CN1634702A - Method for manufacturing rubber diaphragm for diaphragm pump - Google Patents
Method for manufacturing rubber diaphragm for diaphragm pump Download PDFInfo
- Publication number
- CN1634702A CN1634702A CN 200310122853 CN200310122853A CN1634702A CN 1634702 A CN1634702 A CN 1634702A CN 200310122853 CN200310122853 CN 200310122853 CN 200310122853 A CN200310122853 A CN 200310122853A CN 1634702 A CN1634702 A CN 1634702A
- Authority
- CN
- China
- Prior art keywords
- fabric
- diaphragm pump
- rubber
- manufacture method
- diaphragm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention relates to fabric isolation film pump rubber film process method, which is characterized by the following: adopting high intensity fabric as strengthening layer; adopting glue agent between the fabric and the rubber layer by use of sulfuration speed and rubber layer step. The said sulfuration speed step means that it adopts rubber materials composed of film layer and glue materials as the glue agent as rubber glue and fabric.
Description
Technical field
The present invention relates to a kind of manufacture method of technically classified rubber goods, specifically, relate to the manufacture method of the good especially diaphragm pump of a kind of flexible resistance with rubbery membrana dermalis.
Background technique
The diaphragm pump rubbery membrana dermalis is a kind of elastomer diaphragm of bowl-shape embedded reinforced fabric.Be installed in the middle of the diaphragm pump cavity, the edge is fixed on the pump housing, by the effect of its power source (pressurized air, steam etc.) on one side diaphragm is promoted back and forth.Change the space of diaphragm pump another side cavity by the to-and-fro motion of diaphragm, by two one-way valves fluid (water, chemical liquid) is sucked from an end of pump again and discharge to the other end.Therefore, when diaphragm pump was worked, the diaphragm of central authorities is reciprocally swinging back and forth incessantly just, stands the test of flexing fatigue.
The epithelium of similar diaphragm pump elastomer diaphragm is widely used in pneumatic control components, occasions such as automobile, locomotive brake cylinder, and the technical requirements that will calculate braking automobile leather cup (rubber diaphragm of automobile brake chamber) in these products is the highest.But with regard to the braking automobile leather cup, it is to be in segmentation, working state with gap.According to China GB7525 standard, rubber diaphragm of automobile brake chamber flex life under the frequency of per minute 15 times is decided to be more than 250,000 times.
Some are exclusively used in the diaphragm pump requirement of conveying material (as: water, oil, liquid charging stock etc.) under the continuous duty of per second 3 secondary frequencies at present, the flex life of used epithelium reaches more than 1,200 ten thousand times, and this requires to fall far short with foregoing GB7525 set quota.In addition, according to investigations, the average out in working life of the diaphragm pump elastomer diaphragm of selling on the Domestic market is about up to a million times at present.Far can not meet the requirements.
Summary of the invention
In order to satisfy the strict demand that the new types of diaphragm pump proposes rubbery membrana dermalis, develop and have long-life diaphragm pump rubbery membrana dermalis, the inventor has done a large amount of analysis and research with keen determination, find, improve the life-span of diaphragm pump with rubbery membrana dermalis, except used rubber material should have remarkable endurance, low-heat-generation, one of them was ignored easily and crucial aspect is the bonding of fabric and rubber.Because rubber is different with textile fiber surface characteristic between the two, very easily occur in the heat build-up that causes owing to interfacial stress in the diaphragm using process, cause material aging, occur that diaphragm flakes, delamination destruction consequently.Based on this understanding, reach the present invention then.
The present invention realizes like this, it belongs to the manufacture method of a kind of diaphragm pump with rubbery membrana dermalis, it is characterized in that, adopt high-intensity nylon fabric as enhancement layer, it is bonding to adopt the synchronous adhesive of curing rate and rubber layer to realize between fabric and the rubber layer, and the THICKNESS CONTROL of adhesive layer is in 4～7 mu m ranges.
