CN1584065A - X210CrW12钢锭轧制开坯的生产方法 - Google Patents

X210CrW12钢锭轧制开坯的生产方法 Download PDF

Info

Publication number
CN1584065A
CN1584065A CN 200410025101 CN200410025101A CN1584065A CN 1584065 A CN1584065 A CN 1584065A CN 200410025101 CN200410025101 CN 200410025101 CN 200410025101 A CN200410025101 A CN 200410025101A CN 1584065 A CN1584065 A CN 1584065A
Authority
CN
China
Prior art keywords
rolling
steel ingot
cogging
temperature
equal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410025101
Other languages
English (en)
Inventor
续维
顾新根
陈新建
黄俊春
王庆亮
沈燕源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai No5 Iron And Steel Co Ltd Baoshan Iron And Steel Group
Original Assignee
Shanghai No5 Iron And Steel Co Ltd Baoshan Iron And Steel Group
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai No5 Iron And Steel Co Ltd Baoshan Iron And Steel Group filed Critical Shanghai No5 Iron And Steel Co Ltd Baoshan Iron And Steel Group
Priority to CN 200410025101 priority Critical patent/CN1584065A/zh
Publication of CN1584065A publication Critical patent/CN1584065A/zh
Pending legal-status Critical Current

Abstract

X210CrW12钢锭轧制开坯的生产方法，其特征是采用均热炉加热+初轧机一火轧制，对≤1.3吨/支的电炉钢锭热轧开坯：(1)均热炉加热：钢锭入炉温度≤450℃保温150分钟；以≤80℃/h的速度升温至1170℃保温4.5小时，保温期间将钢锭进行翻身；钢锭阴阳面温差≤25℃出炉；(2)初轧机轧制：轧制前关闭轧辊的冷却水，轧辊预热；初轧机轧辊速度≤20转/分；开轧温度≥1130℃，终轧温度≥1060℃；压下道次40道，压下量≤30mm；钢坯回炉进行常规去应力退火热处理。实施本发明专利具有工艺简单、生产组织便捷的特点，冶金制造成本降低660元/吨钢以上，轧制钢坯及成品棒材的质量稳定可靠，检测结果符合标准规定，钢锭开坯、成材合格率100％，经济效益显著。

