CN1803613A - ZSM-5 type molecular sieve and method for preparing the same - Google Patents
ZSM-5 type molecular sieve and method for preparing the same Download PDFInfo
- Publication number
- CN1803613A CN1803613A CN 200510097145 CN200510097145A CN1803613A CN 1803613 A CN1803613 A CN 1803613A CN 200510097145 CN200510097145 CN 200510097145 CN 200510097145 A CN200510097145 A CN 200510097145A CN 1803613 A CN1803613 A CN 1803613A
- Authority
- CN
- China
- Prior art keywords
- zsm
- molecular sieve
- sio
- accordance
- natural mineral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method for small-size ZSM-5 molecular sieve. Wherein, using pearlite and montmorillonite as material for aluminum, adding crystal seed for crystallization reaction on hydrothermal condition, and obtaining a small-size product with 5~95% ZSM-5 that can be used to prepare modified ZSM-5 molecular sieve by different post-treatment method or as the active intergradient or carrier for catalyst. This invention cuts the cost more.
Description
Technical field
The invention belongs to molecular sieve and technology of preparing thereof.Specifically relating to provides the synthetic needed all or part of aluminium of ZSM-5 source with natural mineral, utilizes the technology of the synthetic small-particle type ZSM 5 molecular sieve of crystal seed method simultaneously.
Background technology
The ZSM-5 molecular sieve from 1972 by U.S. Mobil company reported first (USP3702886) since because its unique pore passage structure and shape selective catalysis effect, in many oil refining and chemical process, obtained application.Its preparation method is also being updated, synthetic by initial employing organic amine template, non-amine method finally is synthetic, the manufacturing cost of ZSM-5 is obviously reduced, by development of technology such as post-modification processing, the Application Areas of ZSM-5 molecular sieve is constantly enlarged again to synthetic back ZSM-5 molecular sieve product.For example, the early stage fluid catalytic cracking that is applied to petroleum refining industry (FCC) catalyzer does not all use the ZSM-5 molecular sieve, and current FCC catalyzer majority is added with the ZSM-5 molecular sieve, distributes in order to improve catalyst performance and then to improve product.Because the FCC catalyzer is the very big catalyzer of a class requirement, only just reach tens thousand of tons at Chinese market consumption last year, this has caused the increase to ZSM-5 molecular sieve demand, also requires further to reduce the production cost and the price of ZSM-5 molecular sieve simultaneously.
Say that from another point of view comprise that the effect of zeolite molecular sieve in catalyzer such as FCC catalyzer of ZSM-5 molecular sieve is as active ingredient, the good distribution of active ingredient is very important to catalyzer, can improve the utilising efficiency of active ingredient like this.Improving an important measures of the dispersity of molecular sieve active ingredient in catalyzer, is exactly the zeolite product that as far as possible uses small particle size (small particle diameters).The granular size of molecular sieve is two different notions with grain size.The molecular sieve that crystal grain is little just means that not necessarily granularity is little, because, even the molecular sieve of little crystal grain also can form big particle by agglomeration.So short grained molecular sieve needs for making high performance catalyst.
Usually the method for preparing the ZSM-5 molecular sieve is to adopt the silica-alumina gel system of alkalescence synthetic.System is made up of sodium oxide, aluminum oxide, silicon oxide and water.The silicon source that is used for synthesis material is generally water glass, and the aluminium source is generally Tai-Ace S 150.The 1980's, general in the past quaternary ammonium salt or other organic amine of using synthesized ZSM-5 molecular sieve (being called for short " the amine method is arranged ") as template, because organic formwork agent prices such as quaternary ammonium salt are higher, occur utilizing the technology (be crystal seed method or claim non-amine method) of the synthetic ZSM-5 molecular sieve of ZSM-5 molecular sieve crystal seed organic formwork agents such as (and do not use) quaternary ammonium salts after the 1980's, made the preparation cost of ZSM-5 molecular sieve obviously reduce.
