CN1621457A - Fiber containing paint composition and its preparation method and use - Google Patents
Fiber containing paint composition and its preparation method and use Download PDFInfo
- Publication number
- CN1621457A CN1621457A CN 200310103900 CN200310103900A CN1621457A CN 1621457 A CN1621457 A CN 1621457A CN 200310103900 CN200310103900 CN 200310103900 CN 200310103900 A CN200310103900 A CN 200310103900A CN 1621457 A CN1621457 A CN 1621457A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fibre
- coating composition
- composition
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The fiber containing paint composition for decorating building wall includes natural fiber and/or artificial fiber, softener, mildew inhibitor, cationic agent, adhesive, paint powder, disinfector, waterproof agent, flame retardant, golden filament, silver filament, color powder, color phosphor, and color fluorescent filament material. The preparation process includes dyeing the fiber, softening the fiber, adding other components, drying and other steps. The present invention has rich colors, easy coating and other advantages.
Description
Technical field
The present invention relates to a kind of fibre-bearing coating composition and its production and application, relate in particular to that the building wall decorate to use, can make wall have fibre-bearing coating composition of random pattern and its production and application.
Background technology
At present, the building wall is decorated, and a kind of method is to adopt coating to make wall surface levelling, waterproof, mildew-resistant or add pigment to have made it color, and another kind of method is to adopt wallpaper or decorate wall with figuratum textile cloth.But the former decorative effect is poor, be difficult to reach the effect that people arbitrarily beautify wall, and the latter can't repair after easily polluting, breaking, and can't reach to resemble the effect that can freely apply and repair the coating.
Summary of the invention
The purpose of this invention is to provide a kind of fibre-bearing coating composition and its production and application, especially providing the building wall to decorate uses, can make wall have fibre-bearing coating composition of random pattern and its production and application, having overcome the shortcoming that above-mentioned building wall is decorated, is a kind of novel fibre-bearing coating composition that has coating function and beautification function concurrently.
The objective of the invention is to be achieved through the following technical solutions:
A kind of fibre-bearing coating composition comprises following component: natural fiber and/or artificial fiber, tenderizer, mould inhibitor, cationics, tackiness agent;
Described composition can be following parts by weight of component: natural fiber and/or artificial fiber 40-98, tenderizer 0.1-0.3, mould inhibitor 0.05-0.15, cationics 0.05-0.15, tackiness agent 5-15;
Be preferably following parts by weight of component: natural fiber and/or artificial fiber 68-90, tenderizer 0.05-0.25, mould inhibitor 0.08-0.12, cationics 0.08-0.12, tackiness agent 8-12;
Be preferably following parts by weight of component: natural fiber and/or artificial fiber 88, tenderizer 0.2, mould inhibitor 0.1, cationics 0.1, tackiness agent 10;
The color that this natural fiber and/or artificial fiber can be the nature color or catch by known staining agent, and the color that under light, can present the multicolour variation by known fluorescent dye dyeing back; The color of staining agent can be multiple, as oyster white, light brown, brown, red, black, blueness, green etc. or the multicolour that presents simultaneously.
Described natural fiber can be selected from vegetable fibre, animal fibre or its composition, vegetable fibre is the natural fiber that its seed, stem, skin, leaf, bar etc. obtain, as the bagasse after cottonseed, cotton fibre, xylon, straw fiber, straw, bamboo, reed, the press for extracting juice sugar, wood pulp, straw pulp, paper pulp, the scraps of paper, flaxen fiber, coconut husk, palm fibre, abaca etc.; Animal fibre is hair of animal or the natural fiber that secretory product constitutes, as silk, wool, eider down, the rabbit hair, Pilus Cameli, yak hair, mohair, cashmere etc.
Described artificial fiber can be selected from fiber or its composition that present known artificial raw material is made, the regenerated fiber, the synthon that comprise the usefulness of weaving, as viscose fiber, cellulose acetate, seaweed fiber, terylene, polypropylene fibre, acrylic, nylon etc. are the macromolecular compound that raw material should be made through chemistry side with coal, oil, Sweet natural gas or agricultural byproducts etc., and these raw materials can also be as toughner.
