CN1793191A - Process for preparing environment protection type water retaining agent - Google Patents
Process for preparing environment protection type water retaining agent Download PDFInfo
- Publication number
- CN1793191A CN1793191A CN 200510096414 CN200510096414A CN1793191A CN 1793191 A CN1793191 A CN 1793191A CN 200510096414 CN200510096414 CN 200510096414 CN 200510096414 A CN200510096414 A CN 200510096414A CN 1793191 A CN1793191 A CN 1793191A
- Authority
- CN
- China
- Prior art keywords
- mass ratio
- acrylic acid
- mixed
- acrylamide
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a manufacture method for environment type molding agent that includes the following steps: taking activating by adding NaOH to mixture; mixing acrylic monomers and acrylamide; mixing the mixture with common waaterrthacinth, and adding PVA and NaOH adjusting system, adding initiator made from NaHSO<SUB>3</SUB> and (NH<SUB>4</SUB>)<SUB>2</SUB>S<SUB>2</SUB>O<SUB> 8</SUB> to take reaction; adding K<SUB>2</SUB>S<SUB>2</SUB>O<SUB>8</SUB> and crosslink agent N, N-methylene-bisacrylamide, drying the result, smashing and filtering. The invention sharply decreases the ratio of monomer and raw material, and declines the consumption of monomer.
Description
Technical field
The present invention relates to a kind of preparation method of water-holding agent, particularly a kind of preparation method of environment-friendly type water keeping agent.
Background technology
Vinyl cyanide, vinylformic acid, acrylamide, contain sulfonic acid monomer etc. as the monomer-grafted absorbent resin that on starch, Mierocrystalline cellulose, prepares; The water-absorbing resin of starch derivative; Polyvinyl alcohol crosslinked method prepares insoluble water-absorbing resin etc.
Starch is a kind of poly-hydroxy natural compounds, and as the raw material of synthetic high polymer, it has advantages such as wide material sources, of a great variety, relative low price.Starch graft copolymer reaction has two types of ionic graft copolymerization and free radical grafting copolymerizations.Though starch is that super absorbent resin product water absorbent rate is higher, the preparation process complexity, the industrialization aftertreatment is cumbersome.And starch is as a kind of natural polymer, the product poor heat resistance, and perishable decomposition is difficult to store.So people have begun to reduce gradually to the research of such super absorbent resin in recent years.
The water-retaining capacity of Super Absorbent Resin from Cellulose will be lower than starch system, but can directly make fibrous high absorbency material, make the high-hydroscopicity fabric, the preparation method of Super Absorbent Resin from Cellulose mainly contains etherificate-esterification process, esterification process and grafting copolymerization process etc.The subject matter of cellulose base absorbent resin existence at present is that water-retaining capacity is low and cost is higher.
Synthetic resins is that high absorbency material can be subdivided into polyacrylic, polyethenol series, copolymerization class etc. again, many to polyacrylic super absorbent resin research wherein, synthetic class super absorbent resin is extensive with its raw material sources, rate of water absorption is high, good water-retaining property, production technique are simple, but mildew-resistant is preapred for an unfavorable turn of events long storage and obtained broad research always, but because synthetic class super absorbent resin cost is higher, so the civilian and industrial big area that all is difficult to is used.
Summary of the invention
The objective of the invention is to overcome the shortcoming of above-mentioned prior art, provide a kind of environment-friendly type and the preparation method simple, the preparation method of the environment-friendly type water keeping agent that grafting efficiency is high.
For achieving the above object, the preparation method that the present invention adopts is:
Because the present invention utilizes Herba Eichhorniae to make the feedstock production water-holding agent, greatly reduce the proportioning between monomer and the raw material, in the past monomer and proportion of raw materials are bigger, monomeric add-on is very big, so just improved production cost, adopt Herba Eichhorniae to make raw material, make monomeric consumption reduce greatly, from ratio monomer in the past: raw material=8: 1 is reduced to monomer: raw material=3: 1, reduced production cost to a great extent, and adopt the most frequently used persulphate initiator system to cause for acrylic monomer, select for use vinylformic acid as main monomer, overcome the influence that the acrylonitrile monemer grafting hydrolysis of traditional industry production prepares the residual monomer carcinogenesis of super absorbent resin, adopt water solution polymerization process that preparation process is simplified, test operation is simple, and reaction is easy to control.
