CN1751997A - Method of synthesizing titanium containing porous material - Google Patents
Method of synthesizing titanium containing porous material Download PDFInfo
- Publication number
- CN1751997A CN1751997A CN 200410066637 CN200410066637A CN1751997A CN 1751997 A CN1751997 A CN 1751997A CN 200410066637 CN200410066637 CN 200410066637 CN 200410066637 A CN200410066637 A CN 200410066637A CN 1751997 A CN1751997 A CN 1751997A
- Authority
- CN
- China
- Prior art keywords
- porous material
- containing porous
- titanium containing
- synthetic method
- primary amine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for synthesizing the Ti-contained porous material features that the tetraethyl silicate or silicon sol, tetrabutyl titanate, triamine, organic alcohol and water take part in reaction while the content of water is controlled. Its advantages are no generation of non-skeleton Ti and small pore diameter.
Description
Technical field
The present invention relates to a kind of synthetic method of titanium containing porous material.
Background technology
Molecular sieve containing titanium is a class environment-friendly catalyst, and it successfully synthesizes is the important milestone in molecular sieve catalytic field.U.S. Pat 4410501 has been introduced the synthetic of titanium-silicon molecular sieve TS-1 first.TS-1 has MFI structure micro-pore zeolite, titanium atom has entered its skeleton structure with high dispersion state, titanium-silicon molecular sieve TS-1 has good catalytic activity to the selective oxidation of various organic reactions, selective oxidation preparing benzenediol as phenol, ammoxidation of cyclohexanone preparing cyclohexanone oxime, the epoxidation of alkene etc.Document Nature 368,321-323 (1994) has introduced the synthetic of a kind of novel molecular sieve containing titanium Ti-HMS with middle hole characteristic, this Ti-HMS is a synthetic in water and ethanol mixed solvent, and its water/pure volume ratio is near 2, and the aperture of the Ti-HMS that makes is greater than 25 .In molecular sieve containing titanium synthetic, generally adopting estersil and titanium ester is starting raw material.Yet because the hydrolysis rate of estersil and titanium ester is inconsistent, in containing the system of big water gaging, the hydrolysis rate of titanium ester is too fast, causes TiO easily
2Precipitate and the outer titanium species of generation skeleton.The existence of extra-framework titanium has not only reduced the catalyst activity, also can cause H simultaneously
2O
2Decompose, reduce H
2O
2Effective rate of utilization.
Summary of the invention
The objective of the invention is in order to overcome in the past in the titanium containing porous material synthetic system water-content too high, generate the shortcoming of extra-framework titanium species easily, a kind of synthetic method of new titanium containing porous material is provided, make titanium atom high dispersing in the synthetic titanium containing porous material, promptly avoid the formation of extra-framework titanium species, and the titanium containing porous material that makes have the little characteristics in aperture.
For solving the problems of the technologies described above, the technical solution used in the present invention is as follows: a kind of synthetic method of titanium containing porous material, with tetraethyl orthosilicate or silicon sol is the silicon source, tetrabutyl titanate is the titanium source, primary amine is a template, organic alcohol is solvent, and water composition mixture, wherein be with molar ratio computing: Si/Ti=5~200, primary amine/Si=0.05~0.7, water/pure volume ratio is 0.01~1, above-mentioned reaction mixture was at room temperature stirred crystallization 1~100 hour, crystallized product is through separating, washing, drying, remove template with alcohol extraction or 500~600 ℃ of roastings after, obtain titanium containing porous material.
In the technique scheme, the primary amine preferable range is that carbonatoms is 6~18 primary amine, more preferably amino dodecane or cetylamine.The crystallization time preferable range is 2~24 hours.Used organic alcohol is preferably a kind of of ethanol, Virahol or the trimethyl carbinol or its mixture.Water in the reaction mixture/pure volume ratio preferable range is 0.1~0.5.
The present invention is owing to adopt organic alcohol as reaction solvent, the water yield in the control reaction synthetic system, only added the water yield that guarantees silicon source and the hydrolysis of titanium source, stoped the generation of extra-framework titanium species effectively, and be surprised to find that the titanium containing porous material that makes has the little characteristics in aperture, has obtained better technical effect.
The present invention is further elaborated below by embodiment.