Having occurred some in recent years is the technology of part material crystallization ZSM-5-5 molecular sieve with the clay, has reduced the manufacturing cost of ZSM-5 molecular sieve.For example:
United States Patent (USP) (USP4,091,007, USP5,558,851) technology of disclosed Mobil company, utilize C2~C4 alkyl quaternary ammonium salts as template, can make kaolin that the aluminium source of synthetic ZSM-5 or ZSM-4 molecular sieve needed 70% is provided by specific method, thereby make ZSM-5 or the ZSM-4 molecular sieve relative crystallinity 40%~60% that obtains, and have catalytic material clays such as (macropore is provided) kaolin of unique pore passage structure simultaneously.
EP0,068,817 discloses the method for the synthetic ZSM-5 of the acid-treated metakaolin of a kind of usefulness.Aluminum oxide in the metakaolin is separated out by the effect of strong acid example hydrochloric acid, sulfuric acid, nitric acid, phosphoric acid, and in the presence of 4-propyl bromide, the ZSM-5 molecular sieve is synthesized in acid-treated metakaolin and sodium hydroxide effect.
USP6,004,527 has described the method by the synthetic ZSM-5 of pure silicon microballoon.Aluminium source and sodium source are added by separately nitrate dipping by the initial humidity pickling process.Adopting TPAOH in this method is directed agents, and ZSM-5 zeolite product degree of crystallinity is 25%, and product has kept the shape and size of pure silicon microballoon.
USP4,522,705 have told about preparation is contained the catalyzer of ZSM-5 molecular sieve additive by the clay agglomerates in-situ crystallization method.Clay microphere is handled by the aqueous solution of sodium hydroxide and organic formwork agent, comprises the crystal seed of ZSM-5 molecular sieve in the preformed microballoon, and crystallization is to carry out under the condition of sodium hydroxide and the existence of propyl group amine.
USP5,145,659 have reported that its mesostroma is moulding clay or spray-dried microspheres by the method for the synthetic ZSM-5 molecular sieve of preformed matrix, composition has silicon source, aluminium source, basic metal and other mixture.Silicate solutions floods preformed matrix and makes it be rich in the silicon source.
More than disclosed be though that the technology of the synthetic ZSM-5 molecular sieve of raw material has adopted the kaolin raw material to reduce cost with the roasting kaolin, but still need to add expensive organic template.
USP6,908,603 disclose a technology that is equipped with kaolin microsphere in-situ crystallization ZSM-5-5 with non-template agent legal system.By the directed agents of use y-type zeolite and suitable silicon source, the synthetic ZSM-5 microspherical catalyst that contains, this method crystallization time is short, ZSM-5 degree of crystallinity is higher.But this method only at kaolin microsphere as raw material, its product summary is the in-situ crystallization microspherical catalyst, and the also essential directed agents that relies on of this method.
Chinese invention patent CN02153377 discloses a kind of method of synthetic ZSM-5 molecular sieve, it is characterized in that this method is as silicon source and all or part of aluminium source with diatomite, mix with other aluminium source, NaOH and water, the molecular sieve that adds 0~10 weight % is as kind, and being mixed with mole proportioning is SiO
2/ Al
2O
3=20~80, Na
2O/SiO
2=0.05~0.20, H
2O/SiO
2=4~30 reaction mixture slurry, condition is carried out hydrothermal crystallizing routinely.This technology claims to adopt this method can reduce the gel generation, improves solid content, reduces cost.
As can be seen, in the prior art before the present invention, for the research concern that has been subjected to very in the field of business of preparation type ZSM 5 molecular sieve.But it is pointed out that above mentioned USP6,004,527, USP4,522,705, USP5,145,659, USP6,908,603 disclosed technology, mainly be at the kaolin raw material as silicon source or aluminium source, for reaching goal of the invention, organic formwork agent or directed agents remain essential raw material in preparation process.The technology of CN02153377 has been primarily aimed at utilizes the synthetic method of diatomite as the silicon source, the method that provides according to this technology, and be not suitable for raw material (as kaolin, perlite etc.) beyond the diatomite, and wherein also must use highly basic (NaOH), have certain limitation in force.
In addition, the method for utilizing natural mineral raw to prepare small-particle ZSM-5 molecular sieve is not in the news.
