CN1759778A - Emulsion gloves latex gloves and fabricating method - Google Patents
Emulsion gloves latex gloves and fabricating method Download PDFInfo
- Publication number
- CN1759778A CN1759778A CN 200410067102 CN200410067102A CN1759778A CN 1759778 A CN1759778 A CN 1759778A CN 200410067102 CN200410067102 CN 200410067102 CN 200410067102 A CN200410067102 A CN 200410067102A CN 1759778 A CN1759778 A CN 1759778A
- Authority
- CN
- China
- Prior art keywords
- gloves
- emgloves
- aforementioned
- collagen
- shaping mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of latex gloves features that its internal surface is thoroughly chlorinated and then coated by collagen layer for nursing and activating skin and its external surface is not thoroughly chlorinated for obtain rough surface. Its preparing process includes such steps as shaping by mould, pneumatically demoulding while turning it over, directly chlorinating its internal surface, coating collagen layer, baking, and turning it over again.
Description
Technical field
The present invention relates to the gloves field, particularly the emgloves field specifically is meant a kind of emgloves and manufacture method thereof.
Background technology
The emgloves cover finished product of present emgloves manufacture method gained does not all have collagen, and collagen is for human skin cell's aging effect with maintenance activation, though extensively applied to multiple uses such as cosmetics, fail effectively to be applied in the emgloves.Simultaneously, the general inner layer surface of emgloves in the prior art is not because through the chlorination of excessive level and very smoothless, comparatively difficulty inconvenience during wearing, and its outer surface has passed through abundant chlorination processing, very smooth, cause its frictional force deficiency, hold the easy landing of apparatus, have unsafe factor.
Summary of the invention
The objective of the invention is to have overcome above-mentioned shortcoming of the prior art, the emgloves and the manufacture method thereof that provide a kind of inner surface to be coated with collagen layer, this emgloves has protective action to skin, and dress smooth convenience, hold article and firmly be difficult for skidding, the manufacture method process of this emgloves is simple, production is quick.
In order to realize above-mentioned purpose, emgloves of the present invention has following formation:
This emgloves, its main feature are to be coated with collagen layer on its inner layer surface.
Contain the left-handed C of vitamin, vitamin e or sheep oil in the collagen layer of this emgloves.
The manufacture method of this emgloves comprises the steps:
Mold cleaning: utilize the clear water of cleaning equipment or each gloves shaping mould that cleaning agent will be fixed on the conveyer to clean up;
Oven dry: each gloves shaping mould of aforementioned cleaning is utilized oven for drying;
Bath gel agent: aforementioned each gloves shaping mould is immersed the gel groove and is stained with the layer of gel agent;
Oven dry: utilize baking oven that it is dried the aforementioned gloves shaping mould that has been stained with the layer of gel agent;
Soak the latex groove: aforementioned gloves shaping mould is immersed the latex groove and is stained with latex, utilize baking oven that it is dried again;
Sulfuration: the latex in the aforementioned gloves is vulcanized;
Adhering-resistant is handled: with aforementioned gloves sticking immersion powder or polymer-coated, the gloves internal layer sticks together when avoiding the demoulding;
The demoulding: aforementioned gloves are broken away from the gloves shaping mould fully promptly form general emgloves;
The gloves chlorination is handled: utilize solutions of chlorine that powder residual in the aforementioned adhering-resistant treatment step or other nonrubber impurity are removed the emgloves of aforementioned disengaging gloves shaping mould;
Its main feature is, in the demoulding step of the manufacture method of described emgloves, the mode that gloves is broken away from fully the gloves shaping mould for the inner layer surface of the gloves that gloves shaping mould and keeping breaks away from that use gases at high pressure directly gloves to be blown off outwardly; And in the manufacture method of described emgloves, after gloves chlorination treatment step, further comprising the steps of:
Collagen applies: with collagen solution with spray or the mode of dipping be coated in aforementioned gloves inner layer surface outwardly the surface and form collagen layer;
Oven dry and turn-over operation: with aforementioned gloves through the oven dry handling process after, inner layer surface gloves are outwardly carried out the turn-over operation, then with the described inner layer surface that is coated with collagen layer interior and outer outwardly, thereby make this gloves.
Collagen solution in the manufacture method of this emgloves is the solution that is dissolved in the pure water to be produced with collagen.
Be added with the left-handed C of vitamin, vitamin e or sheep oil in the collagen in the manufacture method of this emgloves.
In the gloves chlorination treatment step of the manufacture method of this emgloves, also can use chlorine that aforementioned adhering-resistant is handled residual powder or other nonrubber impurity in back and be removed.
