CN1840262A - Anti-clog immersion type down spout material - Google Patents
Anti-clog immersion type down spout material Download PDFInfo
- Publication number
- CN1840262A CN1840262A CN 200510024808 CN200510024808A CN1840262A CN 1840262 A CN1840262 A CN 1840262A CN 200510024808 CN200510024808 CN 200510024808 CN 200510024808 A CN200510024808 A CN 200510024808A CN 1840262 A CN1840262 A CN 1840262A
- Authority
- CN
- China
- Prior art keywords
- river
- mouth
- clog
- immersion type
- type down
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anticlogging immersion fireproof material for water port body, which comprises the following parts: 30-70% corundum, 16-40% nitrogen boom or one or two kind material of silicon nitride, 5-25% graphite, one or many kinds of zirconium mullite, carbofrax, metallic silicon and boron carbide, 4-8% bakelite adhesive. The invention has best anti alumina clogging property, anti liquid steel corrosion property and anti thermal shock property, which has long service life.
Description
(1) technical field
The present invention relates to the refractory material of this body and function of anti-clogging submersed nozzle.
(2) background technology
Submersed nozzle comprises body top, the mouth of a river, slag line, body bottom, the mouth of a river, and body bottom, the mouth of a river has the hole that spues, the mouth of a river.Mouth of a river bulk material adopts aluminium carbon material (as CN02135497) usually, is primary raw material with corundum, vitreous silica and graphite, has good thermal shock resistance and anti-molten steel scouring aggressivity.But this mouth of a river is when cast aluminum killed steel, Al in the Chang Yingang liquid
2O
3Be deposited on mouth of a river inwall and spue the hole and stop up Deng field trash, have influence on working continuously of continuous casting.Stick to mouth of a river inner surface simultaneously and the field trash in the hole that spues, in casting cycle, may come off and fall in the molten steel, cause the nonmetal inclusion in the continuous casting billet, thereby influence the quality of continuous casting steel billet.Being easy to generate the position adhered to of deposition in the mouth of a river mainly comprises the following inwall of submersed nozzle slag line and spues position on every side, hole.
In order to prevent nozzle blocking, mainly now adopt following several modes, 1, the Puffer type mouth of a river, argon gas is to force to be blown into by the ventilative lining at the mouth of a river, forms a layer of inert on the inner hole wall of the mouth of a river, has stoped aluminium oxide to adhere to.Though can alleviate nozzle blocking to a certain extent, there is the problem (in the slab process of setting, making the defective of steel formation pinprick owing to the decomposition of argon gas) that billet quality is worsened in blowing argon gas in the mouth of a river.
2, the sub-mouth of a river of the notch cuttype mouth of a river and eddy flow, the inwall at the notch cuttype mouth of a river can change molten steel flow state in the mouth of a river after adopting notch cuttype, thereby improves the aluminium oxide clogging; Also the molten steel flow state reduces the aluminium oxide obstruction in the mouth of a river by changing at the eddy flow mouth of a river.Water under the high situation of number of times for connecting, these two kinds of mouth of a river blocking-proof results can't meet the demands.Secondly, there is the big problem of manufacture difficulty in the notch cuttype mouth of a river.
3, the anti-clogging inwall mouth of a river, Japanese patent laid-open 4-224061 has proposed CaO-ZrO
2-C inner lining material; Chinese patent CN 1062248C discloses the material that a kind of anti-oxidation aluminium stops up, and promptly adds calcirm-fluoride in zirconium material with carbon element or zirconium mullite material with carbon element.These two kinds of patents all be utilize aluminium oxide easily with inner lining material in CaO or calcirm-fluoride reaction formation eutectic, reach the purpose that prevents alumina deposit.Along with the prolongation of casting time, anti-clogging poor effect, secondly CaO-ZrO
2There is the problem of easy aquation in-C inner lining material.The Japan Patent spy opens 2003-145265 and proposes a kind of carbon-free Al
2O
3-MgO matter anti-clogging inner lining material.This patent adopts the inner lining material of low heat conduction, can reduce the roughening with inner lining surface of separating out of steel grade aluminium oxide, stops up thereby reduce aluminium oxide.Though yet this kind material can solve the blockage problem of mouth of a river inwall, can not solve the hole plug problem that spues.
