CN1525104A - Method for preparing coal water slurry - Google Patents
Method for preparing coal water slurry Download PDFInfo
- Publication number
- CN1525104A CN1525104A CNA031047203A CN03104720A CN1525104A CN 1525104 A CN1525104 A CN 1525104A CN A031047203 A CNA031047203 A CN A031047203A CN 03104720 A CN03104720 A CN 03104720A CN 1525104 A CN1525104 A CN 1525104A
- Authority
- CN
- China
- Prior art keywords
- water
- coal
- slurry
- add
- raw coal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a water coal slurry preparing method, its character: crush raw coal into particles less than 20 mm, make dry pre-milling by erect mill, the particle size 70-80 mum, then add into blender and add in water and assistant to blend and mix in the weight ratio of raw coal to water to assistant 65 : 34 : 1, then finely mill by vibrating muller and add in stabilizing agent at 1% of water coal slurry weight, and finely mill until the average particle size is 40-50mum, thus preparing it at once, and able to make it into 18-25% water containing powders by filtering. It has advantages and effects of enhancing the fineness and slurrying property, enhancing producing ability, reducing electricity consumption, etc.
Description
Technical field
The present invention relates to a kind of preparation method of water-coal-slurry, belong to the raw coal manufacture field.
Background technology
Water-coal-slurry is a kind of novel clean fuel, now is listed in the energy policy and the environmental protection policy of " replace oil with coal, compression crude oil ".The preparation method of water-coal-slurry carries out the wet grinding pulping with various ball mills usually at present, though require very high to raw coal quality, but a small amount of coal spoil is arranged unavoidably, add ball mill and do not have classification, cause the granularity of water-coal-slurry inhomogeneous, even thick partially, this water-coal-slurry can only be used for cauldron, and arcola can't use because nozzle is little.
Summary of the invention
Purpose of the present invention is the shortcoming and deficiency in order to overcome above-mentioned prior art just, and the preparation method of the water-coal-slurry of a kind of first dry type pre-grinding rewetting formula fine grinding is provided, thereby improves water-coal-slurry fineness and paste-forming properties, enlarges the scope of application, has reduced cost.
The objective of the invention is to realize by following technical proposal:
The preparation method of water-coal-slurry, it is characterized in that earlier raw coal being crushed to less than 20mm, carry out dry type pre-grinding with vertical mill again, granularity is 70-80 μ m, adds in the mixer then and adds water and the water-coal-slurry auxiliary agent mixes, raw coal: water: the percentage by weight of auxiliary agent is 65: 34: 1, carry out fine grinding with oscillating mill again, and the coal water mixture stabilizing agent of adding water-coal-slurry weight 1%, being milled down to particle mean size is 40-50 μ m, promptly makes water-coal-slurry.
But described water-coal-slurry also filtering means dehydration is made the powder of moisture 18-25%.
Preparation method of the present invention adopts vertical mill can make the bulky grain pre-classification, make the vibromill of fine grinding enlarge output, this vibromill can add material mixing, stirring and auxiliary agent, fine gtinding once be finished, and has improved operating efficiency, cuts down the consumption of energy, stable production process.
Water-coal-slurry auxiliary agent of the present invention and stabilizing agent are that to produce the trade mark by Kunshan, Jiangsu Province enlightening elder brother Fine Chemical Works be SWF.
Owing to take technique scheme to make the technology of the present invention compared with the prior art have following advantage and effect:
A) because two sections grindings have improved water-coal-slurry fineness and paste-forming properties;
B) because pre-grinding has reduced bulky grain and made fine grinding improve production capacity, save energy consumption, reduced cost;
C) water-coal-slurry is made filter cake or is filtered powder and is convenient to transportation, also can reduce the transportation raw coal and cause environmental pollution in producing coal ground production water-coal-slurry, and be that energy policy and environmental protection policy organically combine.
The specific embodiment
Embodiment 1
Getting Inner Mongol raw coal 650kg is crushed to less than 20mm and carries out dry type pre-grinding with vertical mill again, granularity is 70-80 μ m, add in the mixer then and add 340kg water and 10kg water-coal-slurry auxiliary agent adds coal water mixture stabilizing agent 10kg with oscillating mill again after mixing and carries out fine grinding, particle mean size is 40-50 μ m, promptly makes water-coal-slurry.
Embodiment 2
Embodiment 1 is made water-coal-slurry filter, obtain moisture 18% powder with filter.
Embodiment 3
Embodiment 1 is made water-coal-slurry filter, obtain moisture 25% powder with filter.
Claims (2)
1, a kind of preparation method of water-coal-slurry, it is characterized in that earlier raw coal being crushed to less than 20mm, carry out dry type pre-grinding with vertical mill again, granularity is 70-80 μ m, adds in the mixer then and adds water and the water-coal-slurry auxiliary agent mixes, raw coal: water: the percentage by weight of auxiliary agent is 65: 34: 1, carry out fine grinding with oscillating mill again, and the coal water mixture stabilizing agent of adding water-coal-slurry weight 1%, being milled down to particle mean size is 40-50 μ m, promptly makes water-coal-slurry.
2, preparation method according to claim 1, but it is characterized in that described water-coal-slurry also filtering means dehydration make the powder of moisture 18-25%.