CN1644793A - Super-coating material for sand paper and production thereof - Google Patents
Super-coating material for sand paper and production thereof Download PDFInfo
- Publication number
- CN1644793A CN1644793A CN 200510018118 CN200510018118A CN1644793A CN 1644793 A CN1644793 A CN 1644793A CN 200510018118 CN200510018118 CN 200510018118 CN 200510018118 A CN200510018118 A CN 200510018118A CN 1644793 A CN1644793 A CN 1644793A
- Authority
- CN
- China
- Prior art keywords
- component
- super
- coating material
- sand paper
- perhaps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A super coating material for adhesive paper is prepared from components A, B and C through preparing component A from adhesive and solvent, preparing component B from heat absorbent, filler and solvent, preparing component C from solvent, proportionally mixing A with B, stirring, proportionally adding C and stirring. Its advantages are low drying temp and high heat dissipating effect.
Description
Technical field
The present invention relates to material field, particularly a kind of super-coating material for sand paper and preparation method thereof.
Background technology
In the grinding materials and grinding tool industry, sand paper is a kind of milling tools that is widely used.Advantages such as the sand paper of different model has the scope of application extensively, conveniently, and is cheap.But when soft materials such as use sand papering timber, paint, soft metal, general sand paper tends to occur by the chip phenomenon of blocking.
Summary of the invention
Technical problem to be solved by this invention is: a kind of super-coating material for sand paper and preparation method thereof is provided.This super-coating material has the anti-clogging function, thereby can overcome above-mentioned the deficiencies in the prior art.
The technical solution adopted for the present invention to solve the technical problems is: super-coating material for sand paper is formed by first, the second and the third component mixed preparing, and the weight proportion of each component is 100: 200~350: 5~70; The first component is made up of adhesive 10~35% and solvent 65~90%; The second component is made up of heat absorbent 25~40%, filler 20~30% and solvent 30~55%; Third component is a solvent.
The preparation process of super-coating material for sand paper comprises:
(1) preparation of first component: with adhesive 10~35% and solvent 65~90%, pour in the reactor successively, and stir, mix and get final product while pour into.
(2) preparation of second component: with heat absorbent 25~40%, filler 20~30% and solvent 30~55%, pour in the reactor successively, and stir, mix and get final product while pour into.
(3) mixed preparing: be 100: 200~350 mixed preparing by weight with first, the second component that makes, stir that add the third component mixed preparing again, stirring promptly gets super-coating material for sand paper earlier.
Adhesive in the above-mentioned first component is: polyvinyl alcohol, polyethylene glycol, epoxy resin, white glue with vinyl, polyvinyl acetate-ethylene copolymer, polyvinyl acetate, polyvinyl acetate, polyimides, polyacrylamide, neutral dimer acid polyamide resin, N, in N-methylene-bisacrylamide, polyamide, methyl acrylate, methyl methacrylate and the benzoyl peroxide two kinds, perhaps two or more mixtures.
Filler in the above-mentioned second component is: a kind of in talcum powder, titanium dioxide, zinc stearate, calcium stearate, dolomol, odium stearate, aluminum stearate, boron nitride, aerosil, magnesia, calcium oxide, molybdenum bisuphide, mica powder, melamine cyanurate complex compound, potassium borate, Boratex, calcirm-fluoride, boron fluoride, boron chloride, chromium chloride, calcium iodide and the lead iodide, perhaps two kinds, perhaps two or more mixtures.
Above-mentioned third component is a solvent, and its addition is 5~70 by weight.
The solvent in first, the second component and third component are: a kind of in methyl alcohol, ethanol, ethylene glycol, toluene, acetone, solvent naphtha, styrene and the carbon tetrachloride, perhaps two kinds, perhaps two or more mixtures.
Super-coating material is meant in coated abrasive surface and promptly adds the special anti-clogging material of one deck that is coated with at carborundum or corundum sand paper surface.The sand paper that forms with this material is different from common sand paper, its operation principle is to utilize the special anti-clogging material that applies, when grinding produces a large amount of heat energy, make the heat absorption material of its inside take place to change mutually, states of matter is by the solid-state liquid state that changes into, thereby plays the effect that absorbs heat energy, reduces workpiece surface temperature; The material that absorbs heat simultaneously takes place to change the back mutually and form lubricating film on the surface of sand paper, has therefore also improved the ABRASION RESISTANCE and the grinding efficiency of sand paper.
Super-coating material for sand paper provided by the invention owing to adopted suitable adhesive, heat absorbent, filler and solvent system, causes the super coating sand paper made from this material to have many advantages, and mainly contain: surface drying is fast under the middle temperature, and low temperature is surface drying fully also; Be convenient to operation; Furfur during use, heat radiation, be difficult for stopping up effective; Be specially adapted to the soft material for example dry grinding and the polishing of materials such as timber, paint, soft metal; Also improved simultaneously the anti-wear performance of sand paper.
