CN1789192A - Process for preparing self-cleaning glasses by sol-gel method - Google Patents
Process for preparing self-cleaning glasses by sol-gel method Download PDFInfo
- Publication number
- CN1789192A CN1789192A CN 200510100986 CN200510100986A CN1789192A CN 1789192 A CN1789192 A CN 1789192A CN 200510100986 CN200510100986 CN 200510100986 CN 200510100986 A CN200510100986 A CN 200510100986A CN 1789192 A CN1789192 A CN 1789192A
- Authority
- CN
- China
- Prior art keywords
- glass
- self
- cleaning
- sol
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing the self-cleaning glass with sol-gel processing, the main steps of which are: deploying the nano TiO2 photo-catalytic solution with silica gel according to a certain proportion, importing it to the metering device, setting parameter for metering device according to demand to make the solution be sprayed onto the polished, washed and air dried clean glass surface with a certain proportion and measuring, then importing the glass into the heating furnace for solidification treatment, or carrying out tempering treatment directly, cooling and getting the transparent self-cleaning glass. The self-cleaning glass produced with the method in this invention is characterized by the super strong hydrophilicity and photocatalytic activity, uniform membrane layer, long duality, transparent appearance, no stain mark and no rainbow. The operation of this method is simple, and large scale automatic industrial production can be realized by employing this method.
Description
Technical field
That the present invention relates to is the preparation method of self-cleaning glass, especially a kind of preparation method of sol-gel method self-cleaning glass.
Background technology
Nano-TiO
2Super hydrophilic and photochemical catalysis effect discover by Tokyo Univ Japan the earliest.Ultimate principle is: under solar light irradiation, and nano-TiO
2After absorbing near-ultraviolet light, light induced electron and hole make nano-TiO respectively
2The hydrogen reduction of surface adsorption and water oxidation generate O
-2With-the OH active gene, these active genes are enough to make organic dirt, microorganism and the bacterial degradation on surface to become CO
2And H
2Simple inorganics such as O.Meanwhile, also find nano-TiO under study for action
2Film is after rayed, and the surface has Superhydrophilic and photocatalytic activity, if the blocking light source, these characteristics still can keep for some time in the dark.
Based on above principle, various countries are launching a large amount of work aspect fundamental research and the applied research, the research that especially outstanding is in the self-cleaning glass field.Relevant technology includes magnetron sputtering, chemical gaseous phase deposition, electrostatic spraying, cathode electrodeposition, sol-gel method or the like.Because each research institution is different with the method that manufacturer adopts, and makes the finished product performance difference very big.The problem that exists mainly contains: outward appearance rainbow problem, the low problem of glass transmitance, film adhesion difference problem, expensive problem etc.
Summary of the invention
The invention provides a kind of preparation method with self-cleaning glasses by sol-gel method of high-clarity, strong adhesive force and tool photocatalytic activity.
Technical problem of the present invention is solved by the following technical programs.
Self-cleaning glasses by sol-gel method is the preparation method may further comprise the steps successively:
(1), nano-TiO
2Silica gel solution preparation: with nano-TiO
2Photocatalyst solution and silica gel are in (weight ratio) ratio allotment in 1: 0.05～1: 0.59 and the importing measuring apparatus;
(2), measuring apparatus parameter setting: pressure of supply water 2.5～5kg, dilution water ratio 20%～50%.Discharge rate 300～1000ml/min;
(3), spray gun is regulated: adopt the stainless steel nozzle, at the uniform velocity traverse and sweep spray, spraying pressure 3～6kg;
(4), glass spraying plating pre-treatment: glass is polished, washes cleaning and air-dry according to a conventional method;
(5), glass spraying plating: with the nano-TiO of the spray gun after (3) are regulated set by step with step (1)
2Silica gel solution set by step (2) metering of setting to the glass spraying plating;
(6), glass surfacing solidification treatment;
(7), will promptly obtain the self-cleaning glass product after the glass cools after step (6) processing.
The solidification treatment of described step (6) can be that thermofixation processing or tempering are handled.
Self-cleaning glasses by sol-gel method preparation method's of the present invention principle of design is: adopt high-accuracy measuring apparatus with nano-TiO
2Silica gel solution is with constant proportioning and pressure, and high atomisation also is sprayed on the glass surface equably, then through solidification treatment, obtains self-cleaning glass.
Self-cleaning glasses by sol-gel method preparation method of the present invention compares with existing glass with clean preparation method, is that its preparation process or prepared product all have incomparable superiority.Be in particular in:
1, the self-cleaning glass that adopts preparation method of the present invention to make has superpower wetting ability and photocatalytic activity, and even film layer, firm and durable, appearance transparent, no spot, rainbow problem.
2, preparation method of the present invention is simple to operate, can realize extensive full-automatic production.
