CN1560362A - 可降解包装纸 - Google Patents
可降解包装纸 Download PDFInfo
- Publication number
- CN1560362A CN1560362A CNA2004100394885A CN200410039488A CN1560362A CN 1560362 A CN1560362 A CN 1560362A CN A2004100394885 A CNA2004100394885 A CN A2004100394885A CN 200410039488 A CN200410039488 A CN 200410039488A CN 1560362 A CN1560362 A CN 1560362A
- Authority
- CN
- China
- Prior art keywords
- polyethylene
- degradable
- calcium carbonate
- master batch
- package paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明可降解包装纸,以牛皮纸为基体,涂覆高分子膜。高分子膜为无毒低压聚乙烯和聚乙烯碳酸钙降解母料,其重量比为70-85%和15- 30%。高分子膜还包括聚乙烯黑色母料和香料,聚乙烯黑色母料和香料分别为总量的5-8%和0.3-0.5%。其制备方法是:将无毒低压聚乙烯和聚乙烯碳酸钙降解母料均匀混合,并添加聚乙烯黑色母料和香料,加热变成液体,然后在基体上涂覆。本发明有益技术效果是:可降解包装纸废弃物,能在自然环境中较快降解为可消纳的碎片或粉末,并随时间推移进一步降解为二氧化碳和水。有微生物环境中6个月可彻底降解,达到环保要求。该包装纸及其延伸产品防水、防霉、不返潮并具良好的耐用性。
Description
技术领域
本发明涉及包装材料,具体地说是以生物降解复合材料为原料制备的一种可降解包装纸,本发明还涉及该包装纸的制备方法。
背景技术
目前,我国每年有400万吨以上的塑料垃圾,其中塑料包装材料的废弃物占有很大比重。这对改善生态环境和可持续发展来说是一个很大的课题。《中华人民共和国废弃物污染环境防治法》规定,包装材料的废弃物要可回收、可降解,而在制造包装材料及其延伸产品单独采用1C7A和1C7B塑料薄膜时,是不能实现回收或降解的。另外,作为印刷行业重要耗材的PS版,每年有几千万平方米。制备PS版通常采用牛皮纸和黑色塑料薄膜为原料,不仅不利于环保,而且因透气性不好,在温度变化时,极易出现返潮现象。
发明内容
本发明的目的在于克服传统包装材料不能回收或降解的缺陷,提供一种环保型无毒包装材料,对其废弃物污能够充分实现生物降解,并且防水、防霉、不返潮和具有良好的耐用性。
为实现上述目的,本发明提供一种可降解包装纸,包括基体,基体上涂覆有一层高分子膜,高分子膜包括无毒低压聚乙烯和聚乙烯碳酸钙降解母料,其重量比为:无毒低压聚乙烯70-85%,聚乙烯碳酸钙降解母料15-30%。
本发明可降解包装纸,其中,基体为牛皮纸。
本发明可降解包装纸,其中,高分子膜还包括有聚乙烯黑色母料和香料,聚乙烯黑色母料和香料分别为无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%。
本发明可降解包装纸,其中,无毒低压聚乙烯的型号为1C7A和/或1C7B,其粒度为Φ2.5mm,密度为0.918g/cm3,熔融指数为7.0g/10min。
本发明可降解包装纸,其中,聚乙烯碳酸钙降解母料采用型号为MEF0690CB的PE注塑类环保降解母料,其粒度为Φ2.5mm,呈圆片型或圆柱型,密度为1g/cm3,熔融指数为0.7g/10min,降解诱导期≥30天。
本发明可降解包装纸,其中,聚乙烯黑色母料的型号为MBB106LE,其密度为1.16g/cm3,熔融指数为4.0g/10min。
本发明可降解包装纸,其中,高分子膜的厚度为0.01-0.04mm。
本发明的另一个目的在于提供此种环保型包装材料的制备方法。
为实现这一目的,本发明提供一种可降解包装纸的制备方法,将无毒低压聚乙烯和聚乙烯碳酸钙降解母料均匀混合,其重量比为:无毒低压聚乙烯70-85%,聚乙烯碳酸钙降解母料15-30%,并添加聚乙烯黑色母料和香料,聚乙烯黑色母料和香料分别为无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%,将最终混合物加热变成液体,然后用通用薄膜的加工方法如吹塑或挤出成型涂覆在牛皮纸上。
