CN1690688A - Method for detecting speed of melting of protecting slag - Google Patents
Method for detecting speed of melting of protecting slag Download PDFInfo
- Publication number
- CN1690688A CN1690688A CNA2004100180640A CN200410018064A CN1690688A CN 1690688 A CN1690688 A CN 1690688A CN A2004100180640 A CNA2004100180640 A CN A2004100180640A CN 200410018064 A CN200410018064 A CN 200410018064A CN 1690688 A CN1690688 A CN 1690688A
- Authority
- CN
- China
- Prior art keywords
- covering slag
- slag
- moment
- weight
- burn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention concerns testing melt temperature method for mold powder used during casting process of molten steel. The testing method is that check the weightlessness curve of mold powder at some temperature, use the moment all burned of free carbon content as the index of melt speed. Use the moment of 1% free carbon content as the inertial melt time and calculate the melt grade for different time. The invention is fit to take testing on the condition that temperature is high than the completeness melt temperature of mold powder, usually can set 1300 Deg. As the free carbon content all is more than 1%, it can be used to all kinds free mold powder. The method is simple, well to recur and with high accuracy.
Description
(1) technical field
The present invention relates to a kind of method that the covering slag burn-off rate of using in the molten steel casting process is measured.
(2) background technology
Covering slag is requisite a kind of auxiliary material in the molten steel casting process, and the quality of its performance directly has influence on slab surface quality, and even the direct motion of production run.Burn-off rate is the main means of control slag layer thickness, slag film uniformity and slag consumption as an important performance indexes of covering slag.Suitable burn-off rate can make covering slag keep certain thickness molten slag layer and slag layer on the molten steel face, thus the effect of the adiabatic heat-insulation of performance covering slag, anti-oxidation, formation uniform slag film and good lubrication.At present the common methods that the covering slag burn-off rate is measured has three kinds of Seger cone or slag post method, crucible method of testing and molten drop methods.First method is that covering slag is shaped, at high temperature judges its fusion process by the variation of shape.Because pressure forming has destroyed original pattern of covering slag, can not reflect the true pre-arcing characterisitics of covering slag truely and accurately, and the subjective factor that shape is judged is bigger, reappearance is relatively poor; Second method is that covering slag is added certain thickness amount in crucible, at high temperature keep certain hour after, take out also and dissect, judge burn-off rate by measuring slag layer, sinter layer, melting layer thickness.Because the sealing of crucible, the carbon in the covering slag can not be burnt well, therefore is difficult to form desirable stratification state, reduces addition and can't distinguish each layer thickness again.This method also is subjected to the influence of subjective factor bigger; The third method is that covering slag is added in the funnel container of graphite system, and the melt cinder that flows out by weighing drips the burn-off rate that characterizes covering slag.By contrast, this method can be simulated being heated, melting of covering slag and consumption behavior preferably, but greatest problem is the oxygen supply wretched insufficiency, makes covering slag can not melt for a long time, and the continuity extreme difference of molten drop outflow.
(3) summary of the invention
The object of the present invention is to provide a kind of detection method of covering slag burn-off rate, this detection method has solved present covering slag does not still have quantitative and simple and reliable detection method.This detection method is utilized the fusing mechanism of covering slag, reflects the burn-off rate of covering slag by the scaling loss situation that detects free carbon in the covering slag.This detection method is simple, favorable reproducibility, precision height.
The detection method of covering slag burn-off rate of the present invention follows these steps to realize:
(1) high temperature furnace is risen to temperature more than the complete temperature of fusion of covering slag, and constant temperature;
(2) crucible that will fill a certain amount of covering slag is placed on the balance support that stretches in the burner hearth;
(3) by computing machine the balance data are sampled;
(4) disposal data, and draw the weight-time chart of covering slag weightlessness;
(5) second flex point moment corresponding of weight-loss curve t
2For weighing the index of covering slag burn-off rate.
The detection method of above-mentioned covering slag burn-off rate describedly rises to 1300 ℃ as probe temperature with high temperature furnace.
The detection method of above-mentioned covering slag burn-off rate, described weight-time chart from covering slag weightlessness is determined the fusing degree D of the covering slag of arbitrary moment t correspondence, and promptly liquid phase accounts for the ratio of total quantity of slag, and calculating formula is:
In the formula: t
iFor covering slag begins fusing constantly, promptly carbon content is moment of 1% in the covering slag, W
iBe t
iCorresponding weight of the moment, t
2For carbon materials burnouts constantly, W
2Be t
2Corresponding weight of the moment, W is a t corresponding weight constantly.