Description

X210CrW12钢锭轧制开坯的生产方法
技术领域
本发明涉及冶金行业模具钢热加工开坯的生产方法，尤其是指高合金冷作模具钢热加工开坯的生产方法。
背景技术
模具钢是特殊的合金钢，按用途来分，一般可分为热作模具钢和冷作模具钢二大类；按合金比(也就是合金含量)来分，一般可分为低合金模具钢和高合金(合金含量大于12％)模具钢二大类。高合金冷作模具钢是特殊的模具钢，能承受较重的载荷，且具有高的耐磨性，被广泛地使用于制造冷冲模、冷镦模、冷挤压模、拉丝模、滚丝模等模具材料。
X210CrW12高合金含钨冷作模具钢是一种特殊的高合金冷作模具钢，被广泛地应用于高强度成形模具的制造和发动机重要零部件的制造，其主要特点是：高碳(碳含量2.00～2.20％)、高合金(合金含量≥13％)、含钨(钨含量0.70～0.90％)、钢锭铸态组织是“钨类碳化物的莱氏体(莱氏体由于其特殊的形状和物理性能及不均匀性，塑性极差；钨类型碳化物在提高模具钢硬度的同时，也使模具钢塑性有所下降)”；热加工时，钨类碳化物使基体脆性增加，变形不均匀都会导致残余应力的增加，且受拉应力易聚集，温度低于980℃，塑性下降显著；因此，X210CrW12高合金含钨冷作模具钢的固有特性是：导热性低、塑性差、变形抗力大，过热较敏感，热加工温度范围比较窄，且热加工开坯易产生裂纹。
目前，X210CrW12模具钢的生产基本上采用“冶炼铸锭——锻压开坯”的传统生产工艺：≤1.3t的冶金模铸锭(主要是解决钨类型碳化物不均匀分布)经7至9个火次的锻造(锻锤轻打，锻造开坯)，完成140方mm规格的热加工开坯。金属成坯率低，生产周期长，冶金制造成本高。
发明内容
本发明开发一种X210CrW12钢锭轧制开坯的生产方法，用初轧机代替锻压机进行热加工开坯，轧制出合格的X210CrW12钢坯，解决了X210CrW12高合金含钨冷作模具钢生产周期长、金属成坯率低的问题，大大降低冶金制造的生产成本，满足用户要求和市场需要。
本发明提供的X210CrW12钢锭轧制开坯的生产方法，其特征是采用均热炉加热钢锭+初轧机(轧钢机)一火轧制的热加工开坯，将单支重量1.0～1.3吨的电炉钢锭热轧开坯成合格的X210CrW12高合金含钨冷作模具钢坯：
均热炉加热钢锭：
(1)钢锭的入炉温度400～450℃，保温120～150分钟；
(2)以60～80℃/h的速度加热升温至1165～1175℃(温度过低，不能保证钢的高温塑性；温度过高，钢的金相组织易粗化，导致轧制失败)；
(3)在1165～1175℃，保温4小时～4.5小时，保温期间，将钢锭进行翻身，使钢锭温度均匀，钢锭阴阳面温度差≤25℃；
(4)钢锭出均热炉，进入初轧机热加工轧制开坯；
初轧机轧制开坯
(5)轧制前，先关闭轧辊的冷却水，轴瓦的冷却水适当关小，且避免轴瓦的冷却水飞溅到辊身，轧辊预热至170～240℃温度；
(6)初轧机慢速轧制(破碎钢锭铸态中的钨类碳化物，最大限度地降低轧辊对轧件的拉应力)，轧辊速度10～20转/分；
(7)钢锭的开轧温度≥1130℃，终轧温度≥1060℃(若温度＜1060℃，钢的塑性下降很快，可能发生轧件开裂)；
(8)热加工轧制开坯时，压下道次38～43道，前20道次保持单向轧制，轧制压下量15～30mm(压下量太大，钢锭热加工开坯时，可能发生开裂现象；压下量太小，终轧温度过低，轧制开坯困难)；
(9)轧坯回退火炉进行常规去应力退火热处理。
和现有技术相比，本发明具有下列优点：
1、工艺合理，可操作性强；
2、生产周期大大缩短，生产组织便捷；
3、金属成坯率高，质量稳定；
4、冶金制造成本大大降低。
具体实施方案
某钢铁公司实施本发明专利，采用均热炉加热X210CrW12电炉钢锭(锭重1.20吨)+初轧机(800轧机)一火轧制的热加工开坯工艺，生产X210CrW12高合金含钨冷作模具钢坯(140×140mm)。均热炉加热钢锭：(1)钢锭的入炉温度440℃，保温120分钟；(2)以60℃/h的速度加热升温至1165～1175℃；(3)在1165～1175℃，保温4.5小时，保温期间，将钢锭进行翻身，使钢锭温度均匀，钢锭阴阳面温度差≤25℃；(4)钢锭出均热炉，进入初轧机热加工轧制开坯。初轧机轧制开坯：(1)轧制前，先关闭轧辊的冷却水，轴瓦的冷却水适当关小，且避免轴瓦的冷却水飞溅到辊身，轧辊预热至220℃温度；(2)初轧机慢速轧制(破碎钢锭铸态中的钨类碳化物，最大限度地降低轧辊对轧件的拉应力)，轧辊速度10～20转/分；(3)钢锭的开轧温度≥1130℃，终轧温度≥1060℃；(4)压下道次42道，前20道次保持单向轧制，轧制压下量23mm；(5)轧制开坯的成品钢坯(140×140mm)回退火炉进行常规去应力退火热处理。
实施本发明专利对X210CrW12钢锭进行热加工开坯，具有工艺简单、生产组织便捷、冶金制造成本低的特点，与传统的“冶炼铸锭——锻压开坯”生产工艺相比，不仅金属成坯率提高1～1.5％(达81.35％)以上，更重要的是：生产周期大大缩短，冶金制造成本降低660元/吨钢以上；热加工轧制开坯生产的140mm方钢坯及制成的Φ40mm成品棒材，内材质量稳定可靠，检测结果(见表一、表二)符合标准之规定，且钢坯表面质量优于锻压开坯，钢锭开坯、成材合格率100％，经济效益显著。
                 140mm2钢坯的金属成坯率、低倍质量
                                                                                   表1
编号   1.20t钢锭 140mm2钢坯 成坯率％ 中松级   偏析级  共晶网状碳化物级
数量支 重量吨 数量支 重量吨
  1   8   9.30   32 7.58 81.50 1.5   1.5     4.5
  2   8   9.11   32 7.43 81.60 2.0   1.5     4.5
                          Φ40mm成品材物理测试结果
                                                                                 表2
  编号   规格(mm)   中松(级)     偏析(级)   脱碳(mm)   共晶网状碳化物(级)   退火硬度(HB)
  标准规定   φ40   ≤3.0     ≤6.0   ≤0.85     ≤3.5     217-269
  1   φ40   1.0     1.0   0.20     2.5     255
  2   φ40   1.0     1.0   0.20     2.5     239
  3   φ40   1.0     1.0   0.25     2.5     249

Claims (1)

1、X210CrW12钢锭轧制开坯的生产方法，其特征是采用均热炉加热钢锭+初轧机一火轧制的热加工开坯，将单支重量1.0～1.3吨的电炉钢锭热轧开坯成合格的X210CrW12高合金含钨冷作模具钢坯：
均热炉加热钢锭：
(1)钢锭的入炉温度400～450℃，保温120～150分钟；
(2)以60～80℃/h的速度加热升温至1165～1175℃；
(3)在1165～1175℃，保温4小时～4.5小时，保温期间，将钢锭进行翻身，使钢锭温度均匀，钢锭阴阳面温度差≤25℃；
(4)钢锭出均热炉，进入初轧机热加工轧制开坯；初轧机轧制开坯
(5)轧制前，先关闭轧辊的冷却水，轴瓦的冷却水适当关小，且避免轴瓦的冷却水飞溅到辊身，轧辊预热至170～240℃温度；
(6)初轧机慢速轧制，轧辊速度10～20转/分；
(7)钢锭的开轧温度≥1130℃，终轧温度≥1060℃；
(8)热加工轧制开坯时，压下道次38～43道，前20道次保持单向轧制，轧制压下量15～30mm；
(9)轧坯回退火炉进行常规去应力退火热处理。
CN 200410025101 2004-06-11 2004-06-11 X210CrW12钢锭轧制开坯的生产方法 Pending CN1584065A (zh)