CN1660714A - 新型砌筑干粉 - Google Patents
新型砌筑干粉 Download PDFInfo
- Publication number
- CN1660714A CN1660714A CN2004100100735A CN200410010073A CN1660714A CN 1660714 A CN1660714 A CN 1660714A CN 2004100100735 A CN2004100100735 A CN 2004100100735A CN 200410010073 A CN200410010073 A CN 200410010073A CN 1660714 A CN1660714 A CN 1660714A
- Authority
- CN
- China
- Prior art keywords
- dry powder
- percent
- waterproof
- auxiliary material
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种新型砌筑干粉，属建设建筑领域，用于工程砌筑与抹面或道路基层施工、水利工程、矿井塌陷处理等。它主要由以下成分原料按一定重量分数配比而成；粉煤灰60％～90％，赤泥5％～10％，激活剂0.3％～1.0％，石灰，4％～12％，石膏，2％～8％，早强剂0.3％～1.0％；直接销售或与砂干混拌销售均可，能满足砂浆的强度及和易性要求。其组分主要为大宗固体废弃物－粉煤灰、赤泥、建筑垃圾等，与激活剂、辅料混合磨细至0.044mm筛筛余8％。为建设建筑业提供了一种价格低、性能稳定的新型胶凝材料。
Description
技术领域：
本发明涉及一种建筑材料，尤其是利用大宗固体废弃物—粉煤灰、赤泥、建筑垃圾等非高温法生产的新型砌筑干粉。
背景技术：
建设建筑工程中，建筑砂浆现场配置存在有质量不稳定、工作性不良、成本高的缺陷，导致砌筑施工速度慢、砌体质量差，并使结构抗震性能受到影响。此外，砂子、石灰、水泥露天现场堆放及其现场混拌，造成材料本身的相互污染和环境的的污染，影响了建筑企业的文明施工水平。
发明内容：
本发明的目的是提供以大宗固体废弃物—粉煤灰、赤泥、建筑垃圾为主非高温法生产建设建筑用新型砌筑干粉的技术，使我国每年工业生产和城镇建设产生的固体废弃物能够得到充分利用。
本发明的技术方案为：一种新型砌筑干粉，它主要由以下成分原料按一定重量分数配比而成；粉煤灰60％～90％，赤泥5％～10％，激活剂0.3％～1.0％，石灰4％～12％，石膏2％～8％，早强剂0.3％～1.0％。
它还含有下列成分；建筑垃圾1％～20％；熟料或普通硅酸盐水泥1％～10％。
它还含有下列加气辅料中的一种，加气辅料为热聚物皂化剂、碳化钙、次氯酸钙、偶氮二异丁腈，偶氮二甲酰胺、磺酰肼化合物，N，N’-二亚硝五亚甲基四胺、聚氨基甲酸乙酯、十二烷基苯磺酸盐、脂肪酸钠、热脱水沸石、二辛基磺化琥珀酸盐；加气辅料用于配合比中重量分数为0.2～4％。
它还含有下列塑化防水辅料中的一种，塑化防水辅料为硫铝酸盐、碳酸盐、铁盐、氟硅酸盐；塑化防水辅料用于配合比中重量分数为0.2～4％。
本发明是为了适应现代化施工技术和质量管理水平而发明的，可工厂化配制干拌砂浆或泵送商品砂浆，或在工地与砂混配加水搅拌，制成工程所需的建筑砂浆。砌筑干粉制备建筑砂浆，配比合理，流动性好，粘聚性强，保水性好，硬化后强度高，粘结力大，对提高砌体的砌筑质量有决定性的意义。尤其适于高强混凝土砌块、新型墙体材料使用，具有方便、环保、大量利用固体废弃物、消除城市污染、降低材料成本、提高施工质量进度的优点。
本发明是以大宗固体废弃物—粉煤灰、赤泥、建筑垃圾等为主要原料，辅以石灰、石膏、无机矿物(如蛋白石)及少量水硬性材料等组成的细磨混合物，并可根据工程需要加入适量加气剂、塑化剂、防水剂等外加剂。
