CN1970625A - Polyurethane elastic terrace material - Google Patents
Polyurethane elastic terrace material Download PDFInfo
- Publication number
- CN1970625A CN1970625A CN 200610069592 CN200610069592A CN1970625A CN 1970625 A CN1970625 A CN 1970625A CN 200610069592 CN200610069592 CN 200610069592 CN 200610069592 A CN200610069592 A CN 200610069592A CN 1970625 A CN1970625 A CN 1970625A
- Authority
- CN
- China
- Prior art keywords
- polyurethane elastic
- elastic terrace
- silicate
- polyvalent alcohol
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyurethane elastic terrace material, which comprises the following parts: 35-45% polyol, 15-25% liquid isochloric acid ester, 5-10% nanometer material, 5-15% magnesium silicate, 5-15% tricalcium silicate, 1-3% dibutyl phosphonate, 4-8% dye, 2-5% polyethylene wax, 3-6% dihydroxybutane and 1-2% ester.
Description
Technical field
The present invention relates to a kind of floor material, specifically is a kind of polyurethane elastic terrace material.
Background technology
The floor material that uses is that material cement, sand and small amounts of additives stir, mix composition at present, and its defective is easy cracking, plays dirt, dusting, lacks flexibility, and is difficult to satisfy terrace service requirementss such as factory building, laboratory, office, room.
Summary of the invention
Purpose of the present invention is exactly the defective that exists at prior art, and a kind of intensity height, elasticity is strong, tensile strength is good polyurethane elastic terrace material are provided.
Its technical scheme is: the raw material that comprises following weight ratio is formed: polyvalent alcohol 35-45%, liquefaction different chlorate 15-25%, nano material 5-10%, Magnesium Silicate q-agent 5-15%, tricalcium silicate 5-15%, dibutyl phosphate 1-3%, pigment 4-8%, Ployethylene Wax 2-5%, dihydroxyl butane 3-6%, ester class 1-2%.
Preferred plan is made up of the raw material of following weight ratio: polyvalent alcohol 40%, the different chlorate 20% of liquefaction, nano material 5%, Magnesium Silicate q-agent 10%, tricalcium silicate 10%, dibutyl phosphate 2%, pigment 5%, Ployethylene Wax 3%, dihydroxyl butane 4%, ester class 1%.
Material of the present invention has 2 times that very strong sticking power, elasticity are strong, tensile strength is general resilient material, firm, durable, environmental protection after construction.Terraces such as the factory building of having relatively high expectations in suitable multiple ground, laboratory, office, room use.
Specific embodiment
Composition of raw materials sees the following form
| The formula materials title | Specification | Ratio range | Function |
| Polyvalent alcohol | Liquid | 40％ | The soft bubble of elasticity |
| Nano material | Pressed powder | 5％ | Strengthen, resist solarization, frost prevention |
| The different chlorate (import) of liquefying | Liquid | 20％ | Gain in strength, elasticity, environmental protection |
| Magnesium Silicate q-agent | Pressed powder | 10％ | Filler |
| Tricalcium silicate | Pressed powder | 10％ | Filler |
| Dibutyl phosphate | Liquid | 2％ | Auxiliary agent, increase surface treatment |
| Pigment (import) | Pressed powder | 5％ | Toning |
| Ployethylene Wax | Liquid | 3％ | Prevent sedimentation |
| The dihydroxyl butane | Liquid | 4％ | Increase elasticity |
| The ester class | Liquid | 1％ | Dilution elasticity |
Production technique: polyvalent alcohol is placed in the electrical heating type reactor, connect power supply and be heated to 100-120 ℃ of temperature vacuum hydro-extraction 30 minutes.Place shredder to grind in proportion 15-20 minute pigment and water simultaneously, palpus two times.Then ground mill base is added the reactor that fills polyvalent alcohol and fully stir 1.5 hours to color even, no color differnece, the cooling blowing is stand-by.Other dry powder filler mixing 15-20 minute is to evenly, and is stand-by.
Different chlorate is placed in the reactor, be heated to 90-95 ℃ and fully reacted 3-4 hour, dry powder filler after will stirring then and liquid adjuvants thereof add stirring 2 hours, and extremely evenly, cooling discharge is stand-by then.
Technical indicator: (videing infra)
| Project | Index |
| Rebound resilience | ≥35％ |
| Hardness (Shao Shi) | 73 |
| The compression recovery rate | ≥95％ |
| Tensile strength | 2.8Mpa |
| Tensile yield | ≥256％ |
| Fire-retardant | 1 grade |
Material in the above-mentioned prescription not only limits therewith, and the purposes of middle prompting can also adopt other identical material of function to replace to specifications.
Claims (2)
1, a kind of polyurethane elastic terrace material is characterized in that comprising that the raw material of following weight ratio is formed: polyvalent alcohol 35-45%, liquefaction different chlorate 15-25%, nano material 5-10%, Magnesium Silicate q-agent 5-15%, tricalcium silicate 5-15%, dibutyl phosphate 1-3%, pigment 4-8%, Ployethylene Wax 2-5%, dihydroxyl butane 3-6%, ester class 1-2%.
2, polyurethane elastic terrace material according to claim 1 is characterized in that: the raw material that comprises following weight ratio is formed: polyvalent alcohol 40%, the different chlorate 20% of liquefaction, nano material 5%, Magnesium Silicate q-agent 10%, tricalcium silicate 10%, dibutyl phosphate 2%, pigment 5%, Ployethylene Wax 3%, dihydroxyl butane 4%, ester class 1%.