Adhesive method in magnetic material carries out before the circle cutting processing
Technical field
The present invention relates to the adhesive method of magnetic material, particularly relate to the adhesive method before a kind of magnetic material carries out interior circle cutting processing.
Background technology
At present, in carrying out sintered magnet and monocrystalline silicon polysilicon cutting process, generally material to be processed will be cleaned and dry, the purpose of oven dry is to guarantee material surface noresidue moisture to be processed, uses 502 instant drying adhesives to bond then; Long product will carry out oiling (used oil or other are not allowed volatile lubricating oil) processing usually for standing time after the mill processing, generally also will carry out the soda boiling oven dry for such product, uses 502 instant drying adhesives to bond then; Sometimes treat material processed and do not handle direct bonding.Adopting the method for above-mentioned routine to treat material processed bonds, its weak point is to be easy to generate the sheet phenomenon when justifying cutting processing in the material that bonds is carried out in water base working solution, even after cutting is finished, do not fall the sheet phenomenon, also take place easily loosely to be scattered phenomenon and to be unfavorable for that the whole plate of product checks.
Summary of the invention
Purpose of the present invention is intended to overcome above-mentioned shortcoming, provide in a kind of course of processing the magnetic material that is difficult for producing the sheet phenomenon and helps the whole plate test of product carry out in adhesive method before the circle cutting processing.
For reaching above-mentioned purpose, the solution that the present invention adopts is: the adhesive method in a kind of magnetic material carries out before the circle cutting processing, it is characterized in that: it comprises the steps: at the non-water-soluble not volatile organic liquid of magnetic material surface attachment one deck to be processed, then magnetic material to be processed is arranged, bondd with instant drying adhesive.
Adhesive method in above-mentioned magnetic material carries out before the circle cutting processing is characterized in that: before the non-water-soluble not volatile organic liquid of magnetic material surface attachment one deck to be processed, magnetic material to be processed is cleaned or soda boiling, then oven dry.
Adhesive method in above-mentioned magnetic material carries out before the circle cutting processing, it is characterized in that: described at the non-water-soluble not volatile organic liquid of magnetic material surface attachment one deck to be processed, be meant non-water-soluble not volatile organic liquid wiping is used on magnetic material surface to be processed, or directly magnetic material to be processed is immersed in the non-water-soluble not volatile organic liquid, drain then and get final product.
Adhesive method in above-mentioned magnetic material carries out before the circle cutting processing, it is characterized in that: described non-water-soluble not volatile organic liquid is meant one or more in kerosene, diesel oil, transformer oil, lubricating oil, the edible oil.
The adhesive method of circle before the cutting processing in above-mentioned magnetic material carries out is characterized in that: described non-water-soluble not volatile organic liquid is to be any non-water-soluble material that solvent adds other with kerosene, diesel oil or other atoxic organic liquids.
Compared with prior art, the present invention has following advantage:
Since the present invention to magnetic material to be processed the bonding before, carry out immersion treatment with non-water-soluble not volatile organic liquid, make it to form the non-water-soluble organic liquid of one deck at material surface, bond then, in carrying out, justify in the cutting processing process like this, hydrone in the water base plinth hydraulic fluid can not enter because trickle drainage material is arranged bonding surface in the micro gap that produces in the processing vibrations process, and then destroys magnetic material surface adhesion strength.Simultaneously, under the situation that has non-water-soluble organic substance to exist, 502 glue-line edges possess certain elasticity, have reduced the possibility that fragility and slit enter hydrone, thereby protection bonds.So the present invention is difficult for producing the sheet phenomenon in the course of processing, and combination closely helps the whole plate test of product after cutting is finished.
Embodiment
Generally treat material processed and before bonding, will clean and dry, then bonding.The purpose of oven dry is to guarantee bonding surface noresidue moisture.Long material will carry out oiling (used oil or other are not allowed volatile lubricating oil) processing for standing time after the mill processing, generally also will carry out the soda boiling oven dry for such material.All be after original the processing, to bond at once to increase a technology of handling between the link in following embodiment.
Embodiment 1
With the cylindrical magnet of the D11*28 of processing to be cut, select respectively that handle on the surface, surperficial untreated material for use, in pure diesel oil, to soak, wiped clean directly uses 502 arrangements according to every layer of 6-5-6-5-4 (totally 26) to bond then.After this magnet that has bondd is processed 1.5 millimeters of processing thickness.Cutting process does not have the sheet of falling as a result, checks the whole plate that bonds not have and is scattered, and the whole plate sheet bond strength feel of having cut is cut approaching with conventional bonding with diesel oil.The surface is untreated all the same with the surface treatment result, indistinction.
Embodiment 2
With the cylindrical magnet of the D11*28 of processing to be cut, in pure diesel oil, soak, bond with 502 arrangements after the wiped clean according to every layer of 6-5-6-5-4 (totally 26).After this magnet that has bondd is processed 1.5 millimeters of processing thickness.Cutting process does not have the sheet of falling as a result, checks the whole plate that bonds not have and is scattered, and the whole plate sheet bond strength feel of having cut is cut approaching with conventional bonding with diesel oil.
Embodiment 3
With the cylindrical magnet of the D11*28 of processing to be cut, to use in the saturated kerosene that is dissolved with chlorinated paraffin wax and soak, wiped clean directly uses 502 arrangements according to every layer of 6-5-6-5-4 (totally 26) to bond then.After this magnet that has bondd is processed 1.5 millimeters of processing thickness.Cutting process does not have the sheet of falling as a result, checks the whole plate that bonds not have and is scattered, and the whole plate sheet bond strength feel of having cut is cut approaching with conventional bonding with diesel oil.
Embodiment 4
Cylindrical magnet with the D11*28 of processing to be cut, the towel that use was soaked in No. 32 machine oil is screwed onto half-dried, the surface for the treatment of bonded permanent magnet with this towel wiped clean directly uses 502 arrangements according to every layer of 6-5-6-5-4 (totally 26) to bond then then.After this magnet that has bondd is processed 1.5 millimeters of processing thickness.Cutting process does not have the sheet of falling as a result, checks the whole plate that bonds not have and is scattered, and the whole plate sheet bond strength feel of having cut is cut approaching with conventional bonding with diesel oil.
Embodiment 5
Cylindrical magnet with the D11*28 of processing to be cut, the towel that use was soaked in No. 32 machine oil is screwed onto half-dried, the surface for the treatment of bonded permanent magnet with this towel wiped clean directly uses 502 arrangements according to every layer of 6-5-6-5-4 (totally 26) to bond then then.After this magnet that has bondd is processed 1.5 millimeters of processing thickness.Cutting process does not have the sheet of falling as a result, checks the whole plate that bonds not have and is scattered, and the whole plate sheet bond strength feel of having cut is cut approaching with conventional bonding with diesel oil.