CN1927500A - Wax mould combining method for golf rod head - Google Patents
Wax mould combining method for golf rod head Download PDFInfo
- Publication number
- CN1927500A CN1927500A CN 200510098367 CN200510098367A CN1927500A CN 1927500 A CN1927500 A CN 1927500A CN 200510098367 CN200510098367 CN 200510098367 CN 200510098367 A CN200510098367 A CN 200510098367A CN 1927500 A CN1927500 A CN 1927500A
- Authority
- CN
- China
- Prior art keywords
- wax
- pattern
- combination
- combining method
- glof club
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wax mould combine method of golf rod head. Wherein, it comprises: preparing one main body wax mould and one back combined wax mould; adhering the main body wax mould on the back combined wax mould to form one rod head wax mould; repairing the connection between them. Therefore, the invention only needs to repair the connection between the main body wax mould and the back combine, to reduce the cost and improve the reliability.
Description
Technical field
The present invention relates to the wax-pattern of glof club head, especially refer to a kind of body wax-pattern and back of the body combination wax-pattern of tool being carried on the back the cave, cohere into a bar head wax-pattern with the integrated structure that is complementary, this coheres the position only corresponding to the regional area in body wax-pattern back of the body cave, can reduce the trim length of wax-pattern and reduce the Wax mould combining method of glof club head of the surfacing workload of foundry goods.
Background technology
Please refer to shown in Figure 1, commonly use the Wax mould combining method of glof club head, announce as described in No. 514574 " manufacture method of golf iron head " patent of invention as Taiwan, comprise the following step () two-chip type wax-pattern 81,82 operations for forming respectively, it is that wax is injected first mould and second mould (not shown in the figures), to form two-chip type wax-pattern 81,82 respectively; (2) wax-pattern coheres operation, be with respectively independently two-chip type wax-pattern 81,82 cohere and be integral (promptly forming a bar head wax-pattern 8); (3) arenaceous shell mould (not shown in the figures) operation is made in soaking paste, be to cohere the all-in-one-piece surface at this two-chip type wax-pattern 81,82 to carry out soaking paste, to form an arenaceous shell mould, subsequently the wax thermosol is poured out, in this arenaceous shell mould, form a protuberance (not shown in the figures) simultaneously, and form casting gate (not shown in the figures) in a side of this arenaceous shell mould; (4) arenaceous shell is molded makes iron club (not shown in the figures) operation, is that the molten metal with thermosol injects this arenaceous shell mould, after this molten metal solidifies, this arenaceous shell mould is broken up, and takes out the iron club of integral-formed jointless.Wherein this two-chip type wax-pattern 81,82 is respectively a body wax-pattern 81 and a panel wax-pattern 82.
Above-mentioned manufacture method can be in order to making integrated bar head (not shown in the figures), and directly form a back of the body cave 83 at this bar head back side, is particularly conducive to this back of the body cave 83 is manufactured the back of the body cave 83 with deep hole moulding (undercut).Yet this body wax-pattern 81 is not to form complete surface with panel wax-pattern 82, that is crack 84 between still forming necessarily between this two wax-pattern 81,82.When starching for avoiding this bar head wax-pattern 8 to be stained with, slurries infiltrate this two wax-pattern 81,82 in conjunction with in the crack between the intersection 84, and produce bad foundry goods (not shown in the figures) when causing casting, therefore must further repair this bar head wax-pattern 8 is positioned at this two wax-patterns, 81,82 positions in conjunction with intersection, so that produce the foundry goods of the certain quality of tool.Yet, since this two wax-pattern 81,82 in conjunction with intersection, promptly the length at the formation position in gap 84 equals the length of periphery outside this panel wax-pattern 82, thereby above-mentioned manufacture method forms bigger repairing length, so that improves manufacturing cost relatively and increase man-hour.
