CN1861345A - Wood aeolian bells - Google Patents

Abstract

A set of wooden aeolian bells is made of wood through disinfecting, high-pressure steaming, cyclic drying in air, correcting deformation, natural drying, disinfecting by CaO plus H2O, coloring, and shaping by grinding.

Description

Wood aeolian bells

Technical field

What the present invention relates to is a kind of windbell, especially relates to a kind of Wood aeolian bells.

Background technology

Existing windbell form is different, under the blowing of gentle breeze, emits a dulcet sound when colliding during windbell waves, and brings the impression of sensual pleasure U.S. to the people.The various assemblies of existing windbell all are that some aluminum materials or glass are manufactured, and these most of materials can not recycling or effectively utilize regenerated resources, do not meet environmental protection; The audio frequency that sends of the windbell manufactured of aluminum material or glass compares higherly in addition, sounds seeming somewhat ear-piercing, can bring some interference to peripheral living environment.

Summary of the invention

The purpose of this invention is to provide a kind of Wood aeolian bells, that sends is clear melodious, loud, and it is little that sound wave transmits scope, can not bring harmful effect to peripheral living environment.

Purpose of the present invention realizes by following technical measures: a kind of Wood aeolian bells, adopt the timber of handling to form as various windbell component assembling;

Wherein the processing procedure of timber is:

(1) after the timber after sterilization is handled is put high-tension apparatus into and carried out vaporization process more than the 1.275MPa, circulate air-dry again and distortion is proofreaied and correct;

(2) timber after the vaporization process is dried naturally after, use CaO+H again ₂O carries out sterilization to be handled;

(3) paint according to different demands or boil look and handle, and the humidity that keeps timber is below 12 degree;

(4) according to different element shapes requirements, be shaped with mechanical grinding.

Timber of the present invention is through drying, after sterilization and the vaporization process, the timber flintiness being strengthened more than one times, keeps indeformable, colour-fast, nonhygroscopic, not mouldy, the snake not of product; This Wood aeolian bells is clear melodious, and is loud, and it is little that sound wave transmits scope, can not bring harmful effect to peripheral living environment, and can effectively utilize regenerated resources and the waste and old timber of residue, turns waste into wealth, and saves natural resources effectively, possesses environment-friendly function.

Description of drawings

Fig. 1 is the schematic diagram of the wooden windbell of the present invention.

The specific embodiment

After timber after sterilization handled was put high-tension apparatus into and carried out vaporization process more than the 1.275MPa, air-dry and cleaning again circulated; After timber after the vaporization process dried naturally, use CaO+H again ₂O carries out sterilization to be handled; Paint or boil look and handle according to different demands, and the humidity that keeps timber is below 12 degree; According to the difformity requirement, manufacture shaping with mechanical grinding and assemble then.As shown in Figure 1, these are made furred ceiling 1, swing pipe 2, middle pendulum 3 and the bottom 4 of assembly timber as windbell, assemble into windbell with top line 5 with messenger wire 6 between each assembly.Different shape can be manufactured or assemble into to said modules can according to windbell configuration design needs.

Claims (1)

1, a kind of Wood aeolian bells is characterized in that: adopt the timber of handling to form as various windbell component assembling; Wherein the processing procedure of timber is:

(1) after the timber after sterilization is handled is put high-tension apparatus into and carried out vaporization process more than the 1.275MPa, circulate air-dry again and distortion is proofreaied and correct;

(2) timber after the vaporization process is dried naturally after, carry out sterilization with CaO+H2O again and handle;

(3) paint according to different demands or boil look and handle, and the humidity that keeps timber is below 12 degree;

(4) according to different element shapes requirements, be shaped with mechanical grinding.