Mineral such as perlite, kaolin, medical stone, polynite, wilkinite are the huge nonmetallic minerals of reserves on the earth.Wherein the perlite reserves of China occupy the 3rd in the world.Mineral such as perlite are mainly used in building energy conservation at present, lagging material, and on the finishing material, a spot of kaolin is used for catalyst substrates (carrier).The contriver has passed through a large amount of literature surveys, do not see and utilize perlite, medical stone, polynite, the report of the synthetic ZSM-5 molecular sieve of wilkinite, the raw material of also finding to utilize cheap clay (kaolin) and utilizing the synthetic ZSM-5 molecular sieve of other raw mineral materials conduct except that clay (kaolin) and diatomite, utilize inexpensive crystal seed method to prepare the research report of ZSM-5 molecular sieve simultaneously, more do not find to utilize the aluminium source of natural mineral (or the natural mineral after handling) raw material, utilize inexpensive crystal seed method to prepare the report of ZSM-5 molecular sieve simultaneously as synthetic ZSM-5 molecular sieve.
Summary of the invention
Main purpose of the present invention is to provide a kind of method for preparing type ZSM 5 molecular sieve, that this method can be utilized is more cheap, raw material sources widely natural mineral realize the purpose of more low-cost synthetic ZSM-5 molecular sieve as synthesis material.
The method of the ZSM-5 of preparation molecular sieve provided by the invention more can be used for synthetic small-particle ZSM-5 molecular sieve.
The main component of natural mineral such as perlite, kaolin, medical stone, polynite, wilkinite is silicon-dioxide and aluminium sesquioxide.Several mineral facies ratios, silica content is than silica content height in the kaolin in perlite, medical stone, polynite, the wilkinite.
The method for preparing type ZSM 5 molecular sieve provided by the invention is to utilize natural mineral that all or part of aluminium source is provided, and realizes by adding crystal seed, comprises following process:
With natural mineral, silicon source material, acidic substance, water and crystal seed mixed preparing reaction mixture gel, make each component in this gel be by the mol ratio of its oxide compound:
SiO
2/Al
2O
3=5~200
M
2O/SiO
2=0.10~0.40
H
2O/SiO
2=10~50
Wherein, M represents alkali metallic sodium and/or potassium, described natural mineral accounts for total at least 70% the natural mineral raw of forming of oxide compound wherein for the weight percentage sum of wherein silicon oxide and aluminum oxide, and the consumption of described crystal seed is total SiO in natural mineral and the silicon source material
2Quality 0.2~15%;
This gel is warming up to 140~220 ℃, hydrothermal crystallizing 5~200 hours.
After crystallization is finished, more after filtration, washing, drying, make the mixture that contains type ZSM 5 molecular sieve.
Method provided by the present invention, suitable natural mineral can be a kind of or its mixtures in perlite, kaolin, medical stone, polynite, wilkinite, the coal gangue etc.Because method of the present invention can provide the synthetic required all or part of aluminium source of ZSM-5 by natural mineral, so, the extra aluminium source amount of substance that adds can be zero during the preparation reaction mixture gel, certainly, according to the particular case of used raw mineral materials or the target call of sintetics, also can add part aluminium source material in addition, to satisfy the requirement of silica alumina ratio.
According to method provided by the present invention, natural mineral can be through a kind of or its mixture in the mineral such as the perlite of elder generation's process roasting and pulverization process, kaolin, medical stone, polynite, wilkinite, coal gangue.The calcination process temperature can be 550~1200 ℃, preferably 700~1000 ℃; The calcination process time can be 0.3~200 hour, preferably l~10 hour.For pulverization process, use to improve its reaction efficiency after preferably these mineral processings being become particle diameter less than 50 microns fine powders, use after more preferably these mineral processings being become particle diameter less than 10 microns fine powders.
Method provided by the present invention, according to actual needs, natural mineral can additional acid be handled before the experience high-temperature roasting or after the roasting.After for example kaolin stands 800 ℃ of calcination process, handle, can reduce the content of aluminum oxide on the kaolin, be beneficial to the control of silica alumina ratio with the hydrochloric acid extracting; Natural mineral also can and alkali (as sodium hydroxide, yellow soda ash) carry out calcination process again after mixing, thereby the silicon in the mineral is activated, increase utilization to silicon in the mineral, obtain the silica alumina ratio that needs.So method provided by the present invention also can provide the synthetic required part silicon source of ZSM-5 by natural mineral.
