CN1528820A - Method for preparing polysulfoneamide/claynano composite material - Google Patents

Method for preparing polysulfoneamide/claynano composite material Download PDF

Info

Publication number
CN1528820A
CN1528820A CNA031514545A CN03151454A CN1528820A CN 1528820 A CN1528820 A CN 1528820A CN A031514545 A CNA031514545 A CN A031514545A CN 03151454 A CN03151454 A CN 03151454A CN 1528820 A CN1528820 A CN 1528820A
Authority
CN
China
Prior art keywords
clay
polysulfonamides
diaminodiphenylsulfone
dds
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031514545A
Other languages
Chinese (zh)
Other versions
CN1264925C (en
Inventor
唐志勇
张德仁
孙晋良
余泳
任慕苏
张家宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai University
University of Shanghai for Science and Technology
Original Assignee
University of Shanghai for Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Shanghai for Science and Technology filed Critical University of Shanghai for Science and Technology
Priority to CNB031514545A priority Critical patent/CN1264925C/en
Publication of CN1528820A publication Critical patent/CN1528820A/en
Application granted granted Critical
Publication of CN1264925C publication Critical patent/CN1264925C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The invention refers to a manufacturing method of polysulfone amide/clay soil nano compound material. The invention uses monomer liquor inserted layer in situ polymerization technique. The process steps are: the organic clay soil is put into the organic dissolvent, mixing with high speed and forms the clay soil dispersing liquid; then puts the aroma deamine into the liquid, mixes and solves, decreases the temperature to -8deg.C-10deg.C; generates the monomer inserted layer liquid; adds the paraphthaloyl chloride, and carries on fasculation reaction, uses alkali to neutralize them and filters, then gets the product. The compound material has good mechanical performance; it can be made into fiber for producing each kind of protecting clothing and military clothing.

Description

The preparation method of polysulfonamides/clay nanocomposites
Technical field
The present invention relates to a kind of preparation method of polysulfonamides/clay nanocomposites, be particularly related to the preparation method of Polyphenylene Sulfone acid amides/clay nanocomposites, the manufacturing process technology field of the matrix material that genus organic high molecular polymer and mineral filler are formed.
Background technology
The organic high molecular polymer polysulfonamides is to use engineering plastics more widely, has premium propertiess such as resistance to chemical attack, radiation hardness, high temperature resistant, uninflammability and electrical isolation.Can make good filtering material, also can be used for the insulation paper of motor.Especially be made into textile fibres, more, can be used to make some special spe-cial-purpose uniforms, as antigravity suit, pressure compensating suit, fighting uniform and bunker clothing etc. because it has high-strength, lightweight, resistant to elevated temperatures characteristics.Also can be used for making military supplies such as steel helmet.But,, be one of important topic of current material subject so how to improve the over-all properties of polysulfonamides resin because the mechanical property of polysulfonamides does not still satisfy requirement.
How improve on the molecular weight of polymkeric substance in most of doses at the emphasis of research at present, do not see the relevant report that adopts nanotechnology to prepare polysulfonamides and the matrix material of clay as yet.
Summary of the invention
The object of the present invention is to provide a kind of method that improves the polysulfonamides mechanical property.Further purpose of the present invention provides the preparation method of the matrix material of a kind of polysulfonamides resinous polymer and mineral filler clay composition.
The preparation method of a kind of polysulfonamides/clay nanocomposites of the present invention is characterized in that adopting the technology of monomer solution intercalation in-situ polymerization, and the processing step of present method is as follows;
A. raw material is prepared: main raw material and weight percent are: aromatic diamines 40-60%, terephthalamide 60-40%; In addition, press above-mentioned raw materials total amount 100% and add organic clay for benchmark, the add-on of this organic clay is 0.1-10%;
B. organic clay is incorporated in N, in the N dimethylacetamide solvent, high-speed stirring forms clay dispersion solution;
C. aromatic diamines is joined in the above-mentioned clay dispersion solution, stir on the limit, the limit dissolving, and be cooled to 15 ℃~-25 ℃, the best is-8 ℃~-10 ℃; Under low-temperature condition, continue to stir 30 minutes, make to form monomer intercalation solution; Aromatic diamines mainly is a diaminodiphenylsulfone(DDS);
D. in above-mentioned low temperature monomer intercalation solution, add p-phthaloyl chloride while stirring, make it carry out polycondensation, finally form nano composite material;
E. with alkali neutralization and filtration, promptly get product.
Above-mentioned clay is a kind of layer silicate mineral, its essential mineral composition is the layer aluminosilicate of the montomorillonite of 85-93%, this clay is handled through n-alkyl amino acid (n=6-12) properties-correcting agent, the organic clay of optimum for forming after ten diamino acid ion exchange treatment.
Above-mentioned aromatic diamines can be Ursol D, mphenylenediamine, mainly is 4 ' 4 diaminodiphenylsulfone(DDS)s, 3 ' 3 diaminodiphenylsulfone(DDS)s.
Above-mentioned neutralization with alkali can be calcium oxide, to be neutralized to pH value be 6-7.
Among the present invention, typical polysulfonamides is to be formed by diaminodiphenylsulfone(DDS) and p-phthaloyl chloride polycondensation, and its chemical equation is:
Figure A0315145400041
In above-mentioned representative instance, when aromatic diamines was 4 ' 4 diaminodiphenylsulfone(DDS)s and/or 3 ' 3 diaminodiphenylsulfone(DDS)s, then polysulfonamides specifically was expressed as the Polyphenylene Sulfone acid amides.
The present invention has adopted the technology of monomer solution intercalation in-situ polymerization, a kind of monomer is inserted between the clay layer, add another monomer subsequently and make it to carry out polycondensation, length along with polymer molecular chain when the restricted clearance polymerization constantly increases, make the interfloor distance of clay platelet also constantly increase, restraint force between the adjacent sheets is weakened, so that clay layer is fully strutted even is peeled off, and be dispersed in the polymeric matrix with nanoscale, by Coulomb's force and the strong interaction of polymer formation, finally form Organic simultaneously.This material is with the rigidity of inorganics, and the toughness and the workability of dimensional stability and thermotolerance and organic polymer ideally combine.Can give the many employing traditional methods of material unapproachable premium properties.
The advantage of the inventive method is that technology is simple, and is workable, easy to make and with low cost.
The prepared product of the inventive method is polysulfonamides/clay nanocomposites, through precipitation bath solidify, operations such as drawing-off, washing, drying, densification, coiling handle, can make polysulfonamides/clay nanocomposites fiber, this is a kind of novel high-performance fiber.
Conventional polysulfonamides fibre 2.3cN/dtex (2.4 gram/dawn)
Polysulfonamides/clay nanocomposites fiber 2.9cN/dtex (3.1 gram/dawn)
Embodiment
After now embodiments of the invention being described in.
Embodiment one:
A. raw material is prepared: main raw material is 4 ' 4 two amido sulfobenzides, 3 ' 3 two amido sulfobenzides, p-phthaloyl chloride, organic clay.Organic clay is the organic clay that the layer aluminosilicate of montomorillonite and ten diamino acid properties-correcting agent is carried out becoming after the ion exchange treatment organic modification.
B. with 3 gram organic claies with 300 gram N ' N---N,N-DIMETHYLACETAMIDE is put into the high speed tissue mincer of a 1000ml, with the rotating speed high speed shear that per minute 12000 changes, the time is 20 minutes, makes it form clay dispersion suspensoid solution.
C. above-mentioned suspensoid is poured in the four neck reactors of 500ml, is added 4 ' 4 two amido sulfobenzide and 0.03mol (7.5 gram) 3 ' 3 diaminodiphenylsulfone(DDS)s of 0.09mol (22.35 gram) while stirring, be cooled to-8 ℃--10 ℃; Continue at low temperatures to stir 30 minutes.
D. add the p-phthaloyl chloride of 0.12mol (24.4 gram) in above-mentioned cryogenic fluid while stirring, high-speed stirring makes it carry out polycondensation; React and close cooling pump after 3 minutes, it is heated up naturally.
E. continue reaction after 1 hour, it is 6-7 that the adding calcium oxide is neutralized to pH value; Through filtering discharging, promptly get product at last.
Polymkeric substance is measured the d of material medium clay soil through the X diffraction 001The interplanar distance of face diffraction peak and transmission electron microscope observation clay layer thickness shows that clay is strutted even dissociated, and lamellar spacing only is 20-80nm, is dispersed in the polysulfonamides matrix with nanoscale.

