CN1837336A - Honeycomb charcoal with ignition space - Google Patents
Honeycomb charcoal with ignition space Download PDFInfo
- Publication number
- CN1837336A CN1837336A CN 200610050513 CN200610050513A CN1837336A CN 1837336 A CN1837336 A CN 1837336A CN 200610050513 CN200610050513 CN 200610050513 CN 200610050513 A CN200610050513 A CN 200610050513A CN 1837336 A CN1837336 A CN 1837336A
- Authority
- CN
- China
- Prior art keywords
- powder
- ignition
- ignition space
- charcoal
- honeycomb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an ignition honeycomb charcoal, which includes a main body having a lighting hole at the center, the lighting hole is provided with a lighting spot. The charcoal comprises the following constituents (by weight ratio): charcoal powder 100, flavoring powder 0.5-20 and binding agent 150-220.
Description
Technical field
The present invention relates to a kind of burning articles for use on fire, especially a kind of honeycomb briquette honeycomb charcoal with ignition space on fire that is used for.
Background technology
Honeycomb briquette will be to light a fire or with methods such as burnings, honeycomb briquette to be lighted before burning at present.In ignition procedures, owing to be to adopt to light a fire or, not only be difficult for very much lighting, also can emit a large amount of burning smokes with methods such as firewood combustions, cause surrounding environment influence.The people who uses honeycomb briquette is for a little honeycomb briquette fired without lighting a fire every day, and the general honeycomb briquette of all crossing with unburn continues the method that fire spends the night.Only play continuous fire action though solved a little honeycomb briquette fired, the so continuous fiery honeycomb briquette of need not lighting a fire, can not get suitable burning and be worth, and with the continuous fire of honeycomb briquette, very big to the demand of honeycomb briquette, cause unnecessary waste.Since coal be a kind of can not renewable resource, so a kind of sparking mode of more saving need be provided.In addition, if often adopt the continuous fire of honeycomb briquette, make coal stove be in a kind of long-time continuous user mode, high temperature can influence the work-ing life of coal stove.
Summary of the invention
The present invention will solve the shortcoming of above-mentioned prior art, and a kind of honeycomb charcoal with ignition space that is easy to light a fire is provided, and solves the honeycomb briquette many problems of resource consumption that are difficult for, burn on fire.
The present invention solves the technical scheme that its technical problem adopts: this honeycomb charcoal with ignition space, comprise main body, and these main body central authorities have fire hole, and fire hole is provided with point of ignition.
The present invention can be further perfect by following manner:
Be provided with the thin-walled crosspiece in the fire hole, described point of ignition i.e. this crosspiece.The hole wall of fire hole is the thin-walled shape of lighting a fire easily, and described point of ignition i.e. this thin-walled.Body surfaces has and is used for pyrophoric groove, and this groove one end starts from fire hole week edge.Have the pore of the perforation corresponding on the main body with the normal cellular coal.
Honeycomb charcoal with ignition space comprises the component of following weight part ratio: powdered carbon 100, spices powder 0.5-20 and binding agent 150-220.Binding agent can be the component that comprises following weight part ratio: starch 2-3, water 150-220, sodium hydroxide 0.18-0.3.Binding agent also can be to comprise clay powder 5-15, water 190-210.The spices powder is: elm powder or wood powder or Cortex cinnamomi camphorae powder or Tetranthera citrata powder or star anise powder or dried orange peel powder or rosin solution.
The effect that the present invention is useful is: the present invention is provided with fire hole, and fire hole is provided with the thin-walled point of ignition, and result of use is good, can solve the ignition problem of honeycomb briquette effectively; Rational in infrastructure, be easy to the die sinking tool, to be convenient to produce in batch, production cost is low, helps promoting; The raw material that uses all is renewable resources, save energy, and cost is low.
Description of drawings
Fig. 1 is the structural representation of the embodiment of the invention 1;
Fig. 2 is the structural representation of the embodiment of the invention 2;
Fig. 3 is the structural representation of the embodiment of the invention 3;
Fig. 4 is the structural representation of the embodiment of the invention 4.
Description of reference numerals: main body 1, fire hole 2, point of ignition 3, groove 4, pore 5.