The dyeing of described fiber can be adopted known fiber dyeing agent, as the electromagnetic coloured pigment with visual effect of 380-780 nano wave length; Organic dye comprises azoic dyestuff, phthalein cyanogen dyestuff, heterocyclic dye, vat dyes, lake dyes and hair dyes commonly used, as Fast Yellow G, phthalein cyanogen indigo plant, the pyridine of quinoline bifurcation, anthraquinone, azo lake etc.
Described tenderizer can be known chemistry painting industry tenderizer, especially be hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) three (the fragrant penta tetrol base of three hydroxyls) ammonium oxide, purpose is the softening fibre raw material, and hexadecyl three of the present invention (the fragrant penta tetrol base ammonium oxide of three hydroxyls) three (the fragrant penta tetrol base of three hydroxyls) ammonium oxide also has the effect of sterilization.
Described mould inhibitor can be known mould inhibitor, as halogeno-amine, especially as amine bromide, ammonia chloride etc.
Described cationics can be the known cationic salt or derivatives thereof of being with, as positively charged ion silicone oil, purpose is that metope and airborne positively charged ion are isolated, effect with anti-electrostatic, thereby make airborne dust be difficult for absorption on the wall, the purpose that arrival bears dirty can also make surperficial hydrophobic simultaneously, also can be used as softening agent.
Described tackiness agent can be known adhesive for paint, is preferably transparent adhesives, and as polyvinyl alcohol, purpose is to finalize the design after making Mierocrystalline cellulose and other component combination drying.
Described composition also can further comprise: an amount of coating powder, disinfectant, water-resisting agent, fire retardant, spun gold, filamentary silver, colored powder, color phosphor, color fluorescence silk etc. present material or its combination of visual effects such as different color with light, especially be following parts by weight of component: coating powder 10-80, disinfectant 0.05-0.15, water-resisting agent 0.05-0.15, fire retardant 0.05-0.15; Be preferably following parts by weight of component: coating powder 45, disinfectant 0.10, water-resisting agent 0.10, fire retardant 0.10, an amount of spun gold, filamentary silver, colored powder, color phosphor, color fluorescence silk.
Described coating powder can be the coating powder of known different grain size size, as dry powder, mineral powder, rock powder; Described dry powder is the composition that contains Calucium Silicate powder, calcium aluminate that calcinings such as ore such as calcite, rhombspar, marble, limestone soil, clay, high allite form, and can buy from market; Described mineral powder, rock powder comprise natural mineral powder, artificial mineral's powder, as gold and silver, copper, cinnabar, cinnabar, jade, mica, crystal, quartz, feldspar, granite, quartzose sandstone etc., purpose is to make the coating after the moulding present texture, and the coating powder that adds different weight parts can present different texture.
Described disinfectant can be known disinfectant, as titanium oxide, benzoic acid and sodium benzoate, and tribromo salicyl aniline, wherein titanium oxide and hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) are used and have the collaborative effect of strengthening sterilization;
Described water-resisting agent can be known coating water-resisting agent, and as the water-latex type mixture of palm wax and acrylate copolymer emulsion, the coating that adds water-resisting agent has non-reversibility, compares with the coating that does not add water-resisting agent, on the wall difficult repeated use the after the coating.
Described fire retardant can be known coating fire retardant, as halogen contained compound, and the decabromodiphenyl oxide of as usual and antimonous oxide and usefulness, phosphoric acid ester, peroxophosphoric acid amine etc.
The present invention is raw materials used all can directly to be obtained from market.
