CN1590002A - 一种包覆材料的热轧复合方法 - Google Patents

一种包覆材料的热轧复合方法 Download PDF

Info

Publication number
CN1590002A
CN1590002A CN 200310120886 CN200310120886A CN1590002A CN 1590002 A CN1590002 A CN 1590002A CN 200310120886 CN200310120886 CN 200310120886 CN 200310120886 A CN200310120886 A CN 200310120886A CN 1590002 A CN1590002 A CN 1590002A
Authority
CN
China
Prior art keywords
powder
hot rolling
metal powder
rolling
compounding method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200310120886
Other languages
English (en)
Inventor
李晓杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200310120886 priority Critical patent/CN1590002A/zh
Publication of CN1590002A publication Critical patent/CN1590002A/zh
Pending legal-status Critical Current

Abstract

一种金属包覆材料的热轧复合方法属于冶金技术领域,特别涉及到一种金属包覆材料的热轧复合技术。其特征是在覆层金属与基层金属之间填充金属粉末层,然后封焊、热轧成金属复合材料。该热轧复合方法,轧合下压量小,在连轧机组上轧制复合板时,无需改变热轧工艺,对设备和技术要求较低;轧制后的复合层厚度均匀;可用于生产单面复合板和双面复合板,也可用于生产复合管材和异型材。

