CN1858013A - Automobile glass etching glue - Google Patents
Automobile glass etching glue Download PDFInfo
- Publication number
- CN1858013A CN1858013A CN 200510034434 CN200510034434A CN1858013A CN 1858013 A CN1858013 A CN 1858013A CN 200510034434 CN200510034434 CN 200510034434 CN 200510034434 A CN200510034434 A CN 200510034434A CN 1858013 A CN1858013 A CN 1858013A
- Authority
- CN
- China
- Prior art keywords
- automobile glass
- weight portions
- water
- etching glue
- glass etching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The automobile glass etching glue consists of sulfuric 2-4 weight portions, nitric acid 2-3 weight portions, fluoride salt 30-40 weight portions, barium sulfate 5-10 weight portions, ferric oxide 10-15 weight portions and water 3-4 weight portions. It is prepared through mixing the materials through stirring, reaction at 90-110 deg.c for 6-8 hr, standing for 72 hr and adding proper amount of water to regulate viscosity. The automobile glass etching glue may be used to etch clear text on automobile glass and may be also used for other glass product, artistic works, metals, gift, etc.
Description
Affiliated technical field
The present invention relates to a kind of etching reagent, especially relate to a kind of on vehicle glass the etching permanent marking melt the glue preparation.
Background technology
In recent years, along with rapid development of automobile industry, each car type is more and more luxurious.The criminal activity of stealing, smuggling automobile all over the world is very rampant, and each steals the outstanding problem that car group has become influences social security and consumer rights.Though various electronic anti-theft technology are brought in constant renewal in, but still can't take precautions against utilize high-tech crime De Qie ?.In order to contain the rising of theft rate, many in recent years countries; All popularizing the glass etching technology of using in an all-round way such as countries such as the U.S., Switzerland, Britain, Australia and Holland, and each big Insurance Company also must be etched in the Vehicle Certificate of automobile number and bar code on the vehicle glass at the car tube hub that requires various places gradually, in the recent period China also has trend to promote at each automobile own car plate in the etching all, so that the police follows the trail of easily, the thief is difficult to reequip and resell in China.Now the stage, domestic is to adopt traditional frosted method to carry out etching on vehicle glass at this on the one hand always, and this technical costs is higher, does not meet environmental requirement, easy contaminate environment and sedan limousine, and etching printed words sharpness is not high, the working specification complexity.
Summary of the invention
Purpose of the present invention just provides a kind of pollution-free, noiselessness, the automobile glass etching glue that cost easy and simple to handle is low and sharpness is high.
Automobile glass etching glue of the present invention is made by following component: (consumption is a weight part)
Sulfuric acid 2～4 nitric acid 2～3 fluoride salts 30～40
Barium sulfate 5～10 ferric oxide 10～15 water 3～4
The manufacture method of this automobile glass etching glue is:
Add the sulfuric acid, nitric acid, fluoride salt, barium sulfate, ferric oxide and the water that sieve through grinding in turn, and after stirring fully simultaneously,, left standstill afterwards 72 hours, add suitable quantity of water adjusting viscosity at last and get final product 90～110 degree reactions Celsius 6～8 hours.
Preferred weight of the present invention (part) proportioning is:
Sulfuric acid 2.5～3.5 nitric acid 2.25～2.75 fluoride salts 33～37
Barium sulfate 7～8 ferric oxide 12～13 water 3.3～3.8
Optimum weight of the present invention (part) proportioning is:
Sulfuric acid 3 nitric acid 2.5 fluoride salts 35
Barium sulfate 7.5 ferric oxide 12.5 water 3.5
The invention has the beneficial effects as follows: can in five minutes, will clearly be engraved on the vehicle glass by etched word, and can be widely used in aspects such as glasswork, artwork, metal and gift, simple to operate, quick, need not the professional and technical personnel, and pollution-free, noiselessness.
Embodiment
The present invention is further illustrated below by embodiment.
The etching glue of embodiment 1 is made by following component: (consumption is a weight part)
Sulfuric acid 2 nitric acid 2 fluoride salts 30
Barium sulfate 10 ferric oxide 15 water 3
Manufacture method is: add in turn through grinding sulfuric acid, nitric acid, fluoride salt, barium sulfate, ferric oxide and the water of screening, and after stirring fully simultaneously, 90～95 degree reactions Celsius 6 hours, left standstill afterwards 72 hours, add suitable quantity of water adjusting viscosity at last and get final product.
The gained finished product is peach viscose glue shape liquid.
The etching glue of embodiment 2 is made by following component: (consumption is a weight part)
Sulfuric acid 4 nitric acid 3 fluoride salts 40
Barium sulfate 10 ferric oxide 15 water 4
Manufacture method is: add in turn through grinding sulfuric acid, nitric acid, fluoride salt, barium sulfate, ferric oxide and the water of screening, and after stirring fully simultaneously, 100～110 degree reactions Celsius 8 hours, left standstill afterwards 72 hours, add suitable quantity of water adjusting viscosity at last and get final product.
The gained finished product is peach sticking shape liquid.
The etching glue of embodiment 3 is made by following component: (consumption is a weight part)
Sulfuric acid 3 nitric acid 2.5 fluoride salts 35
Barium sulfate 7.5 ferric oxide 12.5 water 3.5
Manufacture method is: add in turn through grinding sulfuric acid, nitric acid, fluoride salt, barium sulfate, ferric oxide and the water of screening, and after stirring fully simultaneously, 98～102 degree reactions Celsius 7 hours, left standstill afterwards 72 hours, add suitable quantity of water adjusting viscosity at last and get final product.
The gained finished product is peach viscose glue shape liquid.
Automobile glass etching glue using method of the present invention:
Will clean clean by etched vehicle glass; the mould that is carved with word is painted paper to be affixed on and to want etched position; determine that no bubble mould is painted paper under the paper is affixed on glass comprehensively; for guaranteeing that font can clearly be etched in glass surface and can use finger floating gently if any the place of injustice; posting blue mould paints to begin behind the paper to paint with the mould that etching solution is applied to word and does not need too many etching solution on the paper; as long as be coated with the place of word, needn't smear repeatedly.
Claims (3)
1, a kind of automobile glass etching glue is characterized in that it is a group by the following weight proportioning
Be grouped into:
Sulfuric acid 2～4 nitric acid 2～3 fluoride salts 30～40
Barium sulfate 5～10 ferric oxide 10～15 water 3～4.
2, automobile glass etching glue according to claim 1 is characterized in that: described each composition weight proportioning is:
Sulfuric acid 2.5～3.5 nitric acid 2.25～2.75 fluoride salts 33～37
Barium sulfate 7～8 ferric oxide 12～13 water 3.3～3.8.
3, automobile glass etching glue according to claim 1 is characterized in that: described each composition weight proportioning is:
Sulfuric acid 3 nitric acid 2.5 fluoride salts 35
Barium sulfate 7.5 ferric oxide 12.5 water 3.5.