The present invention also provides the preparation method of described fibre-bearing coating composition, may further comprise the steps:
Fiber softening is handled;
Fiber is added mould inhibitor carry out the mildew-resistant processing;
In the fiber of above-mentioned processing, add cationics;
With the fiber cryodrying of above-mentioned adding cationics typing, described low temperature can be 50-100 ℃, especially is 70-90 ℃, and purpose is to make fiber be dispersed or gather shape, as pencil, particulate state, tow shape, spherical, cotton-shaped and irregular;
In above-mentioned typing fiber, add tackiness agent, the cryodrying typing, described low temperature can be 50-100 ℃, especially is 70-90 ℃.
Described preparation method also comprises:
With fiber with the staining agent processing of dyeing;
Or add tackiness agent again after also comprising adding coating powder, disinfectant, water-resisting agent, fire retardant, an amount of spun gold, filamentary silver, colored powder, color phosphor, color fluorescence silk or its composition, the cryodrying typing, described low temperature can be 50-100 ℃, especially is 70-90 ℃.
The present invention also provides the application of described fibre-bearing coating composition aspect building wall decoration, during use, described fibre-bearing coating composition adds the water of 3-7 times of volume or weight, especially the water of 5 times of volume or weights, mix, the coating cladding process is coated on the metope routinely, and waiting after the seasoning is that nature is docile and obedient in metope.Because different coating methods, fiber coating will show different texture on metope, and therefore, the present invention is preferably and brushes or roller coating.
The present invention has the following advantages:
1, fibre-bearing coating composition of the present invention is finalized the design after on the metope, can use repeatedly, after an amount of water logging, can take off from metope.
2, present composition raw material compliance with environmental protection requirements.
3, the present composition has anticracking and gas-pervious effect.
4, owing to add the raw material of anti-electrostatic, prevent the bonding metope of dust.
5, after the present composition is applied to metope, attractive in appearance, have stereoscopic sensation and embossment sense, can adopt different materials in conjunction with coatings formulated as required, apply and metope, be rich in aesthetic feeling.
6, easy construction, coating add water can be coated on metope.
7, can directly repair on metope, because fiber coating composition is when applying metope, fiber coating moves brokenly, because its irregularity, and can add the water capacity and easily takes off characteristic from metope, so can directly repair on metope.
8, adopt fibrous material, also have warming effect, because the projection that the surface forms has sound-absorbing, sound damping effect.Add fire retardant and have fire-retardant, anti-pyritous effect.
9, fiber coating composition of the present invention presents the fiber coat with irregular texture, color after applying metope, and flower case change of shape is abundant.
Embodiment
Embodiment 1
A kind of coating composition that contains flax fiber
Take by weighing following component (Kg): flax fiber 88, hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.2, amine bromide 0.1, positively charged ion silicone oil 0.1, polyvinyl alcohol 10.
The preparation method, with flax fiber concentration is the processing of dyeing of 1% Fast Yellow G, with softening processing of hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls), add amine bromide and carry out the mildew-resistant processing, add positively charged ion silicone oil dryness finalization again, temperature is 90 ℃, makes fiber be boundling shape, tow shape, spherical, cotton-shaped and irregular.In the typing fiber, add polyvinyl alcohol, 70 ℃ of dryness finalizations, promptly.
Embodiment 2
The coating composition that contains wool fiber
Take by weighing following component (Kg): wool fiber 68, hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.05, ammonia chloride 0.08, positively charged ion silicone oil 0.08, polyvinyl alcohol 8, dry powder 30, crystal powder 15, titanium oxide 0.1, decabromodiphenyl oxide 0.10.
The preparation method, wool fiber is softened and handles with hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls), adding ammonia chloride, titanium oxide carry out mildew-resistant, sterilising treatment, add positively charged ion silicone oil, dry powder, crystal powder dryness finalization again, temperature is 50 ℃, makes fiber be tow shape, cotton-shaped and irregular.In the typing fiber, add polyvinyl alcohol, decabromodiphenyl oxide, 90 ℃ of dryness finalizations, promptly.
Embodiment 3
The coating composition that contains coir fibre, mohair fiber
Take by weighing following component (Kg): coir fibre 44, mohair fiber 24, hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.05, ammonia chloride 0.08, positively charged ion silicone oil 0.08, polyvinyl alcohol 8, dry powder 10, titanium oxide 0.15, decabromodiphenyl oxide 0.15.