Principle of work of the present invention is to have studied the effect of carbon materials in covering slag, has proposed under the condition that is higher than the covering slag temperature of fusion, and the covering slag weight-loss curve that adopts weight-loss method to record can reflect its burn-off rate.Because as an important component part of covering slag, its function is to serve as skeleton function in slag to carbon materials (carbon black, graphite etc.), the gathering that stops melt cinder to drip, thus play the effect that the control covering slag melts.Because the carbon materials fusing point is high and with slag good not wellability is arranged, have only when carbon materials progressively after the oxidation, melt cinder drips and could assemble mutually, and then forms liquid slag layer.Therefore, the scaling loss speed of carbon has directly reflected the fusing process of covering slag in the slag.
Analyze from the weightless synoptic diagram of covering slag shown in Figure 1,1., 2., 3. number in the figure represents weightless three phases, W respectively
0Be initial weight, t
1Be the moment that the phase one finishes, corresponding weight is W
1t
2Be the moment that subordinate phase finishes, corresponding weight is W
2t
iFor carbon content in the slag is moment of 1%, corresponding weight is W
iW
fIntersection point for weightless extended line of subordinate phase and ordinate; W
sIntersection point for weightless extended line of phase III and ordinate.Phase one is mainly the decomposition scaling loss process of moisture in the slag, cementing agent and carbonate; Subordinate phase is mainly the oxidization burning loss process of carbon materials in the slag; Phase III is the volatiling reaction process of covering slag base-material.Simultaneously carbon materials phase one, covering slag first, second stage also with corresponding weightless process, therefore the intersection point by second, third stage extended line and ordinate can get the weight loss in each stage.In Fig. 1, W
0-W
fBe the scaling loss weight of moisture, cementing agent and carbonate etc. in the slag, W
f-W
sBe the scaling loss weight of carbon materials, t
2For carbon materials burnouts constantly, this moment, covering slag melted fully, therefore can use t
2Weigh the burn-off rate of covering slag.
Covering slag is at t
2Fusing fully constantly, its begin fusing constantly for free carbon content in the slag 1% o'clock moment corresponding because when carbon content is less than 1% in the slag, the gathering that carbon can't stop melt cinder to drip.At t
iCorresponding W of the moment
i, consider W
iIn contain the volatile quantity of covering slag base-material, actually should get W
nPoint makes W
nG
iBe parallel to W
sG
2If satisfy (W
n-W
s)/W
0=1%, can think t
iBe the moment that covering slag begins to melt.Be less than t when the time
iThe time, covering slag keeps powder attitude or sintered state, surpasses t when the time
iThe time, covering slag begins fusing.At t
i~t
2The calculating formula of the fusing degree D of the covering slag of interior a certain moment t correspondence can be expressed as:
W is the corresponding constantly gravimetric value of t in the formula.
The physical significance of covering slag fusing degree D is the ratio that liquid phase accounts for total quantity of slag.
By geometrical similarity principle, can be descended equation:
With (1), (2) in conjunction with cancellation W
n, can get
If the volatile quantity of covering slag base-material seldom, can be similar to and think W
s=W
2, (3) formula can further be reduced to
The calculating formula of fusing degree D that can determine the covering slag of arbitrary moment t correspondence thus is:
The detection method of covering slag burn-off rate of the present invention is to determine burn-off rate by the weight-loss curve that detects covering slag, is characterized in:
(1) with carbon scaling loss end of a period moment t
2The burn-off rate that reflects covering slag.t
2Big more, the burn-off rate of covering slag is slow more.
(2) begin fusing constantly for it during carbon content scaling loss to 1% in the covering slag.
(3) if when the volatile quantity of covering slag base-material can be ignored, the available formula of its fusing degree (5) is calculated.Otherwise at t
i~t
2The scope domestic demand is calculated with formula (3).
(4) the present invention is applicable to that free carbon content is greater than 1% covering slag.
(5) Applicable temperature scope of the present invention need be higher than the complete temperature of fusion of covering slag, and temperature of fusion is usually less than 1100 ℃ fully.
(6) be the comparison between the convenient different covering slags, probe temperature can be fixed as 1300 ℃, and this temperature is commonly referred to be near the temperature the crystallizer meniscus.
Generally speaking, take 1300 ℃ of probe temperature conditions, to arrive t
2The moment of point can be weighed the burn-off rate between the different covering slags.