Another commonly uses the Wax mould combining method of glof club head, announce as described in I232783 number " the multi-disc wax-pattern joint method of golf driver head " patent of invention as Taiwan, it comprises the following step: (1), manufacturing one first wax-pattern and one second wax-pattern, and first wax-pattern has one at least and is embedded the joint portion; (2), first and second wax-pattern utilizes temperature difference to form assembling nargin; (3), second wax-pattern tentatively is embedded at the joint portion that is embedded of first wax-pattern; (4), first wax-pattern is lowered the temperature and shrink process, so that first and second wax-pattern is combined closely into a bar head wax-pattern.Wherein first wax-pattern is a body wax-pattern, and second wax-pattern is a panel wax-pattern.
Above-mentioned manufacture method also can be in order to make integrated bar head, and directly form back of the body cave at the back side of this bar head with deep hole moulding (undercut), particularly its cooling and shrink process can further be dwindled in conjunction with crack between the intersection, engage quality to promote.However, above-mentioned manufacture method still fails to eliminate fully in conjunction with crack between the intersection, therefore, still must repair or tamp the position of this bar head wax-pattern in conjunction with intersection, thereby improves manufacturing cost relatively and increase process time.Moreover, when this two wax-pattern is selected body wax-pattern and panel wax-pattern for use, its length in conjunction with intersection (being that wax-pattern is in conjunction with patch cord) equals the length of these panel wax-pattern outer peripheral edges, thereby above-mentioned manufacture method still can form bigger trim length, so that improves manufacturing cost relatively and increase process time.
The Wax mould combining method of another glof club head, announce as described in I229612 number " manufacture method of golf driver head " patent of invention as Taiwan, it comprises the following step: (1), manufacturing one body wax-pattern and an accessory wax-pattern, this body wax-pattern has first joint portion, and this accessory wax-pattern has second joint portion; (2), tentatively make up first joint portion of this body wax-pattern and second joint portion of accessory wax-pattern, and between this first and second joint portion, form a gap; (3), the volatile high fluidity solvent of tool is inserted in this gap, so that the own wax material of this body wax-pattern and the utilization of accessory wax-pattern is incorporated into a bar head wax-pattern; (4), this bar head wax-pattern soaking paste is formed an arenaceous shell mould, then this arenaceous shell mould is heated dewaxing; (5), utilize this arenaceous shell mould to cast, to make the foundry goods of a bar head.Wherein this accessory wax-pattern is selected a panel wax-pattern or a sealing wax-pattern for use.
Above-mentioned manufacture method can be in order to make integrated bar head, yet, as shown in Figure 2, because the body wax-pattern 91 of above-mentioned manufacture method is made up of three dies (that is a panel part mould 92, a back mould 93 and a bottom die 94), so that produce shortcomings such as increasing die manufacturing cost and form removal difficulty.For these reasons, the necessity that the Wax mould combining method of above-mentioned various glof club heads is had really further improvement.
Summary of the invention
Main purpose of the present invention, be to provide a kind of Wax mould combining method of glof club head, it is provided with a body wax-pattern and a back of the body combination wax-pattern, this body wax-pattern is provided with a body butting section and a supporting part, this back of the body combination wax-pattern is provided with a back of the body combination butting section and a joint portion, an end, this body wax-pattern is only put corresponding to the back of the body acupuncture point of this body wax-pattern with back of the body combination wax-pattern, so this body wax-pattern is bonded in this back of the body combination wax-pattern, to form bar head wax-pattern, the two only in the regional area in back of the body cave, makes the present invention have the effect that reduces surfacing in conjunction with intersection.
Secondary objective of the present invention, be to provide a kind of Wax mould combining method of glof club head, it utilizes the two molds group to make a body wax-pattern and a back of the body combination wax-pattern respectively, and each set of molds only needs to be made up of more a spot of relatively mould, makes the present invention have the effect that reduces wax-pattern manufacturing cost and manufacture difficulty.