Method provided by the present invention, wherein said natural mineral can be implemented acid treatment earlier before calcination process, to reduce the content of some chemical ingredients (for example calcium, iron) in the mineral.But this not necessarily.Because the ZSM-5 molecular sieve of the present invention's preparation can have many application scenarios, the relevant element that small amounts of mineral is brought does not influence its result of use.In addition, can also be by choosing the chemical constitution that suitable mineral source or kind are controlled the raw material mineral.Utilize method provided by the present invention to synthesize type ZSM 5 molecular sieve, can in scope, choose suitable raw mineral materials (cover and take off soil) as perlite, kaolin than broad, mineral are provided synthesize the required aluminium source of ZSM-5 molecular sieve even provide a part of silicon source simultaneously (as calcination process, or alkaline purification adds the perlite of roasting), can also provide a part of macropore or ZSM-5 the carrier of growth by mineral.So, say that strictly synthetic product of the present invention can be called the ZSM-5 molecular screen composite.
According to method provided by the present invention, wherein said crystal seed is a kind of or its several mixtures that are selected from ZSM-5 type, Y type, X type, A type, beta molecular sieve.Type ZSM 5 molecular sieve preferably.
Method provided by the present invention, wherein said silicon source material can be water glass, alkaline silica sol etc., preferably water glass.
Method provided by the present invention, wherein said aluminium source material can or contain one or more mixture in aluminium zeolite etc. for aluminium salt, aluminate, aluminum oxide, aluminium hydroxide, aluminium colloidal sol.Preferably Tai-Ace S 150 and sodium aluminate.The front illustrates, the adding in aluminium source not necessarily, promptly the add-on in aluminium source can be zero.
The method according to this invention need add the potential of hydrogen that acidic substance come the conditioned reaction mixture in preparation during reactant gel, be preferably make mixture the pH value between about 9.5~12.5, preferably the pH value is between 10.3~11.5.The selection of these acidic substance is not particularly limited, and can add mineral acid, for example sulfuric acid, hydrochloric acid, phosphoric acid or nitric acid etc., and the consumption of acidic substance meets the pH value that makes reaction mixture and both can in above-mentioned scope.
According to method provided by the present invention, in the reaction mixture gel that is mixed with, the mol ratio that material is formed is preferably SiO
2/ Al
2O
3=10~160, M
2O/SiO
2=0.15~0.35, H
2O/SiO
2=25~40, wherein M represents alkali metallic sodium and/or potassium.Sodium wherein and potassium also can be from the natural mineral compositions from silicon source material that adds or aluminium source material.
Method provided by the present invention, wherein said hydrothermal crystallizing are that the reaction mixture gel that will be mixed with is carried out crystallization in pressure vessel under temperature constant state or alternating temperature state, that is, and and thermostatic crystallization or variable temperature crystallization.
Method provided by the present invention, wherein said hydrothermal crystallizing are static crystallization, dynamic crystallization or intermittent type dynamic crystallization.
Method provided by the present invention, preferably 145~180 ℃ of wherein said crystallization temperatures, crystallization time preferably 10~80 hours.
Type ZSM 5 molecular sieve provided by the present invention is characterized in that the ratio (SiO of silicon oxide and aluminum oxide in its moiety
2/ Al
2O
3, be called for short silica alumina ratio) and less than 120, preferably silica alumina ratio is 25~70.
The product that makes according to the inventive method has the feature spectrogram of the X-light powdery diffractometry (XRD) of type ZSM 5 molecular sieve.The content (representing with relative crystallinity) of ZSM-5 molecular sieve (zeolite) can be controlled by the add-on of adjusting mineral and with the ratio of silicon source material, aluminium source material, acidic substance in above-mentioned condition and range in the product, treatment temp that also can be by changing mineral and treatment process (as calcination process and acid or/and alkaline purification) are controlled, generally, in the crystallization product content range of ZSM-5 molecular sieve between 5~95%.