Embodiment 1, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.03: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 40 minutes 75 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 5: 1 mixed, and then 3.0% PVA and the mass concentration that add the acrylic acid quality are the pH=6.5 of 45% NaOH regulation system, under 55 ℃, add acrylic acid quality 0.7% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1 hour; The K that adds again acrylic acid quality 1.2%
2S
2O
8, after 45 minutes, add the crosslinking agent N of acrylic acid quality 20% 85 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 60 minutes under 75 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Embodiment 2, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.06: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 80 minutes 80 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 3: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 4: 1 mixed, and then 3.2% PVA and the mass concentration that add the acrylic acid quality are the pH=7.0 of 43% NaOH regulation system, under 48 ℃, add acrylic acid quality 0.5% by NaHSO
3With (NH
4)
2S
2Ox reacts after 1.2 hours by the initator that 1: 1 mass ratio is mixed; The K that adds again acrylic acid quality 1.0%
2S
2O
8, after 60 minutes, add the crosslinking agent N of acrylic acid quality 18% 70 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 52 minutes under 72 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Embodiment 3, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.04: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 60 minutes 70 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.3: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 3: 1 mixed, and then 3.5% PVA and the mass concentration that add the acrylic acid quality are the pH=8.5 of 41% NaOH regulation system, under 50 ℃, add acrylic acid quality 0.6% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.5 hours; The K that adds again acrylic acid quality 1.1%
2S
2O
8, after 55 minutes, add the crosslinking agent N of acrylic acid quality 16% 78 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 45 minutes under 80 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Embodiment 4, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.07: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 50 minutes 72 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.8: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 4: 1 mixed, and then 3.3% PVA and the mass concentration that add the acrylic acid quality are the pH=7.5 of 45% NaOH regulation system, under 45 ℃, add acrylic acid quality 0.5% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.4 hours; The K that adds again acrylic acid quality 1.0%
2S
2O
8, after 50 minutes, add the crosslinking agent N of acrylic acid quality 17% 72 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 48 minutes under 76 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Embodiment 5, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.05: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 70 minutes 76 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.5: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 3: 1 mixed, and then 3.4% PVA and the mass concentration that add the acrylic acid quality are the pH=8.0 of 42% NaOH regulation system, under 52 ℃, add acrylic acid quality 0.7% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.1 hours; The K that adds again acrylic acid quality 1.1%
2S
2O
8, after 58 minutes, add the crosslinking agent N of acrylic acid quality 15% 80 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 58 minutes under 70 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Embodiment 6, at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.08: 1 mass ratio adds NaOH, and makes the water hyacinth of activation in 55 minutes 78 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.6: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 5: 1 mixed, and then 3.1% PVA and the mass concentration that add the acrylic acid quality are the pH=6.5 of 44% NaOH regulation system, under 46 ℃, add acrylic acid quality 0.6% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.3 hours; The K that adds again acrylic acid quality 1.2%
2S
2O
8, after 47 minutes, add the crosslinking agent N of acrylic acid quality 19% 83 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 50 minutes under 78 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
Herba Eichhorniae is commonly called as Herba Eichhorniae, alien species, and waterplant, herb contains trace element and trace proteins such as silicon-dioxide, calcium, magnesium, potassium, iron, amino acid.Making water-loss reducer with Eichhornia crassipes can replenish in soil by the trace element that plant growth is essential, improves the physicochemical property of soil, is conducive to water and soil conservation.In addition, the Herba Eichhorniae asexual multiplication ability is very strong, if untimely processing will pollute environment, if produce in enormous quantities, makes water-holding agent, just can change harmful to treasure, and the whole ecological environment is had profound significance.