The specific embodiment
The present invention is a kind of super-coating material for sand paper and preparation method thereof.
One. super-coating material for sand paper
This material is formed by first, the second and the third component mixed preparing, and the weight proportion of each component is 100: 200~350: 5~70.The first component is made up of adhesive 10~35% and solvent 65~90%.The second component is made up of heat absorbent 25~40%, filler 20~30% and solvent 30~55%.Third component is a solvent.
Adhesive in the above-mentioned first component is: polyvinyl alcohol, polyethylene glycol, epoxy resin, white glue with vinyl, polyvinyl acetate-ethylene copolymer, polyvinyl acetate, polyvinyl acetate, polyimides, polyacrylamide, neutral dimer acid polyamide resin, N, a kind of in N-methylene-bisacrylamide, polyamide, methyl acrylate, methyl methacrylate and the benzoyl peroxide, perhaps two kinds, perhaps two or more mixtures.
Heat absorbent in the above-mentioned second component is: a kind of in boron, dolomite, sand, clay, lead, calcium carbonate, carborundum, schmigel, garnet and the glass sand, perhaps two kinds, perhaps two or more mixtures.
Filler in the above-mentioned second component is: a kind of in talcum powder, titanium dioxide, zinc stearate, calcium stearate, dolomol, odium stearate, aluminum stearate, boron nitride, aerosil, magnesia, calcium oxide, molybdenum bisuphide, mica powder, melamine cyanurate complex compound, potassium borate, Boratex, calcirm-fluoride, boron fluoride, boron chloride, chromium chloride, calcium iodide and the lead iodide, perhaps two kinds, perhaps two or more mixtures.
The solvent and third component in above-mentioned first, the second component are: a kind of in methyl alcohol, ethanol, ethylene glycol, toluene, acetone, solvent naphtha, styrene and the carbon tetrachloride, perhaps two kinds, perhaps two or more mixtures.
Two. the preparation method of super-coating material for sand paper
Super-coating material for sand paper is formed by above-mentioned first, the second and the third component mixed preparing, and its step comprises:
(1) preparation of first component: with adhesive 10~35% and solvent 65~90%, pour in the reactor successively, and stir, mix and get final product while pour into.
(2) preparation of second component: with heat absorbent 25~40%, filler 20~30% and solvent 30~55%, pour in the reactor successively, and stir, mix and get final product while pour into.
(3) mixed preparing: be 100: 200~350 mixed preparing by weight with first, the second component that makes, stir that adding third component again is 5~70 mixed preparing by weight earlier, stirring promptly gets super-coating material for sand paper.
The using method of super-coating material: when normally using, can be in the first component: the second component: the use that stirs of the ratio of third component=100: 200~350: 5~70.Wherein, first component: second component: third component=100: 230~320: 15~55 are preferred value.The first component is made up of adhesive 15~25% and solvent 75~85%.The second component is made up of heat absorbent 25~35%, filler 20~30% and solvent 35~55%.
Super-coating material for sand paper, it in the coating processes condition on the sand paper is: just do on 8~12min surface under 60 ℃ the condition, solidifies fully behind 1.8~2.2h.If wish that hardening time, the longer or shorter consumption that increases adhesive that subtracts was regulated, can not influence intensity and other effect of curing, simple and convenient.
The invention will be further described below in conjunction with instantiation.
Embodiment 1: with the polyvinyl acetate-ethene 20% of first component, ethanol 80% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 30% of second component, titanium dioxide 25%, ethanol 45% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 250.
Embodiment 2: with the polyvinyl acetate-ethene 15% of first component, ethanol 85% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 35% of second component, titanium dioxide 25%, ethanol 40% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 250.
Embodiment 3: with the polyvinyl acetate-ethene 35% of first component, ethanol 65% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 32% of second component, titanium dioxide 23%, ethanol 45% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 260.
Embodiment 4: with the polyvinyl acetate-ethene 22% of first component, ethanol 78% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 28% of second component, titanium dioxide 20%, ethanol 52% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 275.
Embodiment 6: with the polyvinyl acetate-ethene 10% of first component, ethanol 90% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 40% of second component, titanium dioxide 30%, ethanol 30% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 200.
Embodiment 7: with the polyvinyl acetate-ethene 22% of first component, ethanol 78% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the calcium carbonate 25% of second component, titanium dioxide 20%, ethanol 55% adds in the reactor successively, pours into while stirring when pouring into, and it is mixed; With the mixed of first, second component, stir then, add toluene, be adjusted to suitable viscosity and promptly get super-coating material by proportioning by 100: 350.
