CN1557560A - Method for preparing steel slag water washing sand used as a substitute for yellow sand - Google Patents
Method for preparing steel slag water washing sand used as a substitute for yellow sand Download PDFInfo
- Publication number
- CN1557560A CN1557560A CNA2004100161495A CN200410016149A CN1557560A CN 1557560 A CN1557560 A CN 1557560A CN A2004100161495 A CNA2004100161495 A CN A2004100161495A CN 200410016149 A CN200410016149 A CN 200410016149A CN 1557560 A CN1557560 A CN 1557560A
- Authority
- CN
- China
- Prior art keywords
- sand
- magnetic separation
- slag
- steel slag
- washed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the processing and application of steel slag resource, and is especially the preparation process of water washed steel slag sand for replacing yellow sand in building. Steel slag is magnetically selected repeatedly, crushed to size not larger than 5 mm, sorted, water washed and magnetically re-selected to form the water washed steel slag sand. The water washed steel slag sand has iron content less than 1 %, mud content less than 5 % and free calcium oxide content less than 4 %. Detection shows that the water washed steel slag sand has stable performance, no radioactivity and low content of metal iron, free calcium oxide and other harmful components, and may be used as fine aggregate for concrete in building.
Description
Technical field
The invention belongs to the processing and the application of steel slag resource, relate to a kind of preparation method of yellow ground substitute for building, specifically, is a kind of preparation method who is used for the slag washed-out sand of alternative yellow ground.
Background technology
Along with the continuous quickening of process of industrialization, it is more and more rare that resource becomes, along with country to the continuing to increase of rivers protection, yellow ground for building is faced with the problem that exploitation is restricted, and presses for and finds inexpensive substitute as early as possible.
Slag exists the problem of high value added utilization as the byproduct of steel-making always.General slag is after processing through common sorting, magnetic separation, specification according to screen cloth, can form the different slag pellet of fineness, but because it belongs to the byproduct of production magnetic separation iron usually, therefore, by the end of at present, the slag pellet after the sorting still there is not the requirement of performance index, do further deep processing also not to its in addition development and utilization targetedly, and to producing remaining slag pellet.
Summary of the invention
For overcoming the deficiency that steel slag resource is utilized in the prior art, the invention provides a kind of preparation method who is used for the slag washed-out sand of alternative yellow ground, with the resource of expansion yellow ground substitute, and then the utilization rate of raising steel slag resource.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of preparation method who is used for substituting the slag washed-out sand of yellow ground, its substantive distinguishing features is: it is slag to be carried out magnetic separation, fragmentation, sorting to its particle diameter repeatedly be less than or equal to 5mm, and then carry out sorting, the washing magnetic separation forms;
The concrete operations step is:
(1) the slag raw material is carried out sufficient fragmentation, sorting, magnetic separation, and following steel scoria magnetic separation material and the branch of concentrated particle diameter<5mm selected materials;
(2) will after last process is handled, receive<the magnetic separation material of 5mm, divide that selecting materials evenly distributes imports in the washing magnetic separator, fully wash, magnetic separation, when reclaiming the magnetic separation iron sand, will be filtered out by the mortar that water is gone out, again with sand washer receive washed-out sand.
The described slag washed-out sand that is used for substituting yellow ground, its iron-holder is less than or equal to 1%, contains mud amount less than 5%, and free calcium oxide is less than 4%.
Compared with prior art, the present invention has the following advantages:
1, slag is after having experienced multiple working procedure processing, again through washing magnetic separation and sorting, therefore, the content of harmful components such as metallic iron that it is inner and free calcium oxide all meets the specification requirement that substitutes common yellow ground use, and the fine aggregate that just can directly be used as building concrete need not be screened once more to it in the construction site.
2, after testing, the inner "dead" material of slag washed-out sand of the present invention, stable performance.Its surperficial slag micro powder has lateral reactivity, also can improve concrete performance.
