CN1916241A - Acidic cleaner for carbon steel and applications - Google Patents
Acidic cleaner for carbon steel and applications Download PDFInfo
- Publication number
- CN1916241A CN1916241A CN 200610046256 CN200610046256A CN1916241A CN 1916241 A CN1916241 A CN 1916241A CN 200610046256 CN200610046256 CN 200610046256 CN 200610046256 A CN200610046256 A CN 200610046256A CN 1916241 A CN1916241 A CN 1916241A
- Authority
- CN
- China
- Prior art keywords
- carbon steel
- clean
- scavenging solution
- acidic cleaner
- out system
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses an acidic detergent for carbon steel and its application. The acidic detergent is composed of xacin-series antibacterial drug and 0.1-2 M acid solution at a ratio of 0.010-5.0 kg/L. The acidic detergent can be applied by soaking carbon steel in the acidc detergent at room temperature for 15 min-3 h. The acidic detergent can prevent carbon steel from local or whole corrosion, and has such advantages as low usage amount, high corrosion-inhibiting efficiency, long effective time, no harm to the environment or creatures, etc., thus having good application potential.
Description
Technical field
The present invention relates to belong to the inhibiter production technical field, a kind of specifically in order to prevent unnecessary general corrosion and local corrosive carbon steel acidic cleaner and the application thereof in acid cleaning process of carbon steel and goods thereof.
Background technology
Carbon steel has favorable mechanical performance and processing performance, and cheap, and the application in all trades and professions more and more widely.In its product processing and application process, dilute sulphuric acid commonly used or dilute hydrochloric acid carry out pickling, can remove the oxide film or the corrosion product on surface, harmful corrosive that consumes excessively and prevent of metal or acid takes place in the acid cleaning process, and adding inhibiter in acid is effective means.
In the restrainer commonly used at present, mainly comprise the inorganic inhibition compound that contains poisonous chromate, and some organophosphor compounds, its discharging may cause the eutrophication of water body.The inhibiter of existing same domain mostly has toxic side effect, does not possess the market competitiveness.
Therefore, develop new environmental protection, cheapness, wide material sources, restrainer nuisanceless and that inhibition efficiency is high are the new directions of present inhibiter exploitation.
Summary of the invention
The object of the present invention is to provide a kind of environmental protection that has, cheapness, wide material sources, the carbon steel acidic cleaner of nuisanceless characteristics is in order to prevent carbon steel and goods thereof unnecessary general corrosion and local corrosion in acid cleaning process; The application of superloy acidic cleaner also is provided.
Technical scheme of the present invention is: superloy acidic cleaner composition is the xacin-series antibacterials; Wherein: the xacin-series antibacterials are one or both in Ciprofloxacin, norfloxicin, Ofloxacine USP 23, levofloxacin or the enoxacin.When wherein the clean-out system composition is two kinds of xacin-series antibacterials, both by weight percentage compound proportion be 1: 99-99: 1.The application of described carbon steel acidic cleaner is cleaned steel with the scavenging solution submergence that is added with clean-out system.Wherein scavenging solution is an acid solution, and adding cleaning dosage in every liter of acid solution is 0.010Kg-5.0Kg; The submergence temperature is a room temperature, and the time is 0.5-3h; Wherein: acid solution is dilute hydrochloric acid or the dilution heat of sulfuric acid of 0.1-2M.
Principle of the present invention is: the xacin-series antibacterials have the heterogeneous ring compound of pyridine structure, and intramolecularly contains atom or atomic groups such as heterocycle, nitrogen, oxygen, can be adsorbed in steel surface effectively, plays corrosion inhibition.
The invention has the beneficial effects as follows:
(1) clean-out system proportioning of the present invention is simple, the main component xacin-series antibacterials wide material sources that use in the clean-out system, and market quotes in 2006 is at 400-800 unit/kilogram, and cost is lower.
(2) clean-out system of the present invention uses crude substance as inhibiter, from natural Chinese medicinal herb such as the root of herbaceous peony, extract, be nontoxic green matter, compare with the inhibiter of present chemosynthesis, there is not the environmental problem after the use, harmless to environment and biological nontoxic, meet the trend that restrainer develops, have a good application prospect.
