CN1583840A - Grain rubber decorative materials and manufacturing method thereof - Google Patents
Grain rubber decorative materials and manufacturing method thereof Download PDFInfo
- Publication number
- CN1583840A CN1583840A CN 200410022636 CN200410022636A CN1583840A CN 1583840 A CN1583840 A CN 1583840A CN 200410022636 CN200410022636 CN 200410022636 CN 200410022636 A CN200410022636 A CN 200410022636A CN 1583840 A CN1583840 A CN 1583840A
- Authority
- CN
- China
- Prior art keywords
- rubber
- wood grain
- finishing material
- total amount
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A decorative rubber material with wood patterns is produced by: choosing two colored mixed stocks, weighing, vulcanizing and sizing, and edge polishing to obtain the product. The mixed stock as primary material is proportioned at 50 - 90%, meanwhile, the other one as patterning material is proportioned at 10-50%. The product has natural patterns and wear-resistance, and is soft, anti-skid, dielectric, so as to be used for floor decoration in various fields.
Description
Technology neck city
The present invention relates to the material field, relate in particular to a kind of wood grain rubber finishing material, relate to its production method simultaneously.
Background technology
Elastomeric material can keep excellent elasticity in very wide scope (50~150 ℃), and density is little, the physical strength height, and permeability rate is low, dielectric properties good, the more high performance of chemical stability.And finishing material mostly is ceramic, woodwork, bamboo product etc. now, the common non-skid property of these materials is poor, though the change by structure reaches anti-skidding effect during fabrication, because of its elasticity not good, in a single day people especially old man or children falls down, and tends to cause injury in various degree.And because the influence of dielectric properties is limited in some special places uses, as the high voltage power distribution room.The report of at present relevant rubber finishing material mainly concentrates on floor tile, the more stiff not nature of its pattern.
Summary of the invention
The object of the present invention is to provide a kind of wear-resistant, quality is soft, the wood grain rubber finishing material of good antiskid effect and pattern texture harmony and natural.
Another object of the present invention is to provide wood grain rubber finishing material production method.
Wood grain rubber finishing material of the present invention directly forms the grain pattern that runs through the product endoplasm when it is characterized in that rubber-moulding.
Wood grain rubber finishing material production method of the present invention comprises the steps:
(1) rubber unvulcanizate of the two or more different colours of selection, the rubber unvulcanizate of wherein making background color accounts for 50~90% of total amount, and the rubber unvulcanizate of making lines accounts for 10~50% of total amount;
(2) mill is mixed into the film of wood grain quirk;
(3) get finished product after weighing, sulfuration typing, the deburring.
Product of the present invention, grace is beautiful, wear-resistant naturally, quality is soft, good antiskid effect to have pattern, and dielectric properties are good, can be used as the floor decorative material in various places, especially are suitable as adventure playground's floor decorative material in high voltage power distribution room in one's power.And method of the present invention is simple, the also available reclaimed rubber of initial rubber.
Embodiment
Embodiment 1
The production method of the rubber finishing material that the wood texture pattern is less:
Select two kinds of raw materials, be processed into rubber unvulcanizate through conventional method, the rubber unvulcanizate of making background color accounts for 50% of total amount, and the rubber unvulcanizate of making lines accounts for 50% of total amount; Mill is mixed into the film of wood grain quirk; Get finished product after weighing, sulfuration typing, the deburring.
Embodiment 2
The wood texture pattern effect is the production method of rubber finishing material preferably:
Select two kinds of raw materials, be processed into rubber unvulcanizate through conventional method, the rubber unvulcanizate of making background color accounts for 70% of total amount, and the rubber unvulcanizate of making lines accounts for 30% of total amount; Mill is mixed into the film of wood grain quirk; Get finished product after weighing, sulfuration typing, the deburring.
Embodiment 3
The production method of the rubber finishing material that the wood texture pattern is less:
Select two kinds of raw materials, be processed into rubber unvulcanizate through conventional method, the rubber unvulcanizate of making background color accounts for 90% of total amount, and the rubber unvulcanizate of making lines accounts for 10% of total amount; Mill is mixed into the film of wood grain quirk; Get finished product after weighing, sulfuration typing, the deburring.
Except the foregoing description, also can select for use the rubber unvulcanizate of three kinds, four kinds or more colors to make product of the present invention as required.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, any technical solution of the present invention content that do not break away from,, all still belong in the scope of technical solution of the present invention any simple modification, equivalent variations and modification that above embodiment did according to technical spirit of the present invention.
Claims (2)
1, a kind of wood grain rubber finishing material directly forms the grain pattern that runs through the product endoplasm when it is characterized in that rubber-moulding.
2, wood grain rubber finishing material production method as claimed in claim 1 comprises the steps:
(1) rubber unvulcanizate of the two or more different colours of selection, the rubber unvulcanizate of wherein making background color accounts for 50~90% of total amount, and the rubber unvulcanizate of making lines accounts for 10~50% of total amount;
(2) mill is mixed into the film of wood grain quirk;
(3) get finished product after weighing, sulfuration typing, the deburring.