3, the slag washed-out sand that slag processing back is formed is as yellow ground for building, and its economic benefit, environmental benefit are all very remarkable, have also opened up the new approach that utilizes for the slag with lateral reactivity.
Description of drawings
Fig. 1 is used for the process flow diagram of the slag washed-out sand of alternative yellow ground for preparation.
The specific embodiment
The present invention is described in further detail below in conjunction with drawings and Examples.
A kind of preparation method who is used for substituting the slag washed-out sand of yellow ground, it is slag to be carried out magnetic separation, fragmentation, sorting to its particle diameter repeatedly be less than or equal to 5mm, and then carry out sorting, the washing magnetic separation forms.
Its concrete operations step is:
(1) the slag raw material is carried out sufficient fragmentation, sorting, magnetic separation, and following steel scoria magnetic separation material and the branch of concentrated particle diameter<5mm selected materials;
(2) the magnetic separation material of the particle diameter<5mm that will receive after last process is handled, branch being selected materials evenly to distribute and importing in the washing magnetic separator, fully wash, magnetic separation, when reclaiming the magnetic separation iron sand, will be filtered out by the mortar that water is gone out, again with sand washer receive washed-out sand.
The described slag washed-out sand that is used for substituting yellow ground, its iron-holder is less than or equal to 1%, contains mud amount less than 5%, and free calcium oxide is less than 4%.
Process flow diagram shown in Figure 1 has specifically described a kind of preparation method who is used for the slag washed-out sand of alternative yellow ground.Adopt carse, medium and small three kinds of modes that different types of slag raw material is carried out fragmentation respectively, and be equipped with magnetic separation, sorting, make it to form the closed cycle of slag processing, thereby the metallic iron in the slag is fully rejected, except that the particle diameter that will be sub-elected be the slag pellet of 5~10mm do in addition he with, it is then to enter next process below the 5mm again that remaining slag all is converted into particle diameter.Its concrete technological process is as follows:
At first the slag raw material is carried out sorting,, after magnetic separation and granulated iron reclaim, enter thick brokenly, then carry out sorting again when its particle diameter during greater than 50mm; When sorting to less than 50mm the time, after magnetic separation and granulated iron reclaim, enter the sorting operation once more, carry out sorting again after broken during selected particle diameter enters greater than the pellet of 10mm; Particle diameter then enters sorting once more less than the pellet of 10mm, the particle diameter that sub-elects is the slag pellet of 5~10mm, can do him in addition uses, its particle diameter that finally sub-elects is less than the slag pellet of 5mm, quilt is evenly washed in the distribution importing washing magnetic separator, magnetic separation, when reclaiming iron sand, will be filtered out by the mortar that water is gone out, last again with sand washer receive the slag washed-out sand that matches of the particle diameter of the present invention and yellow ground for building.
Claims (2)
1, a kind of preparation method who is used for substituting the slag washed-out sand of yellow ground is characterized in that: it is slag to be carried out magnetic separation, fragmentation, sorting to its particle diameter repeatedly be less than or equal to 5mm, and then carry out sorting, the washing magnetic separation forms;
The concrete operations step is:
(1) the slag raw material is carried out sufficient fragmentation, sorting, magnetic separation, and following steel scoria magnetic separation material and the branch of concentrated particle diameter<5mm selected materials;
(2) the magnetic separation material of its particle diameter<5mm that will receive after last process is handled, branch being selected materials evenly to distribute and importing in the washing magnetic separator, fully wash, magnetic separation, when reclaiming the magnetic separation iron sand, will be filtered out by the mortar that water is gone out, again with sand washer receive washed-out sand.
2, the preparation method who is used for the slag washed-out sand of alternative yellow ground as claimed in claim 1 is characterized in that: the described slag washed-out sand that is used for substituting yellow ground, and its iron-holder is less than or equal to 1%, contains mud amount less than 5%, and free calcium oxide is less than 4%.