本发明具有材料来源广泛，价格低廉，应用面广，市场潜力大，产品与现代化施工技术和质量管理水平相适应，确保砌体砌筑质量，具有方便、高性能、环保、消除城市污染、降低施工造价、提高质量进度等优点。
具体实施方式
将粉煤灰、赤泥、建筑垃圾(干状可直接使用，湿状需干燥)与激活剂、早强剂、石灰、石膏(磷石膏、氟石膏亦可)，比例混匀，经锤式或颚式破碎机粗碎，对辊中碎，雷蒙磨细碎，球磨机磨细至0.044mm筛筛余8％，即成为本发明新型砌筑干粉，其标号与砌筑水泥对比可达12.5MPa～32.5MPa，且粘聚性强，流动性好，保水性好，粘结力大。硬化后强度高，使用方便，成本低廉，性能稳定。
本发明的配合比(重量分数)：
粉煤灰： 60％～80％
赤 泥： 5％～10％
建筑垃圾： 0％～20％
激活剂： 0.3％～1.0％
石 灰： 4％～12％
石 膏： 2％～8％
熟料或普通硅酸盐水泥： 0％～10％
早强剂： 0.3％～1.0％
如需含有加气、塑化、防水等功能，亦可加入热聚物皂化剂、碳化钙、次氯酸钙、偶氮二异丁腈，偶氮二甲酰胺、磺酰肼化合物，N，N’-二亚硝五亚甲基四胺、聚氨基甲酸乙酯、十二烷基苯磺酸盐、脂肪酸钠、热脱水沸石、二辛基磺化琥珀酸盐、铝粉、硫铝酸盐、碳酸盐、铁盐、氟硅酸盐等外加剂组成。其用于配合比中重量分数为0.2～4％。
本发明的基本原理：
本发明新型砌筑干粉水化时，液相被Ca(OH)2所饱和，液相中PH值增高，反应生成Ca(OH)2水化铝(铁)酸钙和水化硅酸钙凝胶等水化物，它们初步表现强度。
粉煤灰、赤泥、建筑垃圾等是经高温煅烧或烧结后的硅铝质为主的大宗固体废弃物，这些具有活性的SiO2，Al2O3，钙铁共熔体和碱性激发剂进行二次反应形成以水化硅酸钙为主体的水化产物，反应式：
所形成的水化硅酸钙与熟料矿物C3S(硅酸三钙)C2S(硅酸二钙)水化后的产物基本相同，有着良好的胶凝作用，常温下废弃物颗粒和Ca(OH)2反应缓慢，二次反应对早期强度影响不大，降低了液相碱度，又促进了混合料和水的反应。随着二次反应的深入，胶凝物质和水化晶体也不断增多，凝聚结构的强度也不断提高。这样Ca(OH)2、水化硫铝酸钙、水化硅酸钙的晶体及呈胶结状态的含水硅酸钙、水化铁铝酸钙等无定形体从各颗粒向外伸展逐渐形成一个连续的网状结构并不断密实化，在宏观上表现出良好的物理力学性能。
实施例1：
粉煤灰： 75％
赤 泥： 10％
激活剂： 0.5％
石 灰： 8％
石 膏： 6％
早强剂： 0.5％
实施例2：
粉煤灰： 65％
赤 泥： 10％
建筑垃圾：10％
激活剂： 0.5％
石 灰： 8％
石 膏： 3％
熟 料： 3％
早强剂： 0.5％
实施例3：
粉煤灰： 71.9％
赤 泥： 7％
激活剂： 0.5％
石 灰： 12％
石 膏： 5％
42.5普通硅酸盐水泥： 3％
早强剂： 0.5％
聚氨基甲酸乙酯： 0.1％
实施例4：
粉煤灰： 71.9％
赤 泥： 7％
激活剂： 0.5％
石 灰： 12％
石 膏： 5％
42.5普通硅酸盐水泥： 3％
早强剂： 0.5％
铁 盐： 0.1％
Claims (4)
1一种新型砌筑干粉，其特征是：它主要由以下成分原料按一定重量分数配比而成；粉煤灰60％～90％，赤泥5％～10％，激活剂0.3％～1.0％，石灰4％～12％，石膏2％～8％，早强剂0.3％～1.0％。
2、根据权利要求1所述的新型砌筑干粉，其特征是：它还含有下列成分；建筑垃圾1％～20％；熟料或普通硅酸盐水泥1％～10％。
3、根据权利要求1所述的新型砌筑干粉，其特征是：它还含有下列加气辅料中的一种，加气辅料为热聚物皂化剂、碳化钙、次氯酸钙、偶氮二异丁腈，偶氮二甲酰胺、磺酰肼化合物，N，N’-二亚硝五亚甲基四胺、聚氨基甲酸乙酯、十二烷基苯磺酸盐、脂肪酸钠、热脱水沸石、二辛基磺化琥珀酸盐；加气辅料用于配合比中重量分数为0.2～4％。
4、根据权利要求1所述的新型砌筑干粉，其特征是：它还含有下列塑化防水辅料中的一种，塑化防水辅料为硫铝酸盐、碳酸盐、铁盐、氟硅酸盐；塑化防水辅料用于配合比中重量分数为0.2～4％。