Claims (8)
1. super-coating material for sand paper, it is characterized in that: super-coating material for sand paper is formed by first, the second and the third component mixed preparing, and the weight proportion of each component is 100: 200~350: 5~70; The first component is made up of adhesive 10~35% and solvent 65~90%; The second component is made up of heat absorbent 25~40%, filler 20~30% and solvent 30~55%; Third component is a solvent.
2. super-coating material for sand paper according to claim 1, it is characterized in that the adhesive in the first component is: polyvinyl alcohol, polyethylene glycol, epoxy resin, white glue with vinyl, polyvinyl acetate-ethylene copolymer, polyvinyl acetate, polyvinyl acetate, polyimides, polyacrylamide, neutral dimer acid polyamide resin, N, a kind of in N-methylene-bisacrylamide, polyamide, methyl acrylate, methyl methacrylate and the benzoyl peroxide, perhaps two kinds, perhaps two or more mixtures.
3. super-coating material for sand paper according to claim 1, it is characterized in that the heat absorbent in the second component is: a kind of in boron, dolomite, sand, clay, lead, calcium carbonate, carborundum, schmigel, garnet and the glass sand, perhaps two kinds, perhaps two or more mixtures.
4. super-coating material for sand paper according to claim 1, it is characterized in that the filler in the second component is: a kind of in talcum powder, titanium dioxide, zinc stearate, calcium stearate, dolomol, odium stearate, aluminum stearate, boron nitride, aerosil, magnesia, calcium oxide, molybdenum bisuphide, mica powder, melamine cyanurate complex compound, potassium borate, Boratex, calcirm-fluoride, boron fluoride, boron chloride, chromium chloride, calcium iodide and the lead iodide, perhaps two kinds, perhaps two or more mixtures.
5. super-coating material for sand paper according to claim 1, it is characterized in that the solvent and third component in first, the second component are: a kind of in methyl alcohol, ethanol, ethylene glycol, toluene, acetone, solvent naphtha, styrene and the carbon tetrachloride, perhaps two kinds, perhaps two or more mixtures.
6. the preparation method of a super-coating material for sand paper is characterized in that super-coating material for sand paper is formed by first, the second and the third component mixed preparing, and its preparation process comprises:
(1) preparation of first component: with adhesive 10~35% and solvent 65~90%, pour in the reactor successively, and stir, mix and get final product while pour into,
(2) preparation of second component: with heat absorbent 25~40%, filler 20~30% and solvent 30~55%, pour in the reactor successively, and stir, mix and get final product while pour into,
(3) mixed preparing: be 100: 200~350 mixed preparing by weight with first, the second component that makes, stir that add the third component mixed preparing again, stirring promptly gets super-coating material for sand paper earlier,
Adhesive in the above-mentioned first component is: polyvinyl alcohol, polyethylene glycol, epoxy resin, white glue with vinyl, polyvinyl acetate-ethylene copolymer, polyvinyl acetate, polyvinyl acetate, polyimides, polyacrylamide, neutral dimer acid polyamide resin, N, in N-methylene-bisacrylamide, polyamide, methyl acrylate, methyl methacrylate and the benzoyl peroxide two kinds, perhaps two or more mixtures
Filler in the above-mentioned second component is: a kind of in talcum powder, titanium dioxide, zinc stearate, calcium stearate, dolomol, odium stearate, aluminum stearate, boron nitride, aerosil, magnesia, calcium oxide, molybdenum bisuphide, mica powder, melamine cyanurate complex compound, potassium borate, Boratex, calcirm-fluoride, boron fluoride, boron chloride, chromium chloride, calcium iodide and the lead iodide, perhaps two kinds, perhaps two or more mixtures
Above-mentioned third component is a solvent, and its addition is 5~70 by weight,
The solvent in first, the second component and third component are: a kind of in methyl alcohol, ethanol, ethylene glycol, toluene, acetone, solvent naphtha, styrene and the carbon tetrachloride, perhaps two kinds, perhaps two or more mixtures.
7. the preparation method of super-coating material for sand paper according to claim 6 is characterized in that first, the second of super-coating material for sand paper and the weight proportion of third component are 100: 230~320: 15~55; The first component is made up of adhesive 15~25% and solvent 75~85%; The second component is made up of heat absorbent 25~35%, filler 20~30% and solvent 35~55%.
8. according to the preparation method of claim 6 or 7 described super-coating material for sand paper, it is characterized in that super-coating material for sand paper, it in the coating processes condition on the sand paper is: just do on 8~12min surface under 60 ℃ the condition, solidifies fully behind 1.8~2.2h.