CN1781965A - Water soluble chelated resin and its synthetic method and use - Google Patents
Water soluble chelated resin and its synthetic method and use Download PDFInfo
- Publication number
- CN1781965A CN1781965A CN 200410089161 CN200410089161A CN1781965A CN 1781965 A CN1781965 A CN 1781965A CN 200410089161 CN200410089161 CN 200410089161 CN 200410089161 A CN200410089161 A CN 200410089161A CN 1781965 A CN1781965 A CN 1781965A
- Authority
- CN
- China
- Prior art keywords
- resin
- water soluble
- epoxy
- reaction
- heavy metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of water soluble chelated resin for eliminating heavy metal ions and its synthesis and application. Macromolecular polyamine with hydrophobic bisphenol A unit is first synthesized through reaction of epoxy resin and excessive organic diamine and subsequent chain expanding with epoxy chloropropane, and then reacted with CS2 in alkali condition to produce water soluble polymer with chelating radical of dithio amino formate. Introducing hydrophobic radical can raise the reaction activity of the macromolecular polyamine and raise the hydrophobicity of the chelated resin, so as to accelerate the deposition of heavy metal ion in very low concentration. The chelated resin of the present invention is used mainly in eliminating Cu, Ni, Zn, Cr and other heavy metal ions from electroplating effluent.
Description
Technical field
The present invention relates to a kind of water soluble chelated resin, with and synthetic method and utilize this liquid resin to remove the application of the heavy metal ion in the trade effluent.
Background technology
The environmental pollution that the modern industry development brings increases the weight of day by day, and the protection environment is the important topic that current social is paid close attention to.The industry of discharging heavy metal ion comprises plating, printed circuit board (PCB), chemical industry and Metal smelting etc., heavy metal ion mainly comprises copper, nickel, chromium, lead, manganese, cobalt, iron, zinc and sexavalent chrome etc., when this type of heavy metal ion as after entering the water source, to make tap water and fishery products be subjected to severe contamination, and use the back that fearful pathology takes place in human body.For taking precautions against in possible trouble, be necessary to provide a kind of efficiently, heavy metal treatment process easily, the problem that this present invention just studied.
Handle heavy metal wastewater thereby at present and mainly rely on method of chemical treatment.As the neutralization precipitation method is to make heavy metal ion and alkali reaction generate water-fast precipitation of hydroxide, and the sulfide precipitation rule is to make heavy metal ion and sulfonium ion reaction generate water-fast metallic sulfide precipitation.These sedimentable matters can be removed with the filtration way simply.Find in the practice that neutralization precipitation method and sulphide precipitation all have certain deficiency, particularly can't reach satisfied effect all the time cupric ion.
In recent years, high-molecular chelating agent begins to be used to handle effluent containing heavy metal ions, and it is better than traditional small molecules precipitation agent to the sedimentation effect of metal ion.Representative is that a class contains a large amount of dithio formate (CSS
-) water-soluble polymer of chelation group.From present known document, the work of the overwhelming majority concentrates on two aspects: the one, and the molecular weight of raising resin, the 2nd, the quantity of increase chelation group.Though this type of resin of reported in literature has good result of use, but find in actual applications, copper ion concentration after the use generally can't reach country-level standard, and can occur precipitation not thoroughly (often needing the polymeric flocculant aids precipitation), water quality redden, the organism secondary pollution problems.Trace it to its cause, these resins all are the strongly hydrophilic polyelectrolyte, want to make its precipitation that the sequestering action of sufficient metal ion must be arranged.When the ionic concn in the waste water is low, have only part chelation group and ionization on the macromolecular chain, and the part that sequestering action does not take place plays solubilizing effect as hydrophilic radical, and whole molecule still can not precipitate, and the effect that the result does not only reach scrubbing can cause secondary pollution on the contrary.Generally speaking, these water-soluble strong sequestrants are to using operational requirement higher, and scrubbing is thorough inadequately, needs further improvement.As patent announcement number is " high molecular heavy metals trapping precipitant " (yellow Cuiping, 2001) of CN1323747A, just adopts the blended chemical reagent to precipitate some metal ions, has wherein just comprised high-molecular chelating agent, also has similar deficiency.
Summary of the invention
Primary technical problem to be solved by this invention is that a kind of easy to operate, water soluble chelated resin that precipitation is thorough, effective is provided at existing background technology.
Another technical problem to be solved by this invention provides a kind of easily synthetic, easy to use, synthetic method that good being used for of sedimentation effect prepares above-mentioned water soluble chelated resin.
Another technical problem to be solved by this invention provides a kind of application of above-mentioned water soluble chelated resin.
