CN1810906A - Termite and insect resisting glue and its application - Google Patents
Termite and insect resisting glue and its application Download PDFInfo
- Publication number
- CN1810906A CN1810906A CN 200510023666 CN200510023666A CN1810906A CN 1810906 A CN1810906 A CN 1810906A CN 200510023666 CN200510023666 CN 200510023666 CN 200510023666 A CN200510023666 A CN 200510023666A CN 1810906 A CN1810906 A CN 1810906A
- Authority
- CN
- China
- Prior art keywords
- proof
- insect
- glue
- termide
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The termite and insect resisting glue consists of white emulsion of 25-50 wt% solid content in 90-99.9 wt% and insecticide 0.1-10 wt%. The glue of the present invention may be used for adhering wooden board, high density fiber board, shaving board and other wood article, and can form termite and insect preventing film, layer or integral product to block eating. It has high termite and insect preventing efficiency, lasting effect, high safety and environment friendship and convenient use.
Description
Technical field
The present invention relates to a kind of aqueous adhesive, relate in particular to a kind of termide-proof and insect-proof glue.
Background technology
At present, the common tackiness agent of bonding employing of wooden boards, high-density medium density fiberboard, shaving board, finger plate, clamping plate does not have the termide-proof and insect-proof function.In addition, the preservation of timber against decay is handled mainly based on infusion method, be about to timber and be immersed in the solution that contains medicine, its shortcoming is that medicine easily runs off, and duration of efficacy is short, and medicine is harmful, can pollute environment.Therefore, at present the termide-proof and insect-proof pesticide application technology of timber or plank can not be applicable to the decorations of the application of woodenware such as modern wooden furniture and family, office.
Summary of the invention
The technical issues that need to address of the present invention provide a kind of termide-proof and insect-proof glue and application thereof, to overcome the defective that does not have the termide-proof and insect-proof function that prior art exists, satisfy the needs of the decorations of the application of woodenware such as modern wooden furniture and family, office.
Termide-proof and insect-proof glue of the present invention is characterized in that, its component and weight percent content comprise:
Solids content is 20%～50% glue 90%～99.9%
Insect-proof agent 0.1%～10%.
Described glue is to be a kind of or its mixture in polyvinyl acetate emulsion or the polyvinyl alcohol solution, is commonly called as white glue with vinyl, is the commercially available prod;
Described insect-proof agent is a kind of or its mixture in the white clever 4-phenelyl of water-based pyrethroid, stuck gram missible oil or silicon [3-(the 4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane.
Described water-based pyrethroid can be selected the aqueous emulsion of a kind of or its mixture in transfluthrin or the effective cypermethrin for use, can adopt the commercially available prod;
The optimum weight per-cent of constituent is that solids content is 30% white glue with vinyl 95%, water-based pyrethroid 5%.
The preparation method of termide-proof and insect-proof glue of the present invention is foolproof, can adopt conventional physical mixed method.
Glue of the present invention can be used for the bonding of woodworks such as wooden boards, high-density medium density fiberboard, shaving board, finger plate, clamping plate, form termide-proof and insect-proof film, layer or whole woodwork, stop the moth erosion of termite and other moth to woodenware, its termide-proof and insect-proof efficient height, medicine are difficult for loss, lasting medicine, safety and environmental protection, easy construction, safety and environmental protection can be widely used in plank, clamping plate bonding in the decorations of bonding and family, office of modern wooden furniture.
Embodiment
The present invention is further illustrated below in conjunction with embodiment.
Among the embodiment:
White glue with vinyl adopts the product of Dongshan District port, Jieyang City, Guangdong Province letter coating viscose glue factory or Zhujiang Yijiang Chemical Co., Ltd., Guangzhou City;
Insect-proof agent can adopt the water-based pyrethroid special efficacy insect-proof agent of Guangdong Province Insects Research Institute development, or adopts the stuck gram missible oil of Britain Shell Co. Ltd production or the white clever 4-phenelyl of silicon [3-(the 4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane that Japan Pyrethrum Co., Ltd produces.
Embodiment 1
Prescription 1:
White glue with vinyl (solids content is 30%) 95%
High performance aqueous emulsion of cypermethrin 5%.
Prescription 2:
White glue with vinyl (solids content: 30%) 90%;
Transfluthrin aqueous emulsion 10%.
Prescription 3:
White glue with vinyl (solids content: 50%) 98%;
Stuck gram missible oil 2%.
Prescription 4:
White glue with vinyl (solids content: 40%) 94%;
Transfluthrin and effective cypermethrin mixing water emulsion (1: 1, weight ratio) 6%.
Prescription 5:
White glue with vinyl (solids content: 40%) 94%;
The white clever 4-phenelyl of silicon [3-(4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane 6%.
Wherein fill a prescription three for optimum formula.
When using preparation, water-based pyrethroid special efficacy insect-proof agent is added white glue with vinyl mix and get final product.During coating decoration, can add an amount of water as the case may be and regulate viscosity.