Facts have proved of production and processing elastomer diaphragm for many years, the high epithelium of bonding strength between glue-line and the fabric, its flexible resistance might not be best.Find that by the analysis that diaphragm is destroyed section the cradle that diaphragm destroys is the interface of rubber and adhesive.In general, in order to reduce interfacial stress, all adopt with the similar material (rubber mass compounding) of rubber layer as adhesive.At this moment, because the cohesion strength of adhesive is come for a short time more than rubber layer, so the leading factor that the cohesional failure of adhesive has become epithelium to destroy.The present invention sets about from this problem crux just, propose, at first will pay special attention to adjust the curing rate of rubber layer material and adhesive (being commonly called as rubber cement), make both as far as possible near so-called synchronic curing, that is to say that both curing rates show as T on the determination data of vulcameter
10And T
90Value was more or less the same 30 seconds.
In addition, between fabric and the rubber on the interface layer thickness of adhesive layer also be The key factor very, this thickness should be controlled in 4～7 mu m ranges, the too high or too low flex life of diaphragm that all can cause of thickness reduces.Can adopt the cement-dipping method adhesive coating, that is: adopt secondary soaking paste technology to control the thickness of adhesive layer (glue-line), with 80 ± 2 ℃ of oven dry 2～2.5 hours, each soaking paste control bondline thickness reached 2～3 μ m after each soaking paste.
Because the usage requirement of this series products is higher, so the reinforced fabric that requires to use has higher rupture strength and elongation at break, should select for use rupture strength and elongation at break all to obtain the high strength polyamide fibre plain weave fabric that takes into account, its warp-wise rupture strength 〉=3450N for this reason; Broadwise rupture strength 〉=2800N; Warp-wise elongation at break 〉=30%; Broadwise elongation at break 〉=28%.The fabric that can satisfy this technical requirements is 601 commercially available polyamide fabrics.
According to the present invention, make the diaphragm pump diaphragm with nitrile butadiene rubber, neoprene and ethylene propylene diene rubber respectively, be installed on and do the test of simulation flex life on the corresponding bench testing machine, the result is all more than 1,200 ten thousand times, do not destroy, reach diaphragm pump design office requirement.
Description of drawings
Fig. 1 is the overall structure schematic representation of diaphragm pump of the present invention with elastomer diaphragm; Fig. 2 is the t cross-sectional view among Fig. 1.Fig. 3 is a process flow diagram of the present invention.
Label among the figure is: 1,5---rubber layer; 2,4---adhesive layer; 3---strengthen and use the high strength nylon fabric.
Embodiment
Further specify the present invention below in conjunction with embodiment, but the present invention is not limited to this embodiment.
Embodiment 1～3 and comparative example 1～9
Use neoprene (CR), nitrile butadiene rubber (NBR) and ethylene propylene diene rubber (EPDM) to make three class diaphragm pump rubbery membrana dermalis as shown in table 2 respectively according to structure illustrated in figures 1 and 2 by technological process shown in Figure 3, amount to 12 kinds of products, i.e. embodiment 1～3 and comparative example 1～9.
The rubber layer [1] of the composition of wherein employed adhesive [2] and [4] and epithelium and the composition of [5] sizing material are basic identical, and make rubber cement with beater by following sizing material/solvent ratios:
Neoprene cement: sizing material/benzene=1/3;
Butadiene-acrylonitrile cement: sizing material/benzene=1/2.5;
Ethylene Propylene Terpolymer rubber cement: sizing material/gasoline=1/3.5.
Measure the T of these rubber cements with vulcameter
10And T
90Be worth, and make comparisons with this two value of sizing material with glue-line glue, understand some difference usually, here as a comparative example discrepant, that is: comparative example 2,3,5,6,8,9.By to the adjustment of curing system, make both difference narrow down to the embodiments of the invention that are decided to be in the 30 second scopes, promptly embodiment 1,2,3.
The high strength nylon fabric layer 3 that strengthens usefulness is 601 commercially available polyamide fabrics, and its performance is as shown in table 1:
Table 1
Adopt four kinds of fabric soaking paste technologies:
A, 601 cloth clean up in acetone, natural air drying 2～2.5 hours, secondary soaking paste in dip coater, dry for standby.
B, 601 cloth clean up in acetone, natural air drying 2～2.5 hours, three soaking paste in dip coater, dry for standby.
C, 601 cloth clean up in acetone, and secondary soaking paste in dip coater, dry for standby were handled in oven dry 2～2.5 hours in 80 ± 10 ℃ environment.