Another purpose of the present invention, be to provide a kind of Wax mould combining method of glof club head, it will be carried on the back the combination wax-pattern and be bonded in the body wax-pattern, make the finishing position of bar head wax-pattern only be formed at the back bottom of body wax-pattern, combine compactness between the panel part of guaranteeing foundry goods and the rod head noumenon, promote of the present invention in conjunction with reliability.
Technical scheme of the present invention is:
A kind of Wax mould combining method of glof club head, it comprises the following step: a prefabricated body wax-pattern and a back of the body combination wax-pattern; This body wax-pattern correspondence is bonded in this back of the body combination wax-pattern, makes this body wax-pattern and back of the body combination wax-pattern be combined into a bar head wax-pattern; And repair processing in conjunction with intersection at this body wax-pattern and back of the body combination wax-pattern.Wherein:
Described body wax-pattern is only put corresponding to the back of the body acupuncture point of this body wax-pattern with the position of cohering of back of the body combination wax-pattern.Described body wax-pattern and the cave is only carried on the back at the position corresponding to this body wax-pattern the back bottom position that coheres of carrying on the back the combination wax-pattern.Described body wax-pattern is provided with a body butting section and a supporting part, and this back of the body combination wax-pattern is provided with a back of the body combination butting section and a joint portion, an end.The body butting section of described body wax-pattern and supporting part are formed at the bottom inner edge of this body wax-pattern, and have one between the body butting section of this body wax-pattern and the supporting part for the back of the body combination butting section of this back of the body combination wax-pattern of corresponding bonding and the angle of joint portion, the end.The actual panel part that is parallel to one of this body wax-pattern in the body butting section of described body wax-pattern, and this supporting part reality is perpendicular to the panel part of this body wax-pattern.Two ends of the joint portion, the end of the supporting part of described body wax-pattern and back of the body combination wax-pattern are extending upward of circular arc.Described body wax-pattern is provided with a supporting part and two side butting sections, and this back of the body combination wax-pattern is provided with joint portion, an end and two side joint portions, and should the corresponding respectively regional area that is bonded in this supporting part and two side butting sections in joint portion, the end and two side joint portions.The bottom inner edge of described body wax-pattern forms and reaches a upwards open short slot backward, and this supporting part is formed at the bottom side of this short slot, and this two sides butting section is formed at this short slot respectively near a toe of this body wax-pattern and two sides of a heel.Described body wax-pattern and the common open room that makes progress that forms of combination wax-pattern.Described room is selected an earthquake absorption block of a ccontaining hyperbaric balancing weight or Highly-absorbing.Described body wax-pattern is provided with a body butting section and two side butting sections, and this back of the body combination wax-pattern is provided with a back of the body combination butting section and two side joint portions.Described body wax-pattern is open shape near the bottom side at the back side, and has one between the body butting section of this body wax-pattern and the two side butting sections for the back of the body combination butting section of this back of the body combination wax-pattern of corresponding bonding and the angle of two side joint portions.The body butting section of described body wax-pattern extends downward the bottom of this body wax-pattern, and two side butting sections of this body wax-pattern are formed at the two side inner edges of this body wax-pattern near a toe and a heel respectively.Described body wax-pattern is provided with a panel part and a cover neck in addition.Described back of the body combination wax-pattern is provided with a wall portion in addition, the common back of the body cave with deep hole moulding that forms of the panel part of this wall portion and this body wax-pattern and the bottom inner edge of body wax-pattern.
Moreover this bar head wax-pattern can further be applied to the hot investment casting processing procedure, its step: this bar head wax-pattern is stained with slurry, then the wax hot melt is poured out, to form an arenaceous shell mould; Molten metal is injected this arenaceous shell mould, treat to break up this arenaceous shell mould after molten metal solidifies, can take out the bar head foundry goods of moulding; At last this bar head foundry goods is carried out surface treatment.