Being to obtain the ZSM-5 molecular sieve according to one of feature of the type ZSM 5 molecular sieve of the inventive method preparation does not have agglomeration to take place.For example, be raw material with particle diameter less than 10 microns perlite mineral powder, 80% grain diameter is not more than 8 microns in the synthetic ZSM-5 product, can realize that especially 80% above particulate grain is through being not more than 4 microns in the product.
The feature of the type ZSM 5 molecular sieve that the present invention is prepared also is to contain in its moiety the chemical element from natural mineral, can also contain the constituent of raw materials used mineral.
For type ZSM 5 molecular sieve provided by the present invention, can also use conventional method to carry out modification and handle.For example, can be with type ZSM 5 molecular sieve provided by the present invention by carrying out ion-exchange with acidic substance (one or more of the aqueous solution such as the example hydrochloric acid aqueous solution, ammonium sulfate, ammonium nitrate, ammonium chloride), the ZSM-5 molecular sieve of preparation H type.Again for example, also can be exchanged into the ZSM-5 molecular sieve of Ca type with calcium salt soln.
Type ZSM 5 molecular sieve provided by the present invention can be applied to prepare catalyzer, support of the catalyst, carrier or sorbent material.For example, gained ZSM-5 molecular sieve of the present invention, after the process ordinary method is exchanged into H type ZSM-5 molecular sieve, can be used as one of FCC activity of such catalysts component and be used to prepare the FCC catalyzer, be used to improve the productive rate of the low-carbon alkene (ethene, propylene, butylene) of high added value.
Synthetic ZSM-5 provided by the invention and preparation method have following characteristics:
1, expanded the raw material range of synthetic ZSM-5 molecular sieve,, also reduced the raw materials cost of preparation ZSM-5 molecular sieve for natural mineral such as perlite, polynite, medical stone, wilkinite, kaolin, coal gangue have found new purposes.
2, the method that the crystal seed method of cheapness is prepared the ZSM-5 molecular sieve, combine with the method for utilizing the synthetic ZSM-5 molecular sieve of natural mineral cheap raw material, and, prepare the ZSM-5 molecular sieve according to method of the present invention, the raw material that is used for being mixed with reaction mixture does not contain sodium hydroxide and organic formwork agent, more can reduce the production cost of molecular sieve.
3, by choosing the raw mineral materials of suitable composition, can when synthetic ZSM-5 molecular sieve, directly bring some element into, as choose suitable perlite, can directly utilize potassium and calcium constituent on the perlite, prepare the ZSM-5 zeolite product of some specific demand.The for example existence of potassium, add precious metal, can improve the aromizing ability of ZSM-5 molecular sieve.
4, owing to be that part aluminium source is for discharging (obtaining) from mineral at least in building-up process, the formation of ZSM-5 molecular sieve is taken place gradually, in conjunction with control suitable material proportion and art breading, molecular sieve provided by the invention has smaller particles, has improved the utilising efficiency of molecular sieve again.
5, because mineral grain provides aluminium source or even the part silicon source that generates the ZSM-5 molecular sieve, in the ZSM-5 molecular screen composite that the present invention obtains the structure formation that is similar to kaolin microsphere in-situ crystallization y-type zeolite is arranged, be the carriers of mineral as the growth of ZSM-5 molecular sieve, growth has the ZSM-5 molecular sieve on the mineral grain carrier, form the structure of similar nucleocapsid, shortened reactant and product molecule path, improved efficient in the diffusion of molecular sieve intracrystalline.Therefore find in the use, when preparation FCC catalyzer, when adding the ZSM-5 of same amount (all adding 10%wt), use commercially available ZSM-5 molecular sieve (relative crystallinity 95%), compare with the ZSM-5 molecular sieve (relative crystallinity 80%) that uses present method preparation, although the ZSM-5 molecular screen composite degree of crystallinity of present method preparation is relatively low, latter's product distributes and is better than the former.It is the catalytic cracking experiment of raw material that the contriver once is used for the molecular sieve with method preparation of the present invention with grand celebration heavy oil, under the identical precursor of other condition, uses the productivity of propylene that catalyzer showed of ZSM-5 molecular sieve of the present invention to improve 1.3%.Because propylene is a price high product, the meaning that raising produced of productive rate should be obvious.
