CN1618529A - Part for motor bicycle - Google Patents
Part for motor bicycle Download PDFInfo
- Publication number
- CN1618529A CN1618529A CN 200410094691 CN200410094691A CN1618529A CN 1618529 A CN1618529 A CN 1618529A CN 200410094691 CN200410094691 CN 200410094691 CN 200410094691 A CN200410094691 A CN 200410094691A CN 1618529 A CN1618529 A CN 1618529A
- Authority
- CN
- China
- Prior art keywords
- coating
- motor bicycle
- filming
- individual layer
- baking temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A part 1 for the motorcycle has a coating film 3 formed on a surface of a casting raw material 2. The coating film 3 is formed by forced-drying a wet coating consisting of a transparent acrylic silicone resin coating containing a curing catalyst setting a drying temperature T so as to be 50[deg.]C<=T<=80[deg.]C. To provide parts for a motorcycle which have a low production cost, and have a coating film where any blister, pinhole or the like is produced.
Description
Technical field
The present invention relates to part for motor bicycle.
Background technology
Part for motor bicycle, when requiring its function because the face that exposes on the surface of vehicle is more, so also require its outward appearance commodity simultaneously.In addition, the reduction of environmental pollution danger has in recent years become needs of society.The present invention is guaranteeing in the application parts on the basis of sufficient outward appearance commodity, when simplifying coating process itself, owing to also can reduce the ratio that is included in the organic solvent in the coating, when improving commodity, can reduce manufacturing cost and environmental pollution danger.
In the past, use the coating of acrylic melamine class or acrylic-amino formic acid lipid from cost and film performance two aspects.In addition, in the coating process of parts,, be important so after operation finishes, enter the state of line off at short notice as far as possible owing to require to improve its production efficiency.Therefore, baking temperature need be set at 140 ℃ than the highland and shorten drying time.Yet, for example on the aluminium alloy casting parts, have the casting flaw of pore etc. and in this defective in surface opening, the gas that is enclosed in is wherein handled by the drying under the high temperature and expansion widely, swell in the film coated surface generation, for this reason, motion has the operation that will implement that making films and constitute 2 layers or 3 layers and then the method (with reference to patent documentation 1) that drying process is set in each aspect.
No. 2947597 specification of [patent documentation 1] special permission
Yet filming in the past has the problem that weight of coated paint, electric power consumption and application man-hour are more, production cost is high.
Summary of the invention
The purpose of this invention is to provide a kind of low above-mentioned two-wheeled application cast component of using of filming of production cost that has.
According to being the purpose that reaches the invention described above, part for motor bicycle of the present invention, it is characterized in that: after forming the filming of individual layer on casting ingot surface and its machined surface, under the baking temperature of 50 ℃≤T≤80 ℃, carry out force drying as 1 secondary response, then by finishing reaction at normal temperatures, imposing thickness is the application of the above individual layer of 10 μ m.
In addition, part for motor bicycle of the present invention, it is characterized in that: after forming the filming of individual layer on casting ingot surface and its machined surface, under the baking temperature of 50 ℃≤T≤80 ℃, carry out force drying as 1 secondary response, then by finishing reaction at normal temperatures, imposing thickness is the application of the above individual layer of 20 μ m.
And then, described filming, be that acrylic silicon resin coating below 50% constitutes by the amount that makes organic solvent be desirable, in addition, use curing catalysts, and use will be under the baking temperature of 50 ℃≤T≤80 ℃ reactivity to reach the coating that time of 60% adjusts to below 2 hours be desirable.
In addition, in order to constitute the coloring and coating parts, the fuel that is blended in the coating is that nonpolarity pigment is desirable.
(invention effect)
In the present invention, by baking temperature T being set in 50 ℃≤T≤80 ℃, filming to become the monolayer constructions will that applies 1 time, even be present in the defective of pore as the surface opening of the cast component of coated object etc., the expansion that is comprised in the gas in this defective is also very little, expand or pore thereby on coated surface, do not produce, even perhaps generation is also very little, the decline that can not bring commodity value.The amount that makes organic solvent is the acrylic silicon resin coating below 50%, adjust to below 2 hours by using curing catalysts reactivity under the temperature of 50 ℃≤T≤80 ℃ can be reached time of 60%, simultaneously, because its good connecting airtight property and viscosity characteristics, so the formation of filming for the individual layer of 1 coating is desirable.In addition, the organic solvent amount of coating in the past is more than 60%.
Such the present invention takes place and need be coated with 2 times, the coating process that is coated with 3 times application cast component and change into and being coated with 1 time by making in the past for fear of defective products, can omit operation, reduce the use amount and the defective goods incidence of coating.
On this basis, though can obtain sufficient film performance with above the filming of individual layer of 10 μ m in the past, further be more than the 20 μ m by making this, can also improve the film performance when being in unusual condition (collisions of gravelstone and sharp sand etc.).The thickness increase of filming in addition, also has the benefit that is difficult in appearance reveal and improves the commodity performance.
In addition, by setting forced drying temperature, also can reduce consumption electric power than the lowland.The effect that these all bring big cost to reduce.And then, be below 50% by the amount that makes the organic solvent in the coating, the contribution to the reduction carrying capacity of environment when reducing weight of coated paint is also big.
