CN1768569A - 植被生态混凝土预制块及其制备方法 - Google Patents

植被生态混凝土预制块及其制备方法 Download PDF

Info

Publication number
CN1768569A
CN1768569A CN 200510030133 CN200510030133A CN1768569A CN 1768569 A CN1768569 A CN 1768569A CN 200510030133 CN200510030133 CN 200510030133 CN 200510030133 A CN200510030133 A CN 200510030133A CN 1768569 A CN1768569 A CN 1768569A
Authority
CN
China
Prior art keywords
layer
culture medium
grass
precast block
concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510030133
Other languages
English (en)
Other versions
CN100415079C (zh
Inventor
何池全
钱光人
智光源
李琳琳
董世祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Shanghai for Science and Technology
Original Assignee
University of Shanghai for Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Shanghai for Science and Technology filed Critical University of Shanghai for Science and Technology
Priority to CNB2005100301334A priority Critical patent/CN100415079C/zh
Publication of CN1768569A publication Critical patent/CN1768569A/zh
Application granted granted Critical
Publication of CN100415079C publication Critical patent/CN100415079C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种植被生态混凝土预制块及其制备方法。本发明的植被混凝土预制块由适于植被生长的顶层培养基层、适于植被根系贯穿的上层多孔混凝土层、适于植被根系生长的中层废砖石培养基混合层和适于植被根系贯穿的下层多孔混凝土层构成四层结构的预制块。其制备步骤是：①先制备尺寸相同的两块上、下层多孔混凝土层；②在下层多孔混凝土层上铺上培养基，在中层培养基上盖上已制好的上层多孔混凝土层，并在四周壁封上平整的水泥；③养护3－4天；④在预制块上覆盖顶层培养基层。预制块铺置于河岸上，约14－20天后即在顶部长草，草根贯穿上层、中层和下层而进入外部土壤，起绿化和保持水土作用。本发明铺设方便，可进行产业化生产。

