CN1935356A - Resin base adsorbent with high selectivity to heavy metal and preparing process thereof - Google Patents
Resin base adsorbent with high selectivity to heavy metal and preparing process thereof Download PDFInfo
- Publication number
- CN1935356A CN1935356A CN200610041365.4A CN200610041365A CN1935356A CN 1935356 A CN1935356 A CN 1935356A CN 200610041365 A CN200610041365 A CN 200610041365A CN 1935356 A CN1935356 A CN 1935356A
- Authority
- CN
- China
- Prior art keywords
- resin
- heavy metal
- group
- resin base
- high selectivity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a resin base adsorbing agent with high selectivity for heavy metal and its preparation method, belonging to the field of macroporous resin. The main structure composition of this adsorbing agent includes: (1), basic skeleton, it is a macroporous polystyrene skeleton; (2), functional group bond-linked on the skeleton is acid group or low-polar group; and (3), effective component of functional material fixedly-loaded on the inner surface of skeleton is Zr(HPO4)2. Said invention also provides its preparation method and concrete steps.
Description
One, technical field
The present invention relates to the macropore polystyrene resin (ps) is resin base adsorbent of parent and preparation method thereof, and a kind of high selectivity that is used for of saying so is more specifically removed heavy metal resin base adsorbents such as water body deleading, zinc, cadmium and preparation method thereof.
Two, background technology
About the preparation of basic zirconium phosphate and to alkali metal or alkaline-earth metal ions switching performance, people such as external AbrahamClearfield have carried out systematic research.(The preparation of crystallinezirconium phosphate and some observation on its ion exchange behaviors, Inorg.Nucl.Chem.1964,26:117-129), but the never concrete report of its counterweight Adsorption Properties for Metal Ions.Simultaneously, because basic zirconium phosphate generally exists with superfine particle (about 0.2~20 micron), the generation that immense pressure is fallen during owing to application is difficult to directly realize the industrialization adsorption applications.Conventional cationic ion-exchange resin is not because good to the selectivity of heavy metal, other conventional cation such as Na in water body or industrial wastewater
+, Mg
2+, K
+, Ca
2+When isoconcentration was higher, its actual detergent power to water body was relatively poor, and application cost is higher.About basic zirconium phosphate to the selective absorption of heavy metal with and do not see the pertinent literature report at present at resin surface immobilized.
It is the preparation method of the resin base adsorbent of parent with anion exchange resin that patent 200510095177.5 (a kind of preparation method of resin-based arsenic-removing adsorption agent) discloses a kind of, and synthetic resin-based arsenic-removing adsorption agent is improved largely to the adsorptive selectivity of micro amount of arsenic in the aqueous solution.
Three, summary of the invention
1, the technical problem that will solve
The purpose of this invention is to provide resin-based heavy metal absorbent that a kind of adsorption capacity is big, selectivity is good and preparation method thereof, basic zirconium phosphate is immobilized in large hole cation exchanger resin or macropore polystyrene resin (ps) surface, and this adsorbent can be widely used in the high selectivity of heavy metal ion in the polluted water body and remove.
2, technical scheme
The technical scheme that adopts is as follows:
A kind of resin base adsorbent that heavy metal is had high selectivity, its primary structure is formed and is comprised:
(1) basic framework is the macroporous polystyrene skeleton;
(2) functional group of binding is an acidic-group or by the low pole group on the skeleton;
(3) the immobilized functional material active ingredient of skeleton inner surface is Zr (HPO
4)
2
The functional group of binding is one of following acidic-group on the skeleton: sulfonic group, phosphate, carboxylic acid group, phenolic hydroxyl group or low pole group chloromethyl.
This adsorbent apparent density 0.8~1.2g/ml; Sulfonic group, phosphate, carboxylic acid group, the about 2.5~6.0mmol/g of phenolic hydroxyl group equal size; Zr (HPO
4)
2Weight percent content is 5~30%; Absorbent particles size 0.5~1.5mm.
