CN1737179A - Method for producing spheroidal graphite cast iron or vermicular cast iron adopting multiple core-spun yarn disposing in iron water - Google Patents
Method for producing spheroidal graphite cast iron or vermicular cast iron adopting multiple core-spun yarn disposing in iron water Download PDFInfo
- Publication number
- CN1737179A CN1737179A CN 200510096852 CN200510096852A CN1737179A CN 1737179 A CN1737179 A CN 1737179A CN 200510096852 CN200510096852 CN 200510096852 CN 200510096852 A CN200510096852 A CN 200510096852A CN 1737179 A CN1737179 A CN 1737179A
- Authority
- CN
- China
- Prior art keywords
- iron
- wire
- line
- cored
- molten iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates a method for producing spheroidal graphite cast iron or vermicular cast iron with adopting core-spun yarn to iron melt treatment, the characteristics of which are following: utilizing core-spun yarn technology, by fuction classifying and combining the substance used in iron melt treatment, in iron melt treatment according to the every process of adjusting, desulfurizing, shielding iron melt interference element, balling, inoculating, organization orienting, sulfur content adjustment, making the corresponding core-spun yarn for every process, and according to iron melt treatment condition, treatment desired value and the weight of iron melt treatment, confirming the species and quantities of core-spun yarn, then confirming the processing sequence of adding core-spun yarn and feeding the core-spun yarn into iron melt with feeding technology. The advantages of the invention are following: producing the high-duty iron because of accurate controlling residual magnesium content, residual rare earth content and sulfur content of the iron melt; accomplishing the production of high- quality vermicular cast iron without titanium because of iron melt preliminary treatment; accomplishing the transformation from grey iron melt to ball iron melt, the iron melt in the same furnace treated to pearlite and ferrite magnesium iron and inserting iron ball alloy production randomly.
Description
Technical field
The present invention relates to a kind of method that adopts multiple cored-wire to carry out molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, concrete is that a kind of wire-feeding technique that adopts is when the nodularization of carrying out molten iron and inoculation, realize adjustment, the control of sulphur content, the processing control of the residual magnesium amount of molten iron, residual Re amount and final-sulphur content afterwards respectively, thereby realize the production of the high quality magnesium iron or the iron of wriggling molten iron carbon, silicone content before the spheroidizing; In molten iron, carry out the composition adjustment, realize being processed into the magnesium iron of different tissues respectively, or grey molten iron is to the method for the conversion of magnesium iron water with a kind of molten iron by line feeding adding alloy element and the contained coherent element of molten iron.
Background technology
Adopting wire-feeding technique to carry out the nodularization of molten iron and inoculation produces ductile cast iron casting or pieces of vermicular cast iron and has that the specific absorption of magnesium is stable, residual magnesium amount fluctuation range is little, accurately controls line feeding length and handle that the final-sulphur content of back molten iron is stable, level of automation is high and advantage such as operating environment close friend.
The cored-wire that is used for the molten iron processing that adopts at present, its core agent mainly is made of compositions such as magnesium, calcium, rare earth and silicon.The main effect of magnesium in molten iron is desulfurization, deoxidation, spheroidization, is the dominant element of nodularization; The effect of calcium and magnesium close, but on efficient not as magnesium; Rare earth classic effect in molten iron is the interference element of shielding molten iron, and desulfurization, deoxidation and spheroidization are arranged, but compares with magnesium, plays same effect, and the consumption of rare earth is big than magnesium; Silicon plays alloying and inoculation(effect), is that carrier as other element adds molten iron but smelt silicon in the nodulizing agent of usefulness, and molten iron is not played inoculation(effect).Existing cored-wire product, no matter its core agent is metallurgy type, or mixed type, and included above-mentioned composition all exists with the fixed ratio, and therefore, in the time of in adding molten iron, the ratio of the shared total amount of each element is subjected to the restriction of the total add-on of cored-wire.
In the present public technology, all be to be purpose how to improve utilization ratio in molten iron of magnesium in the cored-wire, to reduce processing cost.As " the high magnesium alloy nodularization cored-wire " of Wenxin Industry Co Ltd, Baotou (application number: be to be the nodularization cored-wire that the core agent is made greater than 30% high magnesium silicon-base alloy powder 02140811.4) to contain magnesium, be intended to improve the utilization ratio of magnesium in molten iron in the cored-wire, reduce the cored wire injection nodulizing processing cost." the high Mg alloy cored wine of passivation " (application number: be 021408130) by passivation to the cored-wire steel strip surface, prolong the fusing time of steel band in molten iron, control the add magnesium amount of unit time to reduce wire-feeding velocity to molten iron, simultaneously, reduce the pre-heat effect of molten iron, reach the add magnesium amount of control unit time in molten iron, reduce the magnesium vapour pressure, improve the purpose of the utilization ratio of magnesium in molten iron the agent of cored-wire core." magnesium core spun yarn " of Baotou Yixin Metallurgical Technology Co., Ltd. (application number: 200510053233.9) be heat insulation by nucleating agent bisque on every side, reduce the evaporating capacity that magnesium produced and improve the utilization ratio of magnesium in molten iron in passing liquid molten iron process, and realize that nodularization, preparation process single line finish; " containing magnesium core cored-wire " (application number: 200520007239.8) wire-feeding velocity can be reduced by 40%, heat insulation and reduce the unit time and improve the utilization ratio of magnesium in molten iron by bisque to the magnesium amount that adds of molten iron, and realize that nodularization, preparation process single line finish.
Nodularization quality or the bigger condition of wriggling quality influence there are two: the one, the base iron condition, as the height of sulphur, oxygen level, the height of interference element content, the 2nd, the content of coherent element in molten iron after handling is as magnesium, rare earth and the sulphur residual quantity in molten iron.