The preparation method is with embodiment 2.
Embodiment 4
The coating composition that contains brown fiber
Take by weighing following component (Kg): brown fiber 66, hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.05, ammonia chloride 0.08, positively charged ion silicone oil 0.08, polyvinyl alcohol 8, cinnabar 10, titanium oxide 0.05, decabromodiphenyl oxide 0.05.
The preparation method is with embodiment 2.
Embodiment 5
The coating composition that contains polypropylene fibre
Take by weighing following component (Kg): polypropylene fibre 90, hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.25, amine bromide 0.12, positively charged ion silicone oil 0.12, polyvinyl alcohol 12, cinnabar 30, jade powder 10, titanium oxide 0.12.
The preparation method, with polypropylene fibre concentration is the pake purpke dyeing in 0.2% triaryl methane color lake, use softening processing of hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) again, adding amine bromide, titanium oxide carry out mildew-resistant to be handled, add positively charged ion silicone oil, cinnabar, the dry typing of jade dried bean noodles again, temperature is 90 ℃, makes fiber be particulate state and irregular.In the typing fiber, add polyvinyl alcohol, 50 ℃ of dryness finalizations, promptly.
Embodiment 6
The colo(u)r coating composition that contains tynex, thermovyl, cotton fibre
Take by weighing following component (Kg): tynex, thermovyl, cotton fibre 98 (ratio is 1: 1: 1), hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.3, amine bromide 0.15, positively charged ion silicone oil 0.15, polyvinyl alcohol 15.
The preparation method, with tynex, thermovyl, cotton fibre mixture concentration is 0.05% anthraquinone red colouring, use softening processing of hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) again, adding amine bromide, titanium oxide carry out mildew-resistant to be handled, add positively charged ion silicone oil, cinnabar, the dry typing of jade dried bean noodles again, temperature is 70 ℃, makes fiber be particulate state and irregular.In the typing fiber, add polyvinyl alcohol, 60 ℃ of dryness finalizations, promptly.
Embodiment 7
The colo(u)r coating composition that contains polyacrylonitrile fibre, eider down
Take by weighing following component (Kg): polyacrylonitrile fibre, eider down 40 (ratio is 5: 1), the water-latex type mixture 1 of hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) 0.3, amine bromide 0.05, positively charged ion silicone oil 0.05, spun gold 1, filamentary silver 1, colored silk 1, polyvinyl alcohol 5, palm wax and acrylate copolymer emulsion.
The preparation method, with polyacrylonitrile fibre, eider down mixture concentration is concentration 0.1% dioxazine permanent violet RL dyeing, use softening processing of hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) again, adding amine bromide, titanium oxide carry out mildew-resistant to be handled, add positively charged ion silicone oil dryness finalization again, temperature is 70 ℃, makes fiber be particulate state and irregular.The water-latex type mixture that in the typing fiber, adds spun gold, filamentary silver, colored silk, polyvinyl alcohol, palm wax and acrylate copolymer emulsion, 60 ℃ of dryness finalizations, promptly.
Embodiment 8
The application of embodiment 1-7 fibre-bearing coating composition aspect building wall decoration, described fibre-bearing coating composition adds the water of 5 times of volumes respectively, mixes, and the coating cladding process is coated on the metope routinely, and waiting after the seasoning is that nature is docile and obedient in metope.Because different coating methods, fiber coating will show different texture on metope, and therefore, the present invention is for brushing, and it is more smooth to show as the top layer.
Embodiment 9
The application of embodiment 1-7 fibre-bearing coating composition aspect building wall decoration, described fibre-bearing coating composition adds the water of 3 times of volumes respectively, mixes, and the coating cladding process is coated on the metope routinely, and waiting after the seasoning is that nature is docile and obedient in metope.Because different coating methods, fiber coating will show different texture on metope, and therefore, the present invention is roller coating, show as the top layer and have the lofty pattern that interlocks with depression.
