CN1817504A - Production of precisioning-cast mould - Google Patents
Production of precisioning-cast mould Download PDFInfo
- Publication number
- CN1817504A CN1817504A CN 200610044425 CN200610044425A CN1817504A CN 1817504 A CN1817504 A CN 1817504A CN 200610044425 CN200610044425 CN 200610044425 CN 200610044425 A CN200610044425 A CN 200610044425A CN 1817504 A CN1817504 A CN 1817504A
- Authority
- CN
- China
- Prior art keywords
- wax
- pattern
- sodium chloride
- chloride content
- consolidation liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A technology for manufacture precise casting mould features that during the solidification of wax mould, the ammonium bicarbonate and calcium chloride are added to the solidifying liquid for decomposing sodium chloride, decreasing the content of sodium chloride and increasing the content of ammonium chloride, resulting in short solidifying time and high strength of mould.
Description
Technical field
The present invention relates to a kind of manufacture method of precision casting mold.
Background technology
The lost-wax process casting claims precision-investment casting again, is a kind of casting technique of cutting less or not having cutting, is the technology of an excellence in the casting industry, and its application is very extensive.It is not only applicable to the casting of all kinds, various alloys, and the casting dimension accuracy of producing, surface quality are than other casting method height, even other casting method be difficult to cast complexity, high temperature resistant, the foundry goods that is not easy to process, all can adopt precision-investment casting to cast.So-called full form casting process; simple saying is exactly to make meltability model (being called for short fusible pattern or model) with fusible material (for example wax material or plastics); apply the special fireproof coating of several layers thereon; behind super-dry and whole shell of sclerosis formation; from shell, melt model with steam or hot water again; then shell is placed sandbox; around it, fill dry moulding; at last casting mold is put into roaster through high-temperature roasting (when adopting the high strength shell; can moulding and with the shell roasting direct after the demoulding); casting mold or shell are after roasting, in casting molten metal wherein and obtain foundry goods.The model casting biggest advantage is exactly because investment-casting has very high dimensional accuracy and surface smoothness, so can reduce machining work, just the position of having relatively high expectations on part stays a little allowance to get final product, even some foundry goods only stay polishing, the polishing surplus, needn't machining can use.This shows, adopt investment casting method can save machine tool and machining period in a large number, save raw material metal significantly.The sclerosis of shell is a precision-investment casting key, and the quality of shell is directly connected to the quality of foundry goods.In system shell process, it is water-soluble that sodium oxide molybdena in the waterglass and ammonium chloride generation chemical reaction generate sodium chloride, increase along with output, sodium chloride concentration improves in the consolidation liquid, saturated post crystallization is deposited in and solidifies in the pond, influence the dissolving of ammonium chloride, ammonium chloride concentration is reduced, directly influence the hardening strength and the firm time of shell.Low and broken because of intensity when making shell firm time lengthening, casting, cast(ing) surface gets rusty easily.
Summary of the invention
The serious problems of the objective of the invention is curing agent physical removal sodium chloride complex process in the hot investment casting process for hundreds of years that will solve, waste, polluting, take a lot of work provide a kind of manufacture method that adopts chemistry to remove the precision casting mold of sodium new method.
For achieving the above object, the present invention adopts following technical scheme:
The manufacture method of the said precision casting mold of the present invention comprises the steps
A, compacting wax-pattern immerse the wax-pattern that suppresses in the slurries of waterglass and silica flour then, make the wax-pattern hanging; Take out wax-pattern, sprinkle quartz sand on wax-pattern, the wax-pattern that will speckle with slurries and quartz sand then is immersed in and makes shell in the consolidation liquid; In system shell process, detect the sodium chloride content of consolidation liquid at any time, if sodium chloride content is no more than standard, execution in step C then; If sodium chloride content is above standard, execution in step B then;
B: adding carbonic hydroammonium and stirring are dissolved it in consolidation liquid, and the ratio of weight and number of consolidation liquid and carbonic hydroammonium is 1000:(1-10); After treating that carbonic hydroammonium dissolves fully, in solidifying the pond, add calcium chloride while stirring, the weight that adds calcium chloride is 1/4 of the rapid middle carbonic hydroammonium weight of previous step, dissolve fully and produce precipitation of calcium carbonate up to calcium chloride, detect the sodium chloride content that solidifies consolidation liquid in the pond once more, if sodium chloride content still exceeds standard, then repeat this step, do not exceed standard up to sodium chloride content; If sodium chloride content does not exceed standard, execution in step C then;
C: after treating the shell formation on the wax-pattern and reaching requirement, take out wax-pattern, make wax fusing wherein obtain complete mould with the method that heats.
After adopting technique scheme, shortened dramatically the time that shell solidifies in solidifying the pond, the shell solidification effect is more even, and intensity is higher, also avoids simultaneously owing to saliferous in the shell causes foundry goods to get rusty.