Claims (7)
1, a kind of preparation method of environment-friendly type water keeping agent is characterized in that
1) activation of Herba Eichhorniae
At first Herba Eichhorniae is mixed with the mass ratio of water by 1: 30, then in mixture by sodium hydroxide: Herba Eichhorniae is that 0.03～0.08: 1 mass ratio adds sodium hydroxide, and 70-80 ℃ of reaction 40-80 minute;
2) the Herba Eichhorniae graft copolymerization after the activation
With acrylic monomers and acrylamide by 2～3: 1 mass ratio is mixed and made into the mixture of acrylic acid and acrylamide, again with the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 3～5: 1 mass ratio mixes, and then add 3.0%～3.5% PVA of acrylic acid quality and the pH=6.5 that mass concentration is 40%～45% NaOH regulation system～8.5, under 45～55 ℃, add acrylic acid quality 0.5%～0.7% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1～1.5 hour; The K that adds again acrylic acid quality 1.0%～1.2%
2S
2O
8, after 45～60 minutes, adding the crosslinking agent N of acrylic acid quality 15%～20% 70～85 ℃ of lower reactions, the N-methylene-bisacrylamide reacted 45～60 minutes under 70-80 ℃ of constant temperature;
The product that 3) will react after finishing namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
2, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.03: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 40 minutes 75 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 5: 1 mixed, and then 3.0% PVA and the mass concentration that add the acrylic acid quality are the pH=6.5 of 45% NaOH regulation system, under 55 ℃, add acrylic acid quality 0.7% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1 hour; The K that adds again acrylic acid quality 1.2%
2S
2O
8, after 45 minutes, add the crosslinking agent N of acrylic acid quality 20% 85 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 60 minutes under 75 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
3, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.06: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 80 minutes 80 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 3: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 4: 1 mixed, and then 3.2% PVA and the mass concentration that add the acrylic acid quality are the pH=7.0 of 43% NaOH regulation system, under 48 ℃, add acrylic acid quality 0.5% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.2 hours; The K that adds again acrylic acid quality 1.0%
2S
2O
8, after 60 minutes, add the crosslinking agent N of acrylic acid quality 18% 70 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 52 minutes under 72 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
4, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.04: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 60 minutes 70 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.3: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 3: 1 mixed, and then 3.5% PVA and the mass concentration that add the acrylic acid quality are the pH=8.5 of 41% NaOH regulation system, under 50 ℃, add acrylic acid quality 0.6% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.5 hours; The K that adds again acrylic acid quality 1.1%
2S
2O
8, after 55 minutes, add the crosslinking agent N of acrylic acid quality 16% 78 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 45 minutes under 80 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
5, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.07: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 50 minutes 72 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.8: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 4: 1 mixed, and then 3.3% PVA and the mass concentration that add the acrylic acid quality are the pH=7.5 of 45% NaOH regulation system, under 45 ℃, add acrylic acid quality 0.5% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.4 hours; The K that adds again acrylic acid quality 1.0%
2S
2O
8, after 50 minutes, add the crosslinking agent N of acrylic acid quality 17% 72 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 48 minutes under 76 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
6, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.05: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 70 minutes 76 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.5: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 3: 1 mixed, and then 3.4% PVA and the mass concentration that add the acrylic acid quality are the pH=8.0 of 42% NaOH regulation system, under 52 ℃, add acrylic acid quality 0.7% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.1 hours; The K that adds again acrylic acid quality 1.1%
2S
2O
8, after 58 minutes, add the crosslinking agent N of acrylic acid quality 15% 80 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 58 minutes under 70 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.
7, the preparation method of environment-friendly type water keeping agent according to claim 1, it is characterized in that: at first Eichhornia crassipes is mixed with the mass ratio of water by 1: 30, then in mixture by NaOH: Eichhornia crassipes is that 0.08: 1 mass ratio adds NaOH, and makes the Eichhornia crassipes of activation in 55 minutes 78 ℃ of reactions; Acrylic monomers and acrylamide are mixed and made into the mixture of acrylic acid and acrylamide by 2.6: 1 mass ratio, again the mass ratio of the Eichhornia crassipes after the mixture of acrylic monomers and acrylamide and the activation by 5: 1 mixed, and then 3.1% PVA and the mass concentration that add the acrylic acid quality are the pH=6.5 of 44% NaOH regulation system, under 46 ℃, add acrylic acid quality 0.6% by NaHSO
3With (NH
4)
2S
2O
8Initator by 1: 1 mass ratio is mixed reacts after 1.3 hours; The K that adds again acrylic acid quality 1.2%
2S
2O
8, after 47 minutes, add the crosslinking agent N of acrylic acid quality 19% 83 ℃ of lower reactions, the N-methylene-bisacrylamide, reaction is 50 minutes under 78 ℃ of constant temperature; Product after reaction finished namely gets product not being higher than under 80 ℃ the temperature oven dry and pulverizing 80 mesh sieves.