CN1600796A - Water-soluble poly-p-phenylene ethynylene and synthetic method - Google Patents
Water-soluble poly-p-phenylene ethynylene and synthetic method Download PDFInfo
- Publication number
- CN1600796A CN1600796A CN 200410053072 CN200410053072A CN1600796A CN 1600796 A CN1600796 A CN 1600796A CN 200410053072 CN200410053072 CN 200410053072 CN 200410053072 A CN200410053072 A CN 200410053072A CN 1600796 A CN1600796 A CN 1600796A
- Authority
- CN
- China
- Prior art keywords
- group
- reaction
- side chain
- synthetic
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of water soluble polymer that alternating phenyl and ethynul is conjugate backbone and the prepn method. In the invention, the compound being two ethynyl at benzene ring para-position is used as raw material to synthetise a series conjugate polymer that branch conteins water soluble perssad by a series organic reaction of metal catalyzing etc, water soluber perssad is divided to four kinds of neutral, positive, negative and zwitter ions, the main composition of water soluble perssad is the one containing oxygen ether, the main composition of positive ion water soluble perssad is the one containing quaternary ammonium salt, the main composition of negative ion is the one containing sulfonate, phosphate and carboxylate, zwitter into water soluble perssad is combination of negative and position ion perssads. On the basic of composed said kind water soluble conjugate polymer, its applications in biological sensor is researched by the invention.
Description
Technical field
The present invention relates to a class and contain water-soluble group, so that alternately phenyl and ethynyl are the synthetic and application of the polymkeric substance of conjugated main chain.Especially the cation type water-soluble conjugated polymers is synthetic, has adopted first synthetic neutral polymer, replaces the transformation of ammonia to the nitrogen positive ion by the quaternary ammoniated alkyl of finishing then, has realized the cationization of polymkeric substance and water-soluble.The synthetic method of zwitter-ion soluble conjugated polymer also is provided simultaneously.
Background technology
The water-soluble of polymkeric substance generally is to realize by introducing long ether oxygen chain and charged group.In in the past 5 years, the conjugated polymers (ionic conjugated polymers) that contains charged groups, as a member in the conjugated polymers, on the basis that has kept conjugated polymers good electron and optical property, distinctive water-soluble with it, and can pass through electrostatic attraction bonded characteristic with the material of oppositely charged, in the application of traditional chemical sensor and biosensor, demonstrate increasing potentiality.
1999, L.-H.Chen etc. have reported first with the highly effective detection purpurine cationoid quencher of water-soluble PPV sulfonate anionic type polymkeric substance energy, and find that polymkeric substance is by the fluorescence of cancellation can quencher forms the protein of title complex and recovers fully by adding therewith.Can expect, utilize this characteristic can on quencher, introduce range protein part or single-stranded dna fragment, thereby realize easily corresponding proteins matter and DNA are detected by cancellation and the recovery of observing fluorescence.It is being to have launched preliminary research aspect the field of biosensors of material with the soluble conjugated polymer that A.J.Heeger, G.C.Bazan, F.Wudl, D.W.McBranch etc. have begun.
But at present, the ionic soluble conjugated polymer system of research mainly also concentrates on poly-on vinylbenzene support, poly-fluorenes (PPV, the PF) system, and have only anionic PPV derivative to be used for this respect research, need the new material of exploitation to adapt to many-sided requirement with positively charged ion and different conjugated structures.The mechanism research of this type of transmitter simultaneously also is in the preliminary stage, gets that this body structure of material, quencher are selected, the external environment variation has crucial meaning to the influence of detection sensitivity for the development of new sensing material clear.P-phenylene vinylene's support (PPE) is a class conjugated polymers that is used as the change in fluorescence transmitter the earliest.Since its firm bar-shaped backbone structure, and be easy to intermolecular phenyl ring and phenyl ring interaction, and therefore synthetic this type of water-soluble polymers extremely helps to study the influence of the morphological structure of conjugated polymers in the aqueous solution to quenching effect.And the height delocalization of single exciton and along conjugated main chain fast the energy transfer research also make water-soluble p-phenylene vinylene support in the aqueous solution, the oppositely charged material be had the fluorescent quenching effect of amplification.Up to the present, PPE class conjugated polymer derivant has been made into solution or has made film and has been used to detect amethyst or TNT organic micromolecule.
For cationic p-phenylene vinylene support, its water-soluble can realization by regulating quaternary ammoniated degree, and zwitter-ion p-phenylene vinylene support both can detect the negatively charged ion quencher and can detect the positively charged ion quencher.This has crucial meaning to PPE class water-soluble polymers as the biological and chemical transmitter.
