CN1593671A - Preparation method of multi-porous chitosan used for adipose tissue engineering - Google Patents
Preparation method of multi-porous chitosan used for adipose tissue engineering Download PDFInfo
- Publication number
- CN1593671A CN1593671A CN 200410049732 CN200410049732A CN1593671A CN 1593671 A CN1593671 A CN 1593671A CN 200410049732 CN200410049732 CN 200410049732 CN 200410049732 A CN200410049732 A CN 200410049732A CN 1593671 A CN1593671 A CN 1593671A
- Authority
- CN
- China
- Prior art keywords
- chitosan
- preparation
- adipose tissue
- tissue engineering
- freezing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method of multi-porous chitosan used for adipose tissue engineering which comprises, dissolving chitosan into acetic acid, freezing at -20 deg. C in die arrangement, charging precooled oversatured NaOH ethanol solution to neutralize the acetic acid, and forming gel from chitosan, then placing the chitosan gel in vacuum chamber, evacuating the air or baking in 40 deg. C baking oven, thus forming porous spongy mass.
Description
Technical field
The invention belongs to bio-medical material technology of preparing scope, particularly a kind of preparation method that is used for the porous chitosan timbering material of adipose tissue engineering.
Technical background
According to World Health Organization's statistics, the sickness rate of women with breast cancer is the trend that rises year by year, the first place that the sickness rate of present China breast carcinoma has accounted for women's malignant tumor sickness rate.No matter current is domestic or external, and the Therapeutic Method of breast carcinoma is remained tumor and breast based on the excision Ipsilateral.Along with the raising of breast carcinoma early discovery rate and the application of some advanced auxiliary treating methods, the feasible survival rate of suffering from the women of breast carcinoma improves widely.Tumor has been eliminated, and breast is also cut, and patient side is cured.Lost breast, some patient has been full of dislike even has thought that oneself is not the woman the appearance of oneself, has influenced their normal mental health and social communication.
The method of mamaplasty divides prosthese to organize mamaplasty and autologous tissue's breast reconstruction at present.Such as, autologous fat transplantation, injection augmentation mammaplasty and prosthese implantation etc.Some the present the most frequently used breast enlargement and the method for mamaplasty obviously are not suitable for this part has excised breast because of breast tumor women, reason be this part women's needs be breast reconstruction rather than breast enlargement or mamaplasty.And the tissue mass that needs when doing breast reconstruction is bigger, the requirement that present various mamaplasty methods can not provide enough tissue mass to reach this respect, the tissue mass that will cover the shortage with the filling of synthetic materials such as silicon gel prosthese sometimes in this case.Because some physics and chemistry characteristics of these materials itself, make some not corrigibility complication to occur behind the breast enlargement.Stimulate the Periprosthetic tissue to form fibrous connective tissue peplos easily as the outer field silicon capsule of silica gel prosthese, capsule contracture causes zaranthan, makes the breast that reproduces lose its beautiful profile and softish elasticity.
Clinically, autologous fat tissue transplantation breast enlargement, comparatively desirable theoretically, because normal breast is made of fat and mammary gland two parts.The method is divided into two kinds, autologous fat granule injection mamaplasty wherein, be with syringe from other positions of health such as waist, abdominal part, thigh extract part fat, through cleaning, obtain purified relatively lipochondrion, migrate in the breast.Though this method has certain antiobesity action, need repeatedly operation usually, just can reach ideal breast volume.And after the fat injection, breast also can occur and can not well keep its profile attractive in appearance, fatty liquefaction, necrosis etc. also can take place sometimes cause the failure that is shaped.And the fibroid induration that forms has influenced the census operations of breast carcinoma, to some extent so enlarging the bosom of this mode of the present U.S. abandoned substantially.Another kind is that the fat lump of band blood vessel is transplanted, and this method cuts the position and can leave over tangible operative scar fat lump, so difficultly accepted by beauty treatment person.
Chitosan is a kind of good biocompatibility degradable biological material that has.Traditional lyophilization method preparation of porous chitosan sponge material, time-consuming, power consumption, production efficiency is low.
Summary of the invention
The purpose of this invention is to provide a kind of preparation method that is used for the porous chitosan timbering material of adipose tissue engineering, it is characterized in that: described porous chitosan timbering material is the porous chitosan sponge material with the preparation of freezing-gel method:
1) acetic acid that chitosan is dissolved in 1M makes it form the concentration of 2wt%;
2) in straight alcohol, add sodium hydroxide, form supersaturation NaOH alcoholic solution, inserted-20 ℃ of pre-cooling 3-5 hours;
3) chitosan solution with step (1) places mould ,-20 ℃ of freezing 3-5 hour.Take mould apart, freezing body is inserted in the supersaturation NaOH alcoholic solution of step (2) pre-cooling and spend the night;
4) since sodium hydroxide can in and acetic acid, below freezing at chitosan solution, ethanol is separated out the water in the chitosan solution, and makes chitosan form gel.
5) this chitosan gel rubber is inserted cyclic washing in the distilled water, neutralize residual NaOH, make it, use at last in the D-hanks liquid and 2-3 time to neutral;
6) chitosan gel rubber with preparation places vacuum chamber to bleed or inserted 40 ℃ of oven for baking 5 hours, then forms the timbering material that the mandruka body is an adipose tissue engineering.