Description of drawings
Fig. 1 is X-ray diffraction (XRD) spectrogram of raw mineral materials synthetic ZSM-5 molecular screen composite for the embodiment of the invention 1 with the perlite.
Fig. 2 is X-ray diffraction (XRD) spectrogram of raw mineral materials synthetic ZSM-5 molecular screen composite for the embodiment of the invention 1 with kaolin.
Embodiment
Below in conjunction with embodiment the present invention is further detailed.
In an embodiment, said relative crystallinity is to represent with percentage ratio with the ratio of the peak area sum of five characteristic diffraction peaks of 2 θ (2theta) between 22.5~25.0 ° of X-ray diffraction (XRD) spectrogram of products therefrom and ZSM-5 molecular sieve standard specimen.The qualified ZSM-5 molecular sieve industrial goods that standard specimen adopts commercially available Catalyst Factory, Nankai Univ to produce are decided to be 100% with its degree of crystallinity.
The particle diameter of zeolite product adopts laser particle analyzer to measure.
The chemical constitution of mineral is provided by manufacturer or through the X-fluorescence spectrometry.
Embodiment 1
Be raw material with commercially available 400 order perlites (the Sino-German perlite in Dalian factory product, form see attached list 1), get 15g 700 ℃ of roastings 5 hours in retort furnace.Successively water glass (is contained SiO
220.9wt%, Na
2O 6.9wt%) 200g, 1.5g ZSM-5 crystal seed (Catalyst Factory, Nankai Univ, silica alumina ratio 38), distilled water 350g, the perlite of concentration after for about 55g of 3M aqueous sulfuric acid and calcination process drops in the stainless steel reactor, stirs and is mixed with mixture gel (pH is approximately 11.0) in 40 minutes.Each component by the mol ratio of its oxide compound is in the gel: SiO
2/ Al
2O
3=49; (Na
2O+K
2O)/SiO
2=0.26; H
2O/SiO
2=33.Be warmed up to thermostatic crystallization 24h under 180 ℃ of whipped states after the sealing.Mother liquor is cooled off, removed by filter to crystallization after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction (XRD), its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 85% in the product, and fluorometric analysis shows that the silica alumina ratio of product ZSM-5 molecular sieve is 40.Its particle of particle size analyzer determination (referring to be no less than 80% size distribution) diameter is less than 3.5 microns.Its XRD thing phasor is seen Fig. 1.
Subordinate list 1, the perlitic chemical constitution in Dalian (wt%)
SiO 2 | Al 2O 3 | K 2O | Na 2O | Fe 2O 3 | CaO |
73.02 | 11.82 | 4.60 | 3.05 | 1.10 | 0.94 |
Embodiment 2
With the commercially available kaolin of fine particle is raw material (50% particle diameter is not more than 3.1 μ m, form see attached list 2), gets 15g 950 ℃ of roastings 6 hours in retort furnace.Successively water glass (is contained SiO
220.9wt%, Na
2O6.9wt%) 200g, 2g ZSM-5 crystal seed (Catalyst Factory, Nankai Univ commercial goods, silica alumina ratio 38), water 250g, the kaolin of concentration after for about 55g of 3M sulfuric acid and above-mentioned calcination process drops in the stainless steel reactor, stirs and is mixed with mixture gel (pH is approximately 10.6) in 30 minutes.Each component by the mol ratio of its oxide compound is in the gel: SiO
2/ Al
2O
3=14; (Na
2O+K
2O)/SiO
2=0.26; H
2O/SiO
2=28.Be warmed up to 180 ℃ of crystallization 20h after the stainless steel reactor sealing.Mother liquor is lowered the temperature, removed by filter to crystallization after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction (XRD), its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 77% in the product, and fluorometric analysis shows that the silica alumina ratio of product ZSM-5 molecular sieve is 32.Its particle of particle size analyzer determination (being no less than 80% particle) is less than 4 microns.Its XRD thing phasor is seen Fig. 2.
