CN1600568A - Technical method for fabricating glass - Google Patents
Technical method for fabricating glass Download PDFInfo
- Publication number
- CN1600568A CN1600568A CN 03134061 CN03134061A CN1600568A CN 1600568 A CN1600568 A CN 1600568A CN 03134061 CN03134061 CN 03134061 CN 03134061 A CN03134061 A CN 03134061A CN 1600568 A CN1600568 A CN 1600568A
- Authority
- CN
- China
- Prior art keywords
- glass
- hours
- furnace temperature
- carving
- engraving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A process for preparing glass includes using computer to control jet flow generator to jet out superhigh pressure water of 380-450 MPa for carrying out carving and fretwork according to designed pattern on glass of 1.5-60mm, trimming flash of fretwork opus and putting it into heating furnace at temp of 900-1100 deg.C for five hours.
Description
(1) technical field
The present invention relates to a kind of processing technology of glassware, specifically relate to Glass Craft be processed, carry out the glass machining technique that hot melt is handled again with high-pressure spray.
(2) background technology
Various buildings of building or building group are to individualized development at present, and the style in the building is made every effort to other tool style, and ornaments have various stuffs, ornament.People decorate the room of oneself, make every effort to comfortable, elegant style.It is all too busy to get away glassware of ornament in the various buildings such as home decoration or office building, market, hotel.Present glassware all is to carry out embossment at glass surface, as with emery wheel mill flower, with the sand spraying decoration, to be manufactured with the mill of certain depth with the embossment of sand spray certain depth, the diamond-impregnated grinding wheel that computerizeds control colored, makes glass etc. with caustic solution.But all do not have openwork carving, third dimension is not strong, influences the aesthetic feeling of works, and influences its scope of application.
(3) summary of the invention
The technical problem to be solved in the present invention is the technology of glass being carried out openwork carving, and the glass fretting hot melting process that the glassware behind the openwork carving is heat-treated.
Glass fretting hot melting process comprises:
A, be matrix with glass, as the glass plate of thick 1.5-60mm;
B, selected openwork carving pattern, and establishment openwork carving program, this procedure stores is called in internal memory during computer booting in hard disc of computer;
C, by the computer control fluidic generator, carry out glass-engraving and openwork carving by the openwork carving program of establishment, fluidic generator sends the ultra-high pressure water fluid jet that pressure is 300-450MP, the pattern that glass fretting go out is set;
D, the glass burr of carving are repaired with diamond-impregnated grinding wheel;
E, will carve good openwork carving glassware and put into hot melting furnace, in hot melting furnace, place furnace temperature 900-1100 ℃ at least 2-7 hour.
Advantage of the present invention:
1, the invention solves glass can not openwork carving and the carving back edge handle difficult technical problem, in process, solved hard, the crisp characteristic of glass.
But the form true to nature of the various patterns of 2 openwork carvings, landscape, personage, animal and various article, every wooden engraving work can both become glassware by openwork carving with method of the present invention.As a width of cloth landscape painting, screen, tall and erect backplate, tea table, flower stand, desk lamp, the elderly person for whom a birthday celebration is being held, various glass carving ornament or the like.
3, the glass fretting goods with technology creation of the present invention have characteristics such as form is lively, true to nature, exquisitely carved, elegance is luxurious, splendid, have extremely strong decoration and ornamental value, not only can be widely used in decoration, and have reserve value.
(4) description of drawings
Fig. 1 is the glass of technology openwork carving of the present invention.
(5) concrete embodiment
The glass machining technique method comprises:
A, selection high-quality float glass 1, the thick 19mm of float glass;
B, the fluidic generator that computerizeds control (commercial), the water jet pressure of fluidic generator is 360MP, carries out openwork carving on float glass 1, openwork carving goes out the prosperity brought by the dragon and the phoenix space pattern;
C, be that 50,000 rev/mins diamond-impregnated grinding wheel is repaired the glass burr of carving with revolution;
D, will carve the good imperial wind glass of taking on auspicious omen and put into hot melting furnace, furnace temperature is 780 ℃, placed 14 hours, temperature is changed in time therebetween: furnace temperature was 180-200 ℃ in 1 hour, and furnace temperature was 250-300 ℃ in 2 hours, furnace temperature was 350 ℃ in 3 hours, furnace temperature was 450 ℃ in 5 hours, and furnace temperature was 810 ℃ in 6 hours, and furnace temperature was 750 ℃ in 8 hours, furnace temperature was 370 ℃ in 13 hours, and furnace temperature was 175 ℃ in 14 hours.
Claims (3)
1, glass machining technique method comprises jet engraving and hot melt treatment process, it is characterized in that:
A, described jet engraving are openwork carving, and its technical process comprises:
1, with glass is matrix;
2, selected depiction;
3, be the ultra-high pressure water fluid jet of 380-450MP with pressure, glass basis carried out glass-engraving and openwork carving, and carve out the pattern of setting by computer control;
4, with diamond-impregnated grinding wheel the glass burr of carving are repaired;
B, described hot melt treatment process are engraving glass well to be placed in the hot melting furnace heat-treat, and the glassware that engraving is good was placed furnace temperature 900-1100 ℃ at least 2-7 hour in hot melting furnace.
2, glass machining technique method according to claim 1 is characterized in that described glass basis is a float glass, and described diamond-impregnated grinding wheel revolution is 50,000 rev/mins.
3, glass machining technique method according to claim 1, it is characterized in that the glassware of carving is placed on heat-treats 14 hours in the hot melting furnace, temperature is changed in time therebetween: furnace temperature was 180-200 ℃ in 1 hour, furnace temperature was 250-300 ℃ in 2 hours, and furnace temperature was 350 ℃ in 3 hours, and furnace temperature was 450 ℃ in 5 hours, furnace temperature was 810 ℃ in 6 hours, furnace temperature was 750 ℃ in 8 hours, and furnace temperature was 370 ℃ in 13 hours, and furnace temperature was 175 ℃ in 14 hours.