CN1932486A - High-temperature type dye check developer and producing process thereof - Google Patents
High-temperature type dye check developer and producing process thereof Download PDFInfo
- Publication number
- CN1932486A CN1932486A CN 200510029680 CN200510029680A CN1932486A CN 1932486 A CN1932486 A CN 1932486A CN 200510029680 CN200510029680 CN 200510029680 CN 200510029680 A CN200510029680 A CN 200510029680A CN 1932486 A CN1932486 A CN 1932486A
- Authority
- CN
- China
- Prior art keywords
- developer
- temperature
- type dye
- dye check
- temperature type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A developer which is used as a metal in elevated temperature, compact ability non-metal material and as a liquid penetrate test which is high temperature modification is constituted of precipitate silicon acid:40%-70%, acetic acid cellulose: 10%-20%, dioctyl phthalate: 5%-15%. Tentation indicates that the use of this developer, a penetrate and a cleaning solution which are high temperature modification liquid penetrate tests can finish the surface inspection of object which the surface temperature is 150-220DEG Cand can detect a fracture whose breadth is 0.001mm and width depth ratio is 1/60.
Description
Technical field
The present invention relates to the flaw detection on product surface, particularly a kind of high-temperature type dye check developer that is used for the product surface inspection and preparation method thereof.
Background technology
The liquid penetrant examination method is a kind of important method in the modern Non-Destructive Testing, originates in the World War II initial stage, is used for war industry the earliest.Become at present in the modern manufacturing industry for improve the quality of products, service equipment safely, prevent a kind of important means of industry disaster accident.This method can detect that material or surface of the work occur also in the extremely trickle fracture focus of bud.
The ultimate principle that infiltration detects is with a kind of material (overwhelming majority is a liquid, and also having a spot of is gas and solid, so claim that generally it is a bleeding agent), infilters in the microscopic checks and goes; Wipe up with the developer bleeding agent cleaning that the next door is unnecessary then, keep the bleeding agent in the crack as far as possible; Again developer is applied to surface of the work, this reagent can very fast volatilization and stay the solid film that one deck has strong absorption affinity, the bleeding agent that stays in the microscopic checks is sucked out and is enlarged, and makes it to demonstrate the place, position in crack.
Existing penetrant flaw detection agent is made up of penetrating fluid, developer and cleaning fluid, through development for a long time, the employed penetrant flaw detection agent of liquid penetration test that has occurred multiple model in the world, but this class penetrant flaw detection agent, can only detect surface temperature and be in-10 ℃---70 ℃ workpiece.When existing penetrant flaw detection agent is applied to the high temperature surface, can seethes with excitement immediately, bubble, evaporate, smolder, what have also can burn, can't operate as normal.But the high temperature workpiece exists really real-life.For example: carry the pipeline of high-temperature steam and high temperature fluid, boiler in the work and pressure vessel, near the workpiece that the parts after the hot-working just, electric welding weldment soon are with being in thermal source etc.
Some workpiece must at high temperature carry out penetrating inspection, and check that again reason is as follows the temperature of workpiece can't be dropped to below 70 ℃ the time:
1. some power house, particularly nuclear power station, oceangoing voyage boats and ships and chemical industry facility, they Once you begin move, can not stop, but their boiler, pipeline waited until certain time limit and needed maintenance to have only some position of determining to have and just locally after the problem stop work, repair or change parts midway.The inspection of comprehensively search property can only be under the condition of high temperature of carrying labour at them to be carried out.
2. some hot-working parts is in order to guarantee the quality of following process, and process inspection in the middle of need doing if cooling may need the long time cycle, also will heat up again after checking and continue processing.So not only waste energy, also may in the process of temperature one rise and one drop, change the metallographic structure of material, damaged their mechanical property.
3. some pressure vessel has the heat leak situation to exist.In other words, it opens because of radial pressure makes microscopic checks under high-temperature condition, can leak fluent meterial wherein.After its cooling, microfracture is closed again, leaks very not obvious.Such source of leaks always will be found out, and has only and checks that at high temperature ability effectively.
Summary of the invention
The technical problem to be solved in the present invention is to overcome above-mentioned the deficiencies in the prior art, provides a kind of high-temperature type dye check developer that at high temperature carries out permeation flaw detection and preparation method thereof to satisfy the needs of high temperature flaw detection.