Description

植被生态混凝土预制块及其制备方法
技术领域
本发明涉及一种生态混凝土，特别是一种植物生态混凝土预制块及其制备方法。
背景技术
在生态混凝土方面的研究，国外要比国内起步早，如日本、荷兰等。特别是日本，在这方面处于领先水平。早在十年前，日本就已经开始进行生态混凝土的研究和实践工作了。特别是最近几年，环境的保护和人身安全引起了更为广泛的注意，生态混凝土技术的运用成为了重点。生态混凝土的绿化技术主要有三个方面：(1)层面、墙面；(2)道路特殊空间；(3)混凝土直接绿化。
生态混凝土技术在日本已经用于城市住宅的绿化、公路两侧护坡面的绿化、河川防护坡面的绿化以及周围环境的美化。绿化层面是90年代屋面技术发展的新阶段，既可以美化屋面，又可以起到隔热保温的作用。
我国在生态混凝土方面的研究起止较晚，但发展速度快。由吉林省水利实业公司及吉林省吉水工程材料研究所完成的“环保型绿化混凝土研究”目前已通过了水利部国际合作与科技司组织的部级鉴定，该成果已达到了国际先进水平。
另外，在三峡工程高陡岩石边坡、清江隔河岩水电厂混凝土高边坡、无锡灵山大佛高陡混凝土边坡、黄龙滩电厂混凝土边坡、泰安抽水蓄能进库公路岩石边坡、江苏花山石宕山体生态恢复等二十多个工程中，都运用了生态混凝土技术。
日本早在十年前就在生态护坡结构方面做出了实践，当前，日本在软弱岩石边坡生态护坡中常用绿化网作为生态材料。我国在此方面起步晚，2002年4月，由吉林省水利实业公司及吉林省吉水工程材料研究所完成的“环保型绿化混凝土研究及其应用”项目已通过了利水部的部级鉴定，另外，由三峡大学研制出的绿色生态水泥，采用敲桩喷涂的方法，也得到了一致的好评。
上述的生态混凝土均在被绿化面上直接施工构成，铺设不方便，不能进行产业化生产。
发明内容
本发明的目的在于提供一种植被生态混凝土预制块及其制备方法，为绿化环境提供成形块的绿化预制块，用于铺设被绿化面，铺设方便，可形成产业化生产。
为达到上述目的，本发明采用下述技术方案：
一种植被生态混凝土预制块，为多层植生基材，其特征在于由适于植被生长的顶层培养基层、适于植被根系贯穿的上层多孔混凝土层、适于植被根系生长的中层培养基层和适于植被根系贯穿的下层多孔混凝土层构成四层结构的预制块。
上述的预制块四层的厚度分别为：顶层培养基层为3～8mm，上层多孔混凝土层为5～8cm，中层培养基层为5～15mm，下层多孔混凝土层为5～8cm预制的长、宽分别为20～30cm。
上述的预制块的四周壁有水泥薄层构成的粘合及强化结构层，其厚度为2～4mm。
上述的上、下层多孔混凝土层的原料组成按重量配比如下：
骨料100g、水泥50～65g、矿渣微粉95～115g，水450～500g，减水剂45～55g；骨科为建筑废砖石，其碎块粒径为2～5cm；矿渣微粉的粒径＜5mm；减水剂为荼酸甲醛缩合物。
上述的中层培养基的原料组成及重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g，或者泥炭100g、草屑20～30g、添加剂2～3g，所述的添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量配比为5～10∶1。
上的顶层培养基层是培养基中加入草种，其原料组成按重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g、草种400～600粒，或者泥炭100g、草屑20～30g、添加剂2～3g、草种400～600粒；所述的添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量比为5～10∶1。
上述的草种为3A高羊毛草、或美达丽X黑麦草、或高地草的草种。
一种用于上述植被生态混凝土预制块的制备方法，其特征在于制备步骤如下：①制备尺寸相同的两块上、下层多孔混凝土层：首先配备所需原料，按下述工艺流程制备：将水+添加剂+水泥+骨料，经混凝土搅拌机均匀后，注入预制块模盒内并压实，脱模而状块成多孔混凝土层：②在下层多孔混凝土层上铺上中层培养基，在中层培养基上盖上已制备好的上层多孔混凝土层，并在整个预制块的四周壁封上平整的水泥，以达到上下粘合及强化结构的作用；③养护：在温度为18～22℃，相对湿度为80～90％的水泥养护箱内静置3～4天；④在预制块上覆盖上培养基构成顶层培养基层；预制块铺设于河岸上，约14-20天后，顶层培养基层(4)上即长草，草根贯穿过上层多孔混凝土层、中层培养基层和下层多孔混混土层而进入外部土壤。
本发明与现有技术相比较，具有如下显而易见的突出实质性特点和显著优点：本发明将多层植生基本制成四层结构的绿化预制块，用于铺设被绿化面，铺设方便，可形成产业化生产。本发明的四层结的预制块，其顶层培养基层长草，草根贯穿上层多孔混凝土层、中层废砖石培养基混合层和下层多孔混凝土层而进入外部土壤，因而其草起绿化环境作用，根系起保持水土、加固大堤作用。本发明中采用建筑废砖石作为原材料中的骨料，使建筑废料得到有效处理和利用。
附图说明
附图是本发明一个实施例的预制块结构示意图。
具体实施方式
实施例一：参见附图，本植被生态混凝土预制块为多层植生基材，由适于植被生长的顶层培养基层4、适于植被根系贯穿的上层多孔混凝土层3、适于植被根系生长的中层培养基层2和适于植被根系贯穿的下层多孔混凝土层1构成四层结构的预制块。上述的预制块四层的厚度分别为：顶层培养基层4为3mm，上层多孔混凝土层3为5cm，中层废砖培养基混合层2为5mm，下层多孔混凝土层1为5cm；预制的长、宽分别为20cm。预制块的四周壁有水泥薄层7构成的粘合及强化结构层，其厚度为2mm。
上述的上、下层多孔混凝土层3、1的原料组成按重量配比如下：骨料100g、水泥50g、矿渣微粉95g，水450g，减水剂45g；骨科为建筑废砖石，其碎块粒径为2～5cm；矿渣微粉的粒径＜5mm；减水剂为荼酸甲醛缩合物。
中层培养基6的原料组成及重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g，所述的添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量配比为5～10∶1。
上述的顶层培养基层4是培养基中加入草种，其原料组成按重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g、草种400～600粒，添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量比为5～10∶1。草种为3A高羊毛草种。
用于上述植被生态混凝土预制块的制备方法，见制备步骤如下：①制备尺寸相同的两块上、下层多孔混凝土层3、1：首先配备所需原料，按下述工艺流程制备：将水+添加剂+水泥+骨料，经混凝土搅拌机均匀后，注入预制块模盒内并压实，脱模而状块成多孔混凝土层3、1：②在下层多孔混凝土层1上铺上中层培养基6，在中层培养基6上盖上已制备好的上层多孔混凝土层1，并在整个预制块的四周壁封上平整的水泥，以达到上下粘合及强化结构的作用；③养护：在温度为18～22℃，相对湿度为80～90％的水泥养护箱内静置3～4天；④在预制块上覆盖上培养基构成顶层培养基层4；预制块铺设于河岸上，约100天后，顶层培养基层4上即长草5，草根贯穿过上层多孔混凝土层3、中层培养基6和下层多孔混混土层1而进入外部土壤。
实施例二：亦参见附图，本实施例与上述实施例基本相同，所不同之处在于预制块尺寸和原料配比的不同，本实施例中预制块四层厚度分别为：顶层培养基层4为8mm，上层多孔混凝土层3为8cm，中层培养基混合层6为15mm，下层多孔混凝土层1为8cm；预制的长、宽分别为30cm，四周壁水泥薄层7厚度为4mm。
上、下层多孔混凝土层3、1的原料组成按重量配比如下：骨料100g、水泥65g、矿渣微粉115g，水500g，减水剂55g。
中层培养基层6的原料组成及重量配比为：泥炭100g、草屑20～30g、添加剂2～3g。
顶层培养基层4的原料组成按重量配比为：泥炭100g、草屑20～30g、添加剂2～3g、草种400～600粒。草种为美达丽X黑麦草种。
本植被生态混凝土预制块的制备方法与上述实施例的制备方法相同。