The detection method of covering slag burn-off rate is to utilize the fusing mechanism of covering slag, reflects the burn-off rate of covering slag by the scaling loss situation that detects free carbon in the covering slag.In the Range of measuring temp that is suitable for, by naked-eye observation to the analyzing and testing result of covering slag fusing situation and this method fit like a glove, warp compares test to tens of routine finished product protection slags, error is all the time in range of control.This detection method is simple, favorable reproducibility, precision height.
(4) description of drawings
The present invention is described in detail below in conjunction with accompanying drawing.
Fig. 1 is the weightless synoptic diagram of covering slag;
Fig. 2 is the weightless synoptic diagram of the covering slag of embodiment 1;
Fig. 3 is the weightless synoptic diagram of the covering slag of embodiment 2.
Among the figure: 1., 2., 3. represent weightless three phases respectively,
W
0Be initial weight,
t
1Be the moment that the phase one finishes, corresponding weight is W
1
t
2Be the moment that subordinate phase finishes, corresponding weight is W
2
t
iFor carbon content in the slag is moment of 1%, corresponding weight is W
i
W
fIntersection point for weightless extended line of subordinate phase and ordinate;
W
sIntersection point for weightless extended line of phase III and ordinate.
(5) embodiment
Embodiment 1:
Referring to Fig. 2, it is that 5.000g free carbon content is 3.2% the weight-loss curve of a kind of covering slag under 1300 ℃.As shown in Figure 2, curve subordinate phase and phase III intersection point G
2Be covering slag and melt constantly t fully
2=256s.Other each point W
2=4.584g, W
f=4.761g, W
s=4.595g calculates free carbon content thus and is
With chemical analysis value 3.2% error be 3.75%.W
2With W
sBetween the relative carbon content of error be 6.9%.Free carbon content is 1% o'clock G in the further reckoning slag
iThe corresponding W of point
i=4.645g, t
i=151s.As seen from the figure, surpass G
iAfter the point, curvature of curve changes gradually to some extent, and this has proved that also covering slag is lower than at 1% o'clock at free carbon content, and melt cinder drips and begins to assemble gradually and produce liquid phase.When time during less than 151s, because the skeleton function of free carbon, covering slag is solid-state or sintered state, and after the time surpassed 256s, covering slag melted fully, and between 151~256s, available (3) formula or (4) formula are calculated its fusing degree.Weight as covering slag when the 200s is 4.620g, and substitution (3) formula gets
Calculate with the simplification of (4) formula
Embodiment 2:
Fig. 3 is that 5.000g free carbon content is 12.9% the weight-loss curve of a kind of covering slag under 1300 ℃.By scheme the complete fusing time t of this covering slag
2=1031s.The covering slag of burn-off rate in the embodiment 1.The value of other respective points is: W
f=4.716g, W
s=4.124g, W
2=4.088g.Free carbon content is 11.84% in the slag that calculates thus, with assay value deviation-8.2%.From the subordinate phase of weight-loss curve as can be known, early stage, weightless slope was a little more than the slope of extended line, the therefore W that gets by extended line
fValue must be more on the low side than actual value.But this does not influence t
2The accuracy of point can be to W yet
iThe reckoning of point brings error.
W
i=W
s+W
0×1%=4.124+5.000×1%=4.174
Because t
2Point is far away apart from initial point, so W
2Point must depart from W
sPoint, should not adopt shortcut calculation this moment.
Claims (3)
1. the detection method of a covering slag burn-off rate is characterized in that being undertaken by following operation steps:
(1) high temperature furnace is risen to the above temperature of the complete temperature of fusion of covering slag, and constant temperature;
(2) crucible that will fill a certain amount of covering slag is placed on the balance support that stretches in the burner hearth;
(3) by computing machine the balance data are sampled;
(4) disposal data, and draw the weight-time chart of covering slag weightlessness;
(5) second flex point moment corresponding of weight-loss curve t
2For weighing the index of covering slag burn-off rate.
2. the detection method of covering slag burn-off rate according to claim 1 is characterized in that high temperature furnace is risen to 1300 ℃ as probe temperature.
3. the detection method of covering slag burn-off rate according to claim 1 is characterized in that determining from the weight-time chart of covering slag weightlessness the fusing degree D of the covering slag of arbitrary moment t correspondence, and promptly liquid phase accounts for the ratio of total quantity of slag, and calculating formula is:
In the formula: t
iFor covering slag begins fusing constantly, promptly carbon content is moment of 1% in the covering slag, W
iBe t
iCorresponding weight of the moment, t
2For carbon materials burnouts constantly, W
2Be t
2Corresponding weight of the moment, W is a t corresponding weight constantly.