The present invention solves the problems of the technologies described above the technical scheme that is adopted:
A kind of high-temperature type dye check developer that is used to be in the surface of the work flaw detection under the high temperature, its compositing formula is as follows:
Composition wt%
Precipitating type silicic acid anhydride 40-70
Polyacetic acid cellulose 10-20
Adjacent octoil 5-15
Strychnine 15-25
The preparation method of described high-temperature type dye check developer comprises the following steps:
1. select technical pure or chemical pure raw material for use;
2. select the proportioning of high-temperature type dye check developer, each raw material of weighing;
3. the resistant to elevated temperatures polyacetic acid cellulose of institute's weighing, adjacent octoil and strychnine are mixed, are in harmonious proportion, stir,, form transparent film forming agent solution until dissolving fully mutually;
4. the precipitating type silicic acid anhydride with described film forming agent solution and institute's weighing is in harmonious proportion, and forms temper;
5. temper is pushed, integrated, make it to become the semi-solid material;
6. the semi-solid material is packed into to mould in the experienced machine and mould white silk, translucent until becoming, milky clay attitude developer.
The technique effect of high-temperature type dye check developer of the present invention and preparation method thereof is:
This developer is made up of adjacent octoil, polyacetic acid cellulose, precipitating type silicic acid anhydride and strychnine, try out and show that this imaging liquid is used with high-temperature type dye check penetration liquid and high-temperature type dye check cleaning liquid, can finish surface temperature is the flaw detection on 150～220 ℃ product surface, can detect width is 0.001mm, and breadth depth ratio is 1/60 crack.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail.
High-temperature type dye check developer of the present invention is formulated by adjacent octoil, polyacetic acid cellulose, precipitating type silicic acid anhydride and strychnine.
The composition proportioning of embodiment 1 high-temperature type dye check developer is as follows:
Composition wt%
Precipitating type silicic acid anhydride 70
Polyacetic acid cellulose 10
Adjacent octoil 5
Strychnine 15
Its configuration step is as follows:
1. select commercially pure raw material for use;
2. press the proportioning of described high-temperature type dye check developer, each raw material of weighing;
3. the polyacetic acid cellulose of institute's weighing, adjacent octoil and strychnine are mixed, are in harmonious proportion, stir, until dissolving fully mutually, form transparent film forming agent solution, wherein the polyacetic acid cellulose is resistant to elevated temperatures film forming agent, adjacent octoil is high boiling solvent, and strychnine is the high temperature cosolvent;
4. the precipitating type silicic acid anhydride with described film forming agent solution and institute's weighing is in harmonious proportion, and forms temper, and wherein the precipitating type silicic acid anhydride is an adsorbent;
5. described temper is pushed, integrated, make it to become the semi-solid material;
6. the semi-solid material is packed into to mould in the experienced machine and mould white silk, the developer of translucent until becoming, milky clay attitude.
This developer at high temperature uses, and the temperature range on the product surface of being worked is: 150～220 ℃.The using method of this developer is: at first with the developer heating of prepared clay attitude, with resistant to elevated temperatures glass fabric it is wrapped up glomeration again, hold this ball at last and wipe at detected high temperature surface of the work.
The composition proportioning of embodiment 2 high-temperature type dye check developers is as follows:
Composition wt%
Precipitating type silicic acid anhydride 40
Polyacetic acid cellulose 20
Adjacent octoil 15
Strychnine 25
The composition proportioning of embodiment 3 high-temperature type dye check developers is as follows:
Composition wt%
Precipitating type silicic acid anhydride 50
Polyacetic acid cellulose 18
Adjacent octoil 11
Strychnine 21
The configuration step of embodiment 2 and embodiment 3 is identical with embodiment 1 with using method, each proportioning components amount difference when just disposing, and wherein each raw material also can be selected chemical pure raw material.
High-temperature type dye check developer by the preparation of the composition proportion amount of embodiment 1, embodiment 2 and embodiment 3 is tested in the high temperature crack test piece of special use with its supporting high-temperature type dye check clean-out system, high-temperature type dye check bleeding agent, test result shows: can detect width is 0.001mm, breadth depth ratio is 1/60 man-made fracture, and this result meets the level of sensitivity of penetrant flaw detection agent commonly used.
Claims (2)
1. high-temperature type dye check developer that is used to be in metal, compact nonmetallic material and product surface inspection thereof under the high temperature is characterised in that its compositing formula is as follows:
Composition wt%
Precipitating type silicic acid anhydride 40-70
Polyacetic acid cellulose 10-20
Adjacent octoil 5-15
Strychnine 15-25
2. the preparation method of the described high-temperature type dye check developer of claim 1 is characterized in that this method comprises the following steps:
1. select technical pure or chemical pure raw material for use;
2. select the proportioning of high-temperature type dye check developer, each raw material of weighing;
3. the resistant to elevated temperatures polyacetic acid cellulose of institute's weighing, adjacent octoil and strychnine are mixed, are in harmonious proportion, stir,, form transparent film forming agent solution until dissolving fully mutually;
4. the precipitating type silicic acid anhydride with described film forming agent solution and institute's weighing is in harmonious proportion, and forms temper;
5. temper is pushed, integrated, make it to become the semi-solid material;
6. the semi-solid material is packed into to mould in the experienced machine and mould white silk, translucent until becoming, milky clay attitude developer.