Embodiment 10
The application of embodiment 1-7 fibre-bearing coating composition aspect building wall decoration, described fibre-bearing coating composition adds the water of 7 times of volumes respectively, mixes, and the coating cladding process is coated on the metope routinely, and waiting after the seasoning is that nature is docile and obedient in metope.Because different coating methods, fiber coating will show different texture on metope, and therefore, the present invention is roller coating, show as the top layer and have pattern as the embossment.
Claims (10)
1, a kind of fibre-bearing coating composition comprises following component: natural fiber and/or artificial fiber, tenderizer, mould inhibitor, cationics, tackiness agent; Described natural fiber can be selected from vegetable fibre, animal fibre or its composition; Described vegetable fibre is the fiber of plant seed, stem, skin, leaf, bar; Described animal fibre is hair of animal or the natural fiber that secretory product constitutes; The optional regenerated fiber of described artificial fiber, synthon.
2, according to the fibre-bearing coating composition of claim 1, described composition can be following parts by weight of component: natural fiber and/or artificial fiber 40-98, tenderizer 0.1-0.3, mould inhibitor 0.05-0.15, cationics 0.05-0.15, tackiness agent 5-15.
3, according to the fibre-bearing coating composition of claim 1 or 2, described composition can be following parts by weight of component: natural fiber and/or artificial fiber 68-90, tenderizer 0.05-0.25, mould inhibitor 0.08-0.12, cationics 0.08-0.12, tackiness agent 8-12.
4, according to the fibre-bearing coating composition of claim 1 or 2, described composition is following parts by weight of component: natural fiber and/or artificial fiber 88, tenderizer 0.2, mould inhibitor 0.1, cationics 0.1, tackiness agent 10.
5, according to the fibre-bearing coating composition of claim 1 or 2, this natural fiber and/or artificial fiber can be the nature color or pass through the painted fiber of known staining agent; Described regenerated fiber, synthon are viscose fiber, cellulose acetate, seaweed fiber, terylene, polypropylene fibre, acrylic, nylon.
6, according to the fibre-bearing coating composition of claim 1 or 2, described tenderizer can be hexadecyl three (the fragrant penta tetrol base ammonium oxide of three hydroxyls) three (the fragrant penta tetrol base of three hydroxyls) ammonium oxide; Described mould inhibitor can be halogeno-amine; Described cationics can be positively charged ion silicone oil; Described tackiness agent can be polyvinyl alcohol.
7, according to the fibre-bearing coating composition of claim 1 or 2, described composition also can further comprise: an amount of coating powder, disinfectant, water-resisting agent, fire retardant, spun gold, filamentary silver, colored powder, color phosphor, color fluorescence wire material or its composition.
8, according to the fibre-bearing coating composition of claim 7, described coating powder can be dry powder, mineral powder, rock powder; Described disinfectant can be titanium oxide, benzoic acid and sodium benzoate; Described water-resisting agent can be the water-latex type mixture of palm wax and acrylate copolymer emulsion; Described fire retardant can be halogen contained compound.
9, the preparation method of the fibre-bearing coating composition of a kind of claim 1-8 may further comprise the steps:
Fiber softening is handled;
Fiber is added mould inhibitor carry out the mildew-resistant processing;
In the fiber of above-mentioned processing, add cationics;
Fiber drying typing with above-mentioned adding cationics;
In above-mentioned typing fiber, add tackiness agent, dryness finalization;
Or also further comprise fiber with the staining agent processing of dyeing;
Or after also further comprising adding coating powder, disinfectant, water-resisting agent, fire retardant, an amount of spun gold, filamentary silver, colored powder, color phosphor or color fluorescence silk and composition thereof, add tackiness agent again, dryness finalization.
10, the application of the fibre-bearing coating composition of a kind of claim 1-8 aspect building wall decoration, described fibre-bearing coating composition adds the water of 3-7 times of volume or weight, mixes, and brushing or roller coating are on metope.