Embodiment
[embodiment 1]
10 gram tetrabutyl titanates are added in the 208 positive tetraethyl orthosilicates of gram and the 300 milliliters of alcoholic acid mixing solutionss, continuously stirring half hour, form uniform sol A.Again 65 gram cetylamines are dissolved in the mixing solutions of 200 milliliters of ethanol and 80 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 2 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=34, cetylamine/SiO
2=0.27, water/pure volume ratio is 0.16.Template is removed with the alcohol extraction method.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[embodiment 2]
34 gram tetrabutyl titanates are added in the mixing solutions of 210 gram tetraethyl orthosilicates and 300 milliliters of Virahols, and continuously stirring 1 hour forms uniform sol A.Again 84 gram cetylamines are dissolved in the mixing solutions of 262 milliliters of Virahols and 90 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 3 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=10, cetylamine/SiO
2=0.35, water/pure volume ratio is 0.16.Template is removed with the alcohol extraction method.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[embodiment 3]
6.8 gram tetrabutyl titanates are added 150 gram silicon sol (SiO
240 weight %) and in the mixing solutions of 300 milliliters of trimethyl carbinols, continuously stirring half hour, form uniform sol A.Again 96 gram amino dodecanes are dissolved in the mixing solutions of 600 milliliters of trimethyl carbinols and 100 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 18 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=50, amino dodecane/SiO
2=0.52, water/pure volume ratio is 0.11.Template is removed in 530 ℃ of roastings.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[embodiment 4]
3.4 gram tetrabutyl titanates are added 150 gram silicon sol (SiO
240 weight %) and in the 300ml alcoholic acid mixing solutions, continuously stirring half hour, form uniform sol A.Again 28 gram amino dodecanes are dissolved in the mixing solutions of 262 milliliters of ethanol and 90 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 5 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=100, amino dodecane/SiO
2=0.15, water/pure volume ratio is 0.16.Template is removed in 550 ℃ of roastings.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[embodiment 5]
10 gram tetrabutyl titanates are added in the mixing solutions of 210 gram tetraethyl orthosilicates and 200 milliliters of trimethyl carbinols, continuously stirring half hour, form uniform sol A.Again 169 gram cetylamines are dissolved in the mixing solutions of 500 milliliters of trimethyl carbinols and 200 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 8 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=33, cetylamine/SiO
2=0.70, water/pure volume ratio is 0.25.Template is removed with the alcohol extraction method.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[embodiment 6]
2.3 gram tetrabutyl titanates are added in the mixing solutions of 210 gram tetraethyl orthosilicates and 200 milliliters of Virahols, continuously stirring half hour, form uniform sol A.Again 24 gram cetylamines are dissolved in the mixing solutions of 550 milliliters of trimethyl carbinols and 250 ml waters, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 24 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=150, cetylamine/SiO
2=0.10, water/pure volume ratio is 0.33.Template is removed in 530 ℃ of roastings.The surface characteristic of the titanium containing porous material that makes sees Table 1.
[Comparative Examples]
2.3 gram tetrabutyl titanates are added in the mixing solutions of 208 gram tetraethyl orthosilicates and 200 milliliters of Virahols, continuously stirring half hour, form uniform sol A.Again 24 gram cetylamines are dissolved in the 360 ml water solution, until forming uniform sol B.Under violent stirring, Sol A is added in the sol B then, and continue to stir 24 hours.Final solid phase prod separates after filtration, behind deionized water wash, and drying at room temperature 24 hours.Wherein each component with molar ratio computing is: SiO
2/ TiO
2=150, cetylamine/SiO
2=0.10, water/pure volume ratio is 1.8.Template is removed in 530 ℃ of roastings.The surface characteristic of the titanium containing porous material that makes sees Table 1.
The surface characteristic of synthetic titanium containing porous material under table 1 different condition
Embodiment | H 2O/ alcohol vol/vol | Aperture | Pore wall thickness | Pore volume cm 3/g | Specific surface m 2/g |
Embodiment 1 | 0.16 | 16.0 | 21.4 | 1.15 | 1008 |
Embodiment 2 | 0.16 | 14.5 | 22.1 | 1.01 | 960 |
Embodiment 3 | 0.10 | 12.2 | 23.6 | 1.21 | 1193 |
Embodiment 4 | 0.16 | 13.6 | 23.3 | 1.26 | 1233 |
Embodiment 5 | 0.25 | 18.9 | 21.7 | 0.94 | 1100 |
Embodiment 6 | 0.33 | 21.8 | 19.3 | 1.06 | 983 |
Comparative Examples | 1.80 | 37.0 | 20.9 | 1.20 | 1050 |
Claims (6)
1, a kind of synthetic method of titanium containing porous material, with tetraethyl orthosilicate or silicon sol is the silicon source, tetrabutyl titanate is the titanium source, primary amine is a template, organic alcohol is solvent, and water composition mixture, wherein be: Si/Ti=5~200 with molar ratio computing, primary amine/Si=0.05~0.7, water/pure volume ratio is 0.01~1, and above-mentioned reaction mixture was at room temperature stirred crystallization 1~100 hour, and crystallized product is through separation, washing, drying, after removing template with alcohol extraction or 500~600 ℃ of roastings, obtain titanium containing porous material.
2,, it is characterized in that described primary amine is that carbonatoms is 6~18 primary amine according to the synthetic method of the described titanium containing porous material of claim 1.
3,, it is characterized in that described primary amine is amino dodecane or cetylamine according to the synthetic method of the described titanium containing porous material of claim 2.
4,, it is characterized in that crystallization time is 2~24 hours according to the synthetic method of the described titanium containing porous material of claim 1.
5,, it is characterized in that described organic alcohol is a kind of or its mixture in ethanol, Virahol or the trimethyl carbinol according to the synthetic method of the described titanium containing porous material of claim 1.
6,, it is characterized in that water in the reaction mixture/pure volume ratio is 0.1~0.5 according to the synthetic method of the described titanium containing porous material of claim 1.