(3) summary of the invention
The object of the present invention is to provide a kind of anti-clog immersion type down spout material.This bulk material has preferable antioxidation aluminium obstruction, anti-molten steel corrodes and thermal shock resistance long service life.
The present invention is achieved in that a kind of anti-clog immersion type down spout material, it consists of (by % weight): 30～70% corundum, a kind of in the grand or silicon nitride of 16～40% match or two kinds, 5～25% graphite, all the other are a kind of in zirconium mullite, carborundum, metallic silicon, the boron carbide or several, add 4～8% phenolic resin binders.
It is primary raw material that the present invention adopts corundum, Sai Long or silicon nitride and graphite, and phenolic resins is the prepared anti-clogging body submersed nozzle of bond, has higher antioxidation aluminium deposition, the erosion of anti-molten steel and thermal shock resistance.Sai Long or silicon nitride material all have thermal conductivity factor height, characteristics that thermal coefficient of expansion is little, have excellent thermal shock resistance and preferable anti-molten steel erosion performance; Particularly because the angle of wetting of Sai Long and silicon nitride and molten steel is little, molten steel and alumina inclusion are difficult to attached to its surface.Employing is with the submersed nozzle of this material as body, and it can prevent effectively when cast aluminum killed steel in the molten steel that aluminium adheres to the mouth of a river of causing spue hole plug and long service life.
The manufacture method of anti-clog immersion type down spout material is: adopting corundum material, Sai Long or silicon nitride material and graphite is primary raw material, all the other can add a kind of in zirconium mullite, carborundum, metallic silicon, the boron carbide or several, and employing phenolic resins is bond.Through granulation, dry after with isostatic compaction after sintering, promptly can be made into required submersed nozzle.Also can be compound with anti-clogging liner, zirconium carbon slag line, with sintering behind the isostatic compaction, make required submersed nozzle.
The present invention compares with the sub-mouth of a river of staged of the prior art and eddy flow, and the anti-clogging effect is better, and manufacture difficulty is little.With CaO-ZrO
2The zirconium mullite carbon inner lining material of-C inner lining material or interpolation calcirm-fluoride and carbon-free Al
2O
3-MgO matter anti-clogging inner lining material is compared, and has solved the hole plug problem that spues.
(4) specific embodiment
Embodiment is referring to table 1.
Table 1 is listed the composition (percetage by weight) and the performance of bulk material of the present invention.
Table 1
| The prescription number | 1 | 2 | 3 | 4 | 5 | 6 | |
| Raw material is formed (%) | Corundum | 70 | 51 | 50 | 45 | 35 | 30 |
| Sai Long | - | 18 | - | 40 | 15 | 20 | |
| Silicon nitride | 16 | - | 25 | - | 15 | 15 | |
| Graphite | 11 | 25 | 15 | 5 | 20 | 20 | |
| Zirconium mullite | - | - | 5 | 4 | 10 | 10 | |
| Carborundum | - | 2 | 1 | 3 | 2 | 2 | |
| B 4C | 0.5 | 1 | 1 | 0.5 | 1 | 1 | |
| Si | 2.5 | 3 | 3 | 2.5 | 2 | 2 | |
| Phenolic resins (adding) | 6 | 7 | 7 | 5 | 7 | 7 | |
| Performance | Apparent pore, % | 16 | 17 | 16 | 17 | 16 | 16 |
| Compressive resistance, MPa | 22 | 27 | 26 | 25 | 23 | 23 | |
| Rupture strength, MPa | 8.3 | 9.2 | 8.6 | 8.8 | 9.1 | 9.1 | |
| The anti-clogging effect | Very | Very | Excellent | Excellent | Excellent | Excellent | |
| Thermal shock resistance | Excellent | Excellent | Excellent | Excellent | Excellent | Excellent | |
| Service life | Long | Long | Long | Long | Long | Long | |
Claims (1)
1. anti-clog immersion type down spout material, it consists of (by % weight): 30～70% corundum, a kind of in the grand or silicon nitride of 16～40% match or two kinds, 5～25% graphite, all the other are a kind of in zirconium mullite, carborundum, metallic silicon, the boron carbide or several, add 4～8% phenolic resin binders.