CN1853886A - Wooden decorative material strip processing method - Google Patents
Wooden decorative material strip processing method Download PDFInfo
- Publication number
- CN1853886A CN1853886A CN 200510009947 CN200510009947A CN1853886A CN 1853886 A CN1853886 A CN 1853886A CN 200510009947 CN200510009947 CN 200510009947 CN 200510009947 A CN200510009947 A CN 200510009947A CN 1853886 A CN1853886 A CN 1853886A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- make
- sent
- selected surface
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for preparing the stereoscopic wood grains on the wooden decorative material includes such steps as choosing wood material with beautiful annual rings, drying, laying aside in a ventilated dry shed for natural getting damp again, shaping, charring a chosen surface to form a charred black layer, cooling for fixating its shape, and polishing for removing the collected charcoal from the surface.
Description
Technical field
The present invention relates to the method for processing and treatment of woodwork, particularly to the method for processing and treatment of wood product surface wood grain.
Background technology
Because the surface grain of woodwork is processed into the art value and the market price that wood grain that form according to texture is scraggly stereo structure can improve woodwork greatly, and now existing its surface of woodwork is processed into the stereo wood pattern listing and sells.The existing processing method that makes its surface of woodwork present stereo wood pattern has sand-blast, be 90107192.7 as application number and be called the patent of " wood curtain sheet surface grain process for making stereo and goods thereof ", flame blows the burning method, be 95109571.4 as application number and be called the patent of " flame burns the method that timber is made three-dimensional timber sculpture ", there is the inapparent shortcoming of wood grain stereoeffect in the former, the latter exists efficient hand-manipulated low, technic index is judged control by operator's eyesight fully, is difficult to ensure the quality of products and the high shortcoming of production cost.
Summary of the invention
It is remarkable to the purpose of this invention is to provide a kind of wood grain stereoeffect, and production cost is low, the efficient height, and technic index is easy to control, the processing method of stay-in-grade Wooden decorative material strip.
Technical solution of the present invention is: the drying of wood that the annual ring selected is good-looking is to moisture content 6～12%, it is placed into the material shed of aeration-drying, after making its qualitative a period of time of getting damp again naturally, use saw, dig, cut, traditional handicraft such as revolve, be processed into the base material of required specification shape, make substrate surface smooth as far as possible smooth, using carbonizing apparatus that the selected face of base material is carried out charing handles, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 300～800 degree Celsius, the selected face of base material is close to template does the mechanical parallel motion, make selected surface of base material form the black charring layer, again base material is sent into cooling and shaping device cooling and shaping, behind the cooling and shaping, again base material is sent into the carbon removal burnishing device and removed the carbon deposit and the polishing on selected surface, its specific practice is, is the rotating brush of 0.1～2MM with the single diameter of bristle filaments, and its rotating speed is at 1000～6000 rev/mins, brushing is carried out on selected surface of base material, make base material expose the slightly appearance of light.
Technique effect of the present invention is: the wood grain stereoeffect is remarkable, and production cost is low, the efficient height, and technic index is easy to control, steady quality.
The specific embodiment
Embodiment 1: the good-looking pinus sylvestris var. mongolica timber of annual ring with selecting, be processed into sheet material with band sawing machine, and send into the dried cellar for storing things of gas and carry out drying, its moisture content is reached between 8～12%; It is placed into the material shed of aeration-drying, make its get damp again naturally 30～40 hours qualitative after, plane four faces of sheet material smooth smooth with four side moulder, then sheet material is sent into carbonizing apparatus, selected face is carried out charing to be handled, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 500～600 degree Celsius, the selected face of sheet material is close to the speed of template with 1～3 meter of per minute, do the mechanical parallel motion, make selected surface of sheet material form the black charring layer, again sheet material is sent into the cooling and shaping device and carried out cooling and shaping, then, again sheet material is sent into the carbon removal burnishing device and removed the carbon deposit on selected surface, its specific practice is, is the metal rotating brush of 0.1～0.5MM with the single diameter of bristle filaments, and its rotating speed is at 3000～4000 rev/mins, brushing is carried out on selected surface of sheet material, make the convex-concave difference of wood grain reach 2MM, and make selected surface of sheet material present the slightly light brown appearance of light, and then to selected surperficial spary celluloid paint of sheet material.