The invention has the advantages that:
1, because its body wax-pattern has the integrated structure that is complementary with back of the body combination wax-pattern, and two coupling integrated structures are only put corresponding to the back of the body acupuncture point of this body wax-pattern, so being bonded in this back of the body combination wax-pattern, this body wax-pattern forms bar head wax-pattern, the two in conjunction with intersection only in the regional area in back of the body cave, not only can reduce the trim length on bar head wax-pattern surface, and can reduce the surfacing workload of the metallic rod head of casting, and then when reducing the worker of golf driver head and manufacturing cost.
2, because its back of the body combination wax-pattern is bonded in the body wax-pattern, what make bar head wax-pattern only is formed at the back bottom of body wax-pattern in conjunction with intersection, not only can reduce the surfacing workload of bar head wax-pattern and metal casting, and combine compactness between the panel part that can guarantee foundry goods and rod head noumenon, promote of the present invention in conjunction with reliability.
3, since its body wax-pattern and back of the body combination wax-pattern make respectively by two metal dies, and each metal die only needs to be made up of more a spot of relatively mould, can reduce the manufacturing cost of mould and the difficulty of dismounting mould relatively, therefore, the present invention can obviously reduce the manufacturing cost and the manufacture difficulty of wax-pattern.
Description of drawings
Fig. 1, for commonly using the cutaway view of Wax mould combining method of glof club head.
Fig. 2, for commonly using the three-dimensional exploded view of glof club head Wax mould combining method Wax mold group.
Fig. 3, be process block diagram of the present invention.
Fig. 4, be the three-dimensional exploded view of first embodiment of the invention.
Fig. 5, be the rearview of first embodiment of the invention.
Fig. 6, be the 6-6 cutaway view among Fig. 5.
Fig. 7, be the three-dimensional exploded view of second embodiment of the invention.
Fig. 8, be the rearview of second embodiment of the invention.
Fig. 9, be the 9-9 cutaway view among Fig. 8.
Figure 10, be the three-dimensional exploded view of third embodiment of the invention.
Figure 11, be the rearview of third embodiment of the invention.
Figure 12, be the 12-12 cutaway view among Figure 11.
The specific embodiment
Further to understand and be familiar with in order to have, lift the number preferred embodiment now, and conjunction with figs. is described in detail as follows purpose of the present invention, technical characterictic and advantage thereof:
Please refer to shown in Fig. 3,4, the first embodiment of the present invention, a kind of Wax mould combining method of glof club head, first step: a prefabricated body wax-pattern 1 and a back of the body combination wax-pattern 2, this body wax-pattern 1 is provided with a body butting section 13 and a supporting part 14, and this back of the body combination wax-pattern 2 is provided with a back of the body combination butting section 21 and a joint portion, an end 22.At first, wax liquid is injected in the two molds group (not shown in the figures), make this body wax-pattern 1 and back of the body combination wax-pattern 2 respectively, each set of molds is combined by two molds (not shown in the figures) at least respectively.This body wax-pattern 1 constitutes the main framework of this golf driver head wax-pattern (not shown in the figures), and this body wax-pattern 1 has a back of the body cave 10, a panel part 11, cover neck 12, a body butting section 13 and a supporting part 14.The front and the back side of this body wax-pattern 1 is run through in this back of the body cave 10.This panel part 11 is shaped in the front of this body wax-pattern 1.This cover neck 12 is formed at a side of this body wax-pattern 1, with in conjunction with a body of rod (not shown in the figures).This body butting section 13 and supporting part 14 are formed at the bottom inner edge of this body wax-pattern 1, this body butting section 13 and supporting part 14 make up the length of patch cord only corresponding to the position in this body wax-pattern 1 back of the body cave 10 with the wax-pattern that reduces 2 of this body wax-pattern 1 and back of the body combination wax-patterns.Has certain angle between this body butting section 13 and the supporting part 14.These body butting section 13 actual panel part 11 that are parallel to this body wax-pattern 1, these supporting part 14 reality are perpendicular to the panel part 11 of this body wax-pattern 1, and two ends of this supporting part 14 are circular arc and extend upward.