Subordinate list 2, the kaolinic chemical constitution in Suzhou (wt%)
SiO 2 | Al 2O 3 | K 2O | Na 2O | Fe 2O 3 |
56.23 | 43.00 | 0.18 | 0.16 | 0.10 |
Embodiment 3
All reaction raw materials are with example 2, wherein the kaolin roasting condition is 930 ℃ of roastings 7 hours, successively with water glass 250g, 1g ZSM-5 crystal seed (Catalyst Factory, Nankai Univ, silica alumina ratio 38), deionized water 300g, and in the input of the kaolin 18g after the calcination process stainless steel reactor, the mol ratio by its oxide compound in the gel is: SiO
2/ Al
2O
3=14; (Na
2O+K
2O)/SiO
2=0.26.Adding concentration under stirring is about the aqueous nitric acid regulation system pH value to 10.5 of 1M, stirs 30 minutes.Be warmed up to 150 ℃ of crystallization 10h after the stainless steel reactor sealing, be warming up to 180 ℃ of crystallization 10h again.Crystallization removes by filter mother liquor after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction, thing is the ZSM-5 molecular sieve mutually.The relative crystallinity 60% of ZSM-5 molecular sieve in the crystallization product.
Embodiment 4
With commercially available 40 order Huludao City polynites (composition sees attached list 3) is raw material, gets 25g 700 ℃ of roastings 5 hours in retort furnace.Successively water glass (is contained SiO
220.9wt%, Na
2O 6.9wt%) 200g, 2.5g ZSM-5 crystal seed, distilled water 400g, concentration is that the polynite after 3M sulfuric acid 48g and the calcination process drops in the stainless steel reactor, stirs and is mixed with mixture gel (pH about 11.2) in 25 minutes.Each component by the mol ratio of its oxide compound is in the gel: SiO
2/ Al
2O
3=32; (Na
2O+K
2O)/SiO
2=0.22; H
2O/SiO
2=31.Sealing is warmed up to 180 ℃ and stirs crystallization 24h.Mother liquor is cooled off, removed by filter to crystallization after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction (XRD), its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 65% in the product.
The chemical constitution of subordinate list 3, Huludao City's polynite (wt%)
SiO 2 | Al 2O 3 | K 2O | Na 2O | Fe 2O 3 | CaO |
72.34 | 13.27 | 0.32 | 0.24 | 2.08 | 1.82 |
Embodiment 5
Crystal seed uses the NaY type molecular sieve of identical weight to replace ZSM-5 molecular sieve crystal seed, crystallization time 72 hours as crystal seed.Other is with embodiment 1.Products therefrom is measured through X-ray diffraction (XRD), and its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 15% in the product.
Embodiment 6
Protokaolin 15g (with embodiment 2) 950 ℃ of roastings 6 hours in retort furnace.Successively water glass (is contained SiO
220.9wt%, Na
2O 6.9wt%) 250g, 4g Tai-Ace S 150 (Al
2(SO
4)
318H
2The O analytical pure, Beijing chemical reagents corporation), 2g ZSM-5 crystal seed (Catalyst Factory, Nankai Univ, silica alumina ratio 38), deionized water 400g, concentration is that the kaolin after about 48g of the aqueous sulfuric acid of 3M and the calcination process drops in the stainless steel reactor, stirs and is mixed with mixture gel (pH about 11.0) in 30 minutes.Each component by the mol ratio of its oxide compound is in the gel: SiO
2/ Al
2O
3=15; (Na
2O+K
2O)/SiO
2=0.27; H
2O/SiO
2=33.The reactor sealing is warmed up to 180 ℃ of crystallization 24h.Crystallization removes by filter mother liquor after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction (XRD), its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 84% in the product.
Embodiment 7
With the commercially available kaolin of fine particle is that (50% particle diameter is not more than 3.1 μ m to raw material, form and see attached list 2), get 18g 950 ℃ of roastings 6 hours in retort furnace, be that aqueous hydrochloric acid 30 gram of 2M mixes and handled 6 hours with concentration again, filtration, washing, drying obtain roasting and add acid-treated kaolin.Successively water glass (is contained SiO
220.9wt%, Na
2O 6.9wt%) 200g, 2g ZSM-5 crystal seed (Catalyst Factory, Nankai Univ commercial goods, silica alumina ratio 38), water 250g, the kaolin of concentration after for about 55g of 3M sulfuric acid and above-mentioned calcination process drops in the stainless steel reactor, stirs and is mixed with mixture gel (pH is approximately 10.6) in 30 minutes.Be warmed up to 180 ℃ of crystallization 21h after the stainless steel reactor sealing.Mother liquor is lowered the temperature, removed by filter to crystallization after finishing, and washing, dry cake obtain crystallization product.Measure through X-ray diffraction (XRD), its thing belongs to the ZSM-5 molecular sieve mutually, and the relative crystallinity of ZSM-5 molecular sieve is 79% in the product.