A kind of have the preparation method of the resin base adsorbent of high selectivity to heavy metal, and it mainly may further comprise the steps:
(A) with ZrOCl
28H
2O is dissolved in the hydrochloric acid, obtains homogeneous phase A, wherein ZrOCl
28H
2O concentration is 1~3mol/L, and HCl concentration is 1~5mol/L;
(B) macroreticular resin is placed homogeneous phase A, leave standstill at 20~60 degrees centigrade and be no less than 12h, make the resin dehydration afterwards;
(C) resin after will dewatering joins rapidly in 1~8mol/L phosphoric acid solution, reacts 12~36 hours, constantly stirs in course of reaction;
(D) taking out resin, with ammonium nitrate solution or the frozen water cleaning resin of 0.5~2mol/L, is 6~8 with distilled water flushing to pH value then again;
(E) resin is promptly got resin base adsorbent 40~60 degrees centigrade of oven dry.
Macroreticular resin is large hole cation exchanger resin D001, D113, Amberlite 252 resins in the step (B), or macroporous absorbent resin CHA-101, Amberlite XAD-4.Reaction time suggestion in the step (B) is 12~36 hours.
Phosphoric acid solution concentration in the step (C) is 3~5mol/L, and the reaction time is controlled at 12~36h.Can obtain effect preferably in the time effectively like this.
Ubiquitous Na in the water
+, K
+, Ca
2+, Mg
2+Can reduce the selectivity of common cation exchanger resin Deng cation, and the existence of basic zirconium phosphate can reduce cation such as Na in the water greatly on the resin to heavy metal ion
+, K
+, Ca
2+, Ag
2+To adsorbing the interference of heavy metal ion such as lead, zinc, cadmium, the very big selectivity and the operating efficiency that must improve it to heavy metal.
3, beneficial effect
A kind of resin base adsorbent that heavy metal is had high selectivity that the inventive method provides that a kind of adsorption capacity is big, mechanical strength good, power performance and selectivity tool are good and preparation method thereof.Synthetic resin base adsorbent basic zirconium phosphate content: about 300~500mg/g resin.Heavy metal absorbents such as synthetic resin-based deleading, zinc, cadmium are improved largely to the adsorptive selectivity of micro heavy ion in the aqueous solution, and generally the distribution coefficient to heavy metal ion improves ratio about 40~1000; Adsorbance improves 40~300% simultaneously.
Four, the specific embodiment
Further specify the present invention by the following examples
Embodiment 1:
A kind of polystyrene skeleton, surface bonded sulfonic resin base adsorbent and preparation method thereof.In the 200ml beaker, add 40g ZrOCl
28H
2O, the 8ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 2.5mol/l of zirconium oxychloride concentration in this solution, hydrochloric acid 2mol/l.In this beaker, slowly add 30g large pores cation exchange resin (D-001), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.Oven dry back resin is placed the round-bottomed flask of 500ml, slowly add 350ml 4mol/l phosphoric acid solution, and constantly stir, mixing time control 24h.After reaction finishes, with the NH of 1mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 50 ℃ of control temperature just obtain the resin-based heavy metal absorbent.This absorbent particles size 0.5~1.4mm, sulfonic group content is 4.0mmol/g, basic zirconium phosphate content is 430mg/g, to the adsorbance of lead, zinc, cadmium be respectively 300,105,186mg/g.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 917,120,76 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 2:
Resin base adsorbent of a kind of polystyrene skeleton, surface bonded carboxylic acid group and preparation method thereof.In the 200ml beaker, add 30g ZrOCl
28H
2O, the 4ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 2mol/l of zirconium oxychloride concentration in this solution, hydrochloric acid lmol/l.In this beaker, slowly add 30g macroporous acrylic type ion exchange resin (D-113), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.Oven dry back resin is placed the round-bottomed flask of 500ml, slowly add 350ml, the 4mol/l phosphoric acid solution, and constantly stir, mixing time control 24h is after reaction finishes, with the NH of 0.5mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 50 ℃ of control temperature just obtain resin-based deleading adsorbent.This absorbent particles size 0.5~1.5mm, carboxylic acid group's content is 7.3mmol/g, basic zirconium phosphate content is the 310mg/g resin, to the adsorbance of lead, zinc, cadmium be respectively 245,72, the 148mg/g resin.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 726,118,54 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 3
