CN1637045A - Prepn of single-component high-hardness silicone glass resin - Google Patents
Prepn of single-component high-hardness silicone glass resin Download PDFInfo
- Publication number
- CN1637045A CN1637045A CN 200410089351 CN200410089351A CN1637045A CN 1637045 A CN1637045 A CN 1637045A CN 200410089351 CN200410089351 CN 200410089351 CN 200410089351 A CN200410089351 A CN 200410089351A CN 1637045 A CN1637045 A CN 1637045A
- Authority
- CN
- China
- Prior art keywords
- glass resin
- silicone glass
- silicone
- resin
- performed polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation process of single-component high hardness silicone glass resin includes the following steps: dissolving single substance silicon to prepare nanometer silica dispersing liquid; mixing nanometer silica dispersing liquid, methyl trialkoxyl silane, acetic acid and water in the volume ratio of 3.00-8.00 to 5.26-12.00 to 0.05-1.50 to 0.02-1.50 through stirring and sealing to obtain silicone glass resin pre-polymer; diluting the pre-polymer with isopropanol via stirring, filtering and adding polyether silicone oil to obtain the single-component silicone glass resin. The single-component silicone glass resin may be cured to form transparent smooth film with pencil hardness not lower than 7H.
Description
Technical field
The present invention relates to the technology of preparing of the silicone glass resin of single component use, do not need to add solidifying agent when specifically being meant plated film, can obtain the preparation method of the mono-component organic silicone glass resin of film of high hardness after the curing.
Background technology
Silicone glass resin is the highly cross-linked polysiloxane that is formed through hydrolytie polycondensation by the polyfunctional group organosilane, and it solidifies the back outer appearnce like glass, so claim glass resin.By spraying; dip-coating; methods such as roller coat are after matrix is coated silicone glass resin; can obtain having hard, clear after the heating baked and cured; the film of good insulation preformance; this film has heat-resisting; rub resistance; ageing-resistant; radiation hardness; not embrittlement of low temperature; hydrophobic; moistureproof; nontoxic; advantages such as transmittance is strong; can be used as glass; synthetic glass; polycarbonate; the acrylic acid series plastics; camera lens; cowl on aircraft and the automobile; the imitation gold process product; metallized plastic; playing card; the transparent protective coating of senior magazine etc.; can also be used to improve the optical property of transparent plastics, as the insulation of electrical and electronic component and moisture barrier coatings etc.
Common silicone glass resin normally joins ethanol with Union carbide A-162 or methyltrimethoxy silane, water, in the mixed solution of hydrochloric acid, under the reflux condition, make Union carbide A-162 or methyltrimethoxy silane generation hydrolysis condensation reaction and make, the solidifying agent that often needs to add the price comparison costliness when using common silicone glass resin, the pencil hardness of the film of gained also only reaches 2H-3H after being heating and curing, but behind the adding solidifying agent, glass resin very easily generates gel, have only a few hours the work-ing life under the room temperature, the glass resin that does not use for the adding solidifying agent then will add stopper, and notes sealing up for safekeeping to prolong digestion time.Just because of this, common silicone glass resin not only uses inconvenience, and the poor-performing of the film of gained behind the plated film, therefore, how silicone glass resin is carried out modification to remedy its shortcoming, becomes one of focus of technological development research.
Silicone resin is being carried out aspect the research that modification prepares the silicone resin that single component uses, Chinese invention patent " mono-component organic silicone insulating liquid " (application number 97108446.7) discloses and has added Resins, epoxy, linking agent and white mica powder etc. made and be used for colour picture tube anode terminal insulating mono-component organic silicone insulating liquid in pure organosilicon, its formed adhesion of thin film and insulating property are significantly improved, but added white mica powder in preparation process, the light transmission of the film that generates behind this product plated film reduces greatly.
Aspect the film forming hardness research of raising silicone resin, the report that silicone glass resin is carried out modification with propylene glycol and Viscotrol C urethane is arranged, the shock resistance of its film is improved greatly and (is seen " development of organosilicon/polyurethane-modified resin ", Liu Junfengs etc. are published in New Chemical Materials, volume the 4th phase 36-37 page or leaf in 1998); And Chinese invention patent " preparation method of the integrated silicone based thermal protection coating of self-vulcanizing heat-resisting wave-penetrating " (application number 200310107691.7) is with silicone resin with contain organosilyl polymethacrylate and an amount of zinc acetate, under 160～180 ℃ of temperature, react, add silicone resin solidifying agent, the linking agent of polyacrylic ester, initiator, heat-resistant filler, have higher cohesiveness after the silicone based thermal protection coating that makes at room temperature solidifies.