Shown in Fig. 3,4, this back of the body combination wax-pattern 2 is provided with the back of the body combination butting section 21, joint portion, an end 22 and a wall portion 23.This back of the body combination butting section 21 and joint portion, the end 22 are formed at the position of this back of the body combination wax-pattern 2 near the bottom, and this back of the body combination butting section 21 and joint portion, the end 22 correspond respectively to the body butting section 13 and the supporting part 14 of this body wax-pattern 1, and joint portion, the end 22 2 ends that should back of the body make up wax-pattern 2 are circular arc and extend upward.This wall portion 23 is in order to form the back of the body cave 10 with deep hole (undercut) moulding jointly with the panel part 11 of this body wax-pattern 1 and the bottom (not shown) inner edge of body wax-pattern.
Please refer to shown in Fig. 3,5,6, second step of first embodiment of the invention: body butting section 13 and corresponding respectively back of the body combination butting section 21 and the joint portion, the end 22 that is bonded in this back of the body combination wax-pattern 2 of supporting part 14 with this body wax-pattern 1 make this body wax-pattern 1 and back of the body combination wax-pattern 2 be combined into a bar head wax-pattern (not shown in the figures).Utilize suitable sticker (not shown in the figures), as wax liquid or high volatile volatile solvent etc., this body wax-pattern 1 and back of the body combination wax-pattern 2 are cohered combination, back of the body combination butting section 21 correspondences that also are about to this back of the body combination wax-pattern 2 are bonded in the body butting section 13 of this body wax-pattern 1, and joint portion, the end 22 correspondences that will carry on the back combination wax-pattern 2 simultaneously are bonded in the supporting part 14 of this body wax-pattern 1.Take this, the body butting section 13 of this body wax-pattern 1 can avoid this back of the body combination wax-pattern 2 to produce the displacement that is parallel to direction of stroke; The supporting part 14 of this body wax-pattern 1 can avoid this back of the body combination wax-pattern 2 to produce the displacement of above-below direction, and can avoid producing the displacement towards one of this bar head wax-pattern 1 toe a or heel b, thereby increases bond strength relatively.At this moment, this body wax-pattern 1 forms a closing line c (as shown in Figure 6) with the intersection appearance that combines of back of the body combination wax-pattern 2.
Please refer to shown in Fig. 3,5,6 third step of first embodiment of the invention: repair processing at this body wax-pattern 1 and the combination intersection of back of the body combination wax-pattern 2.After this body wax-pattern 1 coheres combination with back of the body combination wax-pattern 2, may form gap or rough surface between this body wax-pattern 1 and the back of the body combination wax-pattern 2, therefore, the repairing to the closing line c position of 2 of this body wax-pattern 1 and back of the body combination wax-patterns can further promote the wax-pattern quality.Because this closing line c only is formed at the regional area at this bar head wax-pattern (not shown in the figures) back side, therefore, can shortens wax-pattern relatively and repair length.
Referring again to shown in Figure 3, the bar head wax-pattern (not shown in the figures) that first embodiment of the invention is made can further be applied to the hot investment casting processing procedure, this processing procedure comprises the following step: (1), this bar head wax-pattern (not shown in the figures) is stained with slurry, afterwards wax liquid hot melt is poured out, to form an arenaceous shell mould (ceramic shell, not shown in the figures).This bar head wax-pattern can and be stained with the sand technology by general known soaking paste, forms the arenaceous shell mould; (2), molten metal is injected this arenaceous shell mould, treat to break up the arenaceous shell mould after molten metal solidifies, can take out the bar head foundry goods (not shown in the figures) of moulding.This arenaceous shell mould can be by general known foundry engieering, to form this bar head foundry goods; (3), this bar head foundry goods is carried out surface treatment.When bar head cast casting moulding of the present invention, may be corresponding to closing line c place generation gap or the rough surface of this body wax-pattern 1 with back of the body combination wax-pattern 2.Therefore, adopt suitable polishing finishing processing, can further promote the surface flatness of this bar head foundry goods.