Embodiment
The invention will be further described below in conjunction with accompanying drawing:
Embodiment 1: with reference to Fig. 1, this honeycomb charcoal with ignition space comprises main body 1, and main body 1 is formed by mixing such as powdered carbon (machine-made carbon, charcoal etc.), spices powder and binding agent compacting, is easy to igniting like this.Have the pore 5 of the perforation corresponding on the main body 1, be and shape like the normal cellular coal facies, promptly cylindrical (also can be other shapes such as rectangular parallelepiped), circular diameter 7-10 centimetre, 2-3.5 centimetre of height with the normal cellular coal.The quantity of pore 5 can consistently with the pore of honeycomb briquette be 12 holes, also can be 4 holes, 8 holes, as long as the pore 5 on it is corresponding with the pore of honeycomb briquette.Pore 5 is easy to honeycomb briquette is lighted.These main body 1 central authorities have the circular fire hole 2 of perforation, and fire hole 2 is provided with point of ignition 3, are provided with a thin-walled crosspiece in the fire hole 2, and point of ignition 3 i.e. this crosspiece.Because therefore point of ignition 3 place's thinner thicknesses can be lighted this place easily.Main body 1 surface has and is used for pyrophoric groove 4, and these groove 4 one ends start from fire hole 2 all edges.Groove 4 is convenient to the flare at point of ignition 3 places is diffused to whole honeycomb charcoal with ignition space.
The prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons (more than 16 mesh sieves); 2.2 parts of starch (as wheat-flour, Semen Maydis powder, Sumstar 190 etc.); Nature water 155-165 part; Sodium hydroxide 0.18-0.22 part; Elm powder (more than 60 mesh sieves) 4-5 part.
During making, starch is added the stirring of nature water be warming up to about 60 degree, add sodium hydroxide and make its gelatinization, make the magma binding agent.Then add the elm powder again and mix (can add during normal temperature).Again binding agent and elm powder are added powdered carbon while stirring, thorough mixing is even, makes moulding then on the forming machine of honeycomb charcoal with ignition space, again the oven dry or dry naturally, get final product.The binding agent cost that is made of starch, water, sodium hydroxide is low, result of use good.The elm powder uses as spices, is used to cover the smell of burning that starch burns generation.After elm powder and water mix, also have bond effect, play the effect of binding agent simultaneously.
During use, with honeycomb charcoal with ignition space (12 passes as shown in Figure 1, consistent with the honeycomb briquette shape), grasp or pliers is clamped, it is lighted at point of ignition 3 places with lighter or match then, clamp with pliers again and put into coal stove (the stove selection has grate), make its pore 5 as much as possible and fire hole 2 towards grate mouth (putting honeycomb briquette fired better effects if like this), then put into beehive coal ball again, the pore 5 of beehive coal ball is alignd with pore on the honeycomb charcoal with ignition space, treat that honeycomb charcoal with ignition space has burnt, beehive coal ball is also just lighted.Attention: during most of burning, coal stove should not have vibration to honeycomb charcoal with ignition space, also should not move coal stove in coal stove.In addition, can discharge materials such as traces of carbon dioxide during the honeycomb charcoal with ignition space combustion, therefore needing ventilates uses.
Cost of the present invention is low, and result of use is good, can effectively solve the ignition problem of honeycomb briquette.
Embodiment 2: with reference to Fig. 2, difference from Example 1 is: the thin-walled shape of the hole wall of fire hole 2 for lighting a fire easily, described point of ignition 3 i.e. this thin-walled.Fire hole 2 is less with adjacent pore 5 intervals, forms thin hole wall, and this hole wall is a point of ignition 3, during igniting, can light at this place easily.
Embodiment 3: with reference to Fig. 3, difference from Example 1 is: be provided with two thin-walled crosspieces in the fire hole 2, be easier to igniting.
Embodiment 4: with reference to Fig. 4, difference from Example 1 is: fire hole 2 is square holes.Fire hole 2 can also be other shape, as long as it has thin-walled point of ignition 3.
Embodiment 5: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; 2.4 parts of starch; Nature water 170-180 part; Sodium hydroxide 0.2-0.24 part; Elm powder 4-5 part; 10 parts of clay powders (more than 40 mesh sieves).
Add clay powder on the basis of embodiment 1, clay powder has cohesive action in moistening, makes the honeycomb charcoal with ignition space moulding more stable, is not easy to loose more anti-burning.During making, other step is identical with embodiment 1, just earlier clay powder and powdered carbon is mixed, and when adding powdered carbon, changes adding clay powder and powdered carbon mixture into.
Embodiment 6: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; Starch 2.3-2.8 part; Nature water 170-210 part; Sodium hydroxide 0.2-2.8 part; Elm powder 4-5 part; Wood ash (more than 40 mesh sieves) 10-30 part.
Add wood ash on the basis of embodiment 1, wood ash is an additive, itself contains a small amount of ash in the charcoal.The adding wood ash can reduce the consumption of powdered carbon, further reduces production costs.During making, other step is identical with embodiment 1, just earlier powdered carbon and wood ash is mixed, and when adding powdered carbon, changes adding wood ash and powdered carbon mixture into.
Embodiment 7: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; Starch 2.4-2.7 part; Nature water 185-205 part; Sodium hydroxide 0.2-0.27 part; Elm powder 4-5 part; 10 parts of clay powders (more than 40 mesh sieves); Coal dust (more than 40 mesh sieves) 5-10 part; Potassium nitrate solution (the molten 100 gram water of 10 gram saltpetre) is an amount of.