Summary of the invention
The objective of the invention is to synthetic a series of be conjugated main chain with p-phenylene vinylene's support, contain the compound of water soluble group.Except common neutrality, anionic, cation type water-soluble conjugated polymers, the present invention has also synthesized a kind of novel amphoteric ion type soluble conjugated polymer.
Purpose of the present invention is to provide a kind of method of novel synthesizing cationic soluble conjugated polymer.The experiment proved that, this method to the purification of polymkeric substance and improve polymkeric substance water-soluble tangible effect arranged all.
It is conjugated main chain with p-phenylene vinylene's support that the present invention has synthesized a series of, contains the compound of water soluble group.In common neutrality, on the basis of cationic and anionic group, the notion of negative and positive double ion type water soluble group has been proposed.We provide a kind of via neutral polymer simultaneously, by quaternary ammoniated, obtain the synthetic method of Ionomer.
The molecular structure of compounds of mentioning among the present invention is as follows:
Wherein, R, R ', R ", R is selected from any in the following groups: R respectively
1R
2R
3R
4N
+, R
5X, R
6N
+R
7R
8R
9X, R
10R wherein
1, R
2, R
3, R
4, R
5, R
6, R
7, R
8, R
9, R
10Be respectively in the following groups any: alkyl, alkoxyl group, halogen band alkyl, aryl, halogenated aryl, fluorenyl, heterocyclic arene or alkylaromatic hydrocarbon;
X is any in the following groups: sulfonic acid group, phosphate group and hydroxy-acid group.
Among the present invention, R, R ', R ", R lays respectively on the C2-C5 position of phenyl ring on the conjugated chain.
Among the present invention, R, R ', R ", R can be identical group simultaneously, also can be diverse group.
According to above-described compound structure, more typically be listed below four kinds:
(1) R, R ', R ", R is identical group, its structure is R
1R
2R
3R
4N
+, R
1For carbonatoms is 2 alkoxy chain, R
2R
3R
4Be ethyl, its structural formula is as follows:
(2) R, R ', R ", R is identical group, the structure that they are taked is R
6N
+R
7R
8R
9X, R
6For carbonatoms is 2 alkoxy chain, R
7R
8Be ethyl, R
9Be propyl group, X is a sulfonic group, and its structural formula is:
(3) R, R ' are identical group, and the structure that they are taked is R
5X, R
5For the C atomicity is 3 alkoxy chain, X is a sulfonic group.And R ", R is identical group, the structure that they are taked is R
1R
2R
3R
4N
+, R
1For carbonatoms is 2 alkoxy chain, R
2R
3R
4Be ethyl, its structural formula is:
(4) R, R ', R ", R is identical group, the structure that they are taked is R
5X, R
5For carbonatoms is 3 alkoxy chain, X is a sulfonic group, and its structural formula is:
Above-claimed cpd among the present invention can be divided into cation type water-soluble conjugated polymers, anionic soluble conjugated polymer and amphoteric ion type soluble conjugated polymer, and its synthetic method is as follows respectively:
(1) the cation type water-soluble conjugated polymers is synthetic
1. side chain is monomeric the synthesizing of benzyne that contains alkyl-substituted amino group
With 1,4-dibromo Resorcinol is a masterplate, adds the 2-chloro triethylamine hydrochloride of 2～3 times of amounts under the base catalysis condition, and 50～60 ℃ of temperature of reaction are the compd A that contains alkyl-substituted amino group thereby obtain side chain.
The trimethyl silicane alkynes of A and 2～3 times is mixed in the solvent of Diisopropylamine, react as catalyzer with the triphenyl phosphorus palladium of cuprous iodide and divalence, 70～80 ℃ of temperature of reaction, obtaining side chain is the benzyne monomer A that contains alkyl-substituted amino group
1
2. side chain is contain alkyl-substituted amino group monomeric synthetic to iodobenzene
With 1,4-diiodo-Resorcinol is a masterplate, adds the 2-chloro triethylamine hydrochloride of 2～3 times of amounts under the base catalysis condition, and 50～60 ℃ of temperature of reaction are the compd A that contains alkyl-substituted amino group thereby obtain side chain
2
The synthetic method of cation type water-soluble conjugated polymers has two kinds:
First kind: via the neutral conjugation polymkeric substance by the quaternary ammoniated cation type water-soluble conjugated polymers polymkeric substance that obtains
[1] the neutral conjugation polymkeric substance is synthetic
With A
1And A
2With mixing in 1: 1, toluene was made solvent, and zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 70～80 ℃ of temperature of reaction, and it is the neutral conjugation polymkeric substance that contains alkyl-substituted amino group that reaction obtains side chain.