The something in common of technology such as above-mentioned patent is that they all are by adding one or more other components; certain performance to the silicone resin that obtained is improved; but utilize the film forming transparency of silicone resin shape of these method preparations generally not high; can not form transparent protective coating on the matrix (as glass, synthetic glass, polycarbonate, acrylic acid series plastics, cowl) that is fit to, its range of application has been subjected to bigger restriction.Therefore, up to now, still how constantly to explore the silicone glass resin of processability superior and easy to use (single component use) both at home and abroad.
Summary of the invention
The objective of the invention is to: it is simple to seek a kind of technology, and processing ease does not need to add solidifying agent and stopper in the low and use of cost, solidifies the preparation method of film hardness height that the back forms, silicone glass resin that transparency is good.
In order to achieve the above object, the present invention has introduced a kind of enhancement component in the hydrolysis-condensation process of the methyl trialkoxysilane that comprises Union carbide A-162 (MTES) or methyltrimethoxy silane (MTMS), promptly adopt the nano silicon dispersion liquid to prepare the silicone glass resin performed polymer, with the solvent Virahol silicone glass resin performed polymer is diluted then, add Silicon surfactant again and promptly make a kind of silicone glass resin that can single component uses after as flow agent, this single component glass resin need not add any solidifying agent in use, the film that heat cross-linking solidifies the back gained is transparent bright and clean, hard wear resistant, its pencil hardness 〉=7H.
Concrete technology is undertaken by following several steps:
(1) preparation of nano silicon dispersion liquid
Adopt one step of elemental silicon dissolution method to prepare the nano silicon dispersion liquid, concrete operations are as follows: the silica flour that takes by weighing the commercially available industrial one-level crystal form of 100g, be immersed in the 120g hot water activation and obtain the silicon body of paste after 12 minutes, under continuous agitation condition this body of paste slowly being added drop-wise to temperature is 65 ℃-68 ℃, concentration is in the 650g dilute sodium hydroxide aqueous solution of 0.36% mass percent, temperature of reaction is controlled at 91-93 ℃, stop to stir when bubble produces when no longer including in the reaction vessel, leave standstill cooling, filter, concentrate, promptly making pH is 8.2-10.6, and density is 1.16-1.20gcm
-3, particle diameter is at 10-25nm, SiO
2Content is the dispersion system of silica nanoparticles in water of 25-30%, and this dispersion system is called the nano silicon dispersion liquid again.
(2) preparation of organic-silicone prepolymer
Elder generation carries out weighing by following volume ratio and gets the raw materials ready, nano silicon dispersion liquid: methyl trialkoxysilane: acetate: water=3.00-8.00: 5.26-12.00: 0.05-1.50: 0.02-1.50, at room temperature methyl trialkoxysilane is put into the single neck flask that has grinding port plug, add acetate with micropipette, even with magnetic stirrer.Then nano silicon dispersion liquid and water are mixed, under continuous agitation condition, add and fill in the flask of methyl trialkoxysilane and acetate mixed solution, continue to stir and became single-phase by original two-phase to reaction system in 3-12 hour.After stopping to stir, reaction solution is transferred in the container, leaves standstill at ambient temperature after the sealing,, make its generation polycondensation to a certain degree, obtain the silicone glass resin performed polymer until beginning timing from reaction till totally 48 hours.
(3) preparation of mono-component organic silicone glass resin
Earlier with the centrifugation of silicone glass resin performed polymer, remove the small amount of solid suspended substance in the performed polymer, measure the Virahol of the 0.15-1.01 volume of performed polymer total amount then, to in its adding performed polymer performed polymer be diluted, stir, filter, obtain the liquid resin that solid content is the clear of 20-21%, add then account for the liquid resin gross weight be the organic silicon surfactant polyether silicone oil of 0.4-0.8% weight percent as flow agent, promptly make the silicone glass resin that can single component uses.It is inserted sealable container, place stand-by under the room temperature.
(4) plated film solidifies
With crystal pulling method (3) are plated in film forming on the good synthetic glass sheet of cleaning, drying, put into baking oven immediately, placed 3-5 minute down at 50 ℃, by the time rete almost tack-free after, temperature slowly is raised to 80 ℃.In 80 ℃, place after 1-3 hour, take out, naturally cooling promptly obtains the glazed single-component high-hardness silicone glass resin thin film coating that has solidified of transparency good outer appearnce, measures the pencil hardness 〉=7H of film according to standard GB/T6739-86 method with QHQ-A pencil hardness meter.