Description of drawings
Accompanying drawing is sol-gel method glass with clean preparation method's a process flow sheet.
Embodiment
Embodiment 1:
Self-cleaning glasses by sol-gel method is the preparation method may further comprise the steps successively:
(1), nano-TiO
2Silica gel solution preparation: with nano-TiO
2Photocatalyst solution and silica gel are in (weight ratio) ratio allotment in 1: 0.2 and the importing measuring apparatus;
(2), measuring apparatus parameter setting: pressure of supply water 2.5kg, dilution water ratio 20%, discharge rate 300ml/min;
(3), spray gun is regulated: adopt the SS100050 nozzle, at the uniform velocity traverse and sweep spray, ejection pressure 3kg;
(4), glass spraying plating pre-treatment: glass is polished, washes cleaning and air-dry according to a conventional method;
(5), glass spraying plating: the spray gun after regulating with (3) set by step with the solution of step (1) set by step (2) metering of setting to the glass spraying plating;
(6), the hot stove solidification treatment of glass surfacing: 350 ℃ of solidification values; 30 minutes set times;
(7), will promptly obtain the self-cleaning glass product after the glass cools after step (6) processing.
Embodiment 2:
The sol-gel method self-cleaning glass is the preparation method may further comprise the steps successively:
(1), nano-TiO
2Silica gel solution preparation: with nano-TiO
2Photocatalyst solution and silica gel are in (weight ratio) ratio allotment in 1: 0.2 and the importing measuring apparatus;
(2), measuring apparatus parameter setting: pressure of supply water 2.5kg, dilution water ratio 20%, discharge rate 300ml/min;
(3), spray gun is regulated: adopt the SS100050 nozzle, at the uniform velocity traverse and sweep spray, ejection pressure 3kg;
(4), glass spraying plating pre-treatment: glass is polished, washes cleaning and air-dry according to a conventional method;
(5), glass spraying plating: the spray gun after regulating with (3) set by step with the solution of step (1) set by step (2) metering of setting to the glass spraying plating;
(6), the hot stove solidification treatment of glass surfacing: 550 ℃ of solidification values; 60 minutes set times.
(7), will promptly obtain the self-cleaning glass product after the glass cools after step (6) processing.
Embodiment 3:
Multifunctional self-cleaned clean method for glass preparation may further comprise the steps successively:
(1), nano-TiO
2Silica gel solution preparation: with nano-TiO
2Photocatalyst solution and silica gel are in (weight ratio) ratio allotment in 1: 0.3 and the importing measuring apparatus;
(2), measuring apparatus parameter setting: pressure of supply water 2.5kg, dilution water ratio 20%, discharge rate 300ml/min;
(3), spray gun is regulated: adopt the SS100050 nozzle, at the uniform velocity traverse and sweep spray, ejection pressure 3kg;
(4), glass spraying plating pre-treatment: glass is polished, washes cleaning and air-dry according to a conventional method;
(5), glass spraying plating: the spray gun after regulating with (3) set by step with the solution of step (1) set by step (2) metering of setting to the glass spraying plating;
(6), glass surfacing tempering is handled: the method by the processing of simple glass tempering is carried out, and the surfacing of glass up during processing.
(7), will promptly obtain the self-cleaning glass product after the glass cools after step (6) processing.
Claims (4)
1, a kind of self-cleaning glasses by sol-gel method preparation method may further comprise the steps successively:
(1), nano-TiO
2Silica gel solution preparation: with nano-TiO
2Photocatalyst solution and silica gel are in (weight ratio) ratio allotment in 1: 0.05～1: 0.59 and the importing measuring apparatus;
(2), measuring apparatus parameter setting: pressure of supply water 2.5～5kg, dilution water ratio 20%～50%, discharge rate 300～1000ml/min;
(3), spray gun is regulated: at the uniform velocity traverse and sweep spray, spraying pressure 3～6kg;
(4), glass spraying plating pre-treatment: glass is polished, washes cleaning and air-dry according to a conventional method;
(5), glass spraying plating: the spray gun after regulating with (3) set by step with the solution of step (1) set by step (2) metering of setting to the glass spraying plating;
(6), glass surfacing solidification treatment;
(7), will promptly obtain the self-cleaning glass product after the glass cools after step (6) processing.
2, self-cleaning glasses by sol-gel method preparation method according to claim 1 is characterized in that:
Described step (6) glass surfacing solidification treatment can adopt thermofixation processing or tempering to handle.
3, self-cleaning glasses by sol-gel method preparation method according to claim 2 is characterized in that:
The solidification value of described hot stove solidification treatment is: 350～550 ℃; Be set time: 30～60 minutes.
4, self-cleaning glasses by sol-gel method preparation method according to claim 2 is characterized in that:
Described tempering is treated to simple glass tempering treatment process, and the surfacing of glass up during processing.