Please refer to shown in Fig. 7-9, the implementation step of second embodiment of the invention and first embodiment are basic identical, difference is: the body wax-pattern 1 of second embodiment is provided with a supporting part 13 ' and two side butting sections 14 ', and this back of the body combination wax-pattern 2 is provided with joint portion, an end 21 ' and two side joint portions 22 '.The bottom inner edge of this body wax-pattern 1 forms backward, upwards one of opening short slot 15, and this supporting part 13 ' is formed at the bottom of this short slot 15, and this two sides butting section 14 ' is formed at two sides of this short slot 15 near toe a and heel b respectively.Has an angle between this supporting part 13 ' and the two side butting sections 14 ', so that combine with the joint portion, the end 21 ' and the two side joint portions 22 ' of this back of the body combination wax-pattern 2.The joint portion, the end 21 ' of this back of the body combination wax-pattern 2 is formed at the bottom of this back of the body combination wax-pattern 2, this two sides joint portion 22 ' is formed at two sides of this back of the body combination wax-pattern 2 respectively, and should joint portion, the end 21 ' and two side joint portions 22 ' correspond respectively to the supporting part 13 ' and the two side butting sections 14 ' of this body wax-pattern 1.
Shown in Fig. 7-9, when second embodiment of the invention is tentatively assembled, the joint portion, the end 21 ' of this back of the body combination wax-pattern 2 is resisted against the supporting part 13 ' of this body wax-pattern 1, and a side near this body wax-pattern 1 back, that is the outside of this back of the body combination wax-pattern 2 side of the panel part 11 of this body wax-pattern 1 (promptly away from) and the back of this body wax-pattern 1 form the back outer surface of this bar head wax-pattern (not shown in the figures) jointly, form one of upwards open room so this back of the body combination wax-pattern 2 and body wax-pattern 1 be common, it is the local space (as shown in Figure 9) of short slot 15, this room can be in order to the balancing weight (not shown in the figures) of ccontaining high specific gravity material, or the earthquake absorption block of ccontaining Highly-absorbing material (not shown in the figures).Simultaneously, the back side of this bar head wax-pattern forms a closing line d.
Shown in Fig. 7-9, when second embodiment of the invention is carried out the surface treatment of wax-pattern repairing or foundry goods, only need to this bar head wax-pattern (not shown in the figures) or bar head foundry goods (not shown in the figures) to should body wax-pattern 1 and back of the body combination wax-pattern 2 in conjunction with intersection, that is the closing line d position of this bar head foundry goods processes processing.
Please refer to shown in Figure 10-12, the implementation step of third embodiment of the invention and first embodiment are basic identical, difference is: the body wax-pattern 1 of the 3rd embodiment is provided with a body butting section 13 " and two side butting sections 14 ", this back of the body combination wax-pattern 2 is provided with a back of the body combination butting section 21 " and two side joint portions 22 ".This body wax-pattern 1 is open shape near the bottom side at the back side, that is the body butting section 13 of this body wax-pattern 1 " extend downward the bottom of this body wax-pattern 1, two side butting sections 14 of this body wax-pattern 1 " be formed at the two side inner edges of this body wax-pattern 1 near toe a and heel b.The body butting section 13 of this body wax-pattern 1 " and two side butting sections 14 " between have an angle so that with the back of the body combination butting section 21 of this back of the body combination wax-pattern 2 " and two side joint portions 22 " combine.Two side joint portions 22 of this back of the body combination wax-pattern 2 " select to be formed at the back of the body combination butting section 21 of this back of the body combination wax-pattern 2 " two sides, and two side butting sections 14 of this body wax-pattern 1 " the side joint portion 22 of making up wax-pattern 2 corresponding to this back of the body ".When preliminary assembling, the back of the body combination butting section 21 of this back of the body combination wax-pattern 2 " be resisted against the body butting section 13 of this body wax-pattern 1 ", and the two side joint portions 22 of should back of the body making up wax-pattern 2 " be incorporated into two side butting sections 14 of this body wax-pattern 1 ".At this moment, this back of the body combination wax-pattern 2 forms same plane with the back side and the bottom surface of body wax-pattern 1, that is forms surface outside the back of this bar head wax-pattern (not shown in the figures) and the bottom jointly.Simultaneously, the back side of this bar head wax-pattern and bottom surface form a closing line e.