The present invention has following advantage:
1. to adopt the nano silicon dispersion liquid of elemental silicon one step dissolution method preparation be raw material in the present invention, this nano silicon dispersion liquid is directly generated with the deionized water reaction under the alkali effect by the pure silicon powder, therefore, it has advantages such as foreign matter content is low, transparency good, micelle is even, compact structure, and its preparation cost cheapness, and can be in 5 months to 8 years stable existence, make that the quality of products obtained therefrom is higher and cost is comparatively cheap.
2. owing to added a kind of enhancement component nano silicon dispersion liquid in the preparation process, promptly in the forming process of methyl silicon resin, introduce silica nanoparticles, the formed methyl silanetriol of methyl trialkoxysilane hydrolysis this moment (CH
3Si (OH)
3) with have the silicon-dioxide generation bonding of the siloxane bond of tetrahedral structure, like this, embed siloxane bond in the methyl silicon resin skeleton structure of gained with tetrahedral structure, it is gentle more that thereby the filming condition that makes the methyl silicon resin of generation becomes, no longer need during use to add any solidifying agent, and the thin film coating that plated film forms becomes hard.Simultaneously, initial period at the hydrolysis-condensation reaction of methyl trialkoxysilane is introduced the nano silicon dispersion liquid, be beneficial to the uniform distribution of silica nanoparticles in methyl silicon resin, and do not reduce the light transmission of methyl silicon resin, thereby make the product of final gained still keep the transparency of simple glass resin formation film.Therefore, the present invention has made the silicone glass resin that a kind of single component is used, and need not add solidifying agent during use, and heat cross-linking solidifies transparent bright and clean, the hard wear resistant of film of back gained, and its pencil hardness 〉=7H surpasses present domestic like product.
3. contain a large amount of methyl trialkoxysilane owing in the hydrolysis presoma, and the CH in the methyl trialkoxysilane
3Hydrolysis can not take place in-Si key, to be retained in the film that finally makes as organic constituent, its existence makes film have excellent hydrophobic property and certain snappiness, therefore, the silicone glass resin that a kind of single component that the present invention makes is used, from exterior appearance, the surface of film is very smooth bright and clean.
4. single-component high-hardness silicone glass resin of the present invention can synthesize at normal temperatures and pressures, production technique is extremely simple again, easy to control, production unit requires low, with existing one-tenth film hardness in the market is that the common silicone glass resin of 2H-3H is compared, and still has appreciable economic benefit.
Embodiment
Embodiment 1
It at first is the preparation of nano silicon dispersion liquid.Take by weighing 100g industry one-level crystal form silica flour (about 200 orders), be immersed in the 120g hot water (deionized water) and activate about 12 minutes, again it slowly is added drop-wise in the dilute sodium hydroxide aqueous solution that 650g concentration is 0.36% mass percent (temperature is about 65-68 ℃), till when 91-93 ℃ of reaction extremely no longer produces bubble, be cooled to room temperature, filter with B, promptly make SiO
2Content is the nano silicon dispersion liquid of 25-30%, and the pH of this nano silicon dispersion liquid is 8.2-10.6, and density is 1.16-1.20gcm
-3, SiO wherein
2The diameter of nanoparticle is at 10-25nm.
Then, under the room temperature, Union carbide A-162 (MTES) is put into the single neck flask that has grinding port plug, add the acetate of pressing following volume ratio calculated amount with micropipette, even with magnetic stirrer.Nano silicon dispersion liquid and water are mixed, under agitation, slowly splash in the flask that fills MTES and acetate, the proportioning of above-mentioned reactant is nano silicon dispersion liquid: MTES: acetate: water=3.00: 5.26: 1.50: 1.50 volume ratio continues stir about 12 hours to reaction system two-phase and becomes a phase.After stopping to stir, reaction solution is transferred in the container, (about 36 hours) are at room temperature left standstill for some time in sealing, make its generation polycondensation to a certain degree, obtain the performed polymer of silicone glass resin.
Then, with reaction solution (performed polymer of silicone glass resin) centrifugation, the Virahol that adds 0.15 volume of performed polymer total amount, stir, make solid content equal 21%, promptly obtain the liquid resin of clear, add again and account for the polyether silicone oil that filters back liquid resin total mass 0.4%, after stirring, seal container, set aside for use under the room temperature.
At last, carry out plated film.Earlier synthetic glass is cut into the sheet that size is about 1.5cm * 7cm, scrubs with liquid detergent, and then use flushing with clean water, then use distilled water flushing.Synthetic glass sheet number consecutively with cleaned is suspended on the lens hanger, is positioned in 50 ℃ of baking ovens drying for standby.Use the crystal pulling method plated film, then put into baking oven immediately, placed several minutes down at 50 ℃, by the time thin film coating almost tack-free after, temperature slowly is raised to 80 ℃ (noting: can not be rapidly heated, in order to avoid temperature raises and too fastly out of handly causes too fast bubble or the thin film coating of causing of some organic constituent volatilization in the thin film coating to turn white).Place in 80 ℃ after about 2 hours, take out, naturally cooling promptly obtains single-component high-hardness silicone glass resin thin film coating of the present invention, transparent bright and clean, the hard wear resistant of this thin film coating, its pencil hardness 〉=7H.