The present invention solves the technical scheme that primary technical problem adopts: a kind of water soluble chelated resin is characterized in that
For having the polymkeric substance of following general structure,
Wherein EPOX represents the Resins, epoxy segment, and its structure can be expressed as:
M is from 1 to 5 integer
x+y＝1，0＜x＜1，0＜y＜1。
What be highly profitable is, its Resins, epoxy of above-mentioned polymkeric substance and quadrol weight ratio are 3: 1 to 4: 1 scope, thereby the concentration that guarantees the aqueous phase heavy metal ion makes the sewage of handling satisfy discharging standards all the time below 0.5ppm.
Useful is that its viscosity of above-mentioned polymkeric substance is in the 16-50Pa.s scope.
The present invention solves the technical scheme that another technical problem adopts: a kind of synthetic method for preparing above-mentioned water soluble chelated resin, its characterization step is followed successively by: with quadrol and bad epoxy resins is 2/1～1/4 to mix gradually by weight, heat release during mixing, react completely at 70～80 ℃, obtain prepolymer, drip the chainextender epoxy chloropropane gradually, epoxy chloropropane and quadrol weight ratio are 1: 0.5～1: 10, obtain versamid 900 at 85～95 ℃ of following sufficient reactings; Described versamid 900 reacts with dithiocarbonic anhydride under alkaline condition, generates the resin that contains nabam, and reaction pH value is controlled at 9～12, and temperature is 30～40 ℃.
Useful is, above-mentioned dithiocarbonic anhydride is 2: 1 with the ratio of quadrol mole, and a small amount of unreacted dithiocarbonic anhydride is removed by nitrogen purging at last in the system of reaction end back, makes its reaction complete as far as possible by short-cut method, simultaneously, dispose unnecessary dithiocarbonic anhydride apace.
What be highly profitable is, moles such as the amount of sodium hydroxide that reaction is added and dithiocarbonic anhydride, for the control sequestrant has solubility property preferably in reaction process, generally to control concentration sodium hydroxide and be controlled between 30～35%, the pH value that reaction finishes the back sequestrant is 12.
The present invention solves the technical scheme that another technical problem adopts: the application of above-mentioned water soluble chelated resin is characterized in that resin uses on the environmental protection treatment containing on the waste water of heavy metal ion.
Above-mentioned heavy metal ion comprises metal ions such as copper, nickel, chromium, lead, manganese, cobalt, iron, zinc or sexavalent chrome.
What be highly profitable is that its Resins, epoxy of above-mentioned resin and quadrol weight ratio are 3: 1 to 4: 1 scope, as the precipitation agent of copper metal ion, control the waste water copper ion concentration below 0.5ppm, satisfy national grade one discharge standard.
Compared with prior art, the invention has the advantages that: in polymer, introduce strong hydrophobic segment, resin is among the hydrophilic and hydrophobic balance, only the sequestering action of the heavy metal ion of need minute quantity is for inducing, just can make high-polymer molecular be converted into water-insoluble and the disengaging water, thereby the concentration of assurance aqueous phase heavy metal ion is all the time below 0.5ppm by water-soluble.Utilize the strong-hydrophobicity of Resins, epoxy and high reactive behavior, can synthesize the poly-ammonia macromole that contains hydrophobic segment, how many its hydrophobic powers can by the regulating of Resins, epoxy add-on, operate more convenient easily.The sedimentation effect of resin is good, thorough, shortens sedimentation time, improves sedimentation effect, reduces residual ion concentration, can not cause secondary pollution, and using method is easy, and cost is low.
Description of drawings
Fig. 1 handles front and back copper ion concentration changing conditions synoptic diagram for sequestrant.
Embodiment
Embodiment describes in further detail the present invention below in conjunction with accompanying drawing.
The Resins, epoxy (trade mark E-44) and the quadrol that in the four-hole boiling flask that agitator, reflux condensing tube, dropping funnel and thermometer are housed, add Different Weight respectively by table 1.Mix back (having a large amount of heats to emit, the cooling of palpus cold water), reacted 2 hours down at 70-80 ℃.After treating that resin and reacting ethylenediamine are fully, press the epoxy chloropropane that table 1 drips different amounts, after in 0.5 hour, dripping off, 100 ℃ of insulations 0.5 hour, abundant again to guarantee polymerization.Obtain the versamid 900 of high temperature thickness low-temperature curing at last.The solvability of polyurethane is relevant with the composition of reactant, its solubleness in water reduces with the increase of Resins, epoxy add-on, the acidity of water also has bigger influence to dissolving resin simultaneously, parahelium on the polyurethane (pH≤4) under acidic conditions forms quaternary ammonium salt easily, thereby water-soluble raising.In addition, the solvability of polyurethane in organic solvent methyl alcohol and dimethyl formamide is also relevant with what of hydrophobic segment, the poly-solvability of ammonia in methyl alcohol consistent with in water, the solvability in dimethyl formamide improves with the increase of content of epoxy resin.The hydrophobicity that high-polymer molecular is described can be controlled by the charging capacity of Resins, epoxy.