[2] the quaternary ammoniated cation type water-soluble conjugated polymers that obtains of neutral conjugation polymkeric substance
The neutral conjugation polymer dissolution that obtains adds a monobromethane of 3～4 times of amounts, 60～65 ℃ of temperature of reaction in tetrahydrofuran (THF).React and promptly obtain the cation type water-soluble conjugated polymers after three days.
Second kind: obtain the cation type water-soluble conjugated polymers by the cationic monomer polymerization
[1] side chain contains monomeric the synthesizing of benzyne of quaternary amine group
Side chain is the benzyne monomer A that contains alkyl-substituted amino group
1React in tetrahydrofuran solution with a monobromethane of 3～4 times of amounts, 60～65 ℃ of temperature of reaction, obtaining side chain is the benzyne monomer A of quaternary amine group
3
[2] side chain contains the monomeric synthetic to iodobenzene of quaternary amine group
Side chain is the compd A that contains alkyl-substituted amino group
2React in tetrahydrofuran solution with a monobromethane of 3～4 times of amounts, 60～65 ℃ of temperature of reaction, obtain side chain and be the quaternary amine group to the iodobenzene monomer A
4
[3] the cation type water-soluble conjugated polymers is synthetic
With A
3And A
4With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, and 50～60 ℃ of reactions of temperature of reaction obtain containing the cation type water-soluble conjugated polymers of amine salt group.
(2) the anionic soluble conjugated polymer is synthetic
(1) the sulfonate soluble conjugated polymer is synthetic
1. the side chain end group is that sulfonic benzyne is monomeric synthetic
With 1,4-dibromo Resorcinol is a masterplate, adds 1 of 2～3 times of amounts under the base catalysis condition, the 3-N-morpholinopropanesulfonic acid lactone, and 50～60 ℃ of temperature of reaction are sulfonic compd B thereby obtain end group.
The trimethyl silicane alkynes of B and 2～3 times is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, 60～65 ℃ of temperature of reaction, and obtaining end group is sulfonic group benzyne monomers B
1
2. the side chain end group is sulfonic monomeric synthetic to iodobenzene
With 1,4-diiodo-Resorcinol is a masterplate, adds 1 of 2～3 times of amounts under the base catalysis condition, the 3-N-morpholinopropanesulfonic acid lactone, and 50～60 ℃ of temperature of reaction are sulfonic compd B thereby obtain end group
2
3. the sulfonate conjugated polymers is synthetic
With B
1And B
2With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, it is sulfonic anionic soluble conjugated polymer that reaction obtains end group.
(2) the phosphoric acid salt soluble conjugated polymer is synthetic
1. the side chain end group is monomeric the synthesizing of benzyne of phosphate
With 2,5-two bromo-1,4-2-bromo phenetole is a masterplate, is solvent with dimethylbenzene, adds the tributyl phosphate of 2～3 times of amounts, 50～60 ℃ of temperature of reaction, thus obtain the Compound C that end group is a phosphate.
The trimethyl silicane alkynes of C and 2～3 times is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, and it is phosphate benzyne monomer C that temperature of reaction obtains end group for 60～70 ℃
1
2. the side chain end group is the monomeric synthetic to iodobenzene of phosphate
With 2,5-two iodo-1,4-2-bromo phenetole is a masterplate, is solvent with dimethylbenzene, add the tributyl phosphate of 2～3 times of amounts, thereby temperature of reaction obtains the Compound C that end group is a phosphate for 50～60 ℃
2
3. the phosphoric acid salt soluble conjugated polymer is synthetic
With C
1And C
2With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 60～70 ℃ of temperature of reaction, reaction obtains the anionic soluble conjugated polymer that end group is a phosphate.
(3) the carboxylate salt soluble conjugated polymer is synthetic
1. the side chain end group is monomeric the synthesizing of benzyne of carboxylicesters
With 2,5-two bromo-methyl benzoate are masterplate, 2～3 times trimethyl silicane alkynes is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, 60～70 ℃ of temperature of reaction, obtaining end group is the benzyne monomer D of carboxylicesters
1
2. the side chain end group is the synthetic of carboxylicesters neutral conjugation polymkeric substance
With D
1With 2,5-two iodo-methyl benzoate mixed with 1: 1, and toluene is made solvent, and zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, and reaction obtains the neutral conjugation polymkeric substance that the side chain end group is a carboxylicesters.