Shown in Figure 10-12, when third embodiment of the invention is carried out the surface treatment of wax-pattern repairing or foundry goods, only need this bar head wax-pattern (not shown in the figures) or bar head foundry goods (not shown in the figures) should body wax-pattern 1 making up the intersection that combines of wax-pattern 2, that is the closing line e position of this bar head foundry goods processes processing with the back of the body.
Please refer to shown in Fig. 3-12, the Wax mould combining method of the glof club head of the present invention first to three embodiment, all utilize at least two molds group (not shown in the figures) to make simply constructed this body wax-pattern 1 and back of the body combination wax-pattern 2 respectively, this bar head wax-pattern (not shown in the figures) of forming complex structure again by this body wax-pattern 1 and back of the body combination wax-pattern 2, therefore mold structure be can effectively simplify, and then the convenience and the processing procedure efficient of processing procedure promoted relatively.In addition, because this body wax-pattern 1 only is formed at the back side of this bar head wax-pattern and the regional area of bottom surface with the intersection that combines of back of the body combination wax-pattern 2, therefore can reduce the trim length of this bar head wax-pattern (not shown in the figures) relatively, and then promote the convenience of processing procedure and effectively reduce process time.Moreover the body butting section 13 of this body wax-pattern 1 and supporting part 14 can provide auxiliary positioning function with the back of the body combination butting section 21 and the joint portion, the end 22 of back of the body combination wax-pattern 2, take this further to promote bond strength.In addition, because the finishing position of this bar head foundry goods only is positioned at the back side of this bar head foundry goods, thereby guarantee the compactness and the structural strength of structure between the rod head noumenon of this bar head foundry goods and panel part (not shown in the figures), and then promote in conjunction with reliability.
As mentioned above, there is the trim length that increases wax-pattern surface engagement line relatively in the Wax mould combining method of commonly using glof club head, so that increases shortcomings such as manufacturing cost and process time; And the present invention as shown in Figure 3, utilize two molds group (not shown in the figures) to make this body wax-pattern 1 and back of the body combination wax-pattern 2 respectively, and this body wax-pattern 1 and cave 10 is only carried on the back at the position corresponding to one of this body wax-pattern 1 the position of cohering of carrying on the back combination wax-pattern 2, so the body butting section 13 of this body wax-pattern 1 is bonded in the back of the body combination butting section 21 of this back of the body combination wax-pattern 2, and the supporting part 14 of this body wax-pattern 1 is bonded in the joint portion, the end 22 of this back of the body combination wax-pattern 2, can have under the preceding topic of enough bond strengths, reduce the length of surface engagement line c as far as possible, can effectively shorten refacing length really.
Claims (16)
1, a kind of Wax mould combining method of glof club head, it comprises the following step:
A prefabricated body wax-pattern and a back of the body combination wax-pattern;
This body wax-pattern correspondence is bonded in this back of the body combination wax-pattern, makes this body wax-pattern and back of the body combination wax-pattern be combined into a bar head wax-pattern; And
Repair processing at this body wax-pattern and back of the body combination wax-pattern in conjunction with intersection.
