CN1869136A - Anticorrosion abrasive resistant paint - Google Patents
Anticorrosion abrasive resistant paint Download PDFInfo
- Publication number
- CN1869136A CN1869136A CN 200510026061 CN200510026061A CN1869136A CN 1869136 A CN1869136 A CN 1869136A CN 200510026061 CN200510026061 CN 200510026061 CN 200510026061 A CN200510026061 A CN 200510026061A CN 1869136 A CN1869136 A CN 1869136A
- Authority
- CN
- China
- Prior art keywords
- resistant paint
- abrasive resistant
- epoxy
- anticorrosion
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relate to anticorrosion and antifriction coating. Its component and weight content are as follows: epoxy resin 20-40%, fluorin olefin resin 10-15%, ceramics micro-powder 30-50%, and epoxy resin curing agent 15-20%. It can be used to make protecting coating with high abrasion resistance and adhesive force.
Description
Technical field
The present invention relates to coating, relate in particular to a kind of anticorrosion abrasive resistant paint.
Background technology
The used pipeline majority of petroleum industry is used for conveying crude oil, sewage, water filling etc., and these delivery mediums not only contain various admixtures in water filling, the sewage and acid, alkali, salt medium, or even drilling mud, seawater etc.This medium not only corrodes tube wall, and quite serious to transducer wall ' s abrasion, wherein also comprises will being subjected to the wearing and tearing of silt particle from the water pipe of water source diversion.The wear-resistant coating that Chinese patent CN1325931A announces changes in 750 gram counterweights 500, and weightlessness just reaches 21mg.Existing epoxy coat under equal conditions, wear-resisting weightlessness is also about 80～100mg.
Summary of the invention
Purpose of the present invention is exactly to provide a kind of anticorrosion abrasive resistant paint in order to overcome the defective that above-mentioned prior art exists, and this coating can be equipment and provides a kind of and have than high-wearing feature, shock resistance, high adhesive force, tough and tensile supercoat.
Purpose of the present invention can be achieved through the following technical solutions: a kind of anticorrosion abrasive resistant paint, it is characterized in that this coating comprises following component and weight % content: Resins, epoxy 20～40%, fluoroolefin resin 10～15%, ceramic 30～50%, epoxy curing agent 15～20%.
Also comprise toughened resin 1～5 weight %.
Also comprise titanium dioxide 5～10 weight %.
Described Resins, epoxy is bisphenol A epoxide resin, and it comprises and is selected from a kind of in E03, E06, E14, E44, the E42 Resins, epoxy.
Described fluoroolefin resin comprises and is selected from a kind of in poly-trifluoro second propylene, tetrafluoroethylene, the daiflon.
Described ceramic is the submicron ceramics powder, comprises the hollow beads ceramics powder.
Described epoxy curing agent comprises and is selected from a kind of among resol, polyamide resin, ARADUR14 (Eylau reaches company's product), the ARADUR960-1 (Eylau reaches company's product).
The invention provides a kind of epoxy ceramic coating, form by titanium dioxide, mica powder, tinting pigment, ceramic and submicron hollow ceramic micro mist, Resins, epoxy, resol, fluoro-resin, toughened resin, epoxy curing agent, curing catalyst with excellent non-corrosibility.Resins, epoxy wherein is base-material with high molecular expoxy resin (molecular weight 2900～3750) with resol, aminoresin, is aided with toughened resin and makes the hot setting coating, can be used for preparing the interior anticorrosive coating of drilling rod coating, oil pipe of petroleum drilling.Adopt low-molecular-weight epoxy resin, be equipped with ambient cure agent, promotor and make ambient cure even can low temperature (15 ℃) solidified epoxy coat.Can be used for oil-field flooding, sewage and city tap-water pipeline internal corrosion erosion coating.The coating that above ambient cure and baked paint are made has fabulous non-corrosibility, wear resistance, adopt Table abrasion instrument, 1000 gram counterweights, 1000 change weightless below 3mg, and the wear-resistant coating that (imponderability is poor sometimes) announces than publication number CN1325931A (750 grams/500 change weightless 21mg) is improved.(general normal-temperature curing epoxy coating, weightlessness under the equal conditions＞80mg) are applicable to that more petroleum drilling, oil recovery, water filling, sewage, seawater and tap water carry (this coating is nontoxic through sanitary inspection) and natural gas line inwall to do drag reduction wear-resistant coating and terrace paint etc.