Description

一种包覆材料的热轧复合方法
技术领域  本发明属于冶金技术领域,特别涉及到一种金属包覆材料的制造技术。
背景技术  轧制的包覆板、棒、管材已经大量应用于化工、冶金、石油、军事甚至民用建筑装饰行业。包覆材料的制造方法也有很多,常用的复合方法大体上分两大类,一类是直接复合技术,有热轧复合、冷轧扩散复合、液—固相轧制复合、爆炸复合、钎焊、堆焊、扩散焊、浇铸复合等;另一类是用预复合的坯料进行轧制的技术,如爆炸焊、钎焊、堆焊、扩散焊、浇铸复合出坯料再进行热轧的方法;也有用粉末烧结预复合后,再冷轧扩散复合等。其他复合方法还有镀层方法、涂层方法和衬套方法等,镀层主要用于镀膜,有化学镀、离子镀、蒸镀、热镀、滚镀和电镀几种;涂层方法有等离子、氧乙炔、电弧、爆炸喷涂、冷喷涂和钎涂等;衬套方法较为简单,但金属层间没有结合力,主要用于要求不严格的场合,如建筑装修用的外套复合管、低压化工容器衬里和部分低温流体管线,其基本技术手段有机械挤压、液压胀配、爆炸胀配(包括液电、电磁成型)、热配合等。
尽管复合金属的方法有很多种,但热轧复合仍是其主要生产手段之一,热轧复合具有生产效率高,产量大的特点,尤其是对于规格、定型的批量产品热轧复合有很大的经济优势。目前的热轧复合方法,主要采用的是美国工艺,即将覆板镀镍,组装在基层板上,然后将这样的组合对扣在一起,封焊两块基板的四周,然后抽空、热轧。这样的复合板需要较大的压下量才能达到冶金结合,一般下压量要在50%以上。改进的方法如USP4,831,708将镀层改为化学镀层,如镀镍磷合金层,由于镍磷合金在轧制温度下已经熔化,又称为液态界面轧制复合。其他的方法还有在覆层上爆炸焊接薄层基板金属,然后与基材组合轧制复合的方法(日本专利57134287);在复合层与基材间加入增强金属网的轧制方法(日本专利61235085);以及用钎焊方法轧钎复合的中国专利98117314。以上改进的方法都能使轧制下压量有所下降。但是都存在着一定的局限性,如采用化学镀方法镀层,化学镀液会污染环境,同时镀层太薄,一旦加热时间过长,合金元素发生扩散,熔化的界面就不在存在,也达不到液态界面轧制复合的效果。如在覆层表面进行爆炸焊接、喷涂基材金属,都会大幅度的增加复合成本。而使用增强金属网可以有效的改善下压量,但必须对金属网材进行合理的选择,同时网材会改变复合层厚的均匀性。专利ZL98117314所提出的轧钎复合方法需要在保护气氛中加热,并在保护气氛下轧制,这对设备要求很高,而且技术难度较大,无疑会增加复合成本。
发明内容  本发明的目的是提供一种技术简单、无污染、均匀覆层的降低下压量,并能在轧制复合板、复合管、复合异型材上通用的金属包覆材料的热轧复合方法。
本发明的技术解决方案是,在覆层金属与基层金属之间填充金属粉末过渡层,封焊,加热到开轧温度,然后在连轧机组上热轧成金属复合材料。该方法原理如下:
其一是,由于开轧温度就是粉末的烧结温度,在对填充粉末的覆层与基层进行加热时,粉末自身、粉末与覆层、粉末与基层会发生烧结,形成点状结合。尽管烧结结合不完全,但烧结所产生的不结合区是粉末粒度大小的微小点,不是大片的不结合区,所以在以后的连轧中不用进行大下压量的轧合,而只需要正常的下压量即可轧合。其二是,尽管在轧制过程中,复合坯整体下压量在50%以下,但每个与基覆层接触的粉末会都有局部位置变形量超过50%。其三是,在轧合过程中粉末层的变形量大,会对基覆板表面形成摩擦、搓剪作用,有利于破坏基覆板表面氧化膜,形成扩散焊接条件。其四是,在加热过程中,由于粉末材料的表面积要远大于基覆层表面积,对于轧合不利的水分、氧气会被粉末吸附,基覆层表面的氧化层较薄,有利于轧合。其五是,如果在粉末中添加部分在开轧温度下熔化的粉末,粉末自身、粉末与覆层、粉末与基层会发生液相烧结,烧结结合程度更好,轧合变得更为容易。其六是,如果在粉末中添加部分在开轧温度下释氢的粉末,粉末自身、粉末、基覆层表面的氧化层会被还原,有利于烧结和轧合。其七是,如果在粉末中添加部分在开轧温度下吸气粉末,便于吸收对轧合不利的氧,有利于烧结和轧合。其八是,由于该方法是先在复合坯上解决复合问题,所以可以用于热轧复合管、拔热轧复合管,以及各种复合异型材。
实现本发明方法的具体步骤是:
首先,是复合坯的准备,将基覆层的复合表面打磨干净、除油后,在完全封焊基覆层之前,在基覆层之间填入1mm直径以下的金属粉。填入的金属粉可以是混合粉末或合金粉末,要保证粉末的烧结温度在开轧温度相当;如果粉末中存在液相,应保证粉末主要部分的熔点在开轧温度以上,即50%体积比以上的粉末在开轧温度下不会发生熔化,以免在轧合过程中从复合板坯中喷出金属液体,造成危险。
在按上述要求装入粉末后,进行封焊、抽空、密封,或者是封焊、抽空、充入惰性气体或还原气体、密封,就准备好了复合坯。
在复合坯准备好后,就可以在连轧机组上对之进行正常的热轧,热轧下压量在20%左右即可,最终,可轧制成复合板。
基于上述原理和操作过程,该方法在制出管坯、异型材坯料厚也可以用于热轧复合管、拔热轧复合管,以及各种复合异型材。
本发明的优点是:
1)轧合的下压量小;
2)在连轧机组上轧制复合板时,无需改变热轧工艺,对设备和技术要求较低;
3)对板坯的处理简单,无污染,容易实现;
4)由于界面的氧化物、杂质等存在于一定厚度的粉末层中,而不象原来的轧制复合集中在界面线上,复合强度较高;
5)轧制后的复合层厚度均匀;
6)可用于生产单面复合板,也可用于生产双面复合板;
7)该方法还可以用于热轧复合管、拔热轧复合管,以及各种复合异型材。
附图说明  下面结合附图和具体实施方式对本发明作进一步的说明。
图1是本发明的单面复合板坯结构图。
图2是本发明的双面复合板坯结构图。
其中,1.基层,2.覆层,3.粉末层,4.封焊焊缝。
具体实施方式
                    实施例1
按图1预制复合板坯。覆板为10mm的不锈钢板,基板为120mm厚的Q235B钢板,宽度均为240mm,在基覆板间放入2mm厚的粒度为-0.5mm的不锈钢粉末。用氩弧焊使用不锈钢焊丝焊接密封复合板坯,在焊缝处留抽气嘴。抽空粉末层,然后掐死抽气嘴,焊接密封。将复合板坯在300mm连轧机组上轧制,开轧温度1000~1200℃,轧制成2.7mm带钢,不锈钢层的厚度为0.21~0.23mm。
                          实施例2
按图2预制复合板坯。覆板为10mm的不锈钢板,基板为120mm厚的Q235B钢板,宽度均为240mm,在基覆板间放入2mm厚的粒度为-1mm的钢粉。用氩弧焊使用不锈钢焊丝焊接密封复合板坯,在焊缝处留抽气嘴。抽空粉末层,然后充入含5%氢的氩气,掐死抽气嘴,焊接密封。将复合板坯在300mm连轧机组上轧制,开轧温度1000~1200℃,轧制成2.7mm带钢,不锈钢层的厚度为0.18~0.19mm。
                          实施例3
按图1预制复合板坯。覆板为12mm的不锈钢板,基板为120mm厚的Q235B钢板,宽度均为240mm,在基覆板间放入2mm厚的粒度为-0.5mm的钢粉,并混入1%的铝粉。用氩弧焊使用不锈钢焊丝焊接密封复合板坯,在焊缝处留抽气嘴。抽空粉末层,然后掐死抽气嘴,焊接密封。将复合板坯在300mm连轧机组上轧制,开轧温度1000~1200℃,轧制成2.7mm带钢,不锈钢层的厚度为0.18~0.19mm。

Claims (8)

1.一种金属包覆材料的热轧复合方法,其特征在于,在覆层金属与基层金属之间填充金属粉末层,然后,封焊密封,热连轧、拔成金属复合材料,填入的金属粉是1mm直径以下的金属粉,金属粉的烧结温度与轧制温度相同。
2.根据权利要求1所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是混合粉末。
3.根据权利要求1所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是合金粉末。
4.根据权利要求1、2或3所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉主要部分的熔点在开轧温度以上,即50%体积比以上的粉末在开轧温度下不会发生熔化。
5.根据权利要求1、2或3所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是释氢型粉末。
6.根据权利要求1、2或3所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是吸气型粉末。
7.根据权利要求1或4所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是释氢型粉末。
8.根据权利要求1或4所述的一种金属包覆材料的热轧复合方法,其特征在于,填入的金属粉是吸气型粉末。
CN 200310120886 2003-12-31 2003-12-31 一种包覆材料的热轧复合方法 Pending CN1590002A (zh)