When the sulphur content of base iron is higher, though also just increase of the magnesium amount that desulfurization consumes; When the interference element of base iron is higher, though the increase also of the shielding needed rare earth content of interference element; Therefore, nodularization cored-wire add-on must be adjusted synchronously with the condition of base iron.
When the sulphur content of molten iron is higher after handling, owing to the magnesium in continuation of the sulphur in the molten iron and the molten iron reacts, decaying spheroidisation phenomenon faster can occur, the sulphur content after handling in the molten iron is crossed when hanging down, and can produce the less phenomenon of number of graphite ball; When the residual Re amount of handling the back molten iron is too high, the graphite pebbles shape is worsened, and when residual Re content is on the low side, the scarce capacity of interference element in the shielding molten iron, can occur decaying spheroidisation phenomenon faster again, simultaneously, be unfavorable for obtaining maximum graphite pebbles quantity.
When the wriggling processing of carrying out molten iron, its key issue is that residual magnesium amount, rare earth residual volume and the final-sulphur content that will handle the back molten iron are controlled at respectively in the narrower scope.
Therefore, with existing single line, be cored wire injection nodulizing technology or two-wire, be that cored wire injection nodulizing and line feeding inoculation technology and existing product carry out molten iron when handling, owing to elements such as the contained magnesium of cored-wire core agent, rare earth all exist in certain proportion, once fluctuation appears in the molten iron condition, just be difficult to reach unification to base iron condition and desired result.
In actual production, often the technical problem that occurs has:
1) when fluctuation appears in the base iron condition,,, then is difficult to guarantee the optimum range of rare earth residual volume if guaranteed the optimum range of residual magnesium amount because the nodularization cored-wire is a fixed with the content of rare earth that breeds in the cored-wire; And guaranteed the optimum range of rare earth residual volume, be difficult to guarantee the optimum range of residual magnesium amount again;
2) when the sulphur content of handling molten iron is higher, adopt the cost of magnesium and rare earth desulfurization higher;
3) when the processing iron water amount is big, if expect higher magnesium recovery rate, add the magnesium amount with regard to controlling the unit time, unit time to add the magnesium amount few more, the cored wire injection nodulizing treatment time is long more, when the treatment time surpasses 150 seconds, tend to occur the phenomenon of the final-sulphur content (less than 0.008% o'clock) on the low side of molten iron, such molten iron nucleation ability just can reduce, and causes number of graphite ball phenomenon on the low side, spherical bigger easily, is unfavorable for obtaining best mechanical property;
4) in adopting molten iron, add element such as antimony when producing pearlitic ductile iron or when increasing number of graphite ball or when producing the magnesium iron of thick and large section, must strictly control its content range in molten iron, content is on the low side, then do not have due effect, content is higher, then plays the effect of interference element-be anti-spheroidization.Present antimony generally is to adopt when pouring the method spheroidizing, in nodulizing agent or in the nucleating agent, add, because the antimony in the nodulizing agent is subject to processing temperature and handles the influence of weight of molten iron fluctuation, antimony in the nucleating agent is subjected to the influence of nucleating agent recovery rate in molten iron, and in multiplex process, be subjected to the influence of the tired content of antimony collection in the foundry returns, antimony fluctuation range of content in molten iron is bigger, and be difficult for adjusting, cause the departure of target value bigger;
When 5) producing vermicular cast iron, because residual magnesium amount, residual Re amount, final-sulphur content and titanium content optimum content scope in the molten iron are narrower, therefore, requirement is before wriggling processing, the sulphur content of molten iron is low more good more, consumes magnesium and rare earth to avoid excessive sulfur content, causes the fluctuation range of Mg content and content of rare earth bigger, be unfavorable for the wriggling production of iron, present wire-feeding technique can't be realized this point;
6) adopt present wire-feeding technique can't realize that a stove molten iron that adopts grey molten iron composition is produced magnesium iron simultaneously, wriggle iron and gray iron;
7) adopt present wire-feeding technique can't realize adopting a stove molten iron to carry out the production of pearl body matrix and ferrite matrix magnesium iron simultaneously.
Summary of the invention
The objective of the invention is problem at above-mentioned prior art existence, a kind of new technical scheme that adopts the method that multiple cored-wire carries out molten iron process for producing spheroidal graphite cast iron or vermicular cast iron is provided, adopt the technical program can accurately control the residual magnesium amount of processing back molten iron, remaining rare amount and final-sulphur content gone up, make it all be in the optimum range, and the quantitative adding of realization alloying elements such as antimony, bismuth etc., obtaining best nodularization quality or wriggling quality, pregnant effect and matrix, and can realize the grey molten iron direct production magnesium iron or the iron of wriggling.