Embodiment 2
This embodiment technology is identical with embodiment 1, but need the nano silicon dispersion liquid among the embodiment 1: MTES: acetate: the volume ratio of water is adjusted into 8.00: 12.00: 0.20: 1.50, continue stirring until reaction system is become a phase by two-phase about 6 hours of the time.After stopping to stir, reaction solution is transferred in the container sealing, at room temperature time of repose is about 42 hours, after making its generation polycondensation to a certain degree,, add 0.70 volume Virahol of performed polymer total amount with the reaction solution centrifugation, make the solid content of silicone glass resin equal 20%, add again and occupy the polyether silicone oil of machine silex glass resin prepolymer total mass 0.6%, after stirring, seal container, set aside for use under the room temperature, through plated film solidify the pencil hardness 〉=7H of thin film coating.
Embodiment 3
This embodiment technology is identical with embodiment 1, but need to change the Union carbide A-162 among the embodiment 1 (MTES) into methyltrimethoxy silane (MTMS), nano silicon dispersion liquid: MTES: acetate: the volume ratio of water is adjusted into 7.00: 6.00: 0.05: 0.02, continue stirring until about 3 hours of the time that the reaction system two-phase becomes a phase.After stopping to stir, reaction solution is transferred in the container sealing, at room temperature time of repose is about 45 hours, make it that to a certain degree polycondensation take place after, with the reaction solution centrifugation, the 1.01 volume Virahols that add the performed polymer total amount, make solid content equal 21%, add again and occupy the polyether silicone oil of machine silex glass resin prepolymer (liquid resin) total mass 0.8%, after stirring, seal container, set aside for use under the room temperature is filmed, the pencil hardness 〉=7H of solidified coating.
Claims (1)
1. the preparation method of single-component high-hardness silicone glass resin is characterized in that:
(1) preparation of nano silicon dispersion liquid
Adopt one step of elemental silicon dissolution method to prepare the nano silicon dispersion liquid, concrete operations are as follows: the silica flour that takes by weighing the commercially available industrial one-level crystal form of 100g, be immersed in the 120g hot water activation and obtain the silicon body of paste after 12 minutes, under continuous agitation condition this body of paste slowly being added drop-wise to temperature is 65 ℃-68 ℃, concentration is in the 650g dilute sodium hydroxide aqueous solution of 0.36% mass percent, temperature of reaction is controlled at 91-93 ℃, stop to stir when bubble produces when no longer including in the reaction vessel, leave standstill cooling, filter, concentrate, promptly making pH is 8.2-10.6, and density is about 1.16-1.20gcm
-3, particle diameter 10-25nm, SiO
2The nano silicon dispersion liquid of content 25-30%;
(2) preparation of organic-silicone prepolymer
Elder generation carries out weighing by following volume ratio and gets the raw materials ready, nano silicon dispersion liquid: methyl trialkoxysilane: acetate: water=3.00-8.00: 5.26-12.00: 0.05-1.50: 0.02-1.50, then under the room temperature, methyl trialkoxysilane is put into the single neck flask that has grinding port plug, add acetate with micropipette, even with magnetic stirrer; Again nano silicon dispersion liquid and water are mixed, under continuous agitation condition, add and fill in the flask of methyl trialkoxysilane and acetate mixed solution, continue to stir and to become a phase by original two-phase to reaction system in 3-12 hour, after stopping to stir, reaction solution is transferred in the container, leave standstill at ambient temperature after the sealing, until beginning timing from reaction till totally 48 hours, make it that to a certain degree polycondensation take place, obtain the silicone glass resin performed polymer;
(3) preparation of mono-component organic silicone glass resin
Earlier with the centrifugation of silicone glass resin performed polymer, remove the small amount of solid suspended substance in the performed polymer, take by weighing the Virahol of the 0.15-1.01 volume of silicone glass resin performed polymer total amount then, to in its adding performed polymer performed polymer be diluted, stir, obtain the liquid resin that solid content is the clear of 20-21%, add then that to account for the liquid resin gross weight be that the organic silicon surfactant polyether silicone oil of 0.4-0.8% weight percent is as flow agent, promptly make the silicone glass resin that can single component uses, it is inserted sealable container, place stand-by under the room temperature; Promptly obtain the single-component high-hardness silicone glass resin coating of the present invention of transparent bright and clean, the pencil hardness 〉=7H of coating through curing of coating.