Resin base adsorbent of a kind of polystyrene skeleton, surface bonded phenolic hydroxyl group and preparation method thereof.At first at the surface bonded phenolic hydroxyl group of resin matrix: 15ml nitrobenzene imported to be added with in the 30g chloromethylated polystyrene spheroid beaker of (being called for short the chlorine ball) soaked 24 hours; the back adds the 2g anhydrous Aluminum chloride and makes catalyst; and progressively add 30g phenol; under nitrogen protection, be warming up to 330K in 1 hour; sustained response 6 hours; and with the resin of ethanol extracting gained, get final product the surperficial polystyrene skeleton that contains phenolic hydroxyl group.In the 200ml beaker, add 50g ZrOCl
28H
2O, the 8ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 3mol/l of zirconium oxychloride concentration in this solution, hydrochloric acid 2mol/l.In this beaker, slowly add the above-mentioned synthetic resin of 30g, make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.With the round-bottomed flask of oven dry back resin as for 500ml, slowly add 350ml, the 3mol/l phosphoric acid solution, and constantly stir, after mixing time control 24h reaction finishes, with the NH of 1mol/l
4NO
3The solution flushing, with the excessive phosphoric acid of flush away, then washing until the pH value repeatedly with a large amount of distilled water is 6~8.Place baking oven to dry resin, 50 ℃ of control temperature just obtain resin-based deleading adsorbent, this absorbent particles size 0.5~1.2mm, and phenolic hydroxyl group base content is 2.6mmol/g, basic zirconium phosphate content is the 532mg/g resin.To the adsorbance of lead, zinc, cadmium be respectively 452,143, the 268mg/g resin.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 328,109,51 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 4:
A kind of surface bonded carboxylic acid group's resin base adsorbent and synthetic method thereof.Be taken in the 200ml beaker, add 20g ZrOCl
28H
2O, the 16ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 1mol/l of zirconium oxychloride concentration in this solution.Hydrochloric acid 4mol/l.In this beaker, slowly add 30g macroporous acrylic type ion exchange resin (D113), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.Resin after the oven dry is placed the round-bottomed flask of 500ml, slowly add 350ml, the 4mol/l phosphoric acid solution, and constantly stir, after mixing time control 24hs reaction finishes, with the NH of 2mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 60 ℃ of control temperature just obtain resin-based deleading adsorbent, this absorbent particles size 0.5~1.5mm, and carboxylic acid group's content is 7.3mmol/g, basic zirconium phosphate content is the 290mg/g resin.To the adsorbance of aluminium, zinc, cadmium be respectively 175,58, the 86mg/g resin.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 817,120,76 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 5:
A kind of surface bonded sulfonic resin base adsorbent and synthetic method thereof.In the 200ml beaker, add 50g ZrOCl
28H
2O, the 20ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 3mol/l of zirconium oxychloride concentration in this solution.Hydrochloric acid 5mol/l.In this beaker, slowly add 30g large pores cation exchange resin (D001), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 36h.Oven dry back resin is placed the round-bottomed flask of 500ml, slowly add 350ml 3mol/l phosphoric acid solution, and constantly stir, after mixing time control 24h reaction finishes, with the NH of 1mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 40 ℃ of control temperature just obtain resin-based deleading adsorbent, this absorbent particles size 0.5~1.2mm, and sulfonic group content is 4.7mmol/g, basic zirconium phosphate content is the 524mg/g resin.Adsorbance to lead, zinc, cadmium is respectively 418,131,234 mg/g resins.With Ca2+ is competing ions, and when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 658,105,56 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 6
A kind of surface bonded carboxylic acid group's resin base adsorbent and synthetic method thereof.Be taken in the 200ml beaker, add 40g ZrOCl
28H
2O, the 8ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 2.5mol/l of zirconium oxychloride concentration in this solution, hydrochloric acid 2mol/l.In this beaker, slowly add 30g macroreticular resin Amberlite XAD-7 (Amberlite XAD-7), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.Oven dry back resin is placed the round-bottomed flask of 500ml, slowly add 350ml, the 4mol/l phosphoric acid solution, and constantly stir mixing time control 24h.After reaction finishes, with the NH of 1mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 50 ℃ of control temperature just obtain resin-based deleading adsorbent, this absorbent particles size 0.6~1.2mm, and carboxylic acid group's content is 7.5mmol/g, basic zirconium phosphate content is the 411mg/g resin.To the adsorbance of lead, zinc, cadmium be respectively 294,121, the 186mg/g resin.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 326,79,45 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Embodiment 7
