CN1710039A - Anti-scuff agent - Google Patents
Anti-scuff agent Download PDFInfo
- Publication number
- CN1710039A CN1710039A CN 200410019634 CN200410019634A CN1710039A CN 1710039 A CN1710039 A CN 1710039A CN 200410019634 CN200410019634 CN 200410019634 CN 200410019634 A CN200410019634 A CN 200410019634A CN 1710039 A CN1710039 A CN 1710039A
- Authority
- CN
- China
- Prior art keywords
- anion surfactant
- metallic material
- aluminium
- fatty acid
- wear agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
One wear-resistant whose characteristic is: using the basic oil to mix the material capable of producing metal ceramic, tallate stabilizer containing magnesium or aluminum and anion surfactant, among them, calculate according to weight matching, the material that can produce the cermets is 0.00005- 80 share, 0.001- 30 share for saline stabilizer of surface-active agent of anion, 0.00l- 50 share of fatty acid containing magnesium or aluminum. The advantage of this invention is: l. This invention can form cermets layer higher in hardness, lower in coefficient of friction in vain, so can fully play a antifriction role , lengthen mechanical service life . Meanwhile, it can save the fuel of 10- 15%. 2. Performance is good, easy to use.
Description
Affiliated field:
The invention belongs to a kind of additive for lubricant, particularly a kind of anti-wear agent.
Background technology:
At present on the big machinery owing to the effect between multiple friction pair is easy to generate sharp wear, for this reason, must on the basis of lubricating oil, add anti-wear agent to slow down the wearing and tearing of parts, the work-ing life of prolonged mechanical.Though the wear preventive additive that uses can improve the fundamental property of lubricating oil to a certain extent now, make lubricating oil under extreme working conditions, improve fastness to wear effectively, keep lubricity, increase the life-span of lubricating oil, but all have deficiency aspect antiwear property and the serviceability.
Summary of the invention:
Purpose of the present invention just is to provide a kind of anti-wear agent, and this wear preventive additive can improve the lubrication oil antiwear ability effectively and reduce wear, and also has good working performance simultaneously.
Technical scheme of the present invention is: a kind of anti-wear agent, it is characterized in that: make with formulation of base oil by the fatty acid salt stablizer and the anion surfactant that can generate ceramic-metallic material, contain magnesium or aluminium, wherein, calculate according to weight proportion: can to generate ceramic-metallic material be 0.00005-80 part, contain fatty acid salt stablizer 0.001-50 part, anion surfactant 0.001-30 part of magnesium or aluminium.
Above-mentionedly generate ceramic-metallic material and can use following raw materials according separately, also can adopt wherein two or more combination arbitrarily, and with Powdered use: Al
2O
3SiO
2, Ca
2(Mg, Fe)
5Si
8O
22(OH, F)
2, Mg
3(Si
2O
5) (OH)
4, H
4Mg
3Si
2O
9, 3MgO.2SiO
2.2H
2O, MgO, Al
2O
3, ZnO, BN, titanium white, aluminium powder and silicate natural goods, synthetic material.
Above-mentioned anion surfactant can adopt wherein a kind of of primary alcohol sulfate,, secondary alkyl sulfonate, linear alkylbenzene sulfonate and sulfated alkyl ether or any two kinds, two or more combination.
Advantage of the present invention is: 1, the present invention can form the cermet coating that hardness is higher, frictional coefficient is lower at friction surface, therefore can give full play to the effect of antifriction, the work-ing life of prolonged mechanical.Simultaneously, can save the fuel oil of 10-15%.2, functional, easy to use.
Embodiment:
Embodiment 1: can generate ceramic-metallic material---Ca
2(Mg, Fe)
5Si
8O
22(OH, F)
240 kilograms, 50 kilograms of the fatty acid salt stablizers and the anion surfactant-primary alcohol sulfate, that contain magnesium or aluminium are made lubricating oil additive with formulation of base oil for 15 kilograms.
Embodiment 2: can generate ceramic-metallic material---Ca
2(Mg, Fe)
5Si
8O
22(OH, F)
2And Al
2O
3Totally 40 kilograms, contain 50 kilograms of the fatty acid salt stablizers of magnesium or aluminium and anion surfactant-primary alcohol sulfate, and secondary alkyl sulfonate totally 15 kilograms make lubricating oil additive with formulation of base oil.
Embodiment 3: can generate ceramic-metallic material---Al
2O
3, 2 kilograms of MgO, BN, 10 kilograms of fatty acid salt stablizers that contain magnesium or aluminium and 10 kilograms of lubricating oil of making direct use with formulation of base oil of anion surfactant-primary alcohol sulfate.
Embodiment 4: can generate ceramic-metallic material---Ca
2(Mg, Fe)
5Si
8O
22(OH, F)
250 kilograms, contain 30 kilograms of fatty acid salt stablizers and 20 kilograms of lubricating esters of making direct use with formulation of base oil of anion surfactant-primary alcohol sulfate, of magnesium or aluminium.
Claims (3)
1, a kind of anti-wear agent, it is characterized in that: make with formulation of base oil by the fatty acid salt stablizer and the anion surfactant that can generate ceramic-metallic material, contain magnesium or aluminium, wherein, calculate according to weight proportion: can to generate ceramic-metallic material be 0.00005-80 part, contain fatty acid salt stablizer 0.001-50 part, anion surfactant 0.001-30 part of magnesium or aluminium.
2, anti-wear agent according to claim 1 is characterized in that: above-mentionedly generates ceramic-metallic material and can use following raw materials according separately, also can adopt wherein two or more combination arbitrarily, and with Powdered use: Al
2O
3SiO
2, Ca
2(Mg, Fe)
5Si
8O
22(OH, F)
2, Mg
3(Si
2O
5) (OH)
4, H
4Mg
3Si
2O
9, 3MgO.2SiO
2.2H
2O, MgO, Al
2O
3, ZnO, BN, titanium white, aluminium powder and silicate natural goods, synthetic material.
3, anti-wear agent according to claim 1 is characterized in that: above-mentioned anion surfactant can adopt wherein a kind of of primary alcohol sulfate,, secondary alkyl sulfonate, linear alkylbenzene sulfonate and sulfated alkyl ether or any two kinds, two or more combination.