3. the carboxylate salt soluble conjugated polymer is synthetic
With the side chain end group that obtains is the sodium hydroxide solution that the neutral conjugation polymkeric substance of carboxylicesters places 2mol/L, reflux one day, and 90 ℃ of temperature of reaction obtain the carboxylate salt soluble conjugated polymer.
(3) the zwitter-ion soluble conjugated polymer is synthetic
1. side chain is that zwitterionic benzyne is monomeric synthetic
Side chain is the benzyne monomer A that contains alkyl-substituted amino group
1With 1 of 3～4 times of amounts, the 3-N-morpholinopropanesulfonic acid lactone reacts in acetonitrile solution, and temperature of reaction obtains the benzyne monomer E that side chain contains the zwitter-ion group for 50 ℃
1
2. side chain is zwitterionic monomeric synthetic to iodobenzene
Side chain is the compd A that contains alkyl-substituted amino group
2With 1 of 3～4 times of amounts, the 3-N-morpholinopropanesulfonic acid lactone reacts in acetonitrile solution, 50 ℃ of temperature of reaction obtain side chain contain the zwitter-ion group to iodobenzene monomer E
2
3. the zwitter-ion soluble conjugated polymer is synthetic
With E
1And E
2Mixed with 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, reaction obtains the zwitter-ion soluble conjugated polymer that side chain contains the zwitter-ion group.
In the synthetic method that the present invention mentions, go up to the compound of ethynyl is an important monomer at 1,4 of phenyl ring, thus monomer with to halogeno-benzene generation organo-metallic catalyzed reaction, obtain the conjugated main chain of growing.And water miscible realization then has to generate water-soluble monomer earlier, and further reaction obtains water-soluble polymers and generates non-soluble polymer earlier, obtains two kinds of methods of water-soluble polymers by reaction (as quaternary ammoniated) again.
The present invention studies its spectral response curve on the basis of the ionic p-phenylene vinylene support that synthesizes, and studies itself and the fluorescent quenching effect that has the counter ion material.See shown in Figure 4.This compounds is widely used in biosensor.
Description of drawings
Fig. 1 illustrates by the quaternary ammoniated synthetic method route that obtains the ionic conjugated polymers via neutral polymer.
The synthetic method route diagram of a kind of negative and positive double ion of Fig. 2 type conjugated polymers.
Fig. 3 is a kind of synthetic method route diagram of anionic soluble conjugated polymer.
Fig. 4. cationic p-phenylene vinylene supports in the aqueous solution by K
4Fe (CN)
6The Stem-Volmer graphic representation of cancellation.
Embodiment
In order to understand content of the present invention better, further specify technical scheme of the present invention below by specific embodiment and legend.
Embodiment 1, and it is synthetic that the cation type water-soluble p-phenylene vinylene supports
1, synthetic (compound 1) of 4-pair-[3-(nitrogen, nitrogen-diethyl amino)-1 '-propoxy-]-2,5 diiodo-benzenes
Add in the 500mL reaction flask salt of wormwood (33.12g, 0.24mol), 1, (14.48g, 0.04mol), and 300mL acetone, mixture refluxed about 30 minutes 4-diiodo-Resorcinol.(16.51g 0.096mol) adds in the reaction flask, and reflux state reacted three days down with 2-chloro triethylamine hydrochloride then.Reaction mixture filters, and filtrate is revolved to steam to remove and desolvated.Enriched product is poured in the water, uses extracted with diethyl ether three times, and the organic layer that obtains washes twice with the 10%NaOH aqueous solution, washing twice, twice of saturated common salt washing.The solution anhydrous magnesium sulfate drying filters, and revolves to boil off to desolventize, and obtains crude product.Crude product gets white crystal 11g with the ethanol/water recrystallization, productive rate 59%.