The emgloves and the manufacture method thereof of this invention have been adopted, because the inner layer surface of this emgloves is coated with collagen layer, thereby dressing when using and directly to contact with user's skin, and help the old and feeble maintenance and the activation of Skin Cell, simultaneously when the chlorination of making this emgloves is handled, its outer layer surface inwardly, especially the position is curling a little because of finger near the finger tip, chlorine liquid or chlorine relatively are not easy to be dipped into finger tip, therefore guarantee not excessively chlorination, make that outer surface frictional force is bigger, and its inner surface outwardly, can reach the chlorination of high level, thereby make its inner surface smooth, when dress using, it is convenient not only to dress, and has and grasp effect preferably; Simultaneously in the manufacture method of this emgloves, only finishing from the demoulding to the emgloves finished product must several operating process, has relatively to simplify manufacturing process, produce fast and the advantage of enhancing productivity and reducing cost.
Description of drawings
Fig. 1 is an emgloves manufacture method flow chart of the present invention.
Fig. 2 is the schematic perspective view of the general gloves of emgloves of the present invention after demoulding program.
Fig. 3 is the gloves coating collagen layer of Fig. 2 and the schematic perspective view after the oven dry.
Fig. 4 is the gloves A-A cross section enlarged diagram of Fig. 3.
Fig. 5 is the schematic perspective view of emgloves finished product of the present invention.
The specific embodiment
In order more to be expressly understood technology contents of the present invention, describe in detail especially exemplified by following examples.
See also Fig. 1 to shown in Figure 5, the manufacturing process of emgloves of the present invention comprises the steps:
Mold cleaning (Washing Forners) 11: utilize each gloves shaping mould (figure does not show) that the clear water of cleaning equipment 1 or cleaning agent will be fixed on the conveyer to clean up;
Oven dry (Dryng Formers) 12: utilize baking oven under temperature Celsius about 100 ℃, to dry (being preferable generally) each gloves shaping mould of aforementioned cleaning with 100 ℃ ± 20 ℃;
Bath gel agent (Coagulant Dipping) 13: aforementioned each gloves shaping mould is immersed the gel groove and is stained with the layer of gel agent.Mainly be to be beneficial to easier even attached work when soaking the latex program described later;
Oven dry (Coagulant Drying) 14: the aforementioned gloves shaping mould shaping mould that has been stained with the layer of gel agent is dried (being preferable with 100 ℃ ± 20 ℃ generally) by baking oven under temperature Celsius about 100 ℃;
Soak latex groove (Latex Dipping) 15: aforementioned gloves shaping mould is immersed the latex groove and is stained with latex, again with oven for drying;
Sulfuration (Vulcanization) 16: with about 120 ℃ temperature heat baking (being preferable generally) with 120 ℃ ± 20 ℃; And the latex in the aforementioned gloves is vulcanized to increase elasticity;
Adhering-resistant handles 17: with aforementioned gloves immersion powder (Wet powdering) or polymer-coated release treatment such as (Polymer), the gloves internal layer is understood oneself and is sticked together when avoiding the demoulding;
The demoulding (Stripping) 18: aforementioned gloves are broken away from the gloves shaping mould fully promptly form ordinary rubber gloves (3);
The chlorination of gloves internal layer handles 19: the general gloves of aforementioned disengaging gloves shaping mould are handled residual powder or other nonrubber impurity in back with solutions of chlorine (Chlorine Solution) or chlorine (Chlorine Gas) with aforementioned adhering-resistant removed to guarantee the cleaning of gloves;
Wherein, the mode that this demoulding flow process 18 gloves 3 wherein break away from the gloves shaping moulds is that the gloves 3 that order breaks away from carry out aforementioned chlorination and handle 19 with the gases at high pressure gloves shaping mould (Former) that directly gloves blown off.Carry out the flow process of collagen coating 20 then.And being formed collagen layer 310 with the surface of the inner layer surface 31 that sprays (Sprayed) or dipping modes such as (Immersed) and be coated in aforementioned gloves 3, collagen solution (sees also Fig. 4, shown in Figure 5), inner layer surface 31 gloves 3 outwardly can be carried out turn-over operation 22 through the handling process of oven dry 21 immediately, promptly finish emgloves finished product 30 (seeing also Fig. 6) and make the aforementioned inner layer surface 31 that is coated with collagen layer 310 (see also Fig. 6) outwardly interior and outer 32, this kind emgloves finished product 30 is because inner layer surface 31 is coated with collagen 310, therefore dressing when using and directly to contact, and helping the old and feeble maintenance and the activation of Skin Cell with user's skin.
Simultaneously, aforementioned collagen solution is produced in pure water (clean pure water) with collagen solution.
In addition, aforesaid collagen is to add the left-handed C of vitamin, vitamin e or sheep oil (Lanolinfrom sheep wool), and then can help the more effective absorption collagen of cell when emgloves finished product 30 contacts with user's skin.