The specific embodiment
With the little shape foundry goods of common dewaxing Foundry Production is example, and the sodium chloride content in the consolidation liquid can not surpass 6%.The step of present embodiment is as follows:
A, compacting wax-pattern immerse the wax-pattern that suppresses in the slurries of waterglass and silica flour then, make the wax-pattern hanging; Take out wax-pattern, sprinkle quartz sand on wax-pattern, the wax-pattern that will speckle with slurries and quartz sand then is immersed in and makes shell in the consolidation liquid; In system shell process, detect the sodium chloride content of consolidation liquid at any time, if sodium chloride content is no more than 6%, execution in step C then; If sodium chloride content surpasses 6%, then execution in step B;
B: adding carbonic hydroammonium and stirring are dissolved it in consolidation liquid, add carbonic hydroammonium 1-10 kilogram in each ton consolidation liquid; After treating that carbonic hydroammonium dissolves fully, in solidifying the pond, add calcium chloride while stirring, the weight that adds calcium chloride is 1/4 of the rapid middle carbonic hydroammonium weight of previous step, dissolve fully and produce precipitation of calcium carbonate up to calcium chloride, detect the sodium chloride content that solidifies consolidation liquid in the pond once more, if sodium chloride content still exceeds standard, then repeat this step, do not exceed standard up to sodium chloride content; If sodium chloride content does not exceed standard, execution in step C then;
C: after treating the shell formation on the wax-pattern and reaching requirement, take out wax-pattern, make wax fusing wherein obtain complete mould with the method that heats.
In above-mentioned B step,, can clear up at any time and solidify the pond if find that deposit is too many.
In other embodiment, the sodium chloride content standard in the consolidation liquid can change, as long as the quantity of corresponding adjustment carbonic hydroammonium and calcium chloride, its objective is that content with sodium chloride is reduced to below the criterion numeral to get final product.
In the above-described embodiments, the time standard that the prescription of compacting method of wax-pattern and slurry, shell form all is a prior art, and those of ordinary skill should be understood that and grasps, no longer is described in detail at this.
The root problem that the present invention will solve is the sodium chloride that will remove in the consolidation liquid, and step B added carbonic hydroammonium in solidifying the pond after, at normal temperatures and pressures, carbonic hydroammonium was very fast water-soluble, and generates ammonium chloride and sodium acid carbonate with sodium chloride generation chemical reaction; Ammonium chloride is the main component in the consolidation liquid just, can promote the sclerosis of shell.The addition of carbonic hydroammonium is directly proportional with sodium chloride concentration in the consolidation liquid.
Adding along with carbonic hydroammonium, the content of sodium acid carbonate progressively improves in the consolidation liquid, influence the concentration of ammonium chloride for the raising that prevents sodium acid carbonate content, in consolidation liquid, add an amount of calcium chloride again, addition is about 1/4 of carbonic hydroammonium, calcium chloride and sodium acid carbonate generation chemical reaction generate precipitation of calcium carbonate and a spot of sodium chloride and hydrogen.
By above-mentioned reaction, make that sodium chloride concentration greatly reduces in the consolidation liquid, know when being lower than standard value, do not influence the sclerosis of shell substantially, thereby reach simplify technology, turn waste into wealth, increase the benefit, the purpose of energy savings, protection environment.
Claims (1)
1, a kind of manufacture method of precision casting mold is characterized in that comprising the steps
A, compacting wax-pattern immerse the wax-pattern that suppresses in the slurries of waterglass and silica flour then, make the wax-pattern hanging; Take out wax-pattern, sprinkle quartz sand on wax-pattern, the wax-pattern that will speckle with slurries and quartz sand then is immersed in and makes shell in the consolidation liquid; In system shell process, detect the sodium chloride content of consolidation liquid at any time, if sodium chloride content is no more than standard, execution in step C then; If sodium chloride content is above standard, execution in step B then;
B: adding carbonic hydroammonium and stirring are dissolved it in consolidation liquid, and the ratio of weight and number of consolidation liquid and carbonic hydroammonium is 1000: (1-10); After treating that carbonic hydroammonium dissolves fully, in solidifying the pond, add calcium chloride while stirring, the weight that adds calcium chloride is 1/4 of the rapid middle carbonic hydroammonium weight of previous step, dissolve fully and produce precipitation of calcium carbonate up to calcium chloride, detect the sodium chloride content that solidifies consolidation liquid in the pond once more, if sodium chloride content still exceeds standard, then repeat this step, do not exceed standard up to sodium chloride content; If sodium chloride content does not exceed standard, execution in step C then;
C: after treating the shell formation on the wax-pattern and reaching requirement, take out wax-pattern, make wax fusing wherein obtain complete mould with the method that heats.