2, according to the Wax mould combining method of the described glof club head of claim 1, it is characterized in that: described body wax-pattern is only put corresponding to the back of the body acupuncture point of this body wax-pattern with the position of cohering of back of the body combination wax-pattern.
3, according to the Wax mould combining method of the described glof club head of claim 2, it is characterized in that: described body wax-pattern and the cave is only carried on the back at the position corresponding to this body wax-pattern the back bottom position that coheres of carrying on the back the combination wax-pattern.
4, according to the Wax mould combining method of the described glof club head of claim 1, it is characterized in that: described body wax-pattern is provided with a body butting section and a supporting part, and this back of the body combination wax-pattern is provided with a back of the body combination butting section and a joint portion, an end.
5, according to the Wax mould combining method of the described glof club head of claim 4, it is characterized in that: the body butting section of described body wax-pattern and supporting part are formed at the bottom inner edge of this body wax-pattern, and have one between the body butting section of this body wax-pattern and the supporting part for the back of the body combination butting section of this back of the body combination wax-pattern of corresponding bonding and the angle of joint portion, the end.
6, according to the Wax mould combining method of the described glof club head of claim 4, it is characterized in that: the actual panel part that is parallel to one of this body wax-pattern in the body butting section of described body wax-pattern, and this supporting part reality is perpendicular to the panel part of this body wax-pattern.
7, according to the Wax mould combining method of the described glof club head of claim 4, it is characterized in that: two ends of the joint portion, the end of the supporting part of described body wax-pattern and back of the body combination wax-pattern are extending upward of circular arc.
8, according to the Wax mould combining method of the described glof club head of claim 1, it is characterized in that: described body wax-pattern is provided with a supporting part and two side butting sections, this back of the body combination wax-pattern is provided with joint portion, an end and two side joint portions, and should the corresponding respectively regional area that is bonded in this supporting part and two side butting sections in joint portion, the end and two side joint portions.
9, the Wax mould combining method of described glof club head according to Claim 8, it is characterized in that: the bottom inner edge of described body wax-pattern forms and reaches a upwards open short slot backward, this supporting part is formed at the bottom side of this short slot, and this two sides butting section is formed at this short slot respectively near a toe of this body wax-pattern and two sides of a heel.
10, according to the Wax mould combining method of claim 1 or 8 described glof club heads, it is characterized in that: described body wax-pattern and the common open room that makes progress that forms of combination wax-pattern.
11, according to the Wax mould combining method of the described glof club head of claim 10, it is characterized in that: described room is selected an earthquake absorption block of a ccontaining hyperbaric balancing weight or Highly-absorbing.
12, according to the Wax mould combining method of the described glof club head of claim 1, it is characterized in that: described body wax-pattern is provided with a body butting section and two side butting sections, and this back of the body combination wax-pattern is provided with a back of the body combination butting section and two side joint portions.
13, according to the Wax mould combining method of the described glof club head of claim 12, it is characterized in that: described body wax-pattern is open shape near the bottom side at the back side, and has one between the body butting section of this body wax-pattern and the two side butting sections for the back of the body combination butting section of this back of the body combination wax-pattern of corresponding bonding and the angle of two side joint portions.
14, according to the Wax mould combining method of the described glof club head of claim 12, it is characterized in that: the body butting section of described body wax-pattern extends downward the bottom of this body wax-pattern, and two side butting sections of this body wax-pattern are formed at the two side inner edges of this body wax-pattern near a toe and a heel respectively.
15, according to the Wax mould combining method of the described glof club head of claim 1, it is characterized in that: described body wax-pattern is provided with a panel part and a cover neck in addition.
16, according to the Wax mould combining method of the described glof club head of claim 15, it is characterized in that: described back of the body combination wax-pattern is provided with a wall portion in addition, the common back of the body cave with deep hole moulding that forms of the panel part of this wall portion and this body wax-pattern and the bottom inner edge of body wax-pattern.