The solvability of the different versamid 900s of table 1
| Sample | Weight/g | Solvability in the water | Organic solvent | |||||
| Resins, epoxy | Quadrol | Epoxy chloropropane | pH≥9 | 4＜pH＜9 | pH≤4 | Methyl alcohol | Dimethyl formamide | |
| Polyamine 1 polyamine 2 polyamine 3 polyamine 4 polyamine 5 | 40 30 20 10 5 | 10 10 10 10 10 | 4.6 7.3 10.0 12.7 14.1 | Insoluble insoluble solvable | Insoluble solvable solvable | Solvable solvable | Insoluble solvable solvable | Solvable solvable insoluble |
The versamid 900 that above-mentioned example is obtained reacts with dithiocarbonic anhydride under alkaline condition.Though wherein polyamine 1, polyamine 2 are not dissolved in the water, but because the existence of hydrophilic radical, can be by water institute swelling, the existence of hydrophobic grouping simultaneously makes polymkeric substance absorb dithiocarbonic anhydride easily, helps the carrying out that reacts.Versamid 900 with the reaction process of dithiocarbonic anhydride, alkali in, the water-soluble increase of whole molecule finally forms water miscible macromolecular solution.Concrete reaction process is as follows:
In above-mentioned resin, add the 80g deionized water, stir, then drip aqueous sodium hydroxide solution and the dithiocarbonic anhydride that concentration is 33wt% simultaneously, in 20 minutes, dropwise by chemical dosage ratio.Add the back solution temperature and rise to 40 ℃ of reactions 2 hours gradually, water-insoluble polymer is dissolved gradually in this process, obtains colourless or flaxen thick liquid at last, with deionized water strength of solution is all adjusted to 35%, measures the viscosity of solution.The viscosity of different chelating agent solutions sees Table 2.As can be seen from Table 2, the polymer viscosity in aqueous solution raises along with the increase of amount of epoxy, this is because the rigidity hydrophobic grouping on the macromolecular chain increases, and can impel the hydrodynamic radius of polymer in the aqueous solution to increase, thereby cause the polymer viscosity in aqueous solution to rise.
The reaction composition and the viscosity in aqueous solution thereof of the different sequestrants of table 2
| Sample | Resins, epoxy and quadrol weight ratio | Epoxy chloropropane (ml) | Dithiocarbonic anhydride (ml) | NaOH solution (ml) | Viscosity (Pa.s) |
| Sequestrant 1 sequestrant 2 sequestrants 3 | 4∶1 3∶1 2∶1 | 3.9 6.1 8.5 | 19.8 19.8 19.8 | 35.6 38.3 41.0 | 40.5 29.8 21.1 |
| Sequestrant 4 sequestrants 5 | 1∶1 0.5∶1 | 10.8 11.9 | 19.8 19.8 | 43.8 45.1 | 17.8 16.2 |
Annotate: the viscosimetric analysis temperature is 25 ℃; The weight of quadrol is 10g.
Can in order to measure the sedimentation function of different resins, the aqueous solution of preparation different Cu ionic concn only adds resin, does not add the flocculation agent and the coagulant aids of other any kind ofs, observe the inner complex precipitation occur in 1 minute.What list in the table 3 is sedimentary required minimum copper ion concentration to occur, adds resin when being lower than this concentration in any case and precipitation can not occur in 1 minute.The content of hydrophobic grouping is high more in the resin, and near the trim point of hydrophobic/hydrophilic, its precipitation threshold is also good more more.Otherwise the content of hydrophobic grouping is few more, means that hydrophilic radical is many more, and it is many more to form the required cupric ion of inner complex precipitation.In fact, sequestrant 1 and sequestrant 2 are in a kind of phase-splitting state at aqueous phase, and promptly hydrophobic grouping associates mutually and forms hydrophobic microcell, and a spot of cupric ion will make system precipitate because of gel takes place.
Table 3 can make cupric ion sedimentary minimum concentration occur
| The resin kind | Cu 2+Minimum precipitation concentration/ppm |
| Sequestrant 1 | 0.10 |
| Sequestrant 2 | 0.50 |
| Sequestrant 3 | 1.0 |
| Sequestrant 4 | 2.5 |
| Sequestrant 5 | 3.0 |
Carry out the experiment of heavy metal ion precipitation with sequestrant 2.Get the 100mlpH value and be 5 electroplating wastewater, the copper, zinc, nickel, cadmium, manganese, lead, the chromium ion that contain 8ppm in it respectively, adding different volumes concentration is the sequestrant 2 of 5wt%, the clear liquid sample is once just got in every adding one time, measures wherein remaining concentration of heavy metal ion with atomic absorption analyzer.The result is as shown in table 4, and this sequestrant all has the effect of removal to these metal ions, adds that the concentration of residual ion can remain on below the 0.5ppm behind the 5ml.