In sum, adopt the present invention, can obtain following technique effect:
(1) as yet not before the demoulding, the inner layer surface 31 of the gloves 3 of gloves shaping mould top is outwardly, therefore directly gloves 3 are blown off after the gloves shaping mould by gases at high pressure, the inner layer surface 31 of gloves 3 still carries out chlorination processing 19 outwardly and immediately after this disengaging, make the inner layer surface 31 of gloves 3 especially can fully contact chlorine liquid or chlorine near the position of finger tip, reach high level chlorination effect, significantly reduce surperficial friction and improve surperficial slippery, when gloves 3 wears, just can be easy to and do not have resistance, fast through finger tip, relatively, therefore the outer layer surface 32 of gloves inwardly the time, especially pad of finger is because of curling slightly, chlorine liquid or chlorine relatively are not easy to reach finger tip, the chlorination effect is had a greatly reduced quality, the friction of surface, position can be than higher and produce very high resistance near the finger tip, and then work as gloves turn-over program 22 and finish, this emgloves 30 is dressed when using and can be guaranteed the effect that its on-slip grasps, relatively when gloves be can avoid relative article landing such as scalpel when being used in medical act and influence medical quality, and can improve security
(2) only finishing from the demoulding 18 to emgloves finished product 30 must several operating process, has relatively to simplify manufacturing process, produce fast and the advantage of enhancing productivity and reducing cost.
Contact with user's skin when (3) dress using, and help the aging maintenance and the reactivation of Skin Cell, make skin moisturizing flexible again.
(4) gloves are airtight, fluid-tight sealer, and when dressing for being close to hand, so it is unsuitable to hand skin, can cause discomfort even produce ill symptoms, especially the long-time wearing of women is more serious, undesirable condition to hand when therefore the present invention allows wearing is of value to skin owing to applying collagen layer, the discomfort, further has the effect of nourishing hand skin when dressing except that reduction.
In this specification, the present invention is described with reference to its certain embodiments.But, still can make various modifications and conversion obviously and not deviate from the spirit and scope of the present invention.Therefore, specification and accompanying drawing are regarded in an illustrative, rather than a restrictive.
Claims (8)
1, a kind of emgloves is characterized in that, is coated with collagen layer on the inner layer surface of described emgloves.
2, emgloves according to claim 1 is characterized in that, contains the left-handed C of vitamin, vitamin e or sheep oil in the described collagen layer.
3, a kind of method of making the described emgloves of claim 1 comprises the steps:
Mold cleaning: utilize the clear water of cleaning equipment or each gloves shaping mould that cleaning agent will be fixed on the conveyer to clean up;
Oven dry: each gloves shaping mould of aforementioned cleaning is utilized oven for drying;
Bath gel agent: aforementioned each gloves shaping mould is immersed the gel groove and is stained with the layer of gel agent;
Oven dry: utilize baking oven that it is dried the aforementioned gloves shaping mould that has been stained with the layer of gel agent;
Soak the latex groove: aforementioned gloves shaping mould is immersed the latex groove and is stained with latex, utilize baking oven that it is dried again;
Sulfuration: the latex in the aforementioned gloves is vulcanized;
Adhering-resistant is handled: with aforementioned gloves sticking immersion powder or polymer-coated, the gloves internal layer sticks together when avoiding the demoulding;
The demoulding: aforementioned gloves are broken away from the gloves shaping mould fully promptly form general emgloves;
The gloves chlorination is handled: utilize solutions of chlorine that powder residual in the aforementioned adhering-resistant treatment step or other nonrubber impurity are removed the emgloves of aforementioned disengaging gloves shaping mould;
It is characterized in that, in the demoulding step of the manufacture method of described emgloves, the mode that gloves are broken away from the gloves shaping mould fully for the inner layer surface of the gloves that gloves shaping mould and keeping breaks away from that use gases at high pressure directly gloves to be blown off outwardly; And in the manufacture method of described emgloves, after gloves chlorination treatment step, further comprising the steps of:
Collagen applies: with collagen solution with spray or the mode of dipping be coated in aforementioned gloves inner layer surface outwardly the surface and form collagen layer;
Oven dry and turn-over operation: with aforementioned gloves through the oven dry handling process after, inner layer surface gloves are outwardly carried out the turn-over operation, then with the described inner layer surface that is coated with collagen layer interior and outer outwardly, thereby make this gloves.
4, the manufacture method of emgloves according to claim 3 is characterized in that, described collagen solution is the solution that is dissolved in the pure water to be produced with collagen.
5, the manufacture method of emgloves according to claim 3 is characterized in that, is added with the left-handed C of vitamin in the described collagen.
6, the manufacture method of emgloves according to claim 3 is characterized in that, is added with vitamin e in the described collagen.
7, the manufacture method of emgloves according to claim 3 is characterized in that, is added with sheep oil in the described collagen.
8, according to the manufacture method of each the described emgloves in the claim 3 to 7, it is characterized in that, in the described gloves chlorination treatment step, use chlorine that aforementioned adhering-resistant is handled residual powder or other nonrubber impurity in back and removed.