1H?NMR(400MHz，CDCl
3，ppm)δ7.23(s，2H)，4.02(t，4H)，2.93(t，4H)，2.67(q，8H)，1.10(t，12H)。
13C?NMR(400MHz，CDCl
3，ppm)δ153.4，123.4，86.5，69.8，52.0，48.4，12.6。
1,4-diacetylene-2, synthetic (compound 2) of 5-pair-[3-(nitrogen, nitrogen-diethyl amino)-1 '-propoxy-] benzene
6.61g (0.01mol) compound 1,0.0952g (0.5mmol) CuI, 0.35g (0.5mmol) PdCl
2(PPh
3)
2, be dissolved in the 40mL Diisopropylamine.2.156g (0.022mol) trimethyl silicane alkynes adds in the above solution.Reflux conditions is reaction 6h down.Reaction mixture is spin-dried for, and enriched material is poured in the water, uses dichloromethane extraction, and organic layer washes twice with water, and the saturated common salt washing is the anhydrous MgSO in back once
4Dry.Organic solvent rotary evaporation under reduced pressure is removed, and the solid that obtains is dissolved in the methyl alcohol, adds the KOH aqueous solution (1g is dissolved in the 2mL water) and stirs one hour.Rotary evaporation removes and desolvates then, and solid is dissolved in the methylene dichloride, washes twice with water, and saturated common salt is washed once.Organic layer removes after with anhydrous magnesium sulfate drying and desolvates.CH with the HCl of 1mol/L
3OH solution acidified solid, the salt that obtains is dissolved in the 100mL acetone, and vigorous stirring is spent the night.Filter, obtain the hydrochloride of product.Use the methanol/ethanol recrystallization, get white crystal.Salt is dissolved in the 150mL water, drips K
2CO
3The aqueous solution (30g K
2CO
3Be dissolved in 150mLH
2Among the O), the organic layer that obtains extracted with diethyl ether three times wash twice with water, and saturated common salt is washed once, uses anhydrous magnesium sulfate drying.Filter, revolve steaming, obtain yellow crystals 3.1g, productive rate 72%.
1H?NMR(400MHz，CDCl
3，ppm)δ6.99(s，2H)，4.07(t，4H)，3.34(s，2H)，2.93(t，4H)，2.66(q，8H)，1.09(t，12H)。
13C?NMR(400MHz，CDCl
3，ppm)δ154.4，118.0，113.6，83.0，80.1，68.7，51.9，48.3，12.4。
Neutral polymer P's is synthetic
0.420g (0.750mmol) compound 1 and 0.272g (0.765mmol) compound 2, the Pd (PPh of 51.9mg (0.045mmol)
3)
4And in the CuI of 42.8mg (0.225mmol) the adding 50mL round-bottomed flask, the mixing solutions of Diisopropylamine and toluene (3: 7,35mL) add subsequently.Reactant is heated to 70 ℃, refluxes 24 hours.After reaction finished, mixture was poured in the water, and with chloroform extraction three times.Organic layer is with 50% NH
4OH washes twice, and washing twice after the saturated common salt washing once, is used anhydrous MgSO
4Dry.Solvent rotates under reduced pressure to be removed, and solid is dissolved in the 10mL chloroform, splashes into then to make in the methyl alcohol to be precipitated out twice so repeatedly.Obtain yellow solid at last.0.42g, productive rate 85%.
1H?NMR(400MHz，CDCl
3，ppm)δ7.04(s，2?H)，4.12(t，4H)，2.95(t，4H)，2.70(q，8H)，1.08(t，12H)。
13C?NMR(400MHz，CDCl
3，ppm)δ153.8，117.5，114.6，91.9，68.8，52.1，48.4，12.6。
Synthesizing of cation type polymer
Add the neutral polymer P of 0.330g and the tetrahydrofuran (THF) of 20mL in the 50mL round-bottomed flask.Add subsequently monobromethane (1.09g, 10mmol) and the DMSO of 5mL.Reaction mixture is heated to 50 ℃ and lasting five days.Obtain yellow mercury oxide and filtration, get 0.41g product, productive rate 75% after the drying.
1H?NMR(400MHz，D
2O，ppm)δ7.26(br，2H)，4.44(br，4H)，3.73(br，18H)，3.60(br，2.2H)，3.40(br，4.3H)，3.31(br，5.4H)，1.20(br，12H)。
13C?NMR(400MHz，D
2O，ppm)δ153.3，117.6，114.1，91.4，64.8，63.6，58.5，56.0，54.3，51.4，49.5，9.1，7.6。
Synthetic route is seen shown in Figure 1.
Embodiment 2, and it is synthetic that the water-soluble p-phenylene vinylene of zwitter-ion supports
Add the neutral polymer P of 0.330g and the acetonitrile of 20mL, the tetrahydrofuran (THF) of 20mL in the 50mL round-bottomed flask.Add 1 subsequently, and the 3-third semi-annular jade pendant acid lactone (1.09g, 10mmol).Reaction mixture is heated to 50 ℃ and lasting five days.Obtain white precipitate and filtration, get 0.41g product, productive rate 75% after the drying.