Table 4 resin precipitation of heavy metals ionic effect
| Reagent volume/ml | Copper | Zinc | Nickel | Cadmium | Manganese | Plumbous | Chromium |
| 1.0 | 2.42 | 3.52 | 3.56 | 2.15 | 4.23 | 2.84 | 3.78 |
| 3.0 | 0.36 | 0.40 | 0.31 | 0.50 | 1.57 | 0.58 | 1.18 |
| 5.0 | 0.18 | 0.23 | 0.19 | 0.30 | 0.48 | 0.28 | 0.24 |
| 7.0 | 0.06 | 0.10 | 0.12 | 0.08 | 0.10 | 0.02 | 0.43 |
| 9.0 | 0.02 | 0.05 | 0.05 | 0.02 | 0.05 | 0.04 | 0.11 |
We have introduced minimum precipitation concentration first as the important indicator of estimating the resin sedimentation effect, and so-called minimum precipitation concentration is meant induced resin to produce sedimentary minimum copper ion concentration in one minute.If the minimum precipitation concentration of certain resin less than 0.5ppm, uses this resin just can guarantee that copper ion concentration reaches country-level standard so.In the actual mechanical process of handling effluent containing heavy metal ions, always fluctuation changes ionic concn in certain scope, and it is bigger to add the wastewater disposal basin volume, is subjected to the restriction of rate of diffusion, partial concn also can be inconsistent in the pond, and the add-on of sequestrant can not change thereupon usually.We do dynamic testing to the performance of resin for this reason, promptly change ionic concentration and keep the add-on of sequestrant constant, observe the variation of survival ion concentration in for some time.
Dynamic analog test: the defective waste water with Electroplate Factory's discharging is experimental subjects, use resin 2 to handle 20Kg waste water, earlier waste water ph is adjusted to 8.5, adding sequestrant makes concentration reach 20ppm, it is complete to stir the 10min postprecipitation, gets supernatant liquid and measures copper ion concentration with atom absorption method.Obtain result as Fig. 1, illustrate used sequestrant after, copper ion concentration all is lower than 0.5ppm in the waste water, has reached national grade one discharge standard.
Claims (10)
1, a kind of water soluble chelated resin is characterized in that for having the polymkeric substance of following general structure,
Wherein EPOX represents the Resins, epoxy segment, and its structure can be expressed as:
M is from 1 to 5 integer
x+y＝1，0＜x＜1，0＜y＜1。
2, water soluble chelated resin according to claim 1 is characterized in that its Resins, epoxy of described polymkeric substance and quadrol weight ratio are 3: 1 to 4: 1 scope.
3, water soluble chelated resin according to claim 1 and 2 is characterized in that described polymer viscosity is in the 16-50Pa.s scope.
4, the synthetic method of the described water soluble chelated resin of a kind of claim 1 is characterized in that steps in sequence is:
(1) be 2/1～1/4 to mix gradually by weight with quadrol and Resins, epoxy, heat release during mixing, react completely at 70～80 ℃, obtain prepolymer, drip the chainextender epoxy chloropropane gradually, epoxy chloropropane and quadrol weight ratio are 1: 0.5～1: 10, obtain versamid 900 at 85～95 ℃ of following sufficient reactings;
(2) described versamid 900 reacts with dithiocarbonic anhydride under alkaline condition, generates the resin that contains nabam, and reaction pH value is controlled at 9～12, and temperature is 30～40 ℃.
5, synthetic method according to claim 4 is characterized in that the described nitric sulfid and the ratio of quadrol mole are 2: 1, and a small amount of unreacted dithiocarbonic anhydride is removed by nitrogen purging at last in the system of reaction end back.
6, synthetic method according to claim 4 is characterized in that the consumption of sodium hydroxide of described its interpolation of reaction and dithiocarbonic anhydride are for waiting mole.
7, synthetic method according to claim 4 is characterized in that its control concentration sodium hydroxide of described reaction between 30～35wt%, and the pH value that reaction finishes the back sequestrant is 12.
8, the application of the described water soluble chelated resin of a kind of claim 1 is characterized in that resin uses on the environmental protection treatment containing on the waste water of heavy metal ion.
9, the application of water soluble chelated resin according to claim 8 is characterized in that comprising in described heavy metal ion metal ions such as copper, nickel, chromium, lead, manganese, cobalt, iron, zinc or sexavalent chrome.
10, the application of water soluble chelated resin according to claim 9, it is characterized in that in its Resins, epoxy of described resin and quadrol weight ratio being 3: 1 to 4: 1 scope, as the precipitation agent of copper metal ion, control the waste water copper ion concentration below 0.5ppm.