The present invention based on know-why be:
Composition adjustment, desulfurization, shielding molten iron interference element, nodularization or wriggling in handling at molten iron, breed, organize in the links such as orientation, final-sulphur content adjustment, different demands to treated substance, the known material that is used for the molten iron processing is carried out sort merge by function, utilize present sophisticated cored wire technology, make various functions comparatively single, have strong specific aim cored-wire, respectively independent adding the in the molten iron that desire is handled, realize purpose of the present invention, concretely, be exactly:
1) to high-sulphur molten iron or the unsettled molten iron of sulphur content, at first carry out the desulfurization and the deoxidation treatment of molten iron in pack processing or in the induction furnace with the desulfurization line, and make it before carrying out spheroidizing, be in a lower level or a stable level as far as possible, the rare earth that makes thereafter to be added, less as far as possible reacts with sulphur and oxygen, give full play to the effect of its shielding interference element, reduce it and cause the high disadvantageous effect of desulphurization cost greatly because of nucleidic mass, and make the magnesium that carries out subsequently handle the less composition fluctuation that desulfurization causes that is subjected to, obtain a residual magnesium weight range than close limit;
2) according to the height of handling interference element content in the molten iron, adopt the rare earth line to adjust flexibly, and do not added the restriction of magnesium amount, and make the content of rare earth in the molten iron be in the optimum content level, the standard of this optimum content scope is that spheroidization of graphite is more, better spherical, and content is lower, and according to the height of interference element, the residual rare earth content of molten iron is generally between 0.01~0.03%, wherein with 0.012~0.015% o'clock, the nodularization quality was better;
3) long or electric furnace molten iron is reused foundry returns and is caused whole sulphur situation on the low side at the treatment time, after nodularization, increase sulphuring treatment to increase the sulphur line, the final-sulphur content of handling the back molten iron is in the optimum range, thereby obtain best nodularization or wriggling quality, the magnesium iron final-sulphur content is generally 0.008~0.012%, and the iron final-sulphur content of wriggling is generally 0.015~0.02%;
4) adding contains antimony alloy in cored-wire, carrying out rare earth processing back feeding, can accurately control the content range in the molten iron, thereby accurately control pearlitic ratio, and can adjust flexibly by the minimizing or the increase of add-on with what of the tired collection amount of this element in the foundry returns in molten iron;
5) when producing vermicular cast iron, can be according to the situation of base iron, carry out the pre-treatment of molten iron with desulfurization line, rare earth line respectively, then, with the processing of magniferous wriggling of cored-wire, carry out inoculation and handle the sulphur content of back molten iron to increase the adjustment that the sulphur line carries out final-sulphur content according to magnesium with covering line, can make the sulphur content of the preceding molten iron of wriggling processing be in a stable level, thereby accurately control residual magnesium amount, residual Re amount and final-sulphur content scope after the wriggling processing, obtain best vermiculation effect, and can fully phase out the adding of the maximum titanium elements of present employing;
6) when needs adopt same stove molten iron production ferrite matrix and pearlite matrix magnesium iron, can smelt the molten iron of the perlite composition of low manganese in advance, then, carry out perlite processing after nodularization, inoculation with the cored-wire that contains manganese, antimony; Carry out carbon, the adjustment of silicon composition of molten iron with carbon, silicon cored-wire, carry out nodularization and inoculation then and can realize;
7) in the molten iron of gray iron composition, carry out carbon, the adjustment of silicon composition of molten iron, adjust the carbon content of grey molten iron and silicon amount to magnesium iron or the desired composition scope of the iron of wriggling with carbon, silicon cored-wire.This method is suitable for cupola furnace or blast furnace and induction furnace duplex and uses, when temperature being adjusted to 1450~1500 ℃ according to weight of molten iron, in induction furnace, carry out the processing of the adjustment of composition and desulfurization, shielding interference element, in pack processing, carry out nodularization or wriggling then and the line feeding of breeding is handled.
Concrete grammar of the present invention is:
Utilize cored wire technology, the known material that is used for the molten iron processing is carried out sort merge by function, composition adjustment, desulfurization, shielding molten iron interference element, nodularization or wriggling in handling at molten iron, breed, organize each link of orientation, final-sulphur content adjustment, make and the corresponding cored-wire of each processing links, i.e. carbon silicon line, desulfurization line, rare earth line, nodularization or wriggling line, covering line, alloying line and increase the sulphur line; Composition to pending molten iron carries out the rapid detection analysis, weight according to detected result, processing target value and processing molten iron, determine the adding kind of cored-wire and the add-on of every kind of cored-wire, utilize wire-feeding technique will determine that at each processing links of molten iron the cored-wire that adds is fed into respectively in the molten iron independently according to handling order then, to reach the purpose of controlling the final content of institute's addition element respectively.
Described composition to pending molten iron carries out the rapid detection analysis, generally adopts stokehold direct reading spectrometry technology commonly used in the casting industry.
Above-mentioned treating processes, can one the step in pack processing, finish, also can be divided into pre-treatment and handle eventually two processes in induction furnace, carry out respectively with pack processing in carry out; The function of utilizing induction furnace to exist eddy current stirring and temperature raising in induction furnace can be carried out composition adjustment, desulfurization, shielding interference element and the directed processing of tissue of molten iron; In pack processing, then can carry out the directed processing of nodularization or wriggling (adding magnesium handles), inoculation, shielding interference element and tissue, increase sulphuring treatment; Wherein, the directed processing of shielding interference element and tissue can be selected to be placed in preprocessing process or the whole treating processes according to actual conditions, with the stable criterion that turns to of final composition.
When the sulphur content of molten iron is in steady state before handling, then can adopts the cored-wire that has nodularization, breeds complex function to carry out single line and handle, so then can save an injecting channel, reduce the input of line feeding equipment.
When the interference element content of handling molten iron is in steady state, then rare earth can be added in the nucleating agent, wrap in the cored-wire as mixing in the nucleating agent powder layer of magnesium core spun yarn or with the magnesium powder, with further minimizing injecting channel.
Compare with existing molten iron line feeding treatment technology, it is characterized in that in whole line feeding treating processes, the cored-wire kind that is adopted is two or more, and wherein to have a kind of cored-wire at least be with nodularization and breed cored-wire, or nodularization, breeds the diverse cored-wire of composite core-spun yarn.