1H?NMR(400MHz，D
2O，ppm)δ7.21(br，2H)，4.28(br，4H)，3.41(br，16H)，2.79(br，4H)，1.96(br，4H)，1.21(br，12H)。Synthetic route is seen shown in Figure 2.
Embodiment 3, and cationic p-phenylene vinylene supports in the aqueous solution by K
4Fe (CN)
6The research of cancellation.
Polymer concentration 1 * 10
-6, the solution pH value is 7, NaCl concentration is 0.Under the situation of polymkeric substance lower concentration, the research yellow prussiate of potash is to its cancellation effect.See shown in Figure 4.
Embodiment 4, and it is synthetic that anionic water-soluble sulfonate p-phenylene vinylene supports
Compound 1
7g (0.044mol) NaOH is dissolved in the 100ml ethanol, is added drop-wise to 7.24g (0.02mol) compound 5 and is dissolved in the 100ml alcoholic acid solution, stirs 1h.5.37g (0.044mol) 1, the 3-third semi-annular jade pendant lactone is dissolved in the 50mL ethanol, adds above-mentioned solution, reaction 12h.Suction filtration gets crude product, and solid is made recrystallization with dehydrated alcohol and water, gets white crystal 7.608g, productive rate 58%.1H?NMR(400MHz，DMSO，ppm)δ7.33(s，2H)，4.04(t，4H)，3.07(t，4H)，2.11(m，4H)。
Compound 2
6.50g (0.01mol) compound 1,0.0952g (0.5mmol) CuI, 0.35g (0.5mmol) PdCl
2(PPh
3)
2, be dissolved in the 40mL Diisopropylamine.2.156g (0.022mol) trimethyl silicane alkynes adds in the above solution.Reflux conditions is reaction 24h down.Reaction mixture filters, and the solid that obtains is soluble in water with the graphite decolouring, and the rotary evaporation under reduced pressure of the solution after the filtration removes and anhydrates.The crude product water recrystallization that obtains three times, at last light yellow needle-like crystal 2.38g, productive rate 53%.
1HNMR(400MHz，D
2O，ppm)87.15(s，2H)，4.14(t，4H)，3.34(s，2H)，2.67(t，4H)，2.06(m，4H)。
Synthesizing of sulfonate polymer
0.650g (1mmol) compound 1 and 0.446g (1mmol) compound 2, the Pd (PPh of 0.0347g (0.03mmol)
3)
4And in the CuI of 0.0057g (0.03mmol) the adding 50mL round-bottomed flask, Diisopropylamine and water and N, and the mixing solutions of N-dimethylformamide (DMF) (1: 2: 3,60mL) add subsequently.Reactant is heated to 60 ℃, refluxes 24 hours.After reaction finished, mixture splashed into 1L methyl alcohol: acetone: in ether=1: 4: 5 mixing solutions.Filtration obtains precipitation, and is soluble in water, adds 0.1gNa
2S filters, and filtrate splashes in a large amount of acetone, filters to such an extent that precipitate.Three times so repeatedly, obtain final product 0.54g, productive rate 56%.
1H?NMR(400MHz，CDCl
3，ppm)δ7.18(s，2H)，4.21(t，4H)，2.77(t，4H)，2.15(t，4H)。Synthesis route is shown in Figure 3 as follows.
Claims (5)
1, a kind of compound is characterized in that having following molecular formula
Wherein, R, R ', R ", R is selected from any in the following groups: R respectively
1R
2R
3R
4N
+, R
5X, R
6N
+R
7R
8R
9X, R
10Here R
1, R
2, R
3, R
4, R
5, R
6, R
7, R
8, R
9, R
10Be respectively in the following groups any: alkyl, alkoxyl group, halogen band alkyl, aryl, halogenated aryl, fluorenyl, heterocyclic arene or alkylaromatic hydrocarbon;
X is any in the following groups: sulfonic acid group, phosphate group and hydroxy-acid group.
2, according to the said compound of claim 1, it is characterized in that R, R ', R ", R lays respectively at the C of phenyl ring on the conjugated chain
2-C
5On the position.
3, according to the said compound of claim 1, it is characterized in that R, R ', R ", R is identical group simultaneously, perhaps is diverse group.
