CN1765748A - Gama-Al2O3 preparation method - Google Patents
Gama-Al2O3 preparation method Download PDFInfo
- Publication number
- CN1765748A CN1765748A CN 200410050745 CN200410050745A CN1765748A CN 1765748 A CN1765748 A CN 1765748A CN 200410050745 CN200410050745 CN 200410050745 CN 200410050745 A CN200410050745 A CN 200410050745A CN 1765748 A CN1765748 A CN 1765748A
- Authority
- CN
- China
- Prior art keywords
- accordance
- add
- temperature
- ammonium oxalate
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses a preparation method for Gamma-Al2O3, which eliminates steps of aging, filtering and cleaning by common pseudo-boehmite to cut product period and protect environment; selecting ammonium oxalate as hole expansion agent with obvious effect. This product has pore volume over 1.0ml/g and large specific surface area, and particular to fit as catalyst carrier in hydrotreating.
Description
Technical field
The present invention relates to a kind of γ-Al
2O
3The preparation method.
Background technology
γ-Al
2O
3Owing to have big specific surface area and thermostability preferably, so be widely used as support of the catalyst in oil refining, petrochemical complex and the chemical fertilizer industry and siccative, sorbent material etc.Preparation γ-Al
2O
3Usual method be produce earlier pseudo-boehmite again under certain temperature calcining be converted into γ-Al
2O
3Pseudo-boehmite generally has three kinds of preparation methods industrial: the neutralization reaction of (1) aluminium salt and alkali, as:
(2) neutralization reaction of aluminate and acid, as:
(3) replacement(metathesis)reaction of aluminium salt and aluminate, as:
。Be usually said aluminium chloride process, carborization and Tai-Ace S 150 method.
CN1247773A discloses a kind of pseudo-boehmite and γ-Al
2O
3The preparation method, be included under at least 50 ℃ the temperature, in a kind of slurries of aluminium hydroxide, add a kind of acid reagent and a kind of alkaline reagents successively, the pH value of slurries is dropped to below 5, make the pH value of slurries go back up to 9.4~10.4 again, filtration, washing and drying obtain pseudo-boehmite, and roasting again obtains γ-Al
2O
3
CN1253909A discloses the method that a kind of Tai-Ace S 150 one sodium metaaluminate prepares pseudo-boehmite, comprises and stream is neutralized into glue, does not need the making beating that repeatedly circulates, not adding any reagent directly washes with water purification on washing device, drying obtains pseudo-boehmite, and roasting again obtains γ-Al
2O
3
CN1254684A discloses the method that a kind of sodium metaaluminate-carbonic acid gas prepares pseudo-boehmite, comprising: (1) is made into dense sodium aluminate solution with aluminium hydrate powder and sodium hydroxide, then dilution; (2) solution with step (1) gained under agitation feeds carbon dioxide, and control pH value reaches at 8~12 o'clock and stops into glue; (3) step (2) gained dope filtration, washing, drying are obtained pseudo-boehmite, roasting again obtains γ-Al
2O
3
So preparation γ-Al
2O
3Step generally comprise: precipitation (one-tenth glue)-aging-filtration-drying-pulverizing-moulding-calcining etc.Contain Cl in the long and washings of their preparation cycle
-, NO
3 -, SO
4 2-And Na
+Plasma, this class washings is if directly discharging is with contaminate environment; To increase production cost if will handle.
CN1425612A relates to a kind of preparation method of activated alumina.With aluminum chloride, ammoniacal liquor and expanding agent ammonium oxalate or ammonium citrate etc. are raw material, are made into mixed aqueous solution, and heating concentrates this solution with the generation aluminum hydroxide precipitation, dry and this throw out of heating, and roasting is converted into activated alumina then.The alumina pore volume that this method obtains is bigger, and pore distribution is more concentrated, but can also further improve.
Summary of the invention
At the deficiencies in the prior art, the invention provides a kind of new γ-Al
2O
3The preparation method can further improve the pore volume of aluminum oxide, and pore distribution is more concentrated.
γ-Al of the present invention
2O
3Preparation process as follows:
Get liquor alumini chloridi, add or do not add ammonium oxalate, add ammoniacal liquor then, keep not producing precipitation.Evaporate above-mentioned solution then, obtain the white solid thing, dry, roasting obtains final activated alumina.Use ultrasonication in evaporation, frequency of ultrasonic is 10~180kHz, and preferred 20~100kHz, ultrasonic power proportionately glue material original volume count 0.01~20W/mL, preferred 0.05~10W/mL.
