product of the present invention.