4, compound according to claim 1 is characterized in that R, R ', R ", R is the one of the following kind:
(1) R, R ', R ", R is identical group, its structure is R
1R
2R
3R
4N
+, R
1For carbonatoms is 2 alkoxy chain, R
2R
3R
4Be ethyl, its structural formula is as follows:
(2) R, R ', R ", R is identical group, the structure that they are taked is R
6N
+R
7R
8R
9X, R
6For carbonatoms is 2 alkoxy chain, R
7R
8Be ethyl, R
9Be propyl group, X is a sulfonic group, and its structural formula is:
(3) R, R ' are identical group, and the structure that they are taked is R
5X, R
5For the C atomicity is 3 alkoxy chain, X is a sulfonic group.And R ", R is identical group, the structure that they are taked is R
1R
2R
3R
4N
+, R
1For carbonatoms is 2 alkoxy chain, R
2R
3R
4Be ethyl, its structural formula is:
(4) R, R ', R ", R is identical group, the structure that they are taked is R
5X, R
5For carbonatoms is 3 alkoxy chain, X is a sulfonic group, and its structural formula is:
5, a kind of synthetic method as the said compound of claim 1～3, comprise the synthetic of cation type water-soluble conjugated polymers, synthesizing of the synthetic and zwitter-ion soluble conjugated polymer of anionic water-soluble conjugated polymers, it is characterized in that concrete steps are as follows:
(1) synthesis step of cation type water-soluble conjugated polymers:
(1) side chain is monomeric the synthesizing of benzyne that contains alkyl-substituted amino group:
With 1,4-dibromo Resorcinol is a masterplate, adds the 2-chloro triethylamine hydrochloride of 2～3 times of amounts under the base catalysis condition, 50～60 ℃ of temperature of reaction, and obtaining side chain is the compd A that contains alkyl-substituted amino group;
The trimethyl silicane alkynes of A and 2～3 times is mixed in the solvent of Diisopropylamine, react as catalyzer with the triphenyl phosphorus palladium of cuprous iodide and divalence, 70～80 ℃ of temperature of reaction, obtaining side chain is the benzyne monomer A that contains alkyl-substituted amino group
1
(2) side chain is contain alkyl-substituted amino group monomeric synthetic to iodobenzene:
With 1,4-diiodo-Resorcinol is a masterplate, adds the 2-chloro triethylamine hydrochloride of 2～3 times of amounts under the base catalysis condition, 50～60 ℃ of temperature of reaction, and obtaining side chain is the compd A that contains alkyl-substituted amino group
2
(3) the synthetic employing of cation type water-soluble conjugated polymers is following two kinds a kind of:
First kind, via the neutral conjugation polymkeric substance by the quaternary ammoniated cation type water-soluble conjugated polymers polymkeric substance that obtains, the steps include:
[1] the neutral conjugation polymkeric substance is synthetic:
With compd A
1And compd A
2With mixing in 1: 1, toluene was made solvent, and zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 70～80 ℃ of temperature of reaction, and it is the neutral conjugation polymkeric substance that contains alkyl-substituted amino group that reaction obtains side chain;
[2] the quaternary ammoniated cation type water-soluble conjugated polymers that obtains of neutral conjugation polymkeric substance:
The neutral conjugation polymer dissolution that obtains in tetrahydrofuran (THF), is added a monobromethane of 3～4 times of amounts, and 60～65 ℃ of temperature of reaction are reacted and are promptly obtained the cation type water-soluble conjugated polymers after three days;
Second kind, obtain the cation type water-soluble conjugated polymers by the cationic monomer polymerization, the steps include:
[1] side chain contains monomeric the synthesizing of benzyne of quaternary amine group:
With side chain is the benzyne monomer A that contains alkyl-substituted amino group
1React in tetrahydrofuran solution with a monobromethane of 3～4 times of amounts, 60～65 ℃ of temperature of reaction, obtaining side chain is the benzyne monomer A of quaternary amine group
3
[2] side chain contains the monomeric synthetic to iodobenzene of quaternary amine group:
With side chain is the compd A that contains alkyl-substituted amino group
2React in tetrahydrofuran solution with a monobromethane of 3～4 times of amounts, 60～65 ℃ of temperature of reaction, obtain side chain and be the quaternary amine group to the iodobenzene monomer A
4
[3] the cation type water-soluble conjugated polymers is synthetic:
With compd A
3And compd A
4With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, and 50～60 ℃ of reactions of temperature of reaction obtain containing the cation type water-soluble conjugated polymers of amine salt group;
(2) synthesis step of anionic soluble conjugated polymer:
(1) the sulfonate soluble conjugated polymer is synthetic:
[1] the side chain end group is that sulfonic benzyne is monomeric synthetic:
With 1,4-dibromo Resorcinol is a masterplate, adds 1 of 2～3 times of amounts under the base catalysis condition, the 3-N-morpholinopropanesulfonic acid lactone, and 50～60 ℃ of temperature of reaction, obtaining end group is sulfonic compd B;
The trimethyl silicane alkynes of compd B and 2～3 times of amounts is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, 60～65 ℃ of temperature of reaction, and obtaining end group is sulfonic group benzyne monomers B
1
[2] the side chain end group is sulfonic monomeric synthetic to iodobenzene:
With 1,4-diiodo-Resorcinol is a masterplate, adds 1 of 2～3 times of amounts under the base catalysis condition, the 3-N-morpholinopropanesulfonic acid lactone, and 50～60 ℃ of temperature of reaction are sulfonic compd B thereby obtain end group
2
[3] the sulfonate conjugated polymers is synthetic:
With compd B
1And compd B
2With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, it is sulfonic anionic soluble conjugated polymer that reaction obtains end group;
(2) the phosphoric acid salt soluble conjugated polymer is synthetic:
1. the side chain end group is monomeric the synthesizing of benzyne of phosphate:
With 2,5-two bromo-1,4-2-bromo phenetole is a masterplate, is solvent with dimethylbenzene, adds the tributyl phosphate of 2～3 times of amounts, 50～60 ℃ of temperature of reaction obtain the Compound C that end group is a phosphate,
The trimethyl silicane alkynes of Compound C and 2～3 times is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, and it is phosphate benzyne monomer C that temperature of reaction obtains end group for 60～70 ℃
1
2. the side chain end group is the monomeric synthetic to iodobenzene of phosphate:
With 2,5-two iodo-1,4-2-bromo phenetole is a masterplate, is solvent with dimethylbenzene, adds the tributyl phosphate of 2～3 times of amounts, 50～60 ℃ of temperature of reaction obtain the Compound C that end group is a phosphate
2
3. the phosphoric acid salt soluble conjugated polymer is synthetic:
With Compound C
1And Compound C
2With mixing in 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 60～70 ℃ of temperature of reaction, reaction obtains the anionic soluble conjugated polymer that end group is a phosphate;
(3) the carboxylate salt soluble conjugated polymer is synthetic:
1. the side chain end group is monomeric the synthesizing of benzyne of carboxylicesters:
With 2,5-two bromo-methyl benzoate are masterplate, 2～3 times trimethyl silicane alkynes is dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, triphenyl phosphorus palladium with cuprous iodide and divalence reacts as catalyzer, 60～70 ℃ of temperature of reaction, obtaining end group is the benzyne monomer D of carboxylicesters
1
2. the side chain end group is the synthetic of carboxylicesters neutral conjugation polymkeric substance:
With D
1With 2,5-two iodo-methyl benzoate mixed with 1: 1, and toluene is made solvent, and zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, and reaction obtains the neutral conjugation polymkeric substance that the side chain end group is a carboxylicesters;
3. the carboxylate salt soluble conjugated polymer is synthetic:
With the side chain end group that obtains is the sodium hydroxide solution that the neutral conjugation polymkeric substance of carboxylicesters places 2mol/L, reflux one day, and 90 ℃ of temperature of reaction obtain the carboxylate salt soluble conjugated polymer;
(3) synthesis step of zwitter-ion soluble conjugated polymer:
(1) side chain is that zwitterionic benzyne is monomeric synthetic:
With side chain is the benzyne monomer A that contains alkyl-substituted amino group
1With 1 of 3～4 times of amounts, the 3-N-morpholinopropanesulfonic acid lactone reacts in acetonitrile solution, and temperature of reaction 50-60 ℃ obtains the benzyne monomer E that side chain contains the zwitter-ion group
1
(2) side chain is zwitterionic monomeric synthetic to iodobenzene:
With side chain is the compd A that contains alkyl-substituted amino group
2With 1 of 3～4 times of amounts, the 3-N-morpholinopropanesulfonic acid lactone reacts in acetonitrile solution, temperature of reaction 50-60 ℃ obtain side chain contain the zwitter-ion group to iodobenzene monomer E
2
(3) the zwitter-ion soluble conjugated polymer is synthetic:
With compd E
1And compd E
2Mixed with 1: 1, be dissolved in Diisopropylamine, water, N, in the miscible agent that dinethylformamide is formed, zeroth order triphenyl phosphorus palladium and cuprous iodide are made catalyzer, 50～60 ℃ of temperature of reaction, reaction obtains the zwitter-ion soluble conjugated polymer that side chain contains the zwitter-ion group.