γ-Al of the present invention
2O
3The method of preparation has been saved general pseudo-boehmite and has been prepared γ-Al
2O
3Steps such as aging, filtration, washing, both can shorten preparation cycle, help environment protection again; Select ammonium oxalate as expanding agent simultaneously, play obvious reaming effect, the product pore volume reaches more than the 1.0ml/g.The most important thing is, in the invention process process because hyperacoustic to effects such as atomic vibration pulverizing, make the aluminium hydroxide of generation more even, particle more also, size, shape and accumulation mode that aluminium hydroxide becomes primary particle in the glue reaction process have been changed, make the finished product have bigger pore volume, specific surface area and mean pore size, character is more even, and pore distribution is more concentrated.Gained γ-Al
2O
3Not only the aperture is big, pore distribution concentration but also specific surface are big, and product is particularly suitable for preparing the carrier of catalyst for hydrotreatment of residual oil.In the carrier production process, also can suitably introduce required auxiliary agent as required.Row simple to operate, flexible, easy.
Embodiment
γ-Al of the present invention
2O
3Concrete preparation process concrete steps comprise:
(1) in a ultrasonic transducer, crystal aluminum chloride and deionized water are made into certain density solution;
(2) take by weighing a certain amount of ammonium oxalate expanding agent then and add in the liquor alumini chloridi of step (1), heating and constant temperature make the ammonium oxalate dissolving at 50~80 ℃ under constantly stirring;
(3) in the solution of step (2), drip again, stream adds or Sprayable adds certain density ammonia soln, not generating under the insoluble sedimentary prerequisite, as often as possible adds ammoniacal liquor.
(4) ultrasonic transducer is opened on the solution limit of limit evaporation step (3), separates out the white solid thing gradually, closes ultrasonic transducer behind the solution evaporation.The gained solids is dry at a certain temperature, and roasting promptly makes final γ-Al then
2O
3Product.
The concentration of above-mentioned liquor alumini chloridi is 0.5~3.0mol/L.Above-mentioned ammonium oxalate expanding agent add-on is 0~100% of a contained aluminum chloride mole number, is preferably 30~70%.Above-mentioned ammonia concn is 0.5~5.0mol/L, is preferably 1.0~2.0mol/L.Ammoniacal liquor drips and to add and can add above becoming the glue jar with stream, spray pattern preferably with ammonia atomization in air or other gas, enter and solution reaction in the bottom of one-tenth glue jar, can remove stirring from.The local pH value is uprushed in the time of can avoiding simultaneously ammoniacal liquor to add, and produces aluminum hydroxide precipitation, and the precipitation that produce this moment is because condition unbalanced and character can heterogeneity.Generally speaking, when reaching 3~4, the pH of reaction system value can stop to add ammoniacal liquor.Frequency of ultrasonic is 10~180kHz, and preferred 20~100kHz, ultrasonic power proportionately glue material count 0.01~20W/mL by original volume, and preferred 0.05~10W/mL can reduce power with the minimizing of solution amount.The solution evaporation temperature can be 60~150 ℃, is preferably 80~100 ℃.The solids drying temperature is 80~140 ℃, is preferably 90~120 ℃; Be 1~5 hour time of drying, is preferably 2~3 hours; Maturing temperature is 180~600 ℃, is preferably 250~500 ℃; Roasting time is 1~5 hour, is preferably 2~4 hours.Gained γ-Al
2O
3Pore volume be generally 1.0~1.2ml/g, specific surface is generally 350m
2More than/the g, the pore volume of pore distribution 4~30nm accounts for total pore volume branch rate and is generally more than 85%.
γ-Al with the inventive method preparation
2O
3Be raw material, make hydrogenation catalyst through conventional method through moulding-roasting-dipping-roasting process or through mixed pinching-moulding-roasting process or through mixed pinching-moulding-roasting-dipping-roasting process, can be used for the hydrotreatment of various petroleum fractionss, be specially adapted to residual hydrocracking.
Further describe technical characterictic of the present invention below by comparative example and embodiment, but be not limited to embodiment.
Embodiment 1
The solution 2000mL that at first crystal aluminum chloride and deionized water is made into 1.0mol/L places the ultrasonic transducer of 5000Ml, the ammonium oxalate expanding agent that takes by weighing 1.0mol adds in the liquor alumini chloridi, heating and constant temperature are at 60 ℃ under constantly stirring, make the ammonium oxalate dissolving, dripping concentration again in reactor is the ammonia soln of 2.0mol/L, not generating under the sedimentary prerequisite, as often as possible adds ammoniacal liquor, and the ammonia vol of record adding, final system pH is 3.8.Above-mentioned solution limit unlatching ultrasonic transducer is evaporated on the limit then, and the control transmitted power is 25kHz for the 200W frequency, and vaporization temperature is 85 ℃, separates out the white solid thing gradually, closes ultrasonic transducer behind the solution evaporation.The gained solids descended dry 3 hours at 100 ℃, then 500 ℃ of roastings 3 hours.Behind the naturally cooling with gained γ-Al
2O
3Product is crushed to 180 orders, promptly makes product A of the present invention.
Embodiment 2
Compare with embodiment 1, the ammonium oxalate expanding agent that takes by weighing 1.5mol adds in the liquor alumini chloridi, and the unclassified stores consumption is identical with embodiment 1 with operational condition, promptly gets product B of the present invention.
