CN1962788A - Refractory adhesive - Google Patents
Refractory adhesive Download PDFInfo
- Publication number
- CN1962788A CN1962788A CN 200510100895 CN200510100895A CN1962788A CN 1962788 A CN1962788 A CN 1962788A CN 200510100895 CN200510100895 CN 200510100895 CN 200510100895 A CN200510100895 A CN 200510100895A CN 1962788 A CN1962788 A CN 1962788A
- Authority
- CN
- China
- Prior art keywords
- weight part
- adhesive
- weight parts
- weight
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a new fire-proof adhesive, which is characterized by the following: adopting neoprene adhesive, 210, 2402 typed resin as basic material; making ethinyltrichloride and carrene as solvent; adding fitful magnesia, aging-proof agent to allocate under normal temperature; obtaining the product with cutting strength at 402N/cm2 without combusting; solidifying rapidly; fitting for bonding cotton canvas core, vinylon and nylon transmission band adaptor as well as rubber, fiber, cotton fabric, leather, bamboo, decorative material and partial plastic.
Description
The present invention relates to a kind of novel refractory adhesive.
At present, be used for the bonding tackiness agent of conveying band joint two classes roughly arranged:
One class is the normal temperature cured type tackiness agent, though this tackiness agent has the cohesive strength height, but it belongs to inflammable articles, is not suitable for emphasis fire prevention units such as colliery, thermal power plant and uses; Advantages such as another kind of is the heat vulcanization type tackiness agent, and strength of joint is big though this tackiness agent has, life cycle is long, need shortcoming high temperature vulcanized, that joint is made and curing time is long also fairly obvious at complex process.
Purpose of the present invention just provides that a kind of not only to have cohesive strength higher, and can meet the non-combustible novel refractory adhesive of naked light, be specially adapted to the colliery, the bonding refractory adhesives of conveying band joint such as the cotton duck core of emphasis such as firepower electrical plant fire prevention unit, polyvinyl, nylon.
Realize that technical scheme of the present invention is: by containing (1) neoprene latex 90-125 weight part, (2) 210 type resin 14-30 weight parts (3) 2402 type resin 5-10 weight part (4) trieline 400-750 weight part (5) methylene dichloride 150-250 weight parts, (6) magnesium oxide 0.04-0.1 weight part (7) anti-aging agent 0.5-1.5 weight part is formed.
Production technique of the present invention is simple, and mix glue, 210 resins, trieline, methylene dichloride under the chlorine earlier mutually (1) at normal temperatures.(2) then 2402 resins, magnesium oxide, trieline are mixed mutually.(3) at last twice reactant mixed mutually, and add anti-aging agent.
Embodiment 1
By neoprene latex 92 weight parts, 210 resins, 12 weight parts, 2402 type resins, 5 weight parts.Three thermal source ethene, 405 weight parts, methylene dichloride 153 weight parts, magnesium oxide 0.04 weight part, anti-aging agent 0.5 weight part is formed.
Embodiment 2:
By neoprene latex 105 weight parts, 210 resins, 20 weight parts, 2402 resins, 8 weight parts, trieline 550 weight parts.Methylene dichloride 210 weight parts, magnesium oxide 0.08 weight part.Anti-aging agent 0.6 weight part is formed.
Cohesive strength height of the present invention, shearing resistance can reach every square metre of 210N in 20 minutes, and final shearing resistance is every square metre of 402N, and stripping strength is 252N/25cm.Have especially and meet naked light and do not burn, characteristics such as quick solidifying can be widely used in the cotton duck core, and polyvinyl, nylon conveyer belt joint normal temperature are bonding fast, also are suitable for the bonding of rubber, chemical fibre, cotton fabric, leather, bamboo wood, finishing material and partly plastic.The present invention is simple for production, and low cost is the optimal selection of like product in the market.
Claims (1)
1, a kind of novel refractory adhesive is characterized in that: (1) neoprene latex 90-125 weight part (2) 210 type resin 14-30 weight parts (3) 2402 type resin 5-10 weight part (4) trieline 400-750 weight part (5) methylene dichloride 150-250 weight part (6) magnesium oxide 0.04-0.1 weight part (7) anti-aging agent 0.5-1.5 weight parts.