When cored-wire adds fashionablely, when promptly carrying out the pre-treatment line feeding,, can adopt parallel feeding (feeding) simultaneously, lapping type feeding or order feeding according to the condition of molten iron and the effect of addition element in induction furnace; When sulphur content is higher in the molten iron, then should at first carry out desulfurization to molten iron handles, then, carry out the composition adjustment again, shield the processing of interference element again, promptly subsequent treatment can avoid the rare earth desulfurization to be unfavorable for that cost reduces like this, and before desulfurization, carry out the composition adjustment, then be unfavorable for reducing temperature loss; If the molten iron interference element is lower and must not carry out desulfurization and handle, then composition adjustment and add rare earth and handle and can carry out simultaneously.
Pour in the pack processing by induction furnace through pretreated molten iron, then can add the nodularization of magnesium or wriggling processing, inoculation; Iron water amount is bigger when handling, and causes and handles back molten iron sulfur content when low, when the final-sulphur content that iron has relatively high expectations is wriggled in processing, then needs to increase sulphuring treatment.When containing magnesium in the covering line, then nodularization line (containing the magnesium cored-wire) and covering line can add in proper order, when not containing magnesium in the covering line, then must add simultaneously, to guarantee the dispersity of nucleating agent particle in molten iron; When iron is wriggled in production, often need higher rare earth content, then need to add rare earth, not magniferous rare earth line then needs to add simultaneously with the nodularization line, to guarantee the dispersity of rare earth in molten iron.Increase the adding of sulphur line, then need certain power, making it has bigger dispersity in molten iron, does not overlap but do not advocate with nodularization or wriggling line, can reduce significantly like this and increase the sulphur effect.
Said process is by two hyperchannel feeding wire machine, finishes in induction furnace and pack processing at twice.
When molten iron can satisfy requiring of teeming temperature after the molten iron treatment capacity is bigger, and the temperature that is enough to guarantee the needed treatment time of desulfurization, handle molten iron is enough to guarantee to handle, two processes then can be carried out in pack processing by a multi-thread feeding wire machine simultaneously.
The composition of the various cored-wires that adopted is:
Carbon silicon line: be the cored-wire of making for the core agent by silicon carbide, Graphite Powder 99 and ferrosilicon powder, be mainly used in grey molten iron when the conversion of magnesium iron water composition or the molten iron composition of wriggling, the pearlitic ductile iron composition adjusts the composition of carbon and silicon in the molten iron when the ferrite composition is changed, its composition depends on difference and the three kinds of materials yield in molten iron of handling front and back molten iron composition, calculates as the case may be to get final product.
The desulfurization line: can adopt contain magnesium and carbide of calcium be main and auxiliary be the cored-wire of sweetening agent with graphite and lime carbonate or sodium bicarbonate, its major limitation link is that the length that will guarantee the treatment time should not be lower than 1 minute, preferably will reach 2 minutes, otherwise desulfurization degree is lower; Its composition scope is: magnesium 5~15%, carbide of calcium 60~85%, carbon 3~10%, lime carbonate 5~20%, total amount are 100%.
The rare earth line: its core agent is by rare earth ferrosilicon alloy, or rare earth ferrosilicon alloy and the ferrosilicon system of mixing forms, according to the difference of handling weight of molten iron, its composition scope is: rare earth 10~30%, silicon 35~60%, all the other are iron, also can add 2~8% the magnesium reaction power so that independent line feeding to be provided.When producing large-section magnesium iron, can add yttrium-based heavy rare earth ferro-silicon alloy replacement or part and replace rare earth ferrosilicon alloy, to improve the fade resistance energy of molten iron, total composition constant rate.
Nodularization or wriggling line, or claim the magnesium line: the composition scope of its core agent is: magnesium 10~40%, silicon 30~60%, calcium 0~5%, barium 0~5%, and all the other are iron, the summation of various elements is 100%; Can adopt magnesium powder and silicon-base alloy powder to mix the core agent of system, also can adopt Si-Mg alloy cored wine, also can adopt magnesium core spun yarn.When adopting magnesium core spun yarn, can realize adding magnesium and inoculation process single line is finished.
Covering line: its major ingredient is silicon, barium, calcium, zirconium etc., according to weight, shape and the matrix requirement of foundry goods, select the nucleating agent of difference in functionality, can be with reference to " the casting composition that handbook provided is selected, goods can be selected to smelt, also the physical mixed goods can be selected.
Alloying line: refer to mainly that in the present invention antimony, bismuth etc. stablize pearlitic alloy element, can certainly add alloy elements such as molybdenum, chromium with this mode.The employed core agent composition that contains the cored-wire of alloy element is among the present invention: alloy element 5~20%, silicon 50~70%, all the other are iron.
Increase the sulphur line: its core agent is formed by sulphur or iron sulphide and the small amounts iron powder system of mixing, and its major ingredient is: sulphur 10~50%, all the other are iron.
Positively effect of the present invention is:
1) by the high quality magnesium iron is produced in the accurate control of handling the residual magnesium amount in back, residual Re amount, final-sulphur content;
2) by to the pre-treatment of molten iron, the production of iron of wriggling of the high quality of realizing not adding titanium;
3) can realize the conversion of grey molten iron to magnesium iron water, the molten iron of wriggling, the subpackage of same stove molten iron is processed into perlite and ferritic spheroidal graphite cast iron, and can insert the production of alloy ball iron at any time.
Description of drawings
Fig. 1 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment one; Fig. 2 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment two; Fig. 3 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment three; Fig. 4 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment four; Fig. 5 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment five; Fig. 6 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment six; Fig. 7 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment seven (2); Fig. 8 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment seven (3); Fig. 9 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment seven (4); Figure 10 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment eight (1); Figure 11 is line feeding order and the synoptic diagram of each shared time of handling procedure of embodiment eight (2).
