CN1632028A - Adhesive for textile industry and method for preparing same - Google Patents
Adhesive for textile industry and method for preparing same Download PDFInfo
- Publication number
- CN1632028A CN1632028A CN 200410067873 CN200410067873A CN1632028A CN 1632028 A CN1632028 A CN 1632028A CN 200410067873 CN200410067873 CN 200410067873 CN 200410067873 A CN200410067873 A CN 200410067873A CN 1632028 A CN1632028 A CN 1632028A
- Authority
- CN
- China
- Prior art keywords
- textile industry
- tackiness agent
- agent
- initiator
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a sticker in cottonracy, comprising of vinyl acetate, butyl acryl ate, acrylic acid, polyvinyl alcohol, emulsifier, initiator, water and sodium bicarbonate. The sticker has low productive cost, better response characteristic and stability of plasticizing,.
Description
Technical field
The invention belongs to chemical field, relate in particular to a kind of tackiness agent that is used for textile industry.
Background technology
Along with the high speed development of society, human life requires more and more comfortable, and for the ease of producing and reduce the cost of product, it is bonding mutually that we use various tackiness agents to be used for the various article of textile industry, to reach good result of use.The production cost of the tackiness agent that is applicable to textile industry of Shi Yonging is all than higher in the market, and plasticizating response characteristic is poor, and performance is very unstable, and viscosity is also lower.
Summary of the invention
The objective of the invention is to address the above problem, provide a kind of production cost the low tackiness agent that is used for textile industry.
Technical scheme of the present invention is: a kind of tackiness agent that is used for textile industry is characterized in that comprising the component of following weight ratio:
Vinyl acetate 20%-30%
Butyl acrylate 2%-3%
Vinylformic acid 1%-2%
Polyvinyl alcohol 2%-3%
Emulsifying agent 0.5%-1%
Initiator 0.1%-3%
Water 60%-73%
Sodium bicarbonate 0.2%-0.4%
Also comprise proper quantity of defoaming agent;
Described initiator is an ammonium persulphate;
Described emulsifying agent is the OP emulsifying agent;
The best composition of tackiness agent of the present invention comprises:
Vinyl acetate 23%
Butyl acrylate 2.5%
Vinylformic acid 1%
Polyvinyl alcohol 2.5%
Emulsifying agent 0.5%
Initiator 0.2%
Water 70%
Sodium bicarbonate 0.3%
Defoamer is an amount of
A kind of preparation method who is used for the tackiness agent of textile industry may further comprise the steps:
(1) configuration mix monomer: vinyl acetate, butyl acrylate, vinylformic acid are mixed;
(2) with the polyethylene alcohol and water at 85 ℃ of-95 ℃ of following mixed dissolutions;
(3) get above-mentioned polyvinyl alcohol water solution and under 60 ℃-75 ℃, add the dissolving that stirs of emulsifying agent, sodium bicarbonate, occur to add defoamer behind the foam, add partially mixed monomer and initiator in the step (1) then, drip remaining mix monomer after the reaction again, be warming up to 85 ℃～90 ℃ after being added dropwise to complete again, reacted 0.5 hour, after the cooling promptly.
By a kind of tackiness agent that is used for textile industry of technical scheme design of the present invention, allow to add more water than conventional conventional products, reduced production cost, also have plasticizating response characteristic and stability preferably, viscosity is also higher.
Embodiment
The present invention is described further below by specific embodiment.
Embodiment 1: the present embodiment tackiness agent adopts following prescription:
Vinyl acetate 120kg butyl acrylate 12kg
Vinylformic acid 6kg polyvinyl alcohol 12kg
OP-10 3kg ammonium persulphate 1kg
Water 350kg sodium bicarbonate 1.5kg
Defoamer N, N, N-three (polyoxyethylene polyoxypropylene) amine is an amount of
Preparation method: press following step:
(1) configuration mix monomer: vinyl acetate, butyl acrylate, vinylformic acid are mixed;
(2) with the polyethylene alcohol and water at 90 ℃ of following mixed dissolutions;
(3) get above-mentioned polyvinyl alcohol water solution and under 75 ℃, add the dissolving that stirs of emulsifier op-10, sodium bicarbonate, occur to add defoamer N behind the foam, N, N-three (polyoxyethylene polyoxypropylene) amine, add partially mixed monomer and initiator ammonium persulfate in the step (1) then, drip remaining mix monomer after the reaction again, be warming up to 85 ℃～90 ℃ after being added dropwise to complete again, reacted 0.5 hour, after the cooling promptly.
Claims (6)
1, a kind of tackiness agent that is used for textile industry is characterized in that comprising the component of following weight ratio:
Vinyl acetate 20%-30%
Butyl acrylate 2%-3%
Vinylformic acid 1%-2%
Polyvinyl alcohol 2%-3%
Emulsifying agent 0.5%-1%
Initiator 0.1%-3%
Water 60%-73%
Sodium bicarbonate 0.2%-0.4%
2, a kind of tackiness agent that is used for textile industry according to claim 1 is characterized in that also comprising proper quantity of defoaming agent.
3, a kind of tackiness agent that is used for textile industry according to claim 1 is characterized in that described initiator is an ammonium persulphate.
4, a kind of tackiness agent that is used for textile industry according to claim 1 is characterized in that described emulsifying agent is the OP emulsifying agent.
5, a kind of tackiness agent that is used for textile industry according to claim 1 is characterized in that being made of following component: vinyl acetate 23%
Butyl acrylate 2.5%
Vinylformic acid 1%
Polyvinyl alcohol 2.5%
Emulsifying agent 0.5%
Initiator 0.2%
Water 70%
Sodium bicarbonate 0.3%
Defoamer is an amount of
6, a kind of preparation method who is used for the tackiness agent of textile industry according to claim 1 may further comprise the steps:
(1) configuration mix monomer: vinyl acetate, butyl acrylate, vinylformic acid are mixed;
(2) with the polyethylene alcohol and water at 85 ℃ of-95 ℃ of following mixed dissolutions;
(3) get above-mentioned polyvinyl alcohol water solution and under 60 ℃-75 ℃, add the dissolving that stirs of emulsifying agent, sodium bicarbonate, occur to add defoamer behind the foam, add partially mixed monomer and initiator in the step (1) then, drip remaining mix monomer after the reaction again, be warming up to 85 ℃～90 ℃ after being added dropwise to complete again, reacted 0.5 hour, after the cooling promptly.