Detect according to GB/T 18260-2000 " wood preservative is to termite toxic effect test method ", GB8583-2001 " limits of harmful substances in the indoor decorating adhesive " and Q/SZC 009-2005 " termite-proof glue ", quality and technical index and harmful substance contents are as follows:
Prescription 1:
| Interventions Requested | Index |
| Outward appearance | The oyster white thick liquid |
| Solids content, % | 30 |
| PH value | 6 |
| Viscosity, mPaS | 4500 |
| Granularity, mm | 2.5 |
| Stability | No layering |
| Free formaldehyde, g/kg ,≤ | 1 |
| Benzene, g/kg ,≤ | 0.2 |
| Toluene+dimethylbenzene, g/kg ,≤ | 10 |
| Total volatile organism, g/L ,≤ | 50 |
| The termide-proof and insect-proof ability, level ,≤ | 1 |
Prescription 2:
| Interventions Requested | Index |
| Outward appearance | The oyster white thick liquid |
| Solids content, % | 30 |
| PH value | 5 |
| Viscosity, mPaS | 5000 |
| Granularity, mm | 2.5 |
| Stability | No layering |
| Free formaldehyde, g/kg ,≤ | 1 |
| Benzene, g/kg ,≤ | 0.1 |
| Toluene+dimethylbenzene, g/kg ,≤ | 5 |
| Total volatile organism, g/L ,≤ | 30 |
| The termide-proof and insect-proof ability, level ,≤ | 1 |
Prescription 3:
| Interventions Requested | Index |
| Outward appearance | The oyster white thick liquid |
| Solids content, % | 50 |
| PH value | 5 |
| Viscosity, mPaS | 3500 |
| Granularity, mm | 2.5 |
| Stability | No layering |
| Free formaldehyde, g/kg ,≤ | 0.5 |
| Benzene, g/kg ,≤ | 0.1 |
| Toluene+dimethylbenzene, g/kg ,≤ | 10 |
| Total volatile organism, g/L ,≤ | 40 |
| The termide-proof and insect-proof ability, level ,≤ | 1 |
Prescription 4:
| Interventions Requested | Index |
| Outward appearance | The oyster white thick liquid |
| Solids content, % | 40 |
| PH value | 4 |
| Viscosity, mPaS | 5500 |
| Granularity, mm | 2.5 |
| Stability | No layering |
| Free formaldehyde, g/kg ,≤ | 1 |
| Benzene, g/kg ,≤ | 0.2 |
| Toluene+dimethylbenzene, g/kg ,≤ | 10 |
| Total volatile organism, g/L ,≤ | 40 |
| The termide-proof and insect-proof ability, level ,≤ | 1 |
Embodiment 2
Adopt with embodiment 1 in 1 identical method and the ratio of filling a prescription, wherein:
Glue is the mixture (weight ratio is 1: 1) of polyvinyl acetate emulsion and polyvinyl alcohol solution
Insect-proof agent is the mixture (weight ratio is 1: 1) of the white clever 4-phenelyl of water-based pyrethroid special efficacy insect-proof agent and silicon [3-(4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane.
Detected result is as follows:
| Interventions Requested | Index |
| Outward appearance | The oyster white thick liquid |
| Solids content, % | 30 |
| PH value | 5 |
| Viscosity, mPaS | 4500 |
| Granularity, mm | 2.5 |
| Stability | No layering |
| Free formaldehyde, g/kg ,≤ | 0.5 |
| Benzene, g/kg ,≤ | 0.2 |
| Toluene+dimethylbenzene, g/kg ,≤ | 5 |
| Total volatile organism, g/L ,≤ | 20 |
| The termide-proof and insect-proof ability, level ,≤ | 1 |
Claims (8)
1. a termide-proof and insect-proof glue is characterized in that, its component and weight percent content comprise:
Solids content is 20%～50% glue 90%～99.9%
Insect-proof agent 0.1%～10%.
2. termide-proof and insect-proof glue according to claim 1 is characterized in that, described glue is selected from a kind of or its mixture in polyvinyl acetate emulsion or the polyvinyl alcohol solution.
3. termide-proof and insect-proof glue according to claim 1, it is characterized in that described insect-proof agent is a kind of or its mixture in the white clever 4-phenelyl of water-based pyrethroid, stuck gram missible oil or silicon [3-(the 4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane.
4. termide-proof and insect-proof glue according to claim 1 is characterized in that, the water-based pyrethroid is the aqueous emulsion of a kind of or its mixture in transfluthrin or the effective cypermethrin.
5. termide-proof and insect-proof glue according to claim 2, it is characterized in that described insect-proof agent is a kind of or its mixture in the white clever 4-phenelyl of water-based pyrethroid, stuck gram missible oil or silicon [3-(the 4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane.
6. according to each described termide-proof and insect-proof glue of claim 1～5, it is characterized in that the weight percent of constituent is that solids content is 30% white glue with vinyl 95%, water-based pyrethroid 5%.
7. according to the application of each described termide-proof and insect-proof glue of claim 1～6, it is characterized in that, be used for the bonding of woodwork.
8. the application of termide-proof and insect-proof glue according to claim 7 is characterized in that, woodwork comprises wooden boards, high-density medium density fiberboard, shaving board, finger plate or clamping plate.