Embodiment
The invention will be further described below by embodiment:
Adopt the inventive method to be used for the vermicular cast iron processing and see embodiment one~three;
Adopt the inventive method to be used for the processing of high quality spheroidal graphite cast iron and see embodiment four~six;
Adopt molten iron that the inventive method is used for the gray iron composition to see embodiment seven to magnesium iron and the iron of wriggling conversion and alloy ball iron;
Adopt the inventive method foundry return moisture bag processing pearlitic ductile iron and ferritic spheroidal graphite cast iron to see embodiment eight.
Embodiment one: adopt cupola furnace molten iron production vermicular cast iron
The base iron major ingredient is: C:3.4%, Si:1.65%, Mn:0.35%, S:0.05~0.06%, Ti:0.045~0.055%.
Handle molten iron temperature: 1430 ℃, the fluctuation range of rule is 1420~1445 ℃,
Handle weight of molten iron: 5000kg/ bag, fluctuation range is 4700~5300kg/ bag;
Handle molten iron height: 1000mm.
According to above-mentioned condition, desulfurization processing, the magnesium core spun yarn that adopts the desulfurization line to carry out molten iron carry out molten iron add magnesium with inoculation, adopt the rare earth line to cooperate to add the processing of wriggling of magnesium, employing to increase the final-sulphur content of molten iron after the sulphur line adjustment processing.The line feeding process is carried out in pack processing, adopts the four-way feeding wire machine.
The various cored-wire parameters, core material composition and the add-on that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | The core agent constitutes % | The cored-wire add-on | |||||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | CaC 2 | RE | Mg | Si | Ba | S | Other | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ |
||
1 | The desulfurization line | 10 | 0.4 | 100 | 240 | 70 | 10 | 20 | 2500 | 6000 | 25 | ||||
2 | The magnesium line | 13-35 | 0.4 | 16.5 | 386 | 7.6 | 70 | 5 | 5412 | 9650 | 25 | ||||
Nucleating agent | 200 | ||||||||||||||
3 | The rare earth line | 12 | 0.4 | 220 | 370 | 30 | 54 | 1890 | 3180 | 8.6 | |||||
5 | Increase the sulphur line | 8 | 0.35 | 90 | 190 | 26 | 5 | 234 | 494 | 2.6 |
Annotate: in the table in the composition not mentioned part be iron.
The line feeding order of embodiment one and shared time of each handling procedure are seen accompanying drawing 1.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/min) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The desulfurization line | 45 | 125 | 167 | 0 | 167 |
2 | The magnesium heart yearn | 35 | 125 | 214 | 0 | 214 |
2 | The rare earth line | 42 | 43 | 62 | 62 | 0 |
5 | Increase the sulphur line | 43 | 13 | 18 | 0 | 18 |
Whole line feeding times | 399 |
Result: 1) sulphur content of the molten iron of line feeding desulfurization is 0.025%;
Handle back composition: C:3.35%, Si:2.18%, Mn:0.35%, S:0.016%, Ti:0.045~0.055%, Mg
Residual: 0.017%, RE
Residual: 0.048%.
Wriggling quality: all require the wall thickness place of performance foundry goods, black content 〉=90% of wriggling, and the tensile strength of requirement is 400MPa, reality is 430MPa, the content of pearlite in alloy of matrix 〉=95%.
Embodiment two: adopt the two-link smelting process of cupola melting, electric furnace temperature raising, adjustment composition to produce vermicular cast iron
The base iron composition is: C:3.48%, Si:1.7%, Mn:0.30%, 0.02%S, 0.03%Ti
Handle molten iron temperature: 1430 ℃
Handle molten iron height: 850mm
Handle weight of molten iron: 1200kg/ bag
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath m m | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC | RE | Mg | Si | Ba | S | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | The rare earth line | 11 | 0.4 | 185 | 335 | 10 | 27 | 54 | 1665 | 3015 | 9 | |||
2 | Magnesium alloy wire | 9 | 0.37 | 120 | 240 | 20 | 55 | 2040 | 4080 | 17 | ||||
3 | Covering line | 13 | 0.42 | 285 | 460 | 70 | 5 | 5000 | 8050 | 17.5 | ||||
4 | Increase the sulphur line | 7 | 0.35 | 65 | 160 | 2 | 0 | 15 | 455 | 1120 | 7.0 |
The line feeding order of embodiment two and shared time of each handling procedure are seen accompanying drawing 2.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | Magnesium alloy wire | 38 | 20.5 | 32.4 | 0 | 32.4 |
2 | The rare earth line | 35 | 10.8 | 18.5 | 18.5 | 0 |
3 | Covering line | 34 | 21 | 37 | 30 | 7 |
4 | Increase the sulphur line | 38 | 8.5 | 13.4 | 5 | 84 |
Whole | 48 |
Result:
Handle back composition: C:3.48%, Si:2.25%, Mn:0.30%, S:0.018%, Mg
Residual: 0.015%, RE
Residual: 0.041%.
Wriggling quality: all require the wall thickness place of performance foundry goods, black content 〉=95% of wriggling, and the tensile strength of requirement is 400MPa, reality is 450MPa, the content of pearlite in alloy of matrix 〉=95%.
Embodiment three: the induction furnace smelting molten iron is produced vermicular cast iron.
