CN1814830A - Method for removing ferrous-iron from manganese sulfate - Google Patents
Method for removing ferrous-iron from manganese sulfate Download PDFInfo
- Publication number
- CN1814830A CN1814830A CN 200610058717 CN200610058717A CN1814830A CN 1814830 A CN1814830 A CN 1814830A CN 200610058717 CN200610058717 CN 200610058717 CN 200610058717 A CN200610058717 A CN 200610058717A CN 1814830 A CN1814830 A CN 1814830A
- Authority
- CN
- China
- Prior art keywords
- solution
- manganese sulfate
- ferrous
- manganese
- oxygen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses a method for removing ferrous iron in the MnSO4 solution, which utilizes the electrocatalysis theory to add 0.1-100gL<SUP>-1</SUP> active carbon as the catalyst, controls the temperature at 10-100deg.C, regulates the pH value of the solution at 0-8 and blasts air or oxygen for 0.5-3h to oxidize the ferrous ions in the solution to trivalence ions quickly.
Description
Technical field
The present invention relates to a kind of method of removing ferrous ion, relate in particular to a kind of method of removing ferrous ion in the manganese sulfate solution.
Background technology
No matter be pyrolusite, or the sulphuric leachate of rhodochrosite, all containing the impurity ferrous ion, the method for removing ferrous ion at present is to control the pH value of solution value below 2.3, adds the oxygenant dioxide ore for manganese, is ferric ion with oxidation of divalent iron ion.Though this method can be reduced to 0.1mg.L with the ferrous ion in the solution
-1Below, but the add-on of manganese oxide ore is big, and utilization ratio is very low, the cost height.Ferrous ion is a kind of reductive agent, and cheap air is a kind of oxygenant, after both contacts, oxygen can be oxidized to ferric ion with ferrous ion on thermodynamics, but because of the reaction activity height, speed of response is very slow on kinetics, can't satisfy industrial requirement.
Summary of the invention
In order to solve the problem of above-mentioned existence, the object of the present invention is to provide a kind of electrocatalysis principle of utilizing, in manganese sulfate solution, add gac as eelctro-catalyst, remove ferrous method in the sulfuric acid manganese solution, with air the ferrous ion in the manganese sulfate solution is oxidized to ferric ion fast under certain condition.
Technical scheme of the present invention is achieved in that a kind of ferrous method in the sulfuric acid manganese solution of removing, and adds eelctro-catalyst gac 0.1～100g.L in manganese sulfate solution
-1, the control solution temperature is 10～100 ℃, and the pH of regulator solution is 0～8, blasts air or oxygen 0.5～3h in manganese sulfate solution.
Described eelctro-catalyst gac add-on is preferably 0.2～20g.L
-1, solution temperature control is preferably 20～80 ℃, and the pH of solution is preferably 1～7, and the time that blasts air or oxygen is preferably 0.8～2h.
Compared with prior art, the invention has the beneficial effects as follows
1, in manganese sulfate solution, adds gac as eelctro-catalyst, utilize air or oxygen that the ferrous ion in the manganese sulfate solution is oxidized to ferric ion fast.
2, effective except that ferrous ion, economize on resources, cost is low.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail, but not as a limitation of the invention.
Embodiment 1: in the 1000ml manganese sulfate solution, adding the 0.5g activity charcoal powder, is 6 o'clock in 30 ℃ of temperature and pH, with air or oxygen oxidation 0.5h, ferrous ion concentration can be reduced to 0.1mg.L
-1Below.
Embodiment 2: in the 1000ml manganese sulfate solution, adding the 3g activity charcoal powder, is 8 o'clock in 50 ℃ of temperature and pH, with air or oxygen oxidation 1h, ferrous ion concentration can be reduced to 0.1mg.L
-1Below.
Embodiment 3: in the 1000ml manganese sulfate solution, adding the 9g activity charcoal powder, is 4 o'clock in 15 ℃ of temperature and pH, with air or oxygen oxidation 2.5h, ferrous ion concentration can be reduced to 0.1mg.L
-1Below.
Embodiment 4: in the 1000ml manganese sulfate solution, adding the 1g activity charcoal powder, is 2 o'clock in 90 ℃ of temperature and pH, with air or oxygen oxidation 3h, ferrous ion concentration can be reduced to 0.1mg.L
-1Below.
Embodiment 5: in the 1000ml manganese sulfate solution, adding the 5g activity charcoal powder, is 1 o'clock in 40 ℃ of temperature and pH, with air or oxygen oxidation 3h, ferrous ion concentration can be reduced to 0.1mg.L
-1Below.
Claims (5)
1, a kind of except that ferrous method in the sulfuric acid manganese solution, it is characterized in that: in manganese sulfate solution, add gac 0.1～100g.L
-1, the control solution temperature is 10～100 ℃, and the pH of regulator solution is 0～8, blasts air or oxygen 0.5～3h in manganese sulfate solution.
2, manganese sulfate solution according to claim 1 removes ferrous method, and it is characterized in that: the gac of adding is 0.2～20g.L
-1
3, a kind of ferrous method in the sulfuric acid manganese solution of removing according to claim 1, it is characterized in that: the temperature of solution is controlled to be 20～80 ℃.
4, a kind of ferrous method in the sulfuric acid manganese solution of removing according to claim 1, it is characterized in that: the pH of solution is 1～7.
5, a kind of ferrous method in the sulfuric acid manganese solution of removing according to claim 1, it is characterized in that: the time that thigh is gone into air or oxygen is 0.8～2h.