Coating of the present invention has excellent abrasion resistance, and this coating makes it more be applicable to petroleum drilling, water filling sink drainage, water source diversion system, potable water supply system, oceanographic engineering, natural gas transmission pipeline and storage tank protection against corrosion in the improvement of acid-and base-resisting corrodibility, wear resistance.
The invention solves oil field downhole drill, oil recovery, water filling sink drainage, under deep-well high salinity, the HI high impact abrasive environment, anticorrosion protecting against shock and abrasion problem.
Embodiment
The invention will be further described below in conjunction with specific embodiment.
Embodiment 1:
A kind of anticorrosion abrasive resistant paint, this coating comprise following component and weight % content: bisphenol A epoxide resin (E03 Resins, epoxy) 30%, tetrafluoroethylene 12%, hollow beads ceramics powder 35%, resol 15%, toughened resin 3 weight %, titanium dioxide 5 weight %.
Embodiment 2
A kind of anticorrosion abrasive resistant paint, this coating comprise following component and weight % content: bisphenol A epoxide resin (E06 Resins, epoxy) 40%, poly-trifluoro second propylene 10%, submicron ceramics powder 30%, polyamide resin 20%.
Embodiment 3
A kind of anticorrosion abrasive resistant paint, this coating comprise following component and weight % content: bisphenol A epoxide resin (E14 Resins, epoxy) 20%, voltalef 10%, hollow beads ceramics powder 50%, ARADUR14 (Eylau reaches company's product) 20%.
Embodiment 4
A kind of anticorrosion abrasive resistant paint, this coating comprise following two-pack and weight % content:
The A component:
Bisphenol A epoxide resin (E44 Resins, epoxy) 30%, poly-trifluoro second propylene 15%, hollow beads ceramics powder 40%, titanium dioxide 5 weight %;
The B component:
ARADUR960-1 (Eylau reaches company's product) 10%.
Claims (7)
1. an anticorrosion abrasive resistant paint is characterized in that, this coating comprises following component and weight % content: Resins, epoxy 20～40%, fluoroolefin resin 10～15%, ceramic 30～50%, epoxy curing agent 15～20%.
2. a kind of anticorrosion abrasive resistant paint according to claim 1 is characterized in that, also comprises toughened resin 1～5 weight %.
3. a kind of anticorrosion abrasive resistant paint according to claim 1 and 2 is characterized in that, also comprises titanium dioxide 5～10 weight %.
4. a kind of anticorrosion abrasive resistant paint according to claim 1 is characterized in that, described Resins, epoxy is bisphenol A epoxide resin, and it comprises and is selected from a kind of in E03, E06, E14, E44, the E42 Resins, epoxy.
5. a kind of anticorrosion abrasive resistant paint according to claim 1 is characterized in that, described fluoroolefin resin comprises and is selected from a kind of in poly-trifluoro second propylene, tetrafluoroethylene, the daiflon.
6. a kind of anticorrosion abrasive resistant paint according to claim 1 is characterized in that described ceramic is the submicron ceramics powder, comprises the hollow beads ceramics powder.
7. a kind of anticorrosion abrasive resistant paint according to claim 1, it is characterized in that described epoxy curing agent comprises and is selected from a kind of among resol, polyamide resin, ARADUR14 (Eylau reaches company's product), the ARADUR960-1 (Eylau reaches company's product).