Add clay powder, coal dust, potassium nitrate solution on the basis of embodiment 1, potassium nitrate solution is an ignition dope, makes the honeycomb charcoal with ignition space moulding more stable, is not easy to loose, and fuel increases, more anti-burning.During making, other step is identical with embodiment 1, just earlier clay powder, coal dust and powdered carbon is mixed, and when adding powdered carbon, changes adding clay powder, coal dust and powdered carbon mixture into.When treating that 7 to 8 one-tenth of type bodies are done, with potassium nitrate solution with being coated with or being sprayed on (its consumption is less) on the fire hole.Potassium nitrate solution also can change other ignition dopes such as SODIUMNITRATE, phosphorus compound into.
Embodiment 8: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; 3 parts of starch (or Sumstar 190); Nature water 160-165 part; Sodium hydroxide 0.22-0.3 part; Spices powder or wood powder are an amount of.
Wood powder can be 4 parts in 4 parts in bamboo powder (more than 40 mesh sieves) or 4 parts in Chinese fir powder (more than 40 mesh sieves) or pine tree powder (more than 40 mesh sieves) etc., and the spices powder can be Cortex cinnamomi camphorae powder (1-2 part) or Tetranthera citrata powder (0.5-1 part) or star anise powder (0.5-1 part) or dried orange peel powder (3-4 part) or rosin solution (1.7-2.2).Spices powder or wood powder are substituted the elm powder, be used to cover the smell of burning that starch produces.
Embodiment 9: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; 10 parts of clay powders; 205 parts in nature water; 18 parts in elm powder.Present embodiment mixes as binding agent with clay powder and water.During making, first powdered carbon, clay powder, elm powder mix, and water are added to mix again, make moulding, dry or dry.
Embodiment 10: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; 10 parts of clay powders; 205 parts in nature water; 18 parts in elm powder; 1.1 parts in sodium hydroxide.The elm powder both as spices, also played the effect of binding agent in the present embodiment.During making, earlier powdered carbon and clay powder are mixed, the elm powder is added entry be warmed up to more than 60 degree, add the sodium hydroxide reaction, make binding agent, add powdered carbon, clay powder mixture while stirring, make moulding, dry or dry.
Embodiment 11: difference from Example 1 is: the prescription of honeycomb charcoal with ignition space is: 100 parts of powdered carbons; 2.4 parts of starch; Nature water 170-180 part; Sodium hydroxide 0.2-0.24 part; Elm powder 4-5 part; 10 parts of coal dusts (more than 40 mesh sieves).
Add coal dust on the basis of embodiment 1, coal dust is made fuel and is added, and combustion heat value is increased.During making, other step is identical with embodiment 1, just earlier coal dust and powdered carbon is mixed, and when adding powdered carbon, changes adding coal ash and powdered carbon mixture into.
Claims (10)
1, a kind of honeycomb charcoal with ignition space comprises main body (1), it is characterized in that: this main body (1) central authorities have fire hole (2), and fire hole (2) is provided with point of ignition (3).
2, honeycomb charcoal with ignition space according to claim 1 is characterized in that: described fire hole is provided with the thin-walled crosspiece in (2), and described point of ignition (3) i.e. is this crosspiece.
3, honeycomb charcoal with ignition space according to claim 1 is characterized in that: the thin-walled shape of the hole wall of described fire hole (2) for lighting a fire easily, described point of ignition (3) i.e. is this thin-walled.
4, according to claim 1,2 or 3 described honeycomb charcoal with ignition space, it is characterized in that: described main body (1) surface has and is used for pyrophoric groove (4), and these groove (4) one ends start from all edges of fire hole (2).
5, according to claim 1,2 or 3 described honeycomb charcoal with ignition space, it is characterized in that: the pore (5) that has the perforation corresponding on the described main body (1) with the normal cellular coal.
6, according to claim 1,2 or 3 described honeycomb charcoal with ignition space, it is characterized in that: described honeycomb charcoal with ignition space comprises the component of following weight part ratio: powdered carbon 100,
Spices powder 0.5-20,
Binding agent 150-220.
7, honeycomb charcoal with ignition space according to claim 6 is characterized in that: described binding agent comprises the component of following weight part ratio: starch 2-3,
Water 150-220,
Sodium hydroxide 0.18-0.3.
8, honeycomb charcoal with ignition space according to claim 6 is characterized in that: described binding agent comprises the component of following weight part ratio: clay powder 5-15,
Water 190-210.
9, honeycomb charcoal with ignition space according to claim 6 is characterized in that: described spices powder is: the elm powder.
10, honeycomb charcoal with ignition space according to claim 6 is characterized in that: described spices powder is: wood powder or Cortex cinnamomi camphorae powder or Tetranthera citrata powder or star anise powder or dried orange peel powder or rosin solution.