CN1896031A - Formula of high-strength light ceramic grain made from fly-ash - Google Patents
Formula of high-strength light ceramic grain made from fly-ash Download PDFInfo
- Publication number
- CN1896031A CN1896031A CNA2006100866654A CN200610086665A CN1896031A CN 1896031 A CN1896031 A CN 1896031A CN A2006100866654 A CNA2006100866654 A CN A2006100866654A CN 200610086665 A CN200610086665 A CN 200610086665A CN 1896031 A CN1896031 A CN 1896031A
- Authority
- CN
- China
- Prior art keywords
- fly
- ash
- formula
- strength
- ceramic grain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Formula of high-strength light fly ash ceramsite consists of fly ash 55-70wt%, binder 25-35wt% and additive 3-8wt%. The pressure of ceramsite reaches to 7.3Mpa and compression strength of concrete reaches to 41.4MP. It is light and has high strength.
Description
One, technical field
The present invention relates to a kind of light, and high-strength fly-ash haydite prescription, belong to building field.
Two, background technology
At present lytag is to be main raw material with flyash, adds a small amount of matrix material, forms through batching balling-up, sintering (or maintenance).The existing good workability of this product reaches the associativity with the cement bond material, so that good heat insulation and heat insulation effect to be arranged.But because lytag self intensity is low, great majority are used for producing light heat insulation blocks, sand-free coarse porous concrete haydite concrete, plain concrete and low strength light weight concrete.Reference; Total utilization of PCA Newest practical technology compilation, the total utilization of PCA magazine was published in 1998.
Light high strength concrete is the material of construction of often using in the building; it has in light weight, advantages of high strength; particularly in heavy construction and high-rise common engineering, has application value; because leca, haydites of book structure and the lytag of producing all belongs to common middle low strength haydite at present, can't be used for the formulation problems of the light ceramsite concrete of production high strength (ultimate compression strength is greater than 30MPa).
Three, summary of the invention
The technical problem that the present invention solves is: a kind of in light weight, high strenght flyash ceramic grain is provided, can makes the light ceramsite concrete of ultimate compression strength greater than 40MPa with the high strenght flyash ceramic grain.
Technical solution:
The present invention is made up of following material: flyash 55-70%, binding agent 25-35%, admixture 3-8%.
Binding agent can be the mixture of clay or clay and water glass.
Admixture can be waste steel slag or pyrite slag.
If adopt the mixture of clay and water glass, the water glass addition is 2%~3%.
Detect through experiment, in light weight through the lytag that the present invention makes, intensity is high, the cylindrical compress strength of haydite reaches 7.3MPa, is that its ultimate compression strength of concrete that aggregate is prepared reaches 41.4MP with the lytag, and its weight ratio adopts the concrete light 26.3% of stone as aggregate.
Five, embodiment
Embodiment 1: the present invention is made up of following material: flyash 65%, clay plasticity index 〉=14, get clay 30%, pyrite slag 5%.
Embodiment 2: the present invention is made up of following material: flyash 65%, 12≤clay plasticity index<14, get clay 27%, water glass 3%, pyrite slag 5%.
Claims (4)
1, formula of high-strength light ceramic grain made from fly-ash is characterized in that: be made up of following material: flyash 55-70%, binding agent 25-35%, admixture 3-8%.
2, formula of high-strength light ceramic grain made from fly-ash according to claim 1 is characterized in that: binding agent can be the mixture of clay or clay and water glass.
3, formula of high-strength light ceramic grain made from fly-ash according to claim 1 is characterized in that: admixture can be waste steel slag or pyrite slag.
4, light, and high-strength fly-ash haydite prescription according to claim 2, it is characterized in that: if adopt the mixture of clay and water glass, the water glass addition is 2%~3%.