本发明的有益技术效果是:本发明可降解包装纸在使用后的废弃物,能在自然环境中,较快地降解为可消纳的碎片或粉末,并随时间推移进一步降解为二氧化碳和水。在微生物活跃的环境中,6个月即可彻底降解,达到国家对环保的有关要求。同时,用该包装纸所制备的PS版等延伸产品可以防水、防霉、不返潮和具有良好的耐用性。
附图说明
图1为本发明可降解包装纸的示意图。
具体实施方式
下面结合附图及实施例详述本发明。
本发明可降解包装纸,以牛皮纸为基体1,基体1上涂覆有一层高分子膜2。高分子膜2包括有无毒低压聚乙烯和聚乙烯碳酸钙降解母料,其重量比为:无毒低压聚乙烯70-85%,聚乙烯碳酸钙降解母料15-30%。高分子膜2还包括有聚乙烯黑色母料香料,聚乙烯黑色母料和香料分别为无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%。
在本发明提供的实施例中,采用型号为1C7A或1C7B的无毒低压聚乙烯,其粒度为Φ2.5mm,密度为0.918g/cm3,熔融指数为7.0g/10min。聚乙烯碳酸钙降解母料采用型号为MEF0690CB的PE吹塑类环保降解母料,其粒度为Φ2.5mm,呈圆片型或圆柱型,密度为1g/cm3,熔融指数为0.7g/10min,降解诱导期≥30天。聚乙烯黑色母料的型号为MBB106LE,其密度为1.16g/cm3,熔融指数为4.0g/10min。
本发明实施例可降解包装纸的制备方法是:将无毒低压聚乙烯和聚乙烯碳酸钙降解母料均匀混合,其重量比为:无毒低压聚乙烯70-85%,聚乙烯碳酸钙降解母料15-30%,并添加聚乙烯黑色母料和香料,聚乙烯黑色母料和香料分别为无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%,将最终混合物加热变成液体,然后用通用薄膜的加工方法如吹塑或挤出成型涂覆在牛皮纸上,形成高分子膜2,其厚度为0.01-0.04mm。
本发明可降解包装纸是一种生物降解复合材料,它可以单独或以各种延伸产品得到广泛应用。其系列制品具有与普通塑料包装纸相当的应用性能和卫生性能,例如:黑密度为4.7-5.3d;纵向抗张强度≥4.5kN/m,横向抗张强度≥2.5kN/m透气度≥3.2Pa.s。使用后的废弃物,能在自然环境中,较快地降解为可消纳的碎片或粉末,并随时间推移进一步降解为二氧化碳和水。在微生物活跃的环境中,6个月即可彻底降解,达到国家对环保的有关要求。同时,用该包装纸所制备的PS版包装材料等延伸产品,防水、防霉、不返潮,具有良好的耐用性。
此外,可降解包装纸这种生物降解复合材料成本低、性价比高,还将在照片胶片行业和造纸行业以及图书发行包装方面得到广泛应用。
Claims (8)
1.可降解包装纸,包括基体(1),其特征在于在所述基体(1)上涂覆有一层高分子膜(2),所述高分子膜(2)包括无毒低压聚乙烯和聚乙烯碳酸钙降解母料,其重量比为:无毒低压聚乙烯为70-85%,聚乙烯碳酸钙降解母料为15-30%。
2.根据权利要求1所述的可降解包装纸,其特征在于,其中所述基体(1)为牛皮纸。
3.根据权利要求1或2所述的可降解包装纸,其特征在于,其中所述高分子膜(2)还包括聚乙烯黑色母料和香料,所述聚乙烯黑色母料和所述香料分别为所述无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%。
4.根据权利要求3所述的可降解包装纸,其特征在于,其中所述无毒低压聚乙烯的型号为1C7A或1C7B,其粒度为Φ2.5mm,密度为0.918g/cm3,熔融指数为7.0g/10min。
5.根据权利要求4所述的可降解包装纸,其特征在于,其中所述聚乙烯碳酸钙降解母料采用型号为MEF0690CB的PE吹塑类环保降解母料,其粒度为Φ2.5mm,呈圆片型或圆柱型,密度为1g/cm3,熔融指数为0.7g/10min,降解诱导期≥30天。
6.根据权利要求5所述的可降解包装纸,其特征在于,其中所述聚乙烯黑色母料的型号为MBB106LE,其密度为1.16g/cm3,熔融指数为4.0g/10min。
7.根据权利要求6所述的可降解包装纸,其特征在于,其中所述高分子膜(2)的厚度为0.01-0.04mm。
8.根据权利要求7所述的可降解包装纸的制备方法,其特征在于:将所述无毒低压聚乙烯和聚乙烯碳酸钙降解母料均匀混合,其重量比为:无毒低压聚乙烯70-85%,聚乙烯碳酸钙降解母料15-30%,并添加聚乙烯黑色母料和香料,所述聚乙烯黑色母料和所述香料分别为无毒低压聚乙烯和聚乙烯碳酸钙降解母料总量的5-8%和0.3-0.5%,将最终混合物加热变成液体,然后用通用薄膜的加工方法如吹塑或挤出成型涂覆在牛皮纸上,形成高分子膜。