Being shaped as spheroidal, box-shaped, thin slice shape or implanting the identical mould of fatty tissue shape of described mould with desire.
The invention has the beneficial effects as follows that 1. adopt " freezing-gel method " preparation chitosan sponge carrier, it is simple that the porous material of the freeze-drying preparation more traditional than employing has preparation, energy efficient.2. because the chitosan material excellent biological compatibility has the advantages such as sponge surface nothing scleroma of molding of being easy to and preparation.Be more suitable for being used for the timbering material of adipose tissue engineering.Carrier as adipose tissue engineering, overcome the toxicity that silica gel material implants for a long time, and the breast of simple autologous fat granule injection shortcoming such as easy-formation not, this degradable biological sponge material is expected extensive use in other soft tissue repair.
The specific embodiment
The purpose of this invention is to provide a kind of preparation method that is used for the porous chitosan timbering material of adipose tissue engineering, it is characterized in that: described porous chitosan timbering material is the porous chitosan sponge material with the preparation of freezing-gel method:
1) acetic acid that chitosan is dissolved in 1M makes it form the concentration of 2wt%;
2) in straight alcohol, add sodium hydroxide, form supersaturation NaOH alcoholic solution, inserted-20 ℃ of pre-cooling 3-5 hours;
3) chitosan solution with step (1) places mould ,-20 ℃ of freezing 3-5 hour.Take mould apart, freezing body is inserted in the supersaturation NaOH alcoholic solution of step (2) pre-cooling and spend the night;
4) since sodium hydroxide can in and acetic acid, below freezing at chitosan solution, ethanol is separated out the water in the chitosan solution, and makes chitosan form gel.
5) this chitosan gel rubber is inserted cyclic washing in the distilled water, neutralize residual NaOH, make it, use at last in the D-hanks liquid and 2-3 time to neutral;
6) chitosan gel rubber with preparation places vacuum chamber to bleed or inserted 40 ℃ of oven for baking 5 hours, then forms the timbering material that the mandruka body is an adipose tissue engineering.
By changing the dissolubility of chitosan, change the aperture of formed mandruka body material at acetic acid.
Being shaped as spheroidal, box-shaped, thin slice shape or implanting the identical mould of fatty tissue shape of above-mentioned mould with desire.
In above-mentioned preparation process, the present invention is a raw material with cheap chitosan material common on the market, filters out the highly purified chitosan material of viscosity-average molecular weight scope about 180,000～1,600,000.Molecular weight is low excessively, can cause the undercapacity of material, can not play a supporting role; Molecular weight is too high, can cause material easily crisp easy to break, and elasticity is not good.The concrete screening parameter of material: deacetylation scope 75%～90%; Indissolvable component in the dilute acetic acid solution is less than 1%.The chitosan raw material should purification in addition: with the dissolving that refluxes in rare organic acid under nitrogen protection of chitosan powder.After cooling, with certain density NaOH solution solution is neutralized pH value in 5～8 scopes, remove heavy metal ion with the method for dialysis then, lyophilization is standby.
The formal name of chitosan is called poly--β-(1,4)-D-glucosamine, and molecular formula is:
Lift the example that is prepared as below, the present invention is further specified as the adipose tissue engineering timbering material of breast implant.
1) the spheroidal mould diameter of preparation chitosan sponge is the 1cm size earlier.
2) the chitosan ball of preparing diameter 1cm by the above-mentioned method for preparing chitosan sponge was inserted in the Matrigel aqueous solution of 10mg/ml 2 hours.
3) vacuum is drained to stick the chitosan sponge of Matrigel ball
4) sterile vacuum packages spare.
Claims (2)
1. preparation method that is used for the porous chitosan timbering material of adipose tissue engineering is characterized in that: described porous chitosan timbering material is that preparation process is with the porous chitosan sponge material of freezing-gel method preparation:
1) acetic acid that chitosan is dissolved in 1M makes it form the concentration of 2wt%;
2) in straight alcohol, add sodium hydroxide, form supersaturation NaOH alcoholic solution, inserted-20 ℃ of pre-cooling 3-5 hours;
3) chitosan solution with step (1) places mould, and-20 ℃ of freezing 3-5 hour, take mould apart, freezing body is inserted in the supersaturation NaOH alcoholic solution of step (2) pre-cooling and spend the night;
4) since sodium hydroxide can in and acetic acid, below freezing at chitosan solution, ethanol is separated out the water in the chitosan solution, and makes chitosan form gel;
5) this chitosan gel rubber is inserted cyclic washing in the distilled water, neutralize residual NaOH, make it, use at last in the D-hanks liquid and 2-3 time to neutral;
6) chitosan gel rubber with preparation places vacuum chamber to bleed or inserted 40 ℃ of oven for baking 5 hours, then forms the timbering material that the mandruka body is an adipose tissue engineering.
2. according to the described preparation method that is used for the porous chitosan timbering material of adipose tissue engineering of claim 1, it is characterized in that: being shaped as spheroidal, box-shaped, thin slice shape or implanting the identical mould of fatty tissue shape of described mould with desire.