Claims (5)

1. the preparation method of a polysulfonamides/clay nanocomposites is characterized in that adopting the technology of monomer solution intercalation in-situ polymerization, and the processing step of present method is as follows;
A. raw material is prepared: main raw material and weight percent are: aromatic diamines 40-60%, terephthalamide 60-40%; In addition, press above-mentioned raw materials total amount 100% and add organic clay for benchmark, the add-on of this organic clay is 0.1-10%;
B. organic clay is incorporated in N, in the N dimethylacetamide solvent, high-speed stirring forms clay dispersion solution;
C. aromatic diamines is joined in the above-mentioned clay dispersion solution, stir on the limit, the limit dissolving, and be cooled to-15 ℃~-25 ℃, the best is-8 ℃~-10 ℃; Under low-temperature condition, continue to stir 30 minutes, make to form monomer intercalation solution; Aromatic diamines mainly is a diaminodiphenylsulfone(DDS);
D. in above-mentioned low temperature monomer intercalation solution, add p-phthaloyl chloride while stirring, make it carry out polycondensation, finally form nano composite material;
E. with alkali neutralization and filtration, promptly get product.
2. the preparation method of a kind of polysulfonamides/clay nanocomposites according to claim 1, it is characterized in that described clay is a kind of layer silicate mineral, its essential mineral composition is the layer aluminosilicate of the montomorillonite of 85-93%, this clay is handled through n-alkyl amino acid (n=6-12) properties-correcting agent, the organic clay of optimum for forming after ten diamino acid ion exchange treatment.
3. the preparation method of a kind of polysulfonamides/clay nanocomposites according to claim 1 is characterized in that described aromatic diamines can be Ursol D, mphenylenediamine, mainly is 4 ' 4 diaminodiphenylsulfone(DDS)s, 3 ' 3 diaminodiphenylsulfone(DDS)s.
4. the preparation method of a kind of polysulfonamides/clay nanocomposites according to claim 1, it is characterized in that described neutralization with alkali can be calcium oxide, to be neutralized to pH value be 6-7.
5. the preparation method of a kind of polysulfonamides/clay nanocomposites according to claim 1, when it is characterized in that described aromatic diamines can be 4 ' 4 diaminodiphenylsulfone(DDS)s and/or 3 ' 3 diaminodiphenylsulfone(DDS)s, then polysulfonamides specifically is expressed as the Polyphenylene Sulfone acid amides.
CNB031514545A 2003-09-29 2003-09-29 Method for preparing polysulfoneamide/claynano composite material Expired - Fee Related CN1264925C (en)