A kind of resin base adsorbent of surface bonded chloromethyl and synthetic method thereof.In the 200ml beaker, add 20g ZrOCl
28H
2O, the 8ml concentrated hydrochloric acid adds water and fully dissolves and be settled to 50ml, the about 3mol/l of zirconium oxychloride concentration in this solution.Hydrochloric acid 2mol/l.In this beaker, slowly add 30g chloromethylated polystyrene spheroid (being called for short the chlorine ball), make solution the complete submergence of resin.Place baking oven to dry this resin, solution solid-liquid mixing system, zirconates is entered in the resin duct fully, 40 ℃ of control temperature, drying time is 12h.Oven dry back resin is placed the round-bottomed flask of 500ml, slowly add 350ml, the 3mol/l phosphoric acid solution, and constantly stir, after mixing time control 24h reaction finishes, with the NH of 1mol/l
4NO
3The solution flushing with the excessive phosphoric acid of flush away, is then washed until neutrality with a large amount of distilled water repeatedly.Place baking oven to dry resin, 50 ℃ of control temperature just obtain resin-based deleading adsorbent.This absorbent particles size 0.5~1.3mm, chloromethyl content is 5.2mmol/g, basic zirconium phosphate content is the 325mg/g resin.To the adsorbance of lead, zinc, cadmium be respectively 163,52, the 81mg/g resin.With Ca
2+Be competing ions, when its molar concentration was lead, zinc, cadmium ion 10 times, the gained resin base adsorbent had improved 521,98,42 times to the distribution coefficient of lead, zinc, cadmium ion respectively than large hole cation exchanger resin D-001.
Claims (8)
1. resin base adsorbent that heavy metal is had high selectivity, its primary structure is formed and is comprised:
(1) basic structure is the macroporous polystyrene skeleton;
(2) functional group of binding is an acidic-group or by the low pole group on the skeleton;
(3) the immobilized functional material active ingredient of skeleton inner surface is Zr (HPO
4)
2
2. a kind of resin base adsorbent that heavy metal is had high selectivity according to claim 1, the functional group that it is characterized in that binding on the skeleton is one of following acidic-group: sulfonic group, phosphate, carboxylic acid group, phenolic hydroxyl group or low pole group chloromethyl.
3. a kind of resin base adsorbent that heavy metal is had high selectivity according to claim 2 is characterized in that absorbent particles size 0.5~1.5mm, and sulfonic group, phosphate, carboxylic acid group, content of phenolic hydroxyl groups are 2.5~6.0mmol/g.
4. according to claim 2 or 3 described a kind of resin base adsorbents that heavy metal is had high selectivity, it is characterized in that Zr (HPO
4)
2Weight percent content is 5~30%.
5. one kind has the preparation method of the resin base adsorbent of high selectivity to heavy metal, and it mainly may further comprise the steps:
(A) with ZrOCl
28H
2O is dissolved in the hydrochloric acid, obtains homogeneous phase A, wherein ZrOCl
28H
2O concentration is 1~3mol/L, and HCl concentration is 1~5mol/L;
(B) macroreticular resin is placed homogeneous phase A, leave standstill at 20~60 degrees centigrade and be no less than 12h, make the resin dehydration afterwards;
(C) resin after will dewatering joins rapidly in 1~8mol/L phosphoric acid solution, reacts 12-36 hour, constantly stirs in course of reaction;
(D) taking out resin, with the ammonium nitrate solution cleaning resin of 0.5~2mol/L, is 6~8 with distilled water flushing to pH value then again;
(E) resin is promptly got resin base adsorbent 40-60 degree centigrade of oven dry.
6. a kind of preparation method who heavy metal is had the resin base adsorbent of high selectivity according to claim 5, it is characterized in that large pores cation exchange resin is cationic ion-exchange resin D001, D113, Amberlite 252 resins of macropore in the step (B), and macroporous absorbent resin CHA-101, AmberliteXAD-4.
7. describedly a kind of heavy metal is had the preparation method of the resin base adsorbent of high selectivity according to claim 5 or 6, it is characterized in that the reaction time in the step (B) is 12~36 hours.
8. describedly a kind of heavy metal is had the preparation method of the resin base adsorbent of high selectivity according to claim 5 or 6, it is characterized in that the phosphoric acid solution concentration in the step (C) is 3~5mol/L, the reaction time is 12~36 hours.