Embodiment 3
Compare with embodiment 1, crystal aluminum chloride and deionized water are made into the solution of 2.0mol/L, the unclassified stores consumption is identical with embodiment 1 with operational condition, and vaporization temperature is 100 ℃, promptly gets products C of the present invention.
Embodiment 4
Compare with embodiment 1, feed the ammonia soln that is atomised to airborne 1.0mol/L from reactor lower part, solution quality is 1g in every litres of air, and the unclassified stores consumption is identical with embodiment 1 with operational condition, promptly gets product D of the present invention.
Embodiment 5
Compare with embodiment 1, it is 50kHz that the ultrasonic transducer transmitted power is become the 800W frequency, and liquor capacity is reduced to a half, and power is reduced to 300W.Drying temperature becomes 120 ℃, and be 2 hours time of drying, and the unclassified stores consumption is identical with embodiment 1 with operational condition, promptly gets product E of the present invention.
Embodiment 6
Compare with embodiment 1, it is 25kHz that the ultrasonic transducer transmitted power is become the 50W frequency, and maturing temperature is become 350 ℃, and roasting time is 2 hours, and the unclassified stores consumption is identical with embodiment 1 with operational condition, promptly gets product F of the present invention.
Embodiment 7
Compare with embodiment 1, do not add ammonium oxalate, other is identical, gets product G.
Comparative example 1
Identical with embodiment 1, just in evaporative process, do not carry out ultrasonication, get product H.
The physico-chemical property of above-mentioned each routine product sees Table 1.
Each routine product physico-chemical property of table 1
Physico-chemical property | Pore volume ml/g | Specific surface m 2/g | Pore distribution % | ||
<4nm | 4~30nm | >30nm | |||
A | 1.14 | 361 | 7.5 | 87.6 | 4.9 |
B | 1.19 | 369 | 6.1 | 87.3 | 6.6 |
C | 1.05 | 373 | 9.4 | 85.8 | 4.8 |
D | 1.20 | 372 | 6.2 | 89.4 | 4.4 |
E | 1.12 | 358 | 7.4 | 87.2 | 5.4 |
F | 1.13 | 363 | 7.5 | 86.3 | 6.2 |
G | 0.84 | 357 | 10.5 | 85.8 | 3.7 |
H | 1.05 | 353 | 9.4 | 85.1 | 5.5 |
As can be seen from Table 1, the present invention uses ultrasonication in the aluminium hydroxide precipitation process, gained γ-Al
2O
3Not only pore volume is big, specific surface area is big, and the aperture is big, pore distribution concentration; Product is particularly suitable for preparing the carrier of catalyst for hydrotreatment of residual oil.
Claims (10)
1, a kind of γ-Al
2O
3The preparation method, get liquor alumini chloridi, add or do not add ammonium oxalate, add ammoniacal liquor then, keep not producing precipitation, evaporate above-mentioned solution then, obtain the white solid thing, dry, roasting obtains final activated alumina, it is characterized in that using ultrasonication in evaporation, frequency of ultrasonic is 10~180kHz, and ultrasonic power proportionately glue material original volume is counted 0.01~20W/mL.
2, in accordance with the method for claim 1, it is characterized in that described frequency of ultrasonic is 20~100kHz, ultrasonic power proportionately glue material original volume is counted 0.05~10W/mL.
3, in accordance with the method for claim 1, the concentration that it is characterized in that described liquor alumini chloridi is 0.5~3.0mol/L, and the ammonium oxalate add-on is 0~100% of a contained aluminum chloride mole number, and ammonia concn is 0.5~5.0mol/L.
4, in accordance with the method for claim 3, it is characterized in that described ammonium oxalate add-on is 30~70% of a contained aluminum chloride mole number, ammonia concn is 1.0~2.0mol/L.
5, in accordance with the method for claim 1, it is characterized in that described ammoniacal liquor adding mode adds above becoming the glue jar for dropping, fed-batch mode.
6, in accordance with the method for claim 1, it is characterized in that ammonia atomization in air or other gas, enter and solution reaction in the bottom that becomes the glue jar.
7, in accordance with the method for claim 1, it is characterized in that when the pH of reaction system value reaches 3~4, stopping to add ammoniacal liquor.
8, in accordance with the method for claim 1, it is characterized in that reducing hyperacoustic power with the minimizing of solution amount.
9, in accordance with the method for claim 1, it is characterized in that described solution evaporation temperature is 60~150 ℃, the solids drying temperature is 80~140 ℃, be 1~5 hour time of drying, maturing temperature is 180~600 ℃, and roasting time is 1~5 hour, and it is 50~80 ℃ that ammonium oxalate adds temperature.
10, in accordance with the method for claim 9, it is characterized in that described solution evaporation temperature is 80~100 ℃, the solids drying temperature is 90~120 ℃, and be 2~3 hours time of drying, and maturing temperature is 250~500 ℃, and roasting time is 2~4 hours.