(3) the present invention is used for the industrial acid-washed of carbon steel and products thereof, can effectively suppress the harmful corrosion of metallic matrix in acid, with restrainer at present commonly used relatively, it is low to have a consumption, the inhibition efficiency height, the outstanding advantage that continuous action ability is strong can be used repeatedly.
Embodiment
The present invention carries out the lacing film zero-G test according to GB10124-88 " metallic substance laboratory uniform corrosion total immersion test method ".
Embodiment 1
The dilute hydrochloric acid of getting 100L concentration 0.1M is scavenging solution, then adds Ciprofloxacin 50g, at ambient temperature, carbon steel to be cleaned is immersed in 15min gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 96%, is shown as clean-out system efficiently.
Embodiment 2
The dilute hydrochloric acid of getting 100L concentration 0.2M is scavenging solution, then adds Ofloxacine USP 23 70g, at ambient temperature, carbon steel to be cleaned is immersed in 2h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 97%, is shown as clean-out system efficiently.
Embodiment 3
The dilute hydrochloric acid of getting 100L concentration 0.5M is scavenging solution, then adds norfloxicin 100g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 97%, is shown as clean-out system efficiently.
Embodiment 4
The dilute hydrochloric acid of getting 100L concentration 0.5M is scavenging solution, then adds levofloxacin 100g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 98%, is shown as clean-out system efficiently.
Embodiment 5
The dilute hydrochloric acid of getting 100L concentration 1M is scavenging solution, then adds enoxacin 150g, at ambient temperature, carbon steel to be cleaned is immersed in 30min gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 98%, is shown as clean-out system efficiently.
Embodiment 6
The dilute hydrochloric acid of getting 100L concentration 0.5M is scavenging solution, then adds norfloxicin 50g, Ciprofloxacin 50g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 98%, is shown as clean-out system efficiently.
Embodiment 7
The dilute hydrochloric acid of getting 100L concentration 1M is scavenging solution, then adds levofloxacin 100g, enoxacin 50g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 99%, is shown as clean-out system efficiently.
Embodiment 8
The dilute sulphuric acid of getting 100L concentration 0.1M is a scavenging solution, then adds norfloxicin 50g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 96%, is shown as clean-out system efficiently.
Embodiment 9
The dilute sulphuric acid of getting 100L concentration 0.5M is a scavenging solution, then adds levofloxacin 100g, at ambient temperature, carbon steel to be cleaned is immersed in 2h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 96%, is shown as clean-out system efficiently.
Embodiment 10
The dilute sulphuric acid of getting 100L concentration 1M is a scavenging solution, then adds Ciprofloxacin 170g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 99%, is shown as clean-out system efficiently.
Embodiment 11
The dilute sulphuric acid of getting 100L concentration 0.5M is a scavenging solution, then adds norfloxicin 50g, Ofloxacine USP 23 100g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is 99%, is shown as clean-out system efficiently.
Embodiment 12
The dilute sulphuric acid of getting 100L concentration 0.5M is a scavenging solution, then adds enoxacin 100g, Ciprofloxacin 100g, at ambient temperature, carbon steel to be cleaned is immersed in 1h gets final product in the scavenging solution.
The highest inhibition efficiency that obtains by experimental test is shown as clean-out system efficiently more than 96%.
Claims (4)
1. superloy acidic cleaner, it is characterized in that: composition is the xacin-series antibacterials; Wherein: the xacin-series antibacterials are one or both in Ciprofloxacin, norfloxicin, Ofloxacine USP 23, levofloxacin or the enoxacin.
2. by right 1 described carbon steel acidic cleaner, it is characterized in that: wherein the clean-out system composition is two kinds of xacin-series antibacterials, its both by weight percentage compound proportion be 1: 99-99: 1.
3. application by right 1 described carbon steel acidic cleaner is characterized in that: clean steel with the scavenging solution submergence that is added with clean-out system.
4. by the application of the described carbon steel acidic cleaner of claim 2, it is characterized in that: wherein scavenging solution is an acid solution, and adding cleaning dosage in every liter of acid solution is 0.010Kg-5.0Kg; The submergence temperature is a room temperature, and the time is 0.5-3h;
Wherein: acid solution is dilute hydrochloric acid or the dilution heat of sulfuric acid of 0.1-2M.