CN1866409A - Long-lasting grounding anti-corrosion resistance reduction agent (modified type) - Google Patents
Long-lasting grounding anti-corrosion resistance reduction agent (modified type) Download PDFInfo
- Publication number
- CN1866409A CN1866409A CN 200610092963 CN200610092963A CN1866409A CN 1866409 A CN1866409 A CN 1866409A CN 200610092963 CN200610092963 CN 200610092963 CN 200610092963 A CN200610092963 A CN 200610092963A CN 1866409 A CN1866409 A CN 1866409A
- Authority
- CN
- China
- Prior art keywords
- oxide
- corrosion
- reducing agent
- graphite
- resistance reducing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Composition | Silica | Titanium oxide | Iron oxide | Aluminium oxide | Calcium oxide | Potassium oxide | Sodium oxide molybdena |
Content (%) | 40-70% | 0.01-3% | 0.5-9% | 2-20% | 1-7% | 0.1-6% | 1-6% |
Sequence number | The pilot project title | Requirement | Test value | Estimate | |
1 | The resistivity measurement test | ρ≤5Ω·m | ρ=1.26Ω·m | Meet the requirements | |
2 | Physicochemical property certification test a, loss-of-coolant experiment (LOCE) b, cyclic test c, the test of water logging bubble | ρ≤6Ω·m | ρ=1.44Ω·m ρ=1.335Ω·m ρ=1.265Ω·m | Meet the requirements | |
3 | The impulse current tolerance | ΔR%≤20% | ΔR%≤1.07% | Meet the requirements | |
4 | The power current tolerance | ΔR%≤20% | ΔR%≤1.51% | Meet the requirements | |
5 | The pH measurement test | PH value is in the 7-12 scope | PH=7.1 | Meet the requirements | |
6 | The experiment of resistivity temperature characterisitic | Carry out | |||
7 | Resistance reducing agent is to metal earth electrode corrosion test | Surface average corrosion rate (mm/) | Scope (mm/) | ||
A, pure resistance reducing agent are to metal earth electrode rate of corrosion experiment with measuring | Surface average corrosion rate≤0.03mm/ | Round steel: 0.0139 band steel: 0.0155 zinc-plated round steel: 0.0044 zinc-coated flat steel sheet: 0.0050 | 0.0098-0.0195 0.0166-0.0211 0.0010-0.0061 0.0037-0.0054 | Meet the requirements | |
B, bury when ground resistance reducing agent to metal earth electrode rate of corrosion experiment with measuring | Average corrosion rate≤0.05mm/ | Round steel: 0.0136 band steel: 0.0191 zinc-plated round steel: 0.0064 zinc-coated flat steel sheet: 0.0069 | 0.0098-0.0150 0.0153-0.0257 0.0053-0.0080 0.0057-0.0076 | Meet the requirements |
Claims (2)