Claims (8)

1.一种植被生态混凝土预制块，为多层植生基材，其特征在于由适于植被生长的顶层培养基层(4)、适于植被根系贯穿的上层多孔混凝土层(3)、适于植被根系生长的中层培养基层(6)和适于植被根系贯穿的下层多孔混凝土层(1)构成四层结构的预制块。
2.根据权利要求1所述的植被生态混凝土预制块，其特征在于所述的预制块四层的厚度分别为：顶层培养基层(4)为3～8mm，上层多孔混凝土层(3)为5～8cm，中层培养基层(6)为5～15mm，下层多孔混凝土层(1)为5～8cm；预制的长、宽分别为20～30cm。
3.根据根利要求1所述的植物生态混凝土预制块，其特征在于所述的预制块的四周壁有水泥薄层(7)构成的粘合及强化结构层，其厚度为2～4mm。
4.根据根利要求1所述的植物生态混凝土预制块，其特征在于所述的上、下层多孔混凝土层(3、1)的原料组成按重量配比如下：骨料100g、水泥50～65g、矿渣微粉95～115g，水450～500g，减水剂45～55g；骨料为建筑废砖石，其碎块粒径为2～5cm；矿渣微粉的粒径＜5mm；减水剂为荼酸甲醛缩合物。
5.根据根利要求1所述的植物生态混凝土预制块，其特征在于所述的中层培养基层(6)的原料组成及重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g，或者泥炭100g、草屑20～30g、添加剂2～3g，所述的添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量配比为5～10∶1。
6.根据根利要求1所述的植物生态混凝土预制块，其特征在于所述的顶层培养基层(4)是培养基中加入草种，其原料组成按重量配比为：泥炭100g、耶糠1～3g、活性炭4～6g、添加剂1～2g、草种400～600粒，或者泥炭100g、草屑20～30g、添加剂2～3g、草种400～600粒；所述的添加剂为干苔藓与植物生长素的混合体，其干苔藓与植物生长素的重量比为5～10∶1。
7.根据根利要求6所述的植物生态混凝土预制块，其特征在于所述的草种为3A高羊毛草、或美达丽X黑麦草、或高地草的草种。
8.根据根利要求1所述的植物生态混凝土预制块的制备方法，其特征在于所述的制备步骤如下：①制备尺寸相同的两块上、下层多孔混凝土层(3、1)：首先配备所需原料，按下述工艺流程制备：将水+添加剂+水泥+骨料，经混凝土搅拌机均匀后，注入预制块模盒内并压实，脱模而状块成多孔混凝土层(3、1)：②在下层多孔混凝土层(1)上铺上中层培养基(6)，在中层培养基(6)上盖上已制备好的上层多孔混凝土层(1)，并在整个预制块的四周壁封上平整的水泥，以达到上下粘合及强化结构的作用；③养护：在温度为18～22℃，相对湿度为80～90％的水泥养护箱内静置3～4天；④在预制块上覆盖上培养基构成顶层培养基层(4)；预制块铺设于河岸上，约14-20天后，顶层培养基层(4)上即长草(5)，草根贯穿过上层多孔混凝土层(3)、中层培养基(6)和下层多孔混混土层(1)而进入外部土壤。
CNB2005100301334A 2005-09-29 2005-09-29 植被生态混凝土预制块及其制备方法 Expired - Fee Related CN100415079C (zh)