CN1818217A - Waterstone-polishing grounding brick with imitated granite and machining method thereof - Google Patents
Waterstone-polishing grounding brick with imitated granite and machining method thereof Download PDFInfo
- Publication number
- CN1818217A CN1818217A CN 200610033299 CN200610033299A CN1818217A CN 1818217 A CN1818217 A CN 1818217A CN 200610033299 CN200610033299 CN 200610033299 CN 200610033299 A CN200610033299 A CN 200610033299A CN 1818217 A CN1818217 A CN 1818217A
- Authority
- CN
- China
- Prior art keywords
- surface layer
- polishing
- waterstone
- brick
- grounding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A pavement brick comprises top layer and bottom layer. The bottom layer is composed by 15-35 wt% cement, 15-35 wt% sand and 30-50 wt% stone particles. The top layer is composed by 15-35 wt% white cement, 30-50 wt% stone particles, 15-35 wt% sand and 0.5-5% brightener. At production, first blend the materials of the top and bottom layer separately. Pave the bottom layer material into the mold then to the top the top layer material. Take off the mold after 24-48 hours then leave it for 20 to 30 days. Finally polish the surface.
Description
Technical field
The present invention relates to a kind of floor tile, refer in particular to a kind of waterstone-polishing grounding brick with imitated granite that is used for the sidewalk, the invention still further relates to the processing method of this floor tile.
Background technology
The sidewalk on highway both sides is emphasis of urban municipal construction, should guarantee pedestrian's walking safety, and is attractive in appearance again, durable, can play the effect of beautifying urban environment.At present, widely usedly change, be to adopt slag to make coloredly, exists intensity low, the deficiency of not wear-resisting, easy fracture damage.
Summary of the invention
A kind of waterstone-polishing grounding brick with imitated granite that the purpose of this invention is to provide a kind of intensity height, wear-resisting, long service life.
Further purpose of the present invention provides the processing method of the simple above-mentioned floor tile of a kind of technology.
Last purpose of the present invention is achieved in that a kind of waterstone-polishing grounding brick with imitated granite, is to be made of bottom and the surface layer that covers bottom surface, and wherein said bottom is to be made of cement 15～35%, sand 15～35% and chicken girt 30～50%; Surface layer is made up of white cement 15～35%, chicken girt 30～50%, sand 15～35% and brightener 0.5～5%; Above-mentioned percentage is weight percentage.
Back of the present invention one purpose is achieved in that a kind of processing method of waterstone-polishing grounding brick with imitated granite, comprises the steps: that (1) adds bottom batching, surface layer batching respectively in an amount of water and mixes in proportion; (2) lay underlying material earlier at mold bottom, then at underlying material top paved surface layered material; The demoulding after (3) 24～48 hours, and maintenance 20 to 30 days; (4) surface layer is carried out grinding process promptly.
Floor tile of the present invention has following advantage:
(1) than present widely used slag floor tile intensity height, average rupture strength C
fReach 5.65MPa.
(2) abrasion resistance is good: mill hole length is less than 21.2mm.
(3) water absorption rate is less than 5.0%.
Description of drawings
Below in conjunction with in the accompanying drawing and embodiment the present invention is described in further detail, but do not constitute any limitation of the invention.
Fig. 1 is the structural representation of floor tile of the present invention.
The specific embodiment
Consult shown in Figure 1ly, waterstone-polishing grounding brick with imitated granite of the present invention is to be made of bottom and the surface layer 2 that covers bottom 1 surface, and bottom 1 is by percentage by weight: cement 15～35%, husky 15～35% and chicken girt 30～50% constitute; Surface layer 2 is by percentage by weight: white cement 15～35%, chicken girt 30～50%, husky 15～35% and brightener 0.5～5% form.
The processing method of waterstone-polishing grounding brick with imitated granite of the present invention comprises the steps: that (1) adds bottom batching, surface layer batching respectively in an amount of water and mixes in proportion; (2) lay underlying material earlier at mold bottom, then at underlying material top paved surface layered material; The demoulding after (3) 24～48 hours, and maintenance 20 to 30 days; (4) surface layer is carried out grinding process promptly.
Embodiment 1
Bottom raw material proportioning: 140 kilograms of cement, husky 140 kilograms, chicken girt 120 kg
Surface layer raw material proportioning: 35 kilograms of white cements, 30 kilograms of chicken girts, 35 kilograms in sand, 0.5 kilogram of brightener
Processing method: above-mentioned bottom, surface layer raw material and an amount of water are mixed, then the bottom raw material is laid in the metal die of 40 * 40 * 5cm, and mechanical pudding, laying depth is about 4cm, lays the surface layer raw material then on the bottom raw material, floating after the mechanical pudding, the about 1cm of thickness, the demoulding after 48 hours, maintenance is after 25 days, to smooth smooth getting final product, warehouse-in is packed in the check back with levigator polishing surface course.
Bottom raw material proportioning: 60 kilograms of cement, 140 kilograms in sand, 200 kilograms of chicken girts
Surface layer raw material proportioning: 15 kilograms of white cements, 50 kilograms of chicken girts, 35 kilograms in sand, 5 kilograms of brighteners
Processing method: above-mentioned bottom, surface layer raw material and an amount of water are mixed, then the bottom raw material is laid in the metal die of 40 * 40 * 5cm, and mechanical pudding, laying depth is about 4cm, lays the surface layer raw material then on the bottom raw material, floating after the mechanical pudding, the about 1cm of thickness, the demoulding after 24 hours, maintenance is after 20 days, to smooth smooth getting final product, warehouse-in is packed in the check back with levigator polishing surface course.
Embodiment 3
Bottom raw material proportioning: 200 kilograms of cement, 200 kilograms in sand, 300 kilograms of chicken girts
Surface layer raw material proportioning: 50 kilograms of white cements, 75 kilograms of chicken girts, 50 kilograms in sand, 2 kilograms of brighteners
Processing method: above-mentioned bottom, surface layer raw material and an amount of water are mixed, then the bottom raw material is laid in the metal die of 40 * 40 * 5cm, and mechanical pudding, laying depth is about 4cm, lays the surface layer raw material then on the bottom raw material, floating after the mechanical pudding, the about 1cm of thickness, the demoulding after 48 hours, maintenance is after 30 days, to smooth smooth getting final product, warehouse-in is packed in the check back with levigator polishing surface course.
Above-mentioned floor tile detects by JC/T446-2000 " rigid pavement commentaries on classics ", and the result is as follows:
Rupture strength C
f: average 5.65MPa
Monolithic minimum value 5.35MPa
Abrasion resistance: mill hole length 21.2mm
Water absorption rate: 5.0%.
Claims (2)
1. waterstone-polishing grounding brick with imitated granite is to be made of bottom (1) and the surface layer (2) that covers bottom (1) surface, it is characterized in that described bottom be by cement 15～35%, husky 15～35% and chicken girt 30～50% constitute; Surface layer is made up of white cement 15～35%, chicken girt 30～50%, sand 15～35% and brightener 0.5～5%; Above-mentioned percentage is weight percentage.
2. the processing method of the described waterstone-polishing grounding brick with imitated granite of claim 1 is characterized in that comprising the steps: that (1) adds bottom batching, surface layer batching respectively in an amount of water and mixes in proportion; (2) lay underlying material earlier at mold bottom, then at underlying material top paved surface layered material; The demoulding after (3) 24～48 hours, and maintenance 20 to 30 days; (4) surface layer is carried out grinding process promptly.