About painted, evenly mix difficult acrylic silicon resin for pigment, adapt to nonpolarity pigment by making, can provide outward appearance good coloring and coating parts with pigment addition same.
Description of drawings
Fig. 1 is two-wheeled side view with the anterior wheel of application.
Fig. 2 is the 2-2 line profile of Fig. 1.
Fig. 3 is two-wheeled side view.
Among the figure: the anterior wheel (part for motor bicycle) of 1-application, the anterior wheel (casting ingot) of 2-, 3-films.
The specific embodiment
In Fig. 1, Fig. 2,, be the parts that form film (Dry Film) on the surface of the anterior wheel 2 of aluminium alloy casting blank as the anterior wheel 1 of the application of part for motor bicycle.This film 3 is the not dry coating (WetCoating) that is made of the clear acrylic silicon resin coating that comprises curing catalysts to be set in 50 ℃≤T of baking temperature≤80 ℃ carry out filming of force drying.
(1) coating adjustment
As the clear acrylic silicon resin coating, use commercially available Nei Aoxilika (neosilica) G007 (Yi Samu paint company system, trade name) etc.Baking temperature T is 50 ℃≤T≤80 ℃, during in T＜50 ℃, can not be reacted fully with the short time.In addition, during in T＞80 ℃, expand from the pore on aluminum surface.Heat time heating time, t was set in 20min≤t≤120min.But, when t＜20min, can not be reacted fully.In addition, the long-living output of activity time will descend when t＞120min.
Use coating as the formation of filming, also can use painted acrylic silicon resin coating.At this moment, in pigment, organic class that is fit to and mineral-type fuel etc., in addition, the use level Lp of this pigment is 1 weight portion≤Lp≤20 weight portions with respect to clear acrylic silicate resin constituent 100 Unit Weight portions.At this moment, a some weight portion can not obtain sufficient tinting strength, tinting power in Lp＜1.In addition, Lp＞20 weight portions rerum natura of can not being filmed fully.
(2) painting operation
(a) use aluminium alloy (JISH2211) to the anterior wheel 2 of two-wheeled usefulness, implement degreasing and chemical membrane processing as Coating Pretreatment with weight casting and casting die casting.(b) to anterior wheel 2 usefulness gunitees coating clear acrylic silicon resin coating.(c) be placed on the surface with 2 minutes the not anterior wheel 2 of dry coating is arranged.(d) anterior wheel 2 is arranged in the drying oven, carries out baking temperature T=50 ℃, heat time heating time t=30min force drying and the thickness that obtains constituting by the transparent propene silicon acid resinous be 10～60 μ m film 3.
(3) film 3 about above-mentioned, check its surface state, what can't see expansion, pore etc. is perfect.
The relation of table 1 expression baking temperature and power consumption, pore etc.In the table, after being meant drying, so-called carrying whether can carry at once.
[table 1]
| Baking temperature T (℃) | Power consumption | Pore | Connecting airtight property | Carrying | Rapid-drying properties |
| Normal temperature≤T＜50 | ????○ | ????○ | ??○ | ????× | ??× |
| ??50≤T≤80 | ????△ | ????○ | ??○ | ????○ | ??○ |
| ??T＞80 | ????× | ????× | ??○ | ????○ | ??○ |
According to table 1, the meaning that baking temperature T is set in 50 ℃≤T≤80 ℃ is understood.
As part for motor bicycle, as shown in Figure 3, remove anterior wheel 2 and can also enumerate following part in addition.Promptly, rear wheel 4 as the aluminium alloy casting parts, swing arm 5 as the aluminium alloy casting parts, engine body 6 as the aluminium alloy casting parts, vehicle frame (comprising seat guide rail) 7 as the aluminium alloy casting parts, as the upper beam 8 of aluminium alloy casting parts, as the bottom girder 9 of aluminium alloy casting parts, as outer tube 10 of the front suspension of aluminium alloy casting parts etc.
Claims (5)
1. part for motor bicycle is characterized in that:
After forming the filming of individual layer on casting ingot surface and its machined surface, under the baking temperature of 50 ℃≤T≤80 ℃, carry out force drying as 1 secondary response, then by finishing reaction at normal temperatures, imposing thickness is the application of the above individual layer of 10 μ m.
2. part for motor bicycle is characterized in that:
After forming the filming of individual layer on casting ingot surface and its machined surface, under the baking temperature of 50 ℃≤T≤80 ℃, carry out force drying as 1 secondary response, then by finishing reaction at normal temperatures, imposing thickness is the application of the above individual layer of 20 μ m.
3. according to claim 1 or 2 described part for motor bicycle, it is characterized in that: described filming is that acrylic silicon resin coating below 50% constitutes by the amount that makes organic solvent.
4. according to claim 1,2 or 3 described part for motor bicycle, it is characterized in that: use curing catalysts, and use will be under the baking temperature of 50 ℃≤T≤80 ℃ reactivity reach time of 60% and adjust to coating below 2 hours.
5. according to claim 1,2,3 or 4 described part for motor bicycle, it is characterized in that: the fuel that is blended in the coating is nonpolarity pigment.