Embodiment 2: the good-looking larchwood of annual ring with selecting, be processed into square bar with band sawing machine, and with the monolithic length sawing of scraping square bar is cut into wood chip again; Send into the dried cellar for storing things of gas and carry out drying, its moisture content is reached between 6～8%; It is placed into the material shed of aeration-drying, make its get damp again naturally 40～60 hours qualitative after, then wood chip is sent into carbonizing apparatus, selected face is carried out charing to be handled, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 500～600 degree Celsius, the selected face of wood chip is close to the speed of template with 1～3 meter of per minute, do the mechanical parallel motion, make selected surface of wood chip form the black charring layer, again sheet material is sent into the cooling and shaping device and carried out cooling and shaping, then, wood chip is sent into the carbon deposit that the carbon removal burnishing device is removed selected surface, its specific practice is again, with the single diameter of bristle filaments is the metal rotating brush of 0.1～0.5MM, its rotating speed carries out brushing at 4000～5000 rev/mins to selected surface of wood chip, makes the convex-concave difference of wood grain reach 1.5MM, and make selected surface of wood chip present the slightly wooden look appearance of light, and then to selected surperficial spary celluloid paint of wood chip.
Claims (3)
1, a kind of processing method of Wooden decorative material strip, it is characterized in that, the drying of wood that the annual ring selected is good-looking is to moisture content 6～12%, it is placed into the material shed of aeration-drying, after making its qualitative a period of time of getting damp again naturally, use saw, dig, cut, traditional handicraft such as revolve, be processed into the base material of required specification shape, make substrate surface smooth as far as possible smooth, use carbonizing apparatus that the selected face of base material is carried out charing and handle, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 300～800 degree Celsius, the selected face of base material is close to template does the mechanical parallel motion, make selected surface of base material form the black charring layer, again base material is sent into cooling and shaping device cooling and shaping, behind the cooling and shaping, again base material is sent into the carbon removal burnishing device and removed the carbon deposit and the polishing on selected surface, its specific practice is, is the rotating brush of 0.1～2MM with the single diameter of bristle filaments, and its rotating speed is at 1000～6000 rev/mins, brushing is carried out on selected surface of base material, make base material expose the slightly appearance of light.
2, the processing method of a kind of Wooden decorative material strip as claimed in claim 1 is characterized in that, the good-looking pinus sylvestris var. mongolica timber of annual ring with selecting is processed into sheet material with band sawing machine, sends into the dried cellar for storing things of gas and carries out drying, and its moisture content is reached between 8～12%; It is placed into the material shed of aeration-drying, make its get damp again naturally 30～40 hours qualitative after, plane four faces of sheet material smooth smooth with four side moulder, then sheet material is sent into carbonizing apparatus, selected face is carried out charing to be handled, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 500～600 degree Celsius, the selected face of sheet material is close to the speed of template with 1～3 meter of per minute, do the mechanical parallel motion, make selected surface of sheet material form the black charring layer, again sheet material is sent into the cooling and shaping device and carried out cooling and shaping, then, again sheet material is sent into the carbon removal burnishing device and removed the carbon deposit on selected surface, its specific practice is, is the metal rotating brush of 0.1～0.5MM with the single diameter of bristle filaments, and its rotating speed is at 3000～4000 rev/mins, brushing is carried out on selected surface of sheet material, make the convex-concave difference of wood grain reach 2MM, and make selected surface of sheet material present the slightly light brown appearance of light, and then to selected surperficial spary celluloid paint of sheet material.
3, the processing method of a kind of Wooden decorative material strip as claimed in claim 1 is characterized in that, the good-looking larchwood of annual ring with selecting is processed into square bar with band sawing machine, with the monolithic length sawing of scraping square bar is cut into wood chip again; Send into the dried cellar for storing things of gas and carry out drying, its moisture content is reached between 6～8%; It is placed into the material shed of aeration-drying, make its get damp again naturally 40～60 hours qualitative after, then wood chip is sent into carbonizing apparatus, selected face is carried out charing to be handled, the specific practice that charing is handled is, the template of carbonizing apparatus is heated to 500～600 degree Celsius, the selected face of wood chip is close to the speed of template with 1～3 meter of per minute, do the mechanical parallel motion, make selected surface of wood chip form the black charring layer, again sheet material is sent into the cooling and shaping device and carried out cooling and shaping, then, wood chip is sent into the carbon deposit that the carbon removal burnishing device is removed selected surface, its specific practice is again, with the single diameter of bristle filaments is the metal rotating brush of 0.1～0.5MM, its rotating speed carries out brushing at 4000～5000 rev/mins to selected surface of wood chip, makes the convex-concave difference of wood grain reach 1.5MM, and make selected surface of wood chip present the slightly wooden look appearance of light, and then to selected surperficial spary celluloid paint of wood chip.