D, 601 cloth clean up in acetone, and three soaking paste in dip coater, dry for standby were handled in oven dry 2～2.5 hours in 80 ± 10 ℃ environment.
Wherein according to the invention is technology C, and promptly embodiment 1,2,3.By data shown in the table 2 as seen, the curing rate of only adjusting adhesive still is not enough, although the curing rate of comparative example 2,4,7 used rubber cements is close with the glue-line sizing material, because the soaking paste inappropriate technology, cause adhesive layer thickness not to be inconsistent requirement, the flex life of products obtained therefrom does not reach index yet.
Table 2
| The glue kind | ?????????T 10 | ???????????T 90 | Soaking paste technology | Bonding strength (kN/m) | Stand test * (ten thousand times) | |||
| Glue-line glue | Adhesive | Glue-line glue | Adhesive | |||||
| Embodiment 1 | ??CR | ??1’55” | ??1’58” | ???20’38” | ???20’40” | ???C | ????4.0 | ??1200 |
| Comparative example 1 | ??CR | ??1’55” | ??1’58” | ???20’38” | ???20’40” | ???A | ????3.0 | ??1050 |
| Comparative example 2 | ??CR | ??1’55” | ??2’38” | ???20’38” | ???21’43” | ???B | ????3.5 | ??1020 |
| Comparative example 3 | ??CR | ??1’55” | ??2’38” | ???20’38” | ???21’43” | ???D | ????4.5 | ??1180 |
| | ??NBR | ??1’33” | ??1’35” | ???18’35” | ???18’40” | ???C | ????3.8 | ??1200 |
| Comparative example 4 | ??NBR | ??1’33” | ??1’35” | ???18’35” | ???18’40” | ???A | ????2.6 | ??1000 |
| Comparative example 5 | ??NBR | ??1’33” | ??2’12” | ???18’35” | ???20’10” | ???B | ????2.9 | ??990 |
| Comparative example 6 | ??NBR | ??1’33” | ??2’12” | ???18’35” | ???20’10” | ???D | ????4.3 | ??1150 |
| | ??EPDM | ??1’18” | ??1’11” | ???13’34” | ???13’38” | ???C | ????2.9 | ??1200 |
| Comparative example 7 | ??EPDM | ??1’18” | ??1’11” | ???13’34” | ???13’38” | ???A | ????2.2 | ??1020 |
| Comparative example 8 | ??EPDM | ??1’18” | ??2’05” | ???13’34” | ???16’12” | ???B | ????2.3 | ??1000 |
| Comparative example 9 | ??EPDM | ??1’18” | ??2’05” | ???13’34” | ???16’12” | ???D | ????3.2 | ??1160 |
* in the flexing fatigue life-span, subdue number of times (ten thousand times), 1,200 ten thousand times do not take place to destroy is qualified.
Claims (5)
1, a kind of diaphragm pump that strengthens with fabric manufacture method of rubbery membrana dermalis, it is characterized in that, adopt high-intensity nylon fabric as enhancement layer, it is bonding to adopt the synchronous adhesive of curing rate and rubber layer to realize between fabric and the rubber layer, and the THICKNESS CONTROL of adhesive layer is in 4～7 mu m ranges.
2, diaphragm pump according to claim 1 is characterized in that with the manufacture method of rubbery membrana dermalis, described fabric and rubber layer be bonding stick with glue the agent composition and rubber layer basic identical, with the T of vulcameter mensuration
10And T
90Being worth both was more or less the same 30 seconds.
3, diaphragm pump according to claim 1 is characterized in that with the manufacture method of rubbery membrana dermalis described high strength nylon fabric is warp-wise rupture strength 〉=3450N; Broadwise rupture strength 〉=2800N; Warp-wise elongation at break 〉=30%; The plain cloth of broadwise elongation at break 〉=28%.
4, diaphragm pump according to claim 2 is characterized in that with the manufacture method of rubbery membrana dermalis described high strength nylon fabric is 601 polyamide fabrics.
5, the diaphragm pump according to claim 1 manufacture method of rubbery membrana dermalis, it is characterized in that, described adhesive layer thickness is controlled by fabric secondary soaking paste technology, and with 80 ± 2 ℃ of oven dry 2～2.5 hours, each soaking paste control bondline thickness reached 2～3 μ m after each soaking paste.