Embodiment 8
The 100g ZSM-5 molecular sieve of example 1 preparation is added the 1000ml deionized water, carry out ion-exchange with ammonium sulfate 100g, give-and-take conditions: pH is 3.0~3.5,90~94 ℃ of temperature, time 0.5~1h, exchange back molecular sieve is washed after filtration, refilter, make one in 120 ℃ of following dryings and hand over material, hand over material to obtain a roasting material with one at 550~600 ℃ of following roasting 1~2h, one roasting material is carried out ion-exchange under a friendship condition, exchange back molecular sieve is washed after filtration, refilters, in 120 ℃ of dry down Hydrogen ZSM-5 molecular sieves that get, relative crystallinity is 95%.
Claims (14)
1, prepare the method for type ZSM 5 molecular sieve, it is characterized in that, this method utilizes natural mineral that all or part of aluminium source is provided, and realizes by adding crystal seed, comprises following process:
(1), make each component in this gel be by the mol ratio of its oxide compound with natural mineral, silicon source material, acidic substance, water and crystal seed mixed preparing reaction mixture gel:
SiO
2/Al
2O
3=5~200
M
2O/SiO
2=0.10~0.40
H
2O/SiO
2=10~50
Wherein, M represents alkali metallic sodium and/or potassium, described natural mineral accounts for total at least 70% the natural mineral raw of forming of oxide compound wherein for the weight percentage sum of wherein silicon oxide and aluminum oxide, and the consumption of described crystal seed is total SiO in natural mineral and the silicon source material
20.2~15% of quality;
(2) this gel is warming up to 140~220 ℃, hydrothermal crystallizing 5~200 hours.
2, in accordance with the method for claim 1, wherein said natural mineral is through one or more the mixture in perlite, kaolin, medical stone, polynite, wilkinite and the coal gangue of roasting and pulverization process.
3, in accordance with the method for claim 1, wherein said crystal seed is a kind of or its several mixtures that are selected from ZSM-5 type, Y type, X type, A type and the beta molecular sieve.
4, in accordance with the method for claim 1, wherein said silicon source material is water glass or alkaline silica sol.
5, in accordance with the method for claim 1, wherein, the preparation reaction mixture gel also can add aluminium source material in addition.
6, in accordance with the method for claim 5, wherein said aluminium source material is aluminium salt, aluminate, aluminium hydroxide or contains one or more mixture in the aluminium zeolite.
7, in accordance with the method for claim 1, wherein, described acidic substance comprise mineral acid, and the consumption of acidic substance is for can make the pH value of described reaction mixture gel 9.5~12.5.
8, in accordance with the method for claim 1, wherein, in the reaction mixture gel, the mol ratio of each component is SiO
2/ Al
2O
3=10~160, M
2O/SiO
2=0.15~0.35, H
2O/SiO
2=25~40.
9, in accordance with the method for claim 1, wherein said crystallization temperature is 145~180 ℃, and crystallization time is 10~80 hours.
10, in accordance with the method for claim 2, wherein, the calcination process temperature of said natural mineral is 550~1200 ℃, and the calcination process time is 0.3~200 hour.
11, in accordance with the method for claim 10, wherein, natural mineral is implemented to implement acid treatment again after acid treatment or the roasting before roasting.
12, in accordance with the method for claim 10, wherein, natural mineral earlier with calcination process again after alkali mixes.
13, a kind of type ZSM 5 molecular sieve is the molecular screen composite that is prepared from by each described method of claim 1~12.
14, the described type ZSM 5 molecular sieve of claim 13, wherein, in this molecular sieve particle diameter less than 8 microns particle more than 80%.