CN1736937A - 用高钙灰、脱硫石膏和水泥制成的软土固化剂 - Google Patents

用高钙灰、脱硫石膏和水泥制成的软土固化剂 Download PDF

Info

Publication number
CN1736937A
CN1736937A CNA2005100358883A CN200510035888A CN1736937A CN 1736937 A CN1736937 A CN 1736937A CN A2005100358883 A CNA2005100358883 A CN A2005100358883A CN 200510035888 A CN200510035888 A CN 200510035888A CN 1736937 A CN1736937 A CN 1736937A
Authority
CN
China
Prior art keywords
cement
soft soil
high calcium
curing agent
desulfurated plaster
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2005100358883A
Other languages
English (en)
Other versions
CN100341814C (zh
Inventor
何国荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005100358883A priority Critical patent/CN100341814C/zh
Publication of CN1736937A publication Critical patent/CN1736937A/zh
Application granted granted Critical
Publication of CN100341814C publication Critical patent/CN100341814C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用高钙灰、脱硫石膏和水泥制成的软土固化剂，其特征在于软土固化剂各组分的重量百分比为：高钙灰25％－40％，脱硫石膏10％－25％，生石灰0％－10％，水泥40％－60％。本发明的原料来自发电厂，因是利用废料，且成本非常低廉，性价比要比单用水泥高得多，施工方法简捷方便，质量稳定可靠。

Description

用高钙灰、脱硫石膏和水泥制成的软土固化剂
技术领域
本发明涉及建筑、公路与港口工程用的软土固化剂，特别是用高钙灰、脱硫石膏和水泥制成的软土固化剂，简称HGC型软土固化剂。
背景技术
电厂燃烧亚烟煤产生的高钙灰(high lime fly ash)由于f-CaO的含量较高，且它的水化速度比水泥慢会引起水泥混凝土的安定性的问题，欧洲标准EN450规定，用作混凝土掺合料的粉煤灰中的f-CaO含量不得超过1％，但高钙灰中含有大量高CaO含量的玻璃微珠是一种活性较高的胶凝物质，在有水及CaSO4·2H2O激发剂的作用下，它可以自凝也可以跟软土中的一些活性物质SiO2，Al2O3发生化学反应生成水硬性的C-S-H、C-A-H胶凝。
作为电厂的脱硫工程的副产品，脱硫石膏它细度高，小于32mm的超过60％，PH值为4-6，且它的纯度CaSO4·2H2O含量不低于95％，因此它可直接用作掺合料而省去石膏的研磨程序。
广东珠江三角洲一带软土主要有：①高含水量高压缩性淤泥；②高液限粘土，其主要的矿物成分以伊利石和高岭石，用排水固结处理效果不理想，采用深层水泥搅拌法加固，效果比较理想。因此深层水泥搅拌法现已在广东三角洲一带被广泛使用，但它要消耗大量的水泥，投资成本高，设计为1.2MPa的水泥土桩，水泥掺量为13％-15％，2MPa以上，则水泥掺量为20％以上。高钙灰，脱硫废石膏价格低廉，如果利用它们制成固化剂，减少水泥的用量，降低工程造价，减少废物污染，将有十分重大的现实意义和经济效益。
发明内容
本发明的目的旨在克服现有技术的不足而提供一种造价低廉、变废为宝、质量稳定可靠的用高钙灰、脱硫石膏和水泥制成的软土固化剂。
本发明的目的是这样实现的：
一种用高钙灰、脱硫石膏和水泥制成的软土固化剂，其特征在于软土固化剂各组分的重量百分比为：高钙灰25％-40％，脱硫石膏10％-25％，生石灰0％-10％，水泥40％-60％。
一种用高钙灰、脱硫石膏和水泥制成的软土固化剂的制法，其特征在于湿法是将脱硫石膏、高钙灰、水泥和水在搅拌机中强制搅拌均匀制成一定水灰比的软土固化剂浆体，然后进行喷浆深层搅拌施工；干法是将高钙灰、脱硫石膏和生石灰粉按一定比例混合，进行强制搅拌，打散物料的结团，由生石灰粉的水化反应消除脱硫石膏中的自由水，制成软土固化剂专用掺合料后再加合适比例的水泥经强制搅拌均匀后进行喷粉深层搅拌施工或在专用掺合料的掺合过程中直接添加适量水泥进行强制搅拌均匀再行喷粉深层搅拌施工。
——所述湿法中的水灰比在0.4-0.6。
本发明的突出进步和显著效果是：原料来自发电厂，因是利用废料，且成本非常低廉，性价比要比单用水泥高得多，无侧限抗压强度更高，抗渗性能更好，施工方法简捷方便，质量稳定可靠。
具体实施方式
实施例1：湿法，此时生石灰为0％
取脱硫石膏15kg、高钙灰30kg和水泥50kg，加入48kg水，使水灰比近为0.5在搅拌机中强制搅拌成均匀浆体后即可进行喷浆深层搅拌施工。
实施例2：干法
取5kg生石灰与15kg的脱硫石膏拌合、碾压，让生石灰吸收脱硫石膏中的自由水，强制搅拌后制成专用掺合料，施工前加入50kg水泥粉，强制搅拌均匀后进行喷粉深层搅拌施工。

Claims (3)

1.一种用高钙灰、脱硫石膏和水泥制成的软土固化剂，其特征在于软土固化剂各组分的重量百分比为：高钙灰25％-40％，脱硫石膏10％-25％，生石灰0％-10％，水泥40％-60％。
2.一种用高钙灰、脱硫石膏和水泥制成的软土固化剂的制法，其特征在于湿法是将脱硫石膏、高钙灰、水泥和水在搅拌机中强制搅拌均匀制成一定水灰比的软土固化剂浆体，然后进行喷浆深层搅拌施工；干法是将高钙灰、脱硫石膏和生石灰粉按一定比例混合，进行强制搅拌，打散物料的结团，由生石灰粉的水化反应消除脱硫石膏中的自由水，制成软土固化剂专用掺合料后再加合适比例的水泥经强制搅拌均匀后进行喷粉深层搅拌施工或在专用掺合料的掺合过程中直接添加适量水泥进行强制搅拌均匀再行喷粉深层搅拌施工。
3.根据权利要求2所述的软土固化剂的制法，其特征在于湿法中的水灰比在0.4-0.6。
CNB2005100358883A 2005-07-14 2005-07-14 一种软土固化剂 Expired - Fee Related CN100341814C (zh)