The base iron composition is: C:3.45%, Si:1.75%, Mn:0.30%, 0.025%S 0.035%Ti
Handle molten iron temperature: 1450 ℃
Handle molten iron height: 500mm
Handle weight of molten iron: 500kg/ bag
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath m m | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC | RE | Mg | Si | Ba | S | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | The rare earth line | 9 | 0.37 | 120 | 240 | 20 | 25 | 50 | 1440 | 2880 | 12 | |||
2 | Magnesium alloy wire | 7 | 0.35 | 65 | 160 | 20 | 55 | 2080 | 5120 | 32 | ||||
3 | Covering line | 12 | 0.40 | 240 | 400 | 2 | 68 | 5 | 4320 | 7200 | 18 |
The line feeding order of embodiment three and shared time of each handling procedure are seen accompanying drawing 3.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | Magnesium alloy wire | 22 | 16 | 44 | 0 | 44 |
2 | The rare earth line | 21 | 6 | 17 | 17 | 0 |
3 | Covering line | 21 | 9 | 15 | 5 | 10 |
Whole | 54 |
Result:
Handle back composition: C:3.42%, Si:2.35%, Mn:0.30%, S:0.015%, Mg
Residual: 0.015%, RE
Residual: 0.034%.
Wriggling quality: all require the wall thickness place of performance foundry goods, black content 〉=95% of wriggling, and the tensile strength of requirement is 400MPa, reality is 450MPa, the content of pearlite in alloy of matrix 〉=95%.
Embodiment four: the molten iron of temperature raising in cupola furnace iron, the induction furnace, the base iron composition is: 0.07%S 0.045%Ti.
Handle molten iron temperature: 1500 ℃
Handle weight of molten iron: 500kg/ bag
Handle molten iron height: 500mm
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath m m | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC | RE | Mg | Si | Ba | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn addition m/ | |||
1 | The rare earth line | 9 | 0.37 | 120 | 240 | 20 | 15 | 4 | 58 | 1440 | 2880 | 12 | ||
2 | The core cored-wire | Sub-line | 7 | 0.3 | 48 | 110 | 80 | 9 | 960 | 2200 | 20 | |||
Bus | 15 | 0.42 | 250 | 440 | 70 | 5 | 5000 | 8800 |
The line feeding order of embodiment four and shared time of each handling procedure are seen accompanying drawing 4.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | Ask during with preceding line overlap | The independent shared | ||||
1 | The core line | 10 | 10 | 60 | 0 | 60 |
2 | The rare earth line | 21 | 6 | 17 | 0 | 17 |
Whole line feeding times | 77 |
Result:
Handle back composition: C:3.76%, Si:2.7%, Mn:0.35%, S:0.010%, Mg
Residual: 0.045%, RE
Residual: 0.018%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, 180~200/mm of graphite quantity
2
Embodiment five: induction furnace is interior to be the molten iron of raw material remelting with the pig iron and steel scrap, and the base iron composition is: 0.025%S 0.03%Ti.
Handle molten iron temperature: 1450 ℃
Handle weight of molten iron: 3000kg/ bag
Handle molten iron height: 1000mm
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | |||||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC | RE | Mg | Si | Ba | Ca | S | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ |
1 | The rare earth line | 11 | 0.4 | 185 | 335 | 10 | 20 | 54 | 925 | 1675 | 5 | ||||
2 | The nodularization line | 11 | 0.4 | 145 | 295 | 30 | 45 | 2 | 3915 | 7965 | 27 | ||||
3 | Covering line | 15 | 0.42 | 350 | 535 | 70 | 5 | 5000 | 7650 | 14. 3 | |||||
4 | Increase the sulphur line | 7 | 0.35 | 65 | 160 | 2 | 15 | 97.5 | 240 | 1.5 |
Embodiment five line feeding order and shared time of each handling procedure see accompanying drawing 5.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The nodularization line | 42 | 81 | 116 | 0 | 116 |
2 | The rare earth line | 38 | 15 | 23.7 | 23.7 | 0 |
3 | Covering line | 40 | 43 | 65 | 65 | 0 |
4 | Increase the sulphur line | 42 | 4.5 | 6.4 | 0 | 6.4 |
Whole line feeding times | 122.4 |
Result:
Handle back composition: C:3.55%, Si:2.38%, Mn:0.35%, S:0.014%, Mg
Residual: 0.043%, RE
Residual: 0.016%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, 150~180/mm of graphite quantity
2
Embodiment six: the cupola melting molten iron, and process for producing spheroidal graphite cast iron in the bag, the base iron composition is: 0.06%S 0.045%Ti.
Handle molten iron temperature: 1480 ℃
Handle weight of molten iron: 1500kg/ bag
Handle molten iron height: 800mm
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | |||||||||||
Line footpath m m | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | RE | Mg | Si | Ba | SiC | Other | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn addition m/ | |||
1 | The desulfurization line | 7 | 0.35 | 70 | 165 | 15 | 85 | 1400 | 3300 | 20 | |||||
2 | The rare earth line | 9 | 0.37 | 120 | 240 | 15 | 55 | 30 | 1800 | 3600 | 15 | ||||
3 | The coating magnesium core spun yarn | The magnesium line | 4.5 | 0.42 | 27 | 390 | 966 | 14040 | 36 | ||||||
Bus | 13 | 180 | 65 | 5 | 5 | 6480 |
Embodiment six line feeding order and shared time of each handling procedure see accompanying drawing 6.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The desulfurization line | 35 | 30 | 52 | 0 | 52 |
2 | The rare earth line | 30 | 22.5 | 45 | 0 | 45 |
3 | Coating magnesium heart yearn | 26 | 54 | 125 | 45 | 80 |
Whole line feeding times | 177 |
Result:
Handle back composition: S:0.012%, Mg
Residual: 0.044%, RE
Residual: 0.022%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, 150~200/mm of graphite quantity
2
Embodiment seven: adopt molten iron, induction furnace temperature raising or the insulation of cupola melting gray iron composition, grey cast iron, spheroidal graphite cast iron and vermicular cast iron are handled in subpackage.
The base iron composition is: C:3.2%, Si:1.4%, Mn:0.35%, S:0.06%, P :≤0.06%
1) when adopting this composition molten iron to carry out the production of gray iron H250 foundry goods, need in bag, dash molten ferromanganese, final composition is adjusted to 0.6%, the whole silicon amount after the processing is 1.8%, adjusts by the adding of nucleating agent.
2) when the molten iron that adopts above-mentioned composition was handled magnesium iron, treatment condition were:
Weight of molten iron: 500kg/ bag;
Molten iron height: 500mm;
Molten iron temperature: 1520 ℃;
Spheroidization treatment temperature: 1470 ℃.
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC or CaC | RE | Mg | Si | Ba | C | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | Carbon silicon line | 15 | 0.42 | 275 | 470 | 75 | 25 | 13750 | 23500 | 50 | ||||
2 | The desulfurization line | 7 | 0.35 | 60 | 155 | 70 | 15 | 2280 | 5890 | 38 | ||||
3 | The rare earth line | 9 | 0.37 | 120 | 240 | 15 | 58 | 1440 | 2880 | 12 | ||||
4 | Coating magnesium heart yearn | 5 | 0.42 | 34 | 379 | 16.7 | 55 | 5 | 5304 | 9854 | 26 | |||
13 | 170 |
Embodiment seven (2) line feeding order and shared time of each handling procedure see accompanying drawing 7.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | Carbon silicon line | 22 | 25 | 68 | 0 | 68 |
2 | The desulfurization line | 23 | 19 | 50 | 50 | 0 |
3 | The rare earth line | 21 | 6 | 17 | 0 | 17 |
4 | Coating magnesium heart yearn | 17 | 13 | 46 | 17 | 29 |
Whole line feeding times | 114 |
Result:
Handle back composition: C:3.82%, Si:2.6%, Mn:0.36%, S:0.012%, Mg
Residual: 0.042%, RE
Residual: 0.022%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, 160~190/mm of graphite quantity
2
3) when iron was wriggled in the molten iron processing of adopting above-mentioned composition, treatment condition were:
Weight of molten iron: 500kg/ bag;
Molten iron height: 500mm;
Molten iron temperature: 1500 ℃;
Wriggling treatment temp: 1440 ℃.
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC or CaC | RE | Mg | Si | Ba | C | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | Carbon silicon line | 15 | 0.42 | 275 | 470 | 75 | 25 | 6875 | 11750 | 25 | ||||
2 | The desulfurization line | 7 | 0.35 | 60 | 155 | 70 | 15 | 2040 | 5270 | 34 | ||||
3 | The rare earth line | 9 | 0.37 | 120 | 240 | 15 | 58 | 2400 | 4800 | 20 | ||||
4 | Coating magnesium heart yearn | 4 | 0.42 | 21 | 529 | 6.5 | 55 | 5 | 6420 | 10580 | 20 | |||
15 | 300 |
Embodiment seven (3) line feeding order and shared time of each handling procedure see accompanying drawing 8.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The desulfurization line | 23 | 17 | 44 | 0 | 44 |
2 | Carbon silicon line | 22 | 12.5 | 34 | 0 | 34 |
3 | The rare earth line | 21 | 10 | 29 | 0 | 29 |
4 | Coating magnesium heart yearn | 17 | 10 | 36 | 29 | 7 |
Whole line feeding times | 114 |
Result:
Handle back composition: C:3.45%, Si:2.4%, Mn:0.36%, S:0.015%, Mg
Residual: 0.018%, RE
Residual: 0.032%.
Wriggling quality: all require the wall thickness place of performance foundry goods, black content 〉=95% of wriggling, and the tensile strength of requirement is 400MPa, reality is 430MPa, the content of pearlite in alloy of matrix 〉=95%.
4) when the molten iron that adopts above-mentioned composition was handled Martensitic ductile iron, treatment condition were:
Weight of molten iron: 500kg/ bag;
Molten iron height: 500mm;
Spheroidization treatment temperature: 1480 ℃.
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | SiC | RE | Mg | Si | Mn/ B | C | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn addition m/ | ||
1 | Carbon silicon line | 15 | 0.42 | 275 | 470 | 75 | 25 | 8250 | 14100 | 30 | ||||
2 | Manganese boron line | 16 | 0.42 | 400 | 650 | 10 | 60/2 | 38461 | 55250 | 85 | ||||
3 | The rare earth line | 9 | 0.37 | 120 | 330 | 25 | 55 | 2400 | 4800 | 12 | ||||
4 | Coating magnesium heart yearn | 4 | 0.42 | 21 | 385 | 10.4 | 50 | 8040 | 15400 | 40 | ||||
13 | 180 |
Embodiment seven (4) line feeding order and shared time of each handling procedure see accompanying drawing 9.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | Carbon silicon line | 22 | 15 | 41 | 0 | 41 |
2 | Manganese boron line | 22 | 42.5 | 116 | 0 | 116 |
3 | The rare earth line | 21 | 6 | 17 | 0 | 17 |
4 | Coating magnesium heart yearn | 17 | 20 | 71 | 17 | 54 |
Whole line feeding times | 228 |
Result:
Handle back composition: C:3.45%, Si:2.8%, Mn:2.6%, S:0.018%, Mg
Residual: 0.018%, RE
Residual: 0.034%.
Nodularization quality: nodularization rate 〉=85%, graphite size: 6~7 grades; Graphite quantity: 〉=150/mm
2
Embodiment eight: adopt induction furnace remelting foundry return moisture bag to handle pearlitic ductile iron and ferritic spheroidal graphite cast iron.
The base iron composition is: C:3.8%, Si:1.8%, Mn:0.4%, S:0.03%, P :≤0.06%
(1) when the molten iron that adopts above-mentioned composition was handled ferritic spheroidal graphite cast iron, treatment condition were:
Weight of molten iron: 500kg/ bag;
Molten iron height: 500mm;
Molten iron temperature: 1480 ℃;
The cored-wire parameter and the core material composition that are adopted see the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | ||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | RE | Mg | Si | Ba | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | The nodularization line | 9 | 0.37 | 120 | 240 | 0 | 25 | 50 | 2 | 3840 | 7680 | 32 |
2 | The rare earth line | 9 | 0.37 | 120 | 240 | 15 | 3 | 58 | 1440 | 2880 | 9.5 |
3 | Covering line | 13 | 0.42 | 250 | 430 | 3 | 55 | 4 | 5000 | 8600 | 20 |
Embodiment eight (1) line feeding order and shared time of each handling procedure see accompanying drawing 10.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The nodularization line | 21 | 16 | 46 | 0 | 46 |
2 | The rare earth line | 19 | 4.8 | 15 | 0 | 15 |
3 | Covering line | 19 | 10 | 32 | 32 | 0 |
Whole | 61 |
Result:
Handle back composition: C:3.85%, Si:2.78%, Mn:0.35%, S:0.013%, Mg
Residual: 0.041%, RE
Residual: 0.016%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, ferrite content 〉=95%, 150~170/mm of graphite quantity
2
(2) handle ferritic spheroidal graphite cast iron when the molten iron that adopts above-mentioned composition, when treatment condition were constant, the cored-wire parameter and the core material composition that are adopted saw the following form:
Sequence number | The cored-wire title | The cored-wire parameter | Chemical Composition % | The cored-wire add-on | |||||||||
Line footpath mm | Thickness of strips mm | Core agent weight g/m | Heart yearn weight g/m | Sb | RE | Mg | Si | Ba | Core agent add-on g/t | Heart yearn add-on g/t | Heart yearn add-on m/ | ||
1 | The nodularization line | 9 | 0.37 | 120 | 240 | 25 | 50 | 2 | 3840 | 7680 | 32 | ||
2 | The rare earth line | 9 | 0.37 | 120 | 240 | 15 | 3 | 58 | 960 | 1920 | 8 | ||
3 | The antimony alloy line | 9 | 0.35 | 120 | 240 | 20 | 55 | 1440 | 2880 | 12 | |||
4 | Covering line | 13 | 0.42 | 250 | 430 | 65 | 4 | 4500 | 7740 | 18 |
Embodiment eight (2) line feeding order and shared time of each handling procedure see accompanying drawing 11.
The line feeding parameter of being imported sees the following form:
Sequence number | The cored-wire kind | Wire-feeding velocity parameter (m/s) | Line feeding length parameter (m) | The line feeding time (second) | ||
The single line line feeding time | With front overlapping time | The independent shared | ||||
1 | The nodularization line | 21 | 16 | 46 | 0 | 46 |
2 | The rare earth line | 19 | 4 | 13 | 0 | 13 |
3 | The antimony alloy line | 19 | 6 | 19 | 19 | 0 |
4 | Covering line | 19 | 9 | 28.5 | 28.5 | 0 |
Whole line feeding times | 59 |
Result:
Handle back composition: C:3.78%, Si:2.34%, Mn:0.35%, S:0.014%, Mg
Residual: 0.043%, RE
Residual: 0.016%, Sb:0.026%.
The nodularization quality: nodularization rate 〉=90%, the graphite size: 6~7 grades, either pearlite occurred 〉=70%, 150~180/mm of graphite quantity
2
Claims (5)
1. method that adopts multiple cored-wire to carry out molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, it is characterized in that: utilize cored wire technology, the known material that is used for the molten iron processing is carried out sort merge by function, composition adjustment, desulfurization, shielding molten iron interference element, nodularization or wriggling in handling at molten iron, breed, organize each link of orientation, final-sulphur content adjustment, make and the corresponding cored-wire of each processing links, i.e. carbon silicon line, desulfurization line, rare earth line, nodularization or wriggling line, covering line, alloying line and increase the sulphur line; Composition to pending molten iron carries out the rapid detection analysis, weight according to detected result, processing target value and processing molten iron, determine the adding kind of cored-wire and the add-on of every kind of cored-wire, utilize wire-feeding technique will determine that at each processing links of molten iron the cored-wire that adds is fed in the molten iron respectively independently according to handling order then.
2. the multiple cored-wire of employing according to claim 1 carries out the method for molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, it is characterized in that: nodularization and breed two treating processess and adopt nodularization lines and two kinds of cored-wires of covering line to finish, or adopt the nodularization line, breed composite core-spun yarn and finish.
3. the multiple cored-wire of employing according to claim 1 carries out the method for molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, it is characterized in that: in whole line feeding treating processes, the cored-wire kind that is adopted is two or more, wherein to have a kind of cored-wire at least be with nodularization and breed cored-wire, or nodularization, breed the diverse cored-wire of composite core-spun yarn.
4. the multiple cored-wire of employing according to claim 1 carries out the method for molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, it is characterized in that: the line feeding treating processes adopts a multi-thread feeding wire machine to finish in pack processing, or adopts two feeding wire machine to be divided into two processes of pre-treatment and whole processing and finish in induction furnace neutralizing treatment bag respectively.
5. the multiple cored-wire of employing according to claim 1 carries out the method for molten iron process for producing spheroidal graphite cast iron or vermicular cast iron, it is characterized in that: one or more the mode that two or more cored-wire adopts parallel feeding, lapping type feeding and order to feed in three kinds of feeding modes in the process of feeding molten iron is carried out.