CN1955211A - Resin-base glass fibre sheet for table tennis table - Google Patents
Resin-base glass fibre sheet for table tennis table Download PDFInfo
- Publication number
- CN1955211A CN1955211A CN 200510104462 CN200510104462A CN1955211A CN 1955211 A CN1955211 A CN 1955211A CN 200510104462 CN200510104462 CN 200510104462 CN 200510104462 A CN200510104462 A CN 200510104462A CN 1955211 A CN1955211 A CN 1955211A
- Authority
- CN
- China
- Prior art keywords
- resin
- glass fibre
- parts
- shares
- base glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention belongs to area of sports equipment and technology, concretely relates to a Sheet material of resin matrix fiberglass that is used for table top of ping-pong. Its characteristic is that according to weight share , 0.9-1.2 Shares of benzoyl peroxide is added into 36-55 shares of 191 resin which is added acrylic acid monomer, progress sufficient mixing and combination, after uniformity 1-1.5 shares of oxide or hydroxide of Ca or Mg, 53-62 shares of carbonica calcarea (CaCO3), 0-1.5 shares of zinc stearate are added and mixed to produce resinous paste, then 70 shares of resinous paste and 30 shares of fiberglass according to weight share are soaked, smoothly displayed on thin coating, Sheet material of resin matrix fiberglass is produced by winding and ripening.
Description
Technical field: the invention belongs to the sports apparatus technical field, be specifically related to a kind of resin-base glass fibre sheet for table tennis table.
Background technology: mostly existing court is xyloid, manually and be machined into sheet material, makes behind polishing, dipping lacquer again, and its shortcoming is to be placed in open area for a long time, otherwise flexible type rots.For this reason, useful reinforced concrete is made table tennis table on some open areas, its shortcoming be fixed-site, heavy, can not change the position and carry out the layout adjustment, elastic index can not reach national requirements.
Summary of the invention: the purpose of this invention is to provide a kind of resin-base glass fibre sheet for table tennis table, have sturdy and durable, the indeformable advantage of not splitting, not being afraid of Exposure to Sunlight and drenching with rain, being particluarly suitable for outdoor open area use with its product processed.
Technical scheme of the present invention is: a kind of resin-base glass fibre sheet for table tennis table, it is characterized in that by weight with benzoyl peroxide 0.9-1.2 part, join and add in the monomeric 191 resin 36-55 parts of acrylic acid, fully mix, evenly the oxide compound of back adding Ca or Mg or oxyhydroxide 1--1.5 part, lime carbonate CaCO
353--62 part, Zinic stearas 0--1.5 part mix and make resin paste, flood for 30 parts with 70 parts of resin paste of weight part and glass fibre then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Realize that a kind of preferred forms of the present invention is: a kind of resin-base glass fibre sheet for table tennis table, it is characterized in that by weight with 1 part of benzoyl peroxide, join and add in 50 parts of monomeric 191 resins of acrylic acid, fully mix, evenly the oxide compound of back adding Ca or Mg or 1.2 parts in oxyhydroxide, lime carbonate CaCO
356 parts, Zinic stearas mix for 1.2 parts and make resin paste, and 70 parts of resin paste and the glass fibre with weight part floods for 30 parts then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Compared with the prior art the present invention has high-lighting characteristics and marked improvement, with its product processed have the ability of sturdy and durable, resistance to deformation cracking resistance strong, be not afraid of Exposure to Sunlight and drench with rain, be particluarly suitable for the obvious advantage that outdoor open area uses.
Embodiment:, describe resin-base glass fibre sheet for table tennis table of the present invention in detail below in conjunction with embodiment in order to understand better and to implement.
Embodiment 1, a kind of resin-base glass fibre sheet for table tennis table with benzoyl peroxide 0.9kg, join in the container that fills the monomeric 191 resin 36kg of interpolation acrylic acid, fully mix, and evenly the back adds calcium oxide 1kg, lime carbonate CaCO
353kg, mix and make resin paste, flood with resin paste 70kg and the glass fibre 30kg that makes then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Embodiment 2, a kind of resin-base glass fibre sheet for table tennis table, with benzoyl peroxide 1.2kg, join in the container that fills the monomeric 191 resin 55kg of interpolation acrylic acid, fully mix, evenly the back adds magnesium oxide 1.5kg, lime carbonate CaCO
362kg, Zinic stearas 1.5kg mix and make resin paste, flood with resin paste 70kg and the glass fibre 30kg that makes then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Embodiment 3, a kind of resin-base glass fibre sheet for table tennis table, with benzoyl peroxide 1kg, join in the container that fills the monomeric 191 resin 50kg of interpolation acrylic acid, fully mix, evenly the back adds magnesium hydroxide 1.2kg, lime carbonate CaCO
356kg, Zinic stearas 1.2kg mix and make resin paste, flood with resin paste 70kg and the glass fibre 30kg that makes then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Embodiment 4, a kind of resin-base glass fibre sheet for table tennis table, with benzoyl peroxide 1.1kg, join in the container that fills the monomeric 191 resin 56kg of interpolation acrylic acid, fully mix, evenly the back adds calcium hydroxide 1.3kg, lime carbonate CaCO
360kg, Zinic stearas 1.3kg mix and make resin paste, flood with resin paste 70kg and the glass fibre 30kg that makes then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
Claims (2)
1, a kind of resin-base glass fibre sheet for table tennis table, it is characterized in that by weight with benzoyl peroxide 0.9-1.2 part, join and add in the monomeric 191 resin 36-55 parts of acrylic acid, fully mix, evenly the oxide compound of back adding Ca or Mg or oxyhydroxide 1--1.5 part, lime carbonate CaCO
353--62 part, Zinic stearas 0--1.5 part mix and make resin paste, flood for 30 parts with 70 parts of resin paste of weight part and glass fibre then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.
2, by the described a kind of resin-base glass fibre sheet for table tennis table of claim 1, it is characterized in that by weight with 1 part of benzoyl peroxide, join and add in 50 parts of monomeric 191 resins of acrylic acid, fully mix, evenly the oxide compound of back adding Ca or Mg or 1.2 parts in oxyhydroxide, lime carbonate CaCO
356 parts, Zinic stearas mix for 1.2 parts and make resin paste, and 70 parts of resin paste and the glass fibre with weight part floods for 